• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.329.1-329.1
• /
• 2014

In this paper, we report electrical, optical and structural properties of Al-doped zinc oxide (AZO) thin films deposited at different substrate temperatures and pressures. The films were prepared by radio frequency (RF) magnetron sputtering on glass substrates in argon (Ar) ambient. The X-ray diffraction analysis showed that the AZO films deposited at room temperature (RT) and 20 Pa were mostly oriented along a-axis with preferred orientation along (100) direction. There was an improvement in resistivity ($3.7{\times}10^{-3}{\Omega}-cm$) transmittance (95%) at constant substrate temperature (RT) and working pressure (20 Pa) using the Hall-effect measurement system and UV-vis spectroscopy, respectively. Our results have promising applications in low-cost transparent electronics, such as the thin-film solar cells and thin-film transistors due to favourable deposition conditions. Furthermore our film deposition method offers a procedure for preparing highly oriented (100) AZO films.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.131-132
• /
• 2017

As the building is becomes bigger and larger, it can lead to big damage in case of fire. Also, tunnel, machine room and underground joint are spaces that can cause high temperature fire above 1,350℃ in case of fire. Therefore, a refractory material is need that can be withstand in high temperatures for long time. One side, the composition of oyster shell is CaCO₃ of 90% or more. It is expected that it will be possible to use it as a high calcium natural material which is the material of the refractory board. According to, Study on bending, compressive strength of mortar according to temperature and heating time change using oyster shell as aggregate the most commonly occurring particle sizes form 2.5mm to 5mm.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.2
• /
• pp.142-147
• /
• 2005

In this work, a gel polymer electrolyte (GPE) was prepared using polyoxyalkylene glycol acrylate (POAGA) as a macromonomer LiCoO$_2$/GPE/graphite cells were prepared and their electrochemical properties were evaluated at various current densities and temperatures. The ionic conductivity of the GPE was more than 6.2${\times}$10$^{-3}$ S$.$$cm^{-1}$ / at room temperature. The GPE had good electrochemical stability up to 4.5 V vs. Li/Li$^{+}$. POAGA-based cells were showed good electrochemical performances such as rate capability, low-temperature performance, and cycleability. The cells, also, passed a safety test such as the overcharge and nail-penetration test.t.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1996.05a
• /
• pp.170-173
• /
• 1996

The optical and the electrical properties of octadecylviologen-(TCNQ$\^$-/)$_2$LB(Langmuir-Blodgett) films have been studied. The films were made at 25mN/m with Y-type formation using kuhn type apparatus. According to a study of UV/visible absorption spectra, DS C, ESR, and I-V characteristics depending on temperatures, there is an internal change in OV-(TCNQ$\^$-/)$_2$ LB films near 350K. We have observed a status of Langmuir films using Brewster angle microscope at room temperature.

• Journal of the Korean institute of surface engineering
• /
• v.29 no.6
• /
• pp.724-727
• /
• 1996

Electrolytic impregnation of nickel hydroxide into porous sintered nickel plaque from various nickel solutions were carried out at room or high temperatures and current density range of 2.5mA $cm^{-2}$ to 25mA $cm^{-2}$. The morphology of the deposited surface was observed with an electron microscope and the surface products were analyzed by means of X-ray diffraction method. Nickel hydroxide was deposited in nickel nitrate electrolyte, while deposits from sulphate or chloride solutions were almost metallic nickel. The loading level of nickel hydroxide from nitrate solutions was 1.6g$cm^{-3}$ void volume and the appearance of the surface was good quality. Discharge capacity of prepared electrodes in nickel nitrate electrolyte was larger than that of the others bath. It was considered that the cell capacity was dependent on the surface roughness of active material.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.6
• /
• pp.233-238
• /
• 2011

The friction and wear characteristics of CrN and TiN coatings on SKD61 which is mold material using for extrusion of AZ80 magnesium alloy were investigated. The coatings were deposited by the arc ion-plating method, and the thickness were about $3.59{\mu}m$ and $3.28{\mu}m$, respectively. Reciprocating friction wear tests were conducted by varying pin load and temperature of counter substrate at un-lubricated condition. The pin loads were 11, 15 and 19 kgf, and the substrate temperatures were room temperature and $120^{\circ}C$. CrN coating which has a lower friction coefficient and a smaller adhesive wear with AZ80 magnesium alloy showed better wear resistance than TiN coating.

• Journal of Korea Foundry Society
• /
• v.3 no.4
• /
• pp.256-261
• /
• 1983

In this study, the variations of tensile strength and yield strength of Al-20% Si alloy were studied. Copper, magnesium and nickel as alloying elements added from 1% to 3% respectively. The temperature range was from room temperature to $350^{\circ}C$. The refinement of primary silicon crystal was treated with phosphorous addition. The results obtained are as follows: 1. Tensile strnegth and yield strength showed more increased strength in refining treated alloy than that of in nonrefining alloy at elevated temperature. 2. Tensile strength and yield strength were increased with the contents of copper. Tensile strength showed the maximum at $150^{\circ}C$, but yield strength was decreased with increasing temperature. 3. The effect of magnesium addition on tensile strength and yield strength showed the maximum at 1% addition and $150^{\circ}C$. 4. Tensile strength and yield strength showed a slight increase with the content changes of nickel and they were decreased with increasing temperature.

• Tribology and Lubricants
• /
• v.11 no.5
• /
• pp.144-149
• /
• 1995

Use of high-quality basestocks is increasing to produce high-performance lubricants. However, their tribological characteristics have not been understood clearly yet. In this study, a newly developed basestock from a fuel hydrocracker and a poly-alpha-olefin are selected and investigated on the properties of lubricants formulated with them. The Lubricants are prepared by blending the basestocks with typical additives such as a zinc dialkyldithiophosphate, a dispersant, a detergent and a dispersant-inhibitor package. Frictional and wear-preventing properties are investigated using an oscillating-type wear-testing machine. The contact is a ball-on-disk mode and the testing temperature is varied from room temperature to 200$^{\circ}$C. The results show that their frictional property is varied significantly and that the non-conventional oils result in lower friction and lower wear compared with conventional lubricants, especially at the higher temperatures.

• Transactions of Materials Processing
• /
• v.19 no.7
• /
• pp.429-434
• /
• 2010

The material used is a commercial magnesium based alloy AZ31(Mg-3Al-1Zn) sheet with a thickness of 0.8 mm. Friction tests at various temperatures(R.T. to $200^{\circ}C$) and at various holding forces in the 4 type molds were carried out to investigate the coefficient of friction. A warm drawing process with a local heating and cooling technique was developed in the Mg alloy sheet forming to improve formability because it is very difficult for Mg alloy to deform at room temperature by the conventional method. So, the coefficient of friction at various mold surface treatment conditions in this study was needed to develop the Mg alloy sheet forming technology.

• Transactions of Materials Processing
• /
• v.25 no.3
• /
• pp.155-160
• /
• 2016

Magnesium(Mg) alloys have been evaluated as replacements for steel or aluminum parts in the automobile industry because of the fuel economy they can provide through reducing weight. The application of Mg alloys has been limited due to its low formability at room temperature, which results from a small number of active slip systems. In the current study, an extruded TAZ711(Mg-7Sn-1Al-1Zn) alloy was warm forged into an automotive control arm to evaluate its formability at various forging temperature. Warm forging was conducted at temperatures of 200, 250, 350 and 450℃. Static strength evaluation was performed on the as-forged specimen at 250℃. The results showed good static strength.