COMPARISON OF THE RESIDUAL STRESS OF THE NANOFILLED COMPOSITES (Nanofilled 복합레진의 잔류응력 비교)

  • Park, Jeong-Won
    • Restorative Dentistry and Endodontics
    • /
    • v.33 no.5
    • /
    • pp.457-462
    • /
    • 2008
  • "Residual stress" can be developed during polymerization of the dental composite and it can be remained after this process was completed. The total amount of the force which applied to the composite restoration can be calculated by the sum of external and internal force. For the complete understanding of the restoration failure behavior. these two factors should be considered. In this experiment. I compared the residual stress of the recently developed nanofilled dental composite by ring slitting methods. The composites used in this study can be categorized in two groups. one is microhybrid type-Z250, as control group, and nanofilled type-Grandio, Filtek Supreme. Ceram-X, as experimental ones. Composite ring was made and marked two reference points on the surface. Then measure the change of the distance between these two points before and after ring slitting. From the distance change, average circumferential residual stress $({\sigma}{\theta})$ was calculated. In 10 minutes and 1 hour measurement groups, Filtek Supreme showed higher residual stress than Z250 and Ceram-X. In 24 hour group, Filtek showed higher stress than the other groups. Following the result of this experiment, nanofilled composite showed similar or higher residual stress than Z250, and when comparing the Z250 and Filtek Supreme, which have quite similar matrix components. Filtek Supreme groups showed higher residual stress.

Residual Stress Comparison of Type III Hydrogen Tank by Curing Conditions (Type III 수소탱크 경화조건에 따른 잔류응력 비교)

  • Yong-Chul Shin
    • Composites Research
    • /
    • v.37 no.1
    • /
    • pp.15-20
    • /
    • 2024
  • Since the residual stress of hydrogen tank is directly related to durability, it is very important to reduce it for safety. Type II~IV hydrogen tank are manufactured by the filament winding method, in which the fiber is impregnated with resin and wound around the liner. Residual stress in composite is affected by curing conditions and fiber tension etc. In this study, the effect of curing conditions on residual stress was analyzed when manufacturing a Type III hydrogen tank using carbon fiber filament winding process. First, the curing behavior of the epoxy resin was analyzed using a differential scanning calorimetry. Through this, the curing temperature was set to 140℃. During the same curing time, the specimens were cured under 2-stage curing condition that reached 140℃ earlier and a 4-stage curing condition that reached 140℃ later, respectively. After curing, the residual stress of the composite material was measured by the ring slitting method, and the experimental values were compared with numerical values. It was confirmed that there was a significant difference in residual stress according to the optimization of curing conditions.