본 실험에서 SA508 CL.3 강재의 서브머지드아크 용접부에 대한 연구로 입열량의 차이에 따라서 인성과 미세조직과의 관계를 조사하였다. 강도가 크면 인성이 작아지고 연성이 작아지는 것을 확인하고, 입열량이 3-5kJ/$\textrm{mm}^2$를 표준으로 하는데, 본 실험에서는 1.6kJ/$\textrm{mm}^2$, 3.2kJ/$\textrm{mm}^2$, 5.0kJ/$\textrm{mm}^2$ 세 가지 조건으로 실험해 보았다. (중략)

• Proceedings of the Korean Nuclear Society Conference
• /
• 2004.05a
• /
• pp.330-330
• /
• 2004

• Journal of Welding and Joining
• /
• v.13 no.2
• /
• pp.139-149
• /
• 1995

Many pressure vessels for the power plants are fabricated from low alloy ferritic steels. The inner sides of the pressure vessels are commonly weld_cladded with austenitic stainless steels to minimize problems of corrosive attack. The submerged-arc welding(SAW) process is now used in preference to other processes because of the possibilities open to automation to reduce the overaII welding times. The most reliable way to avoid underclad cracks(UCC) which are often detected at the overlap of the clad beads is to use nonsusceptible steels such as SA508 class 3. At present domestically developed forging steel of SA508 cl.S is now being cladded with single layer by using 90mm wide strip, which transfers higher heat input into the base metal compared to the conventional two layers strip cladding which has been in wide use with 30-60 mm wide strip. But the current indices for the influence of heat input on crack susceptibility are not accurate enough to express the subtle difference in crack susceptibility of the steel. Therefore, the purpose of this present study is: l) To determine UCC susceptibility on domestic forging steel, SA508 cl.S cladded with single layer by using submerged arc 90mm strip and, 2) To optimize heat input range by which the crack susceptibility could be eliminated.

• Journal of Welding and Joining
• /
• v.22 no.5
• /
• pp.38-45
• /
• 2004

The present study is to investigate the effect of heat input on the microstructure, tensile properties and toughness of single-pass submerged arc bead-in-groove welds produced on SA508 class 3 steels. The heat input was varied in the range of 1.6, 3.2 and 5.0 kJ/mm. The toughness of weld metals was evaluated by using subsize Charpy V-notch specimens in the temperature range of -19$0^{\circ}C$ to 2$0^{\circ}C$. The weld microstructure and fractography were observed by optical and scanning electron microscopies, respectively. With increasing heat inputs, tensile strength and hardness of weld metals were decreased while elongation was increased. The poor notch toughness at 1.6 kJ/mm was attributed to the formation of ferrite with aligned second phase and banitic microstructure with high yield strength while that at 5.0 kJ/mm was due to the presence of grain boundary and polygonal ferrites. The microstructure of the intermediate energy input welds consisted of a high proportion of acicular ferrite with limited polygonal ferrites, which provide improved notch toughness.

• Proceedings of the Korean Nuclear Society Conference
• /
• 2003.05a
• /
• pp.243.2-243.2
• /
• 2003

• Journal of Welding and Joining
• /
• v.28 no.5
• /
• pp.69-74
• /
• 2010

Irradiation behavior of the reactor pressure vessel SA508 class 3 steel weld metals was examined by Charpy V Notch impact specimens. The specimens were exposed to a fluence of $2.8{\times}1019$ neutrons(n)/$cm^2$(E>1 MeV) at $288^{\circ}C$. The irradiation damage of weld metal was evaluated by comparison between unirradiated and irradiated specimens in terms of absorbed energy and lateral expansion. The specimens for neutron irradiation were welded by submerged arc welding process at a heat input of 3.2 kJ/mm which showed good toughness in terms of weld microstructure, absorbed energy and lateral expansion. The post-irradiation Charpy V notch 41J and 68J transition temperature elevation were $65^{\circ}C$ and $70^{\circ}C$, respectively. This elevation was accompanied by a 20% reduction in Charpy V notch upper shelf energy level. The lateral expansion at 0.9mm irradiated Charpy specimens showed temperature elevation of $65^{\circ}C$ and was greatly decreased due to radiation damage.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.390-396
• /
• 2000

The dynamic elastic constants of the simulated weld HAZ (heat-affected zone) of SA 508 Class 3 reactor pressure vessel (RPV) steel were investigated by resonant ultrasound spectroscopy (RUS). The resonance frequencies of rectangular parallelepiped samples woe calculated from the initial estimates of elastic stiffness $c_{11},\;c_{12}\;and\;c_{44}$ with an assumption of isotropic property, dimension and density. Through the comparison of calculated resonant frequencies with the measured resonant frequencies by RUS, very accurate elastic constants of SA 508 Class 3 steel were determined by iteration and convergence processes. Clear differences of Youngs modulus and shear modulus were shown from samples with different thermal cycles and microstructures. Youngs modulus and shear modulus of samples with fine-grained bainite were higher than those with coarse-grained tempered martensite. This tendency was confirmed from other results such as micro-hardness test.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.08a
• /
• pp.127.1-127
• /
• 1998

• Proceedings of the Korean Nuclear Society Conference
• /
• 1998.05b
• /
• pp.305-311
• /
• 1998

