• 한국응용과학기술학회지
• /
• 제28권3호
• /
• pp.321-328
• /
• 2011

The autothermal reforming reaction of methane was investigated to produce hyd rogen with Ni/$CeO_2-ZrO_2$, Ni/$Al_2O_3$-MgO and Ni-Ru/$Al_2O_3$-MgO catalysts. Honeycomb metalli c monolith was applied in order to obtain high catalytic activity and stability in autothermal r eforming. The catalysts were characterized by XRD, BET and SEM. The influence of various catalysts on hydrogen production was studied for the feed ratio($O_2/CH_4$, $H_2O/CH_4$). The $O_2/CH_4$ and $H_2O/CH_4$ ratio governed the methane conversion and temperature profile of reactor. Th e reactor temperature increased as the reaction shifted from endothermic to exothermic reactio n with increasing $O_2/CH_4$ ratio. Among the catalysts used in the experiment, the Ni-Ru/$Al_2O_3$-MgO catalyst showed the highest activity. The 60% of $CH_4$ conversion was obtained, and th e reactor temperature was maintained $600^{\circ}C$ at the condition of GHSV=$10000h^{-1}$ and feed ratio S/C/O=0.5/1/0.5.

• 한국자기학회지
• /
• 제18권4호
• /
• pp.136-141
• /
• 2008

Ru-Co가 복합 치환된 M-type Ba-ferrite($BaFe_{12-2x}Ru_xCo_xO_{19}$)의 치환량 x의 변화에 따른 자기적 특성과 전파흡수 특성에 관해 조사하였다. 기존의 Ti-Co를 치환시킨 경우보다 적은 양의 치환(x=0.3)으로 면내 자기이방성을 보이는 낮은 보자력($H_c$)과 높은 포화자화($M_s$) 값을 얻을 수 있었다. 따라서 Ru-Co 치환량 조절에 의해 GHz 대역에서 자연공명주파수의 조절이 가능하였다. 소결체 및 복합체에서 흡수 주파수 대역은 보자력이 증가할수록 고주파 대역으로 이동한다. 복합체에서 페라이트 혼합량이 증가함에 따라 복소투자율과 복소유전율의 값이 증가하기 때문에 정합주파수는 저주파 대역으로 이동한다. 이러한 특성들을 이용하여 순수한 M-형 육방정 페라이트에 Ru-Co의 치환량, 복합체에서 페라이트 분말의 혼합량, 그리고 흡수체의 두께의 제어를 통하여 GHz 주파수 대역에서 양호한 전자파 흡수체, 노이즈 감쇠재의 제조가 가능함을 제시할 수 있다.

• 한국세라믹학회지
• /
• 제30권11호
• /
• pp.974-978
• /
• 1993

Glass viscosity effects on the electrical properties and microstructure of RuO2 based thick film resistors (TFR) using alumina modified lead borosilicate glasses were studied. AT 85$0^{\circ}C$, the glass viscosities were increased from 4.24Pa.s to 51.5Pa.s when the alumina was added from none to 14 weight percent to the standard glass of 63% PbO, 25% B2O3 and 12% SiO2. The resistivities of resistors were generally decreased and the microstructure development was retarded as the viscosity of the glass increased. This is contrary to the generally accepted thought that the low resistivity is due to fast microstructure development kinetics in TFR. Even though the glass viscosity retards the microstructure development kinetics, the overall network formations are favored for higher viscosity of glass, such that the sheet resistivities were decreased as the glass viscosity increased.

• 한국수소및신에너지학회논문집
• /
• 제25권5호
• /
• pp.459-467
• /
• 2014

The catalytic steam reforming of toluene, a major component of biomass tar, was studied using several catalysts at various temperatures $400-800^{\circ}C$, kind of metal, and metal loading content. Ru and K promoted Ni-base catalyst were prepared, and used for steam reforming of toluene with steam/toluene molar ratio of 25. Concentration of toluene in reactant flow is $30g/Nm^3$ that is usual content of tar from biomass gasifier. The result from experiments showed that $H_2$ content in product gas and toluene conversion increased with temperature. Where in high temperature range, CO and $CO_2$ content in product gas were affected mainly by Boudouard reaction. Ni/Ru-K(3wt%)/$Al_2O_3$ catalyst showed best performance on steam reforming of toluene than used catalysts in this study at whole temperature. Catalysts have been characterized by XRD, TG. XRD analysis displayed that Ni particle size on Ni/Ru-K (3wt%)/$Al_2O_3$ catalyst was 29.4nm. Activation energy of Ni/Ru-K (3wt%)/$Al_2O_3$ catalyst was calculated 36.8kJ/mol by Arrhenius plot.

• 센서학회지
• /
• 제20권2호
• /
• pp.82-89
• /
• 2011

Ruthenium(Ru)-doped $TiO_2$ nanofibers were prepared using electrospun Ru-$TiO_2$/poly(vinyl acetate) (PVAc) fibers and subsequent annealing for 1 h at temperatures in the range of $500^{\circ}C$ to $1000^{\circ}C$ in air. The properties of the Ru-$TiO_2$ fibers were characterized as a function of the Ru content and calcination temperature using X-ray diffraction, thermal gravimetry with differential scanning calorimetry, Fourier transform infrared spectroscopy, scanning electron microscopy, transmission electron microscopy, and viscometer, pycnometer and dynamic tensiometer measurements. Although the diameter of the fiber decreased slightly with increasing calcination temperature, no dramatic changes were observed with respect to the ruthenium content. The XRD and FT-IR results revealed that anatase phase and ruthenium metal began to be formed after calcination at temperatures above $500^{\circ}C$. Anatase and rutile phases and ruthenium metal coexisted in the fibers calcined above $600^{\circ}C$. No anatase phase was detected in the fibers containing ruthenium when they were calcined at $1000^{\circ}C$. The morphology of the fibers changed from smooth and uniform to porous with increasing temperature. The experimental results suggest that the calcination temperature and Ru content were influential in determining the morphology and structure of the fibers.

