• Journal of the Korean Society for Heat Treatment
• /
• v.36 no.6
• /
• pp.382-388
• /
• 2023

In this study, hydrogen embrittlement (HE) behavior of a SA-723 steel via controlling gaseous hydrogen pre-charging condition has been analyzed. The gaseous hydrogen charging of the SA-723 steel was performed under a constant pressure of 20 MPa of gaseous H₂ at 150℃ and 300℃ for 2 and 6h, and TDS, SSRT and Charpy tests were conducted to analyze the hydrogen embrittlement (HE) behavior of the SA-723 steel. Furthermore, prior to commencing the test, these specimens were coated with Zn to prevent hydrogen from diffusing out of a specimen during the tests. The TDS results showed that the 300℃-6h and 150℃-6h charged steels contain larger amounts of hydrogen than 300℃-2h and 150℃-2h charged steel. The SSRT and Charpy test results also showed the similar trends that the mechanical properties of the steels deteriorate as the amount of hydrogen charged in the steel increases. Therefore, this study suggests that, for SA-723 steel, the charging time parameter is more effective to charge more amount of hydrogen into SA-723 steel, rather than the charging temperature.