• Journal of Powder Materials
• /
• v.16 no.4
• /
• pp.268-274
• /
• 2009

For the purpose of obtaining basic information on the development of lead-free materials, a high density composites (a) W-Cu, (b) W-Sn (c)W-Cu-Sn and (d) W-Cu-Ni were fabricated by the P/M method. The particle size of used metal powders were under 325 mesh, inner size of compaction mould was $\phi8$ mm, and compaction pressure was 400 MPa. A High density composite samples were sintered at a temperature between $140^{\circ}C$ and $1050^{\circ}C$ for 1 hour under Ar atmosphere. The microstructure, phase transformation and physical properties of the sintered samples were investigated. As the results, the highest relative density of 95.86% (10.87 g/$cm^3$) was obtained particularly in the sintered W-Cu-Sn ternary system sample sintered at 450 for 1hr. And, Rockwell hardness (HRB) of 70.0 was obtained in this system.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.24 no.6
• /
• pp.594-598
• /
• 2015

The effects of Ni on the mechanical properties of WC-Xwt.%Ni-1.5wt.%Si-1.1wt.%$B_4C$ composite (X = 21.6, 23.6, 25.6 and 27.6 wt.%) were investigated in order to replace Co with Ni as the binder metal for hard materials based on WC-Co system. Using X-ray diffraction, optical microscopy, field-emission scanning electron microscopy results, the microstructure, pore distribution and grain size of the composites sintered at $1,150^{\circ}C$ were examined with different fraction (X = 21.6, 23.6, 25.6 and 27.6 wt.%) of binder metal Ni. The average WC grain size of the $WC-Ni-Si-B_4C$ composites was about $1{\mu}m$. The Rockwell hardness : A (HRA) and transverse rupture strength were about 88HRA and $110kgf/mm^2$, respectively. The obtained sample was bonded with SM45C at a temperature of $1,050^{\circ}C$. The thickness and mechanical properties of the bonded area were investigated with different dwell time at a bonding temperature of $1,050^{\circ}C$.

• Korean Chemical Engineering Research
• /
• v.43 no.1
• /
• pp.21-26
• /
• 2005

Experimental researches on the preparation of porous polymeric monoliths in supercritical carbon dioxide have been performed and the effects of monomer and polymerization parameters on the physical properties of the monolith prepared were examined. Polymerizations were carried out in the high pressure stainless steel reactor with sapphire window to show the phase change during the polymerization reaction, and continuous and dry porous monolithic polymer could be obtained. The specific surface area of monolithic polymer increased with monomer contents in reaction mixture and reaction pressure. The Rockwell hardness could be enhanced by the addition of co-monomer MMA in reaction mixtures.

• Journal of Powder Materials
• /
• v.22 no.6
• /
• pp.426-431
• /
• 2015

Microstructural examination of the Nb-Si-B alloys at Nb-rich compositions is performed. The Nb-rich corner of the Nb-Si-B system is favorable in that the constituent phases are Nb (ductile and tough phase with high melting temperature) and $T_2$ phase (very hard intermetallic compound with favorable oxidation resistance) which are good combination for high temperature structural materials. The samples containing compositions near Nb-rich corner of the Nb-Si-B ternary system are prepared by spark plasma sintering (SPS) process using $T_2$ and Nb powders. $T_2$ bulk phase is made in arc furnace by melting the Nb slug and the Si-B powder compact. The $T_2$ bulk phase was subsequently ball-milled to powders. SPS is performed at $1300^{\circ}C$ and $1400^{\circ}C$, depending on the composition, under 30 MPa for 600s, to produce disc-shaped specimen with 15 mm in diameter and 3 mm high. Hardness tests (Rockwell A-scale and micro Vickers) are carried out to estimate the mechanical property.

• Korean Journal of Materials Research
• /
• v.4 no.5
• /
• pp.524-534
• /
• 1994

The effects of transformation temperature and mechanical properties by thermal cycle of CuZnAl shape memory alloy with a small of misch metal and Zr contents were investigated. The addition of misch metal and Zr was very effective for reducing the grain size. After solution treatment, the specimens were post-quench aged or step quenched at $100^{\circ}C$ to $350^{\circ}C$ for variation of Rockwell hardness value. It was found that the Rockwell hareness value was very increased at $200^{\circ}C$ and $250^{\circ}C$. The fracture strength and ductility have been significantly increased with the increase of misch metal conten when tensile tested below $M_f$ temperature. Also, the fracture strength has been more increased in the case of post quench aging treatment than that of the as-quenching treatment. Aging of the $\beta$-phase decreases the $M_s$ temperature, but that of the martensite phase increases the $A_s$ temperature. The change in $A_s$ temperature with post-quench aging can be attributed to recovery of order in the $\beta$phase. The hystersis of transformation temperature ($A_s-M_s$) has an increasing tendency by thermal cycles.

