• Bulletin of the Korean Chemical Society
• /
• 제19권2호
• /
• pp.174-178
• /
• 1998

Blowout of NR and SBR vulcanizates was studied using a microwave oven. Rubber vulcanizates with different contents of carbon black (0, 30, 50, 70 phr) and various cure systems (conventional, semi-EV, and EV) were prepared. Unfilled rubber vulcanizates did not exploded by irradiation of microwave, while carbon black-filled ones exploded within 10 min. A blowout time of the carbon black-filled rubber vulcanizate decreases with an increase of the content of carbon black in the vulcanizate. A blowout temperature of the organic additive-extracted vulcanizate is higher than that of the not-extracted one, but the extracted vulcanizate blows out faster than the not-extracted one. A blowout temperature of the overcured vulcanizate is higher than that of the undercured one with the same cure system. Temperatures of unfilled SBR vulcanizates heated by the microwave irradiation are lower than those of unfilled NR ones. The carbon black-filled SBR vulcanizates blow out at higher temperatures than the carbon black-filled NR ones. Blowout times of the carbon black-filled SBR vulcanizates are longer than those of the carbon black-filled NR ones.

• Elastomers and Composites
• /
• 제40권4호
• /
• pp.237-241
• /
• 2005

스티렌 함량이 SBR 가황물의 회복 거동에 미치는 영향에 대해 연구하였다. 스티렌 함량이 15와 21 wt%인 SBR을 사용하였다. 스티렌 함량이 적은 가황물이 스티렌 함량이 많은 가황물에 비해 더 낮은 온도에서 회복하기 시작하였으며, 스티렌 함량이 적은 가황물의 회복 속도가 스티렌 함량이 많은 가황물보다 느렸다. 두 가황물 간의 회복 차이는 카본블랙으로 보강된 가황물이 실리카로 보강된 것보다 컸다. 실험 결과는 유리전이온도와 모듈러스로 설명하였다.

• Elastomers and Composites
• /
• 제17권3호
• /
• pp.151-158
• /
• 1982

The purpose of this study is to get comparitive results on the combined accelerator systems comprised of MBT, MBTS, DPG and CBS with TMTD, TMTM, Zn-MDC and DPG to SBR compound. Vulcanization characterstics and physical properties of the combined accelerators have been studied by mean of the Mooney viscometer, tensile testing machine, aging chamber and so on. According to the test results, TMTD with DPG system has shown faster Mooney scorch time than other system. The vulcanizate comprise of Zn-MDC with DPG and TMTD with DPG accelerator system has taken advantage of heat resistance.

• Elastomers and Composites
• /
• 제42권2호
• /
• pp.102-106
• /
• 2007

카본블랙, 커플링제가 없는 실리카, 그리고 커플링제를 함유한 실리카 등 다른 충전 시스템을 갖는 SBR 가황물의 수팽윤 거동에 대해 연구하였다. 증류수와 3.5% NaCl 용액을 팽윤 매질로 사용하였다. 증류수에서의 수팽윤비가 소금물에서의 그것보다 높았다. 카본블랙으로 보강된 가황물의 수팽윤비가 실리카로 보강된 것보다 낮았다. 실리카로 보강된 SBR 가황물의 경우, 커플링제가 없는 것이 커플링제를 함유한 것보다 더 큰 수팽윤비를 나타내었다. 1,2-유니트 함량이 다른 SBR 가황물의 수팽윤 거동에 대해서도 비교하였다. 수팽윤비는 1,2-유니트 함량이 증가함에 따라 감소하는 경향을 보였다.

• Elastomers and Composites
• /
• 제17권4호
• /
• pp.215-225
• /
• 1982

The purpose of this study is to get comparitive results on the combined accelerator systems comprised of MBT, MBTS, DPG and CBS with TMTD, TMTM and Zn-MDC to SBR compound. Vulcanization characterstics and physical properties of the combined accelerators have been studied by means of the Mooney viscometer, the Monsanto disc rheometer, tensile testing machine, aging chamber and so on. According to the test results, DPG, MBT and Zn-MDC system have show faster Mooney scorch time and optimum cure time than other systems. The Vulcanizate comprise of DPG, MBT and TMTD accelerator system has taken adventage of tensile strength, elongation, 100% modulus, resilience, compresion set.

• Elastomers and Composites
• /
• 제17권2호
• /
• pp.77-90
• /
• 1982

The purpose of this study is to get comparative results on the combined antioxidant systems comprised of MHPPD with IPPD, MHPPD with PBN and MHIPPD with MB when they are individually added to NR and SBR compound. Vulcanization characterstics and physical properties of the combined antioxidants have been studied by means of the Mooney viscometer, the Monsanto disc rheometer and so on. According to the test results, MHPPD with IPPD system has shown faster cure rate, better optimum cure time and shorter scorch time than other systems. The vulcanizate comprised of the MHPPD with IPPD antioxidant system has taken advantage of heat resistance, fluid resistance and antiozone resistance.

