• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.7
• /
• pp.77-82
• /
• 2019

In this study, we study the change of surface roughness during cutting machining by changing the cutting conditions such as feed rate and spindle velocity with chromium molybdenum steel (SCM415) material and TiCN and TiAlN coated end mill tools. The surface roughness value of the test specimen for SCM415, was found to be 3,000 rpm in TiCN coated end mill and $0.634{\mu}m$ in surface roughness at a feed rate of 100 mm/min. In the TiAlN coated end mill, 300 mm/min, the surface roughness was the best at $0.699{\mu}m$. The overall average surface roughness of each coating tool was better than that of TiAlN.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.10 no.2
• /
• pp.84-89
• /
• 2011

This paper studied the carburizing of chromium molybdenum steel which the heat treatment effect of gear geometric tolerance, OPD, Runout, the surface hardness, the maximum hardness, the core hardness and the bending fatigue strength were investigated. Firstly, the deformation is observed, and the results of circularity, squareness, OPD and Runout of SCM822, SCM425, and SCM415 are obtained in order. Secondly, in order to investigate the gear hardness, the surface hardness, the maximum hardness and the core hardness of SCM822, SCM425, and SCM415 are obtained; and the surface hardness of SCM822 is about 10% higher than SCM415's, and about 3% higher than SCM425's. Thirdly, the fatigue strength of SCM822 is about 10% higher than SCM415's, and about 7% higher than SCM425's in the fatigue test results. At last, for the purpose of the minimum deformation of heat treatment, and also the improvement of fatigue strength, the best gear material is SCM822 in this test.

• Tribology and Lubricants
• /
• v.26 no.3
• /
• pp.162-166
• /
• 2010

The purpose of this study is to show the friction and wear characteristics on the vapor deposited Tiseries coating layers on the SCM415 steel. In this research, frictional wear characteristic of coating materials such as TiN, TiCN, TiAlN was investigated under room temperature, normal air pressure and dry lubricating condition. Therefore this study carried out research on the friction coefficient, micro hardness(Hv), roughness, SEM on the vapor deposited coating layers on the SCM415 steel.

• Journal of the Korean Society of Safety
• /
• v.14 no.4
• /
• pp.20-27
• /
• 1999

The standard of the allowed stress in designing components such as shafts used in machinery and aircraft should be determined. It is very important to estimate fatigue strength of a component analytically, because service stress of the components is usually under the level of its fatigue limit. Improving the fatigue strength of each component in machinery is essential for high performance, lightness, and endurance. Surface treatment of components is widely used for these purpose. In this research, the fatigue behaviors of SCM415 steel and carbonitried SCM415 steel are examined. In the analysis of the fatigue behaviors of the carbonitrided SCM 415 steel, we propose a modified fatigue strength evaluation model and modified formulae.

• Korean Journal of Materials Research
• /
• v.3 no.5
• /
• pp.538-545
• /
• 1993

By using propagation characteristics of ultrasonic surface wave, the depth of the surface hardened layer of SCM440 steel with different high frequency induction heat treatments was measured and the same was done on the carburized SCM415 steel. The propagation velocity of surface wave was constant and independent of frequency in t.he specimens with identical microstructure, it was, however, decreased by 59m/s in the hardened layers compared to the unhardened part. From t.he relationship between the effective case depth and the wave length of surface wave, the depth of the hardened layer could be measured and evaluated nondestructively for both induction hardened and carburized steels.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.10
• /
• pp.873-878
• /
• 2016

SCM415 steel for the control valve undergoes wear because of continuous movement between the valve and valve case. The wear of the valve interrupts the performance of the valve, and decreases the service life. In this study, wear characteristics of the as-received and carburized SCM415 steels are evaluated. The wear tests are conducted for various temperatures and loads using a reciprocating wear tester. From these results, wear loss, specific wear rate, and coefficient of friction are analyzed. The wear mechanism was analyzed by SEM. The interaction effects between loads and temperatures on wear loss are determined for analysis of variance using MINITAB.