• 한국환경과학회지
• /
• 제18권1호
• /
• pp.61-72
• /
• 2009

Fabrication and oxidants production of 3 or 4 components metal oxide electrode, which is known to be so effective to destruct non-biodegradable organics in wastewater, were studied. Five electrode materials (Ru as main component and Pt, Sn, Sb and Gd as minor components) were used for the 3 or 4 components electrode. The metal oxide electrode was prepared by coating the electrode material on the surface of the titanium mesh and then thermal oxidation at $500^{\circ}C$ for 1h. The removed RhB per 2 min and unit W of 3 components electrode was in the order: Ru:Sn:Sb=9:1:1 > Ru:Pt:Gd=5:5:1 > Ru:Sn=9:1 > Ru:Sn:Gd=9:1:1 > Ru:Sb:Gd=9:1:1. Although RhB decolorization of Ru:Sn:Sb:Gd electrode was the highest among the 4 components electrode, the RhB decolorization and oxidants formation of the Ru:Sn:Sb=9:1:1 electrode was higher than that of the 3 and 4 components electrode. Electrogenerated oxidants (free Cl and $ClO_2$) of chlorine type in 3 and 4 components electrode were higher than other oxidants such as $H_2O_2\;and\;O_3$. It was assumed that electrode with high RhB decolorization showed high oxidant generation and COD removal efficiency. OH radical which is electrogenerated by the direct electrolysis was not generated the entire 3 and 4 components electrode, therefore main mechanism of RhB degradation by metal oxide electrode based Ru was considered indirect electrolysis using electrogenerated oxidants.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.1125-1128
• /
• 2002

Electrochemical capacitor made with metal oxide electrode uses rapid and reversible protonation/deprotonation of metal oxide material under the aqueous acidic solution, generally. Electrochemical stability window of aqueous electrolyte-type capacitor is narrow compared to that of organic electrolyte-type capacitor. Electrochemical characteristics of electrochemical capacitor made with metal oxide electrode and lithium cation based organic electrolyte were evaluated. Electrochemical capacitor based on $RuO_2$ electrode material and 1M $LiPF_6$ in mixed solvents of EC, DEC, and EMC has anodic and cathodic specific capacitance of 145 and 142 F/g-$RuO_2{\cdot}nH_2O$, respectively, by using cyclic voltammetry with scan rate of 2 mV/sec g-$RuO_2$ in potential range of 2.0~4.2V(Li|$Li^+$).

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2004년도 추계총회 및 연구발표회 초록집
• /
• pp.79.2-79.2
• /
• 2004

• 마이크로전자및패키징학회지
• /
• 제11권3호
• /
• pp.63-70
• /
• 2004

The structural, electrical properties of $(Ba, Sr)TiO_3[BSTO]/RuO_2$ thin films were examined by the addition of amorphous BSTO layer between crystlline BSTO film and $RuO_2$ substrate. We prepared BSTO films with double-layered structure, that is, amorphous layers deposited at $60^{\circ}C$ and crystalline films. Crystalline films were prepared at 550 on amorphous BSTO layer. The thickness of the amorphous layers was varied from 0 to 170 nm. During the deposition of crystalline films, the crystallization of the amorphous layers occurred and the structure was changed to circular while crystalline BSTO films showed columnar structure. Due to insufficient annealing effect, amorphous BSTO phase was observed when the thickness of the amorphous layers exceeded 30 nm. Amorphous BSTO layer could also prevent the formation of oxygen deficient region in $RuO_2$ surface. Leakage current of total BSTO films decreased with increasing amorphous layer thickness due to structural modifications. Dielectric constant showed maxi-mum value of 343 when amorphous layer thickness was 30 nm at which the improvement by grain growth and the degradation by amorphous phase were balanced.

• Transactions on Electrical and Electronic Materials
• /
• 제1권4호
• /
• pp.30-39
• /
• 2000

The variation of electrical properties of (Ba, Sr)TiO$_3$[BST] thin films deposited of RuO$_2$electrode with (Ba+Sr)/Tr ration was investigated. BST thin films with various (Ba+Sr)/Tr ration were deposited on RuO$_2$/Si substrates using in-situ RF magnetron sputtering. It was found that the electrical properties of BST films depends on the composition in the film. The dielectric constant of the BST films is about 190 at the (Ba+Sr)/Tr ration of 1.0, 1,025 and does not change markedly. But , the dielectric constant degraded to 145 as the (Ba+Sr)/Tr ratio increase to 1.0. In particular, the leakage current mechanism of the films shows the strong dependence on the (Ba+Sr)/Tr ration in the films. At the ration (Ba+Sr)/Tr=1,025, the Al/BST/RuO$_2$ capacitor show the most asymmetric behavior in the leakage current density, vs, electric field plot. It is considered that the leakage current of the (Ba+Sr)/Tr=1,025 thin films is controlled by the battier-Iimited process, i,e, Schottky emission.