• Advances in materials Research
• /
• v.5 no.4
• /
• pp.263-277
• /
• 2016

Mechanical properties of $Al/Al_2O_3$ and $Al/B_4C$ composites prepared through powder metallurgy are estimated up to 50% $Al_2O_3$ and 35% $B_4C$ weight fractions using micromechanics models and experiments. The experimental Young's modulus up to 0.40 weight fraction of ceramic is found to lie closely between Ravichandran's/Hashin-Shtrikman lower/upper bounds, and close to self consistent method/Miller and Lannutti method/modified rule of mixture/fuzzy logic method single value predictions. Measured Poisson's ratio lies between rule of mixture/Ravichandran lower and upper bound/modified Ravichandran upper bounds. Experimental Charpy energy lies between Hopkin-chamis method/equivalent charpy energy/Ravichandran lower limit up to 20%, and close to the reciprocal rule of mixture for higher $Al_2O_3$ content. Rockwell hardness (RB) and Micro-hardness of $Al/Al_2O_3$ are closer to modified rule of mixture predictions.

• Journal of the Korean Society of Industry Convergence
• /
• v.22 no.6
• /
• pp.681-688
• /
• 2019

SM45C steel, which is widely used for mechanical structure, was carburized at 870℃ for 4 hours and tempered at 300℃ and 400℃ for 1, 3 and 6 hours. The tempered materials were evaluated for tensile test, hardness test and impact test. In particular, the hardness and the absorption energy were evaluate the reliability by the Weibull statistical analysis. 300℃-1h specimen is considered to be the best heat treatment condition in the tensile stress and the observation of fracture surface. 300℃-1h specimen showed larger shape and scale parameter than the other specimens, and Rockwell hardness variance was small and showed the best characteristics. 400℃-3h specimen showed larger shape and scale parameter than the other specimens, the dispersion of impact absorption energy is small, and showed excellent characteristics.

• Journal of Korea Foundry Society
• /
• v.21 no.1
• /
• pp.24-32
• /
• 2001

Recently, iron aluminides based on Fe3Al and FeAl are ordered intermetallic alloys that offer good oxidation resistance, excellent sulfidation resistance, and potentially lower cost than many high-temperature structural materials. They have better strength, elasticity to weight ratio and high temperature strength, therefore, they can be cosidered as candidate heat resistance structural materials for automobiles, ships, airplanes and spaceships applications. The changes in the mechanical properties and fracture behavior were investigated for Fe-30at.%Al-5at.%Cr alloys when Ti, Hf and Zr were added respectively. For mechanical properties such as Rockwell hardness and yield strength at room temperature, those were decreased in the case of Fe-30at.%Al-5at.%Cr alloy then increased in the case of 5at.% and 10at.% addition of Ti alone. However, Rockwell hardness and yield strength decreased again at 15%Ti then increased dramatically due to the precipitation hardening of the second phase on the specimen at 20%Ti. For fracture modes, cleavage fracture showed in the case of Fe-30at.%Al and Fe-30at.%Al-5at.%Cr alloys. As the amount of Ti addition changed cleavage to transgranular fracture and to quasi-cleavage fracture at 20%Ti. When Hf, Zr and Hf+Zr were added respectively, transgranular, cleavage and quasi-cleavage fracture were coexisted.

• Polymer(Korea)
• /
• v.35 no.6
• /
• pp.565-573
• /
• 2011

The nanocomposites containing graphene oxide (GO) were prepared in order to improve the mechanical properties of poly(methyl methacrylate)/aluminum hydroxide (PMMA/AH) composites. GO was prepared from graphite by oxidation of Hummers method followed by exfoliation with thermal treatment. The surface of GO was modified by oxygen plasma in various exposure times from 0 to 70 min to improve interfacial compatibility. Compared with PMMA/AH composites, the nanocomposites containing GO modified with oxygen plasma for the exposure time up to 50 min showed significant increases in flexural strength, flexural modulus, Rockwell hardness, Barcol hardness, and Izod impact strength. The morphology of fracture surface showed an improved interfacial adhesion between PMMA/AH composites and GO, which was properly treated with oxygen plasma. The mechanical properties of nanocomposites were deteriorated by increasing the content of GO above 0.07 phr due to the nonuniform dispersion of GO.

• Journal of the Korean Society for Heat Treatment
• /
• v.12 no.4
• /
• pp.327-337
• /
• 1999

A series of Ni-Cr-Mo alloy steels were austenitized, quenched to martensite, and tempered at various temperature and time conditions. Tensile testing was conducted at room temperature with cylindrical specimens, and hardness was measured using Rockwell hardness tester. In the tempering stage I, high strain hardening and yield strength accounted for the high ultimate strength and hardness. In the tempering stage II, strengths and hardness linearly decreased with increasing tempering temperature. Specimens tempered in the temperin stage III showed incipient discontinuous yielding and tensile strengths only slightly higher than yield strengths. Ductilities decreased slightly in specimens tempered in the tempered martensite embrittlement range, and severely decreased in specimens tempered for 10 hours at $500^{\circ}C$ in the temper embrittlement range. Specimens tempered at $600^{\circ}C$ for 10 hours showed recrystallized microstructures, a number of fine dimples, and increased strain hardening, probably due to the precipitation of alloy carbides. The simple formulae for the mechanical properties of these steels were suggested as a function of carbon content and Hollomon-Jaffe tempering parameter.