• Korean Journal of Materials Research
• /
• v.8 no.8
• /
• pp.707-713
• /
• 1998

The influence of plasma carburizing process on the surface hardness of SCM415 low-alloy steel (0.15% C) was investigated under the various process conditions of gas composition. gas pressure, plasma current density. temperature and time. The effective case depth was found to depend on the amount of methan gas containing carbon. thus the deepest case depth and the uniform hardeness were obtained with the 100% methan gas. The case depth increased with the plasma current density. The effective plasma carburizing temperature of SCM415 steel was found to be higher than 85$0^{\circ}C$, and the case depth was proportional to the square root of carburizing time under the same current density. The bending fatigue strength of the plasma carburized specimen is' higher than those of as- received specimen or reheat-quenched specimen.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.5
• /
• pp.27-34
• /
• 2021

This study analyzes machining characteristics and presents optimal cutting conditions by measuring the surface roughness, dimensional accuracy, and dimension straightness based on the feed rate after processing the inner diameter hall of SCM415 steel using an automatic CNC(Computerized Numerical Control) lathe. The testing material was cut using an 11.8 mm-diameter Chamdrill after mounting the 32 mm-diameter round bar on an automatic CNC lathe. The cut depth was set at 3 mm, and the cutting speed was fixed at 1500 rpm. The surface roughness, dimensional accuracy, and dimension straightness of 15 testings were measured by changing the feed rate to 0.05, 0.1, and 0.15 mm/rev, respectively. It was difficult to process more than 15 tests during the maching due to noise or break. Additionally, the optimum cutting of SCM415 steel showed excellent surface roughness in the 10^th and 11^th of testing at cutting speed and feed speed of 1500 rpm and 0.05 mm/rev, respectively. The dimensional accuracy was measured in three dimensions after drilling, which showed good results with an average range of 0.0138-0.0208 mm. Moreover, the lower the feed speed, the higher the accuracy. Additionally, the measurement results of the dimensional straightness showed that the straightness is the straightness was the best at the 1^th and 2^th cutting regardless of the feed speed.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.4
• /
• pp.23-30
• /
• 2022

Small-scale production is increasing, and the manufacturing industry is gradually changing into a smart manufacturing industry. Therefore, research on securing optimal cutting conditions for factors affecting machining precision during cutting is very important. Therefore, the purpose of this study is to After machining the inner diameter hole of SCM415 steel with a cermet tool on a CNC automatic lathe, the surface roughness, dimensional accuracy, and dimensional straightness are measured according to the feed rate to analyze the machining characteristics and suggest optimal cutting conditions. The test material was cut using a cermet tool for secondary cutting after a round bar with a diameter of 20 mm was mounted on a CNC automatic lathe. The cutting length was fixed at 0.5 mm, and the cutting speed was fixed at 3200 rpm. When the feed rate was changed to 0.05, 0.1, and 0.15 mm/rev, the respective surface roughness during the 15th test was measured. Consequently, The lower the feed rate, the better is the surface roughness. In addition, the optimum cutting conditions for SCM415 steel were observed to be the most ideal cutting conditions than the condition of 0.05 mm/rev at a cutting speed of 3,200 rpm and a feed rate of 0.1 mm/rev.

• Journal of the Korean Society for Precision Engineering
• /
• v.15 no.2
• /
• pp.90-98
• /
• 1998

Forging of internal involute gears with alloy steel has been analyzed by means of upper bound method. Kinematically admissible velocity fields for forging of internal gear were proposed. It was assumed that the shape of free flow surface during forging operation is a straight line perpendicular to the plane of symmetry. Using the suggested velocity fields, forging loads and relative pressures were calculated by numerical method. Consequently forging die should be successfully designed without fracture or failure during forging operation. Experiments were carried out with the designed die and SCM415 alloy steel as billet material. The calculated loads were compared with experimental one and they are in good agreement with experimental inspections. As a result, the calculated solutions would be useful to predict the loads and the designed die is suitable for forging of internal involute spur gear with alloy steel. The forged gear is measured to be KS 4 class and its class should be improved by subsequent working such as shaving after forging operation.