• 한국세라믹학회지
• /
• 제46권1호
• /
• pp.53-57
• /
• 2009

The h-BN powder was synthesized by amorphous $B_2O_3$ and activated carbon at $1550^{\circ}C$ in nitrogen atmosphere, whose properties were examined according to $MgB_6$ addition. Amount of $MgB_6$ addition was varied in the range of $0{\sim}$10\;wt% of the initial mixture. It was observed that $MgB_6$ addition led to an increase in the amount and the grain size of h-BN and decrease in the amount of $B_4C$ forming. When $MgB_6$ added 5 wt%, the amount and crystallinity of h-BN increased as the holding time at the synthesis temperature was prolonged. It was also confirmed that the regularity of three-dimensional ordering of h-BN increases.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2002년도 춘계학술발표회 초록집
• /
• pp.12-12
• /
• 2002

hexagonal Boron Nitride (hBN), rhombohedral Boron Nitride (rBN)과 고밀도의 wurzitic Boron N Nitride (wBN), cubic Boron Nitride (cBN) 등의 다양한 상을 갖는 Boron nitride는 그 결정구조에 따라 저밀도, 고밀도 박막으로 분류되며 이중 hBN과 rBN은 층간 결합이 약한 $sp^2$ 결합특성을 가지고, wBN 과 cBN은 강한 $sp^3$ 결합특성을 가지고 있다. 현재까지 $sp^3$결합을 갖는 BN의 우수한 특성을 응용하기 위한 수 많은 연구들이 있어왔다. 특히 cBN은 다이아몬드에 버금가는 높은 경도뿐만 아니라 높은 화 학적 안정성 및 열전도성 등 우수한 물리화학적 특성을 가지고 있어 마찰.마모, 전자, 광학 등의 여러 분야에서의 산업적 응용이 크게 기대되고 있다. 그러나 이와 같이 BN박막의 기계적 물성과 관련한 연 구는 많이 진행되어 왔으나 전기.전자적, 광학적 특성에 관한 연구는 미비한 실정이다. 따라서 본 연구에서는 BN박막의 또 다른 웅용 분야를 탐색하고자 ME - ARE (Magnetically Enhanced A Activated Reactive Evaporation)법 에 의 해 합성 된 BN박막의 광학적 특성 에 관하여 조사하였다. BN박 막합성 은 전자총에 의 해 증발된 보론과 질소.아르곤 플라즈마의 활성 화반응증착(Activated Reactive E Evaporation)에 의해 이루어졌다. 기존의 ARE장치와 달리 열음극(hot cathode)과 양극(anode)사이에 평 행자기장을 부가하여 플라즈마의 증대시켜 반웅효율을 높였다. 합성실험용 모재로는 기본적인 특성 분 석을 위해 p-type으로 도핑된 (100) Si웨이퍼를 $30{\times}40mm$크기로 절단 후, 10%로 희석된 완충불산용액 에 10분간 침적하여 표면의 산화층을 제거한 후 사용하였으며, 광학특성 분석을 위해 $30{\times}30mm$의 glass를 아세톤으로 탈지.세척한 후 사용하였다. 박막합성실험에서 BN의 광학적 특성에 미치는 공정변수의 영향을 파악하기 위하여, 기판바이어스 전압, discharge 전류, $Ar/N_2$가스 유량비 등을 달리하여 증착하였다. 증착된 박막은 FTIR 분석을 통하 여 결정성을 확인하였으며, AFM 분석을 통하여 코팅층의 두께를 측정하였고, UV - VIS spectormeter를 이용하여 투광특성을 평가하였다.