• Elastomers and Composites
• /
• 제50권3호
• /
• pp.196-204
• /
• 2015

Crosslink density of a rubber vulcanizate determines the chemical and physical properties, while bound rubber is an important factor to estimate reinforcement of a filled rubber compound. Extender oil is added to a raw rubber with very high molecular weight for improving processability of a rubber composite. Influence of extender oil on crosslink density, bound rubber formation, and physical properties of solution styrene-butadiene rubber (SSBR) composites with differing microstructures was investigated. Crosslink densities of non-oil-extended SSBR (NO-SSBR) vulcanizates were higher than those of oil-extended SSBR (OE-SSBR) ones. Bound rubber contents of NO-SSBR compounds were also greater than those of OE-SSBR ones. The experimental results could be explained by interfering of extender oil. The OE-SSBR vulcanizates had low modulus but long elongation at break, whereas the NO-SSBR ones had high modulus but short elongation at break. It was found that the crosslink densities affected the physical properties more than the bound rubber contents. The moduli increased with increase in the crosslink density irrespective of extender oil, while the elongation at break decreased. Each variation of the tensile strengths of NO-SSBR and OE-SSBR vulcanizates with the crosslink density showed a decreasing trend. Tear strength of the OE-SSBR vulcanizate increased with increase in the crosslink density, whereas variation of the tear strength of NO-SSBR vulcanizate with the crosslink density showed a weak decreasing trend.

• Elastomers and Composites
• /
• 제44권4호
• /
• pp.397-400
• /
• 2009

오존은 상온에서 폴리머 이중 결합의 산화작용을 활발하게 하여 표면 갈라짐을 유발시킨다. 왁스는 고무 표면으로 이동하여 물리적 방어막을 형성하여 오존의 작용을 방지한다. 비보강 NR, SBR, BR 가황물을 상온에서 6개월간 노화 시켜 노화 전후의 왁스의 분자량 분포 변화를 조사하였다. 상온 조건에서 고무 가황물에 있는 왁스의 이동과 증발 거동은 노화방지제로서의 왁스의 역할과 고무 제품의 외관 오염을 이해하는데 도움을 준다. NR 시험편에서 알칸의 상대 세기 분포는 노화 후 고분자량쪽으로 이동하였으나 SBR 시험편의 경우에는 노화 전후의 분자량 분포 모양에는 큰 차이가 없었다.

• Elastomers and Composites
• /
• 제30권1호
• /
• pp.20-31
• /
• 1995

The purpose of this study is to investigate the reinforcement of inorganic filler silica, treated by MDI about SBR vulcanizate. The characteristics of vulcanization, physical properties, surface properties and dynamic properties were investigated after mixing those silica with SBR and unmodified silica with SBR. In this experiment only the quantity of silica was variable. In the vulcanization characteristics tested by rheometer, S-series showed the fastest scorch $time(t_{10})$ and optimum cure $time(t_{90})$. And in test or tensile characteristics hardness, tensile strength, 100%, 300% modulus and elongation were all appeared in the order of M>S-series. The characteristic bonding of urea between unmodified silica and MDI could be confirmed in IR spectrum. The shapes of silicas treated chemically were observed by SEM. And the dispersion of the filler in the SBR composite was uniform. In the dynamic characteristics by the RDS, the order of elastic modulus G' values was as follows : M>S-series, and also the order of damping values was as follows : M>S-series.

• Elastomers and Composites
• /
• 제29권1호
• /
• pp.18-29
• /
• 1994

The purpose of this study is to investigate reinforced effect between silica treated by coupling agents and rubber matrix under the configuration chemical bonds, and the effect of silica particles coated by organic polymers using aluminum chloride as the catalyst. In vulcanization characteristies were tested by Curastometer. The M-series vulcanizates were reached to the fastest optimum cure $time(t_{90})$ and R-series vulcanizates with the same formula had the shorted optimum cure times. Tensile characteristics measuring with a tensile tester revealed that the M-series vulcanizate was the best in the physical properties, such as tensile strength. In 100% modulus, however, the S-series vulcanizates appeared to be better than the other vulcanizates. Also, hardness showed the following order : S-series>R-series>M-series with the order of elongation R-series>M-series>S-series. In SEM test, shapes of chemical treated silicas were observed. The dispersion of filler in the SBR composite appeard uniformly. In RDS test for the dynamic characteristics, G' indicates that S-3 shows the highest value with the next order M-3>R-3, and the order of damping values are as followe: M-3>M-3>R-3.