• Applied Chemistry for Engineering
• /
• v.5 no.6
• /
• pp.981-989
• /
• 1994

For the development of new material used bentonite in ceramic/organic material composite, ABS(acrylonitrile-butadiene-styrene) material was used as a matrix polymer and a series of bentonite was blended together. This bentonite, filler like talc or mica for plastic material, was used since natural bentonite(Ca type) is easily obtainable in Korea, Na-bentonite changed from natural bentonite by $Na_2CO_3$ based on the specified compositions, changes in the static and dynamic mechanical properties. It was discovered that the increased content of natural and Na- bentonite results in higher modulus with reduced impact strength. And Rockwell hardness was constant. And Na- bentonite filled polymer showed improvement in impact strength and lower in modulus as the natural bentonite filled polymer. The storage modulus(E') of Na- bentonite filled ABS resin was higher than that of Ca- bentonite filled ABS resin, while higher temperature, storage modulus(E') decreased. At higher frequency, tan ${\delta}$ peak was shifted at high temperature.

• Journal of Korea Foundry Society
• /
• v.38 no.1
• /
• pp.9-15
• /
• 2018

Electromagnetic continuous casting (EMCC) was used to fabricate Ti-6Al-4V alloys with properties suitable for medical applications. Ti-6Al-4V alloy ingots fabricated by EMCC were subjected to heat treatment, such as residual stress removing (RRS), furnace cooling after solution treatment (ST-FC) and water-cooling after solution treatment (ST-WC), in order to obtain characteristics suitable for the standard. After component analysis, the microstructure and mechanical properties (tensile strength and elongation) were evaluated by ICP, gas analysis, OM, SEM, a Rockwell hardness tester and universal testing machine. The Ti-6Al-4V alloy ingot fabricated by EMCC was fabricated without segregation, and the lamellar structure was observed in the RRS and ST-FC specimens. The ST-WC specimen showed only martensite structure. As a result of evaluating the mechanical properties based on the microstructure results, we found that the water-cooled heat treatment condition after the solution treatment was most suitable for the Ti-6Al-4V ELI standard.

• Corrosion Science and Technology
• /
• v.17 no.6
• /
• pp.279-286
• /
• 2018

Austenitic stainless steels used in nuclear power plants mainly use pipes made of seamless pipes, which depend on imports. The manufacturing process and high cost are some of the problems associated with seamless pipes. Therefore, in this study, the corrosion characteristics of the seamless pipe and the SAW pipe were assessed to determine the safety and reliability of the SAW pipe in a bid to replace the seamless pipe. Microstructure was analyzed using an optical microscope and the degree of hardness was measured using a Rockwell B scale. Intergranular corrosion resistance was evaluated by ASTM A262 Practice A, C, and E methods. The degree of sensitization was determined using a DL-EPR test. Anodic polarization test was performed in deaerated 1% NaCl solution at $30^{\circ}C$ and the U-bend method was used to evaluate the SCC resistance in 0.01 M $Na_2S_4O_6$ at $340^{\circ}C$ and 40% NaOH solution at $290^{\circ}C$. Weld metal of the SAW pipe specimen showed relatively high degree of sensitization and intergranular corrosion rate. However, annealing to SAW pipes improved the corrosion properties in comparison to that of the seamless pipe.

• Transactions of Materials Processing
• /
• v.31 no.2
• /
• pp.51-56
• /
• 2022

In this study, finite element analyses were performed by applying a stress ring and split die design to relieve the tensile stress acting on the die due to high surface pressure during warm-closed forging. The applied material was a yield-ratio-control-steel (YRCS). It was used without quenching or tempering after forging. In the case of stress rings design, the number of stress rings and the tolerance for shrink fit were different. Vertical and horizontal splits were applied for insert die split design. Case 5 die with three stress rings, 0.2 % shrink fit tolerance, and vertical split was selected as an effective die design for tensile stress reduction. Based on die stress reduction analyses, Case 5 die for warm-closed forging was produced and smooth forgeability was secured, making it possible to manufacture forging product of yoke with the required geometry. In addition, controlled cooling using warm forging heat was applied to secure mechanical properties of yokes. When oil cooling was used for direct controlled cooling after warm-closed forging, a relatively uniform Rockwell hardness distribution and high mechanical properties could be obtained.

• Journal of Powder Materials
• /
• v.24 no.3
• /
• pp.195-201
• /
• 2017

In this study, H13 tool steel sculptures are built by a metal 3D printing process at various laser scan speeds. The properties of commercial H13 tool steel powders are confirmed for the metal 3D printing process used: powder bed fusion (PBF), which is a selective laser melting (SLM) process. Commercial H13 powder has an excellent flowability of 16.68 s/50 g with a Hausner ratio of 1.25 and a density of $7.68g/cm^3$. The sculptures are built with dimensions of $10{\times}10{\times}10mm^3$ in size using commercial H13 tool steel powder. The density measured by the Archimedes method is $7.64g/cm^3$, similar to the powder density of $7.68g/cm^3$. The hardness is measured by Rockwell hardness equipment 5 times to obtain a mean value of 54.28 HRC. The optimum process conditions in order to build the sculptures are a laser power of 90 W, a layer thickness of $25{\mu}m$, an overlap of 30%, and a laser scan speed of 200 mm/s.