• Journal of the Korean Society for Precision Engineering
• /
• v.31 no.12
• /
• pp.1115-1119
• /
• 2014

In this article, a 20 kHz ultrasonic waveguide for nano-surface treatment was designed and manufactured. When designing the system, finite element analysis with ANSYS software was performed to find optimal dimensions of the waveguide, which can raise energy efficiency. Consequently an anti-resonance frequency of an Al waveguide with a piezoelectric actuator was 20 kHz, which predicted the experimentally obtained value of 18 kHz well. For the assessment of the performance, Steel Use Stainless (SUS) 304 and chromium molybdenum steel (SCM) 435 specimens were tested. Cross-sectional microscopies of SUS304 were taken and they showed that the treated thickness was $30{\mu}m$. Additionally, hardness tests of SCM435 were done and the hardness before the process was 14.0 Rockwell Hardness-C scale (HRC) and after the process was 20.5 HRC, respectively, which means 46% increase. Considering these results, the developed ultrasonic system is thought to be effective in the nano-surface treatment process.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1065-1066
• /
• 2006

The aging behavior of sintered Al composites with various ceramic contents was investigated. 2xxx series blended powder was used as the starting powder. Ceramic contents were 0wt.% and 5wt.%. The blended powders were compacted at 250MPa. The sintering process was performed at $620^{\circ}C$ for 60min in a $N_2$ atmosphere. Each part was solution-treated at $518^{\circ}C$ for 60min and aged at $180^{\circ}C$. The Rockwell hardness at the peak aging time increased with ceramic contents. However, the peak aging time at maximum hardness was reduced with increased ceramic contents.

• Journal of Technologic Dentistry
• /
• v.21 no.1
• /
• pp.43-53
• /
• 1999

The mechannical properties and corrosion resistance of alloy added commercially pure titanium for dental implants have been investigated. Ti, To-65Zr, Ti-10.1Ta and Ti-17Sn alloys were melthed in arc furnace and the corrosion resistance of Ti alloys was evaluated by anodic polarization test. The microstructure and mechanical properties of Ti alloy were analysed by optical micrograph. hardness tester and instron. In isothermal test, Ti-10.1Ta and Ti-17Sn alloys exhibited the best oxidation resistance below $1100^{\circ}C$. Ti65Zr, Ti-10.1Ta and Ti-17Sn alloys showed better rockwell hardness compared with commercially pure. Ti As the result of the anodic polarization test in 5%HCl, it 5%HCl, it was known knows that Ti-65Zr, alloy showed a rapid decrease in current density at higher potenial in comparision with other Ti alloys.

• Journal of Korea Foundry Society
• /
• v.37 no.1
• /
• pp.14-20
• /
• 2017

The microstructure, electrical conductivity and hardness variation of an AZ91-5wt%Sn Mg alloy sample during a solid-solution and aging heat treatment were instigated by optical microscopy, scanning electron microscopy, X-ray diffraction and by Rockwell hardness techniques in this study. The XRD result shows that the main phases in the as-casted alloy are ${\alpha}$-Mg, $Mg_{17}Al_{12}$ and $Mg_2Sn$. From the SEM images of the AZ91-5wt%Sn Mg alloy after the solution treatment, the $Mg_{17}Al_{12}$ phases in the alloy were found to have dissolved into the matrix with an increase in the holding time during the solution treatment, but $Mg_2Sn$ phases were clearly observable. The highest peak hardness of the AZ91-5wt%Sn Mg alloy is 82HRE at an aging temperature of $200^{\circ}C$.

• Journal of Korea Foundry Society
• /
• v.17 no.5
• /
• pp.443-449
• /
• 1997

The purpose of this study is to investigate the effect of P addition and homogenizing heat treatment on the mechanical properties of Cu-Sn-Ni alloy. The addition of P was 0.025wt.%P to 0.085wt.%P and homogenizing heat-treated at 400, 500, $600^{\circ}C$ under $N_2$ gas atmosphere. Mechanical properties was investigated in this study were Rockwell hardness, tensile strength, and elongation. Tensile strength and elongation increased with P and homogenizing time. Temperature was significantly influence on mechanical properties. Hardness decreased with increasing homogenizing time and temperature, but 0.085wt.%P specimen was showed higher hardness and lower tensile strength and elongation than 0.073wt.%P specimen due to the presence of more $Cu_3P$ in matrix.