최근들어 고려된 LBB(Leak Before Break) 적용요건중 동적파괴시힘 절차에는 울진 3&4호기 이후 파단전누설개념이 적용되는 배관이 탄소강으로 제작될 경우. 이 배관이 Dynamic Strain Aging (DSA)에 의해 파괴저항치가 감소되지 않는다는 것이 정량적으로 입증되지 않는 한, 동 배관의 파괴 물성치 결정시 DSA의 영향이 고려되어야 하며, DSA 영향을 평가하기 위해서는 동적과괴시험이 수행되어야 함을 요건화 하고 있다. 본 연구에서는 DSA 효과에 의한 파괴저항(J-R) 특성의 저하가차세대원전 원자로냉각재배관 파단전누설개넘(LBB) 적용시 설계 안전여유도에 영향을 미치지 않는 정도임을 평가하는데 있다. 따라서 ASME Section III에서 탄소강으로 분류하고 있는 강종별 파괴인성 변화를 고찰하고, 차세대원전 주냉각재배관 재료인 SA508 Class la의 최대 파괴인성 감소치를 예측하여, 울진 3&4호기에서 측정된 엘보우용 SA516-Gr.70 강의 DSA 영향 평가 결과와 비교 분석하여 차세대원전 주냉각재배관의 DSA영향을 평가하였다. 도출된 결론으로는 DSA 영향을 고려한 SA508 Class la의 J 및 dJ/dA 값은 극히 보수적으로 추정할 때 50% 이상 감소하는 것으로 예측된다. 이러한 DSA 영향을 고려하였을 경우 배관재 모재의 파괴인성치는 Weld-SAW의 J/T 값 수준으로 감소하였다. 그러나 현 LRB 해석이 가장 낮은 J/T값을 갖는 Weld-SAW Auto의 균열길이 2a인 J/T선도에 의거하여 수행되고 있다는 점을 고려한다면 비록 DSA가 배관재에 영향을 주는 가장 보수적인 값(J 및 dJ/dA값을 50% 이상)을 사용한다고 하더라도 차세대원전 LBB 적용에 문제가 되지 않음을 알 수 있다. 즉 차세대원자로 주냉각재배관에 LBB를 적용하는데는 DSA 영향은 상대적으로 중요하지 않다는 결론을 얻었다. 표면에 수소화물이 농축되어 있는 hydride layer가 형성됨을 관찰하였으며 ～5,000ppm 이상의 경우에는 수소화물의 방향성이 random하였으며 특히, ZIRLO$^{TM}$ 시편의 경우에서는 원주방향으로 길게 이어진 수소화물과 기계적 성질에 치명적인 반경방향의 수소화물이 평행하게 배열된 것을 관찰하였다.하였을 때는 Li$_2$O의 첨가에 의해 치밀화가 주로 일어났고, 반면에 $N_2$-7vol.%H$_2$ 분위기에서 소결하면 Li$_2$O의 첨가에 의해 작은 기공은 소멸되고 큰 기공이 생성되었다.지나치게 모국어의 영향만 강조하고 다른 요인들에 대해서는 다분히 추상적인 언급으로 끝났지만 이 분석을 통 해서 배경어, 목표어, 특히 중간규칙의 역할이 괄목할 만한 것임을 가시적으로 관찰할 수 있 다. 이와 같은 오류분석 방법은 학습자의 모국어 및 관련 외국어의 음운규칙만 알면 어느 학습대상 외국어에라도 적용할 수 있는 보편성을 지니는 것으로 사료된다.없다. 그렇다면 겹의문사를 [-wh]의리를 지 닌 의문사의 병렬로 분석할 수 없다. 예를 들어 누구누구를 [주구-이-ν가] [누구누구-이- ν가]로부터 생성되었다고 볼 수 없다. 그러므로 [-wh] 겹의문사는 복수 의미를 지닐 수 없 다. 그러면 단수 의미는 어떻게 생성되는가\ulcorner 본 논문에서는 표면적 형태에도 불구하고 [-wh]의미의 겹의문사는 병렬적 관계의 합성어가 아니라 내부구조를 지니지 않은 단순한 단어(minimal $X^{0}$ elements)로 가정한다. 즉, [+wh] 의미의 겹의문사는 동일한 구성요 소를 지닌 병렬적 합성어([$[W1]_{XO-}$ $[W1]_{XO}$ ]$_{XO}$)로

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.17-22
• /
• 1997

ASME SA508 Class 3 원자로압력용기강을 대상으로, 용접열영향부(heat affected zone, HAZ)의 최고온도(peak temperature) 등온분포도(isothermal diagram)를 작성 및 해석하였고, 재현(simulated) 열영향부 시험편을 제작하여 미세조직검사 및 기계적특성 시험을 실시하였다. 그 결과, 최고온도 등온분포도를 이용하여, 미소열영향부(subzone of HAZ)의 미세조직(microstructure)에 미치는 예열(preheat)온도와 용접입열량(weld heat input)의 크기 효과를 예측할 수 있었다. 또한, 재현 HAZ 의 기계적특성 시험결과, 용접용융선(fusion line) + 1 mm 이내의 위치로 대표되는 열 cycle 조건에서는 모재보다 양호한 강도와 인성을 보였고, 용접용융선 + 2~3mm부근에서 가장 미세한 조직(fine tempered lower bainite)과 우수한 충격인성을 나타냈다. 한편, 용접용융선 + 약 5mm 위치에서의 열 cycle 을 재현한 시험편에서는 미세조직의 변화(spheroidization of carbides)와 함께 인성 및 기계적 특성이 저하하여 모재보다 낮은 값을 보이는 것을 발견할 수 있었다.