• Journal of Industrial Technology
• /
• v.24 no.A
• /
• pp.3-8
• /
• 2004

This study was performed to investigate the effect of two step austenitized treatment on the mechanical properties and fracture characteristic of the ductile cast iron and austempered ductile cast iron(ADI). The obtained results of this study were as follows. The matrix structures of specimens were changed differently by austenitizing heat treatment. Microstructure of austempered ductile cast iron obtained by two step austenitized treatment was bainitic ferrite and retained austenite. With two step austenitized treatment, vield strength, tensile strength and hardness decreased, while the elongation increased.

• Journal of the Korean Society for Heat Treatment
• /
• v.18 no.2
• /
• pp.83-90
• /
• 2005

Failure cause of the fractured engine parts was analyzed by microstructural observation. These parts were failed far earlier than the expected service life. By the stereoscope and SEM examinations of the fractured surface, the fracture modes have been identified as wear and fatigue failure. From the observation of microstructure and microhardness measurements of the failed gears, the probable cause for failures are internal oxidation during using and retained austenite and carbide networks due to heat-treatment, respectively. These defected structures at near surface contributed to the wear and fatigue failure.

• Journal of Korea Foundry Society
• /
• v.10 no.5
• /
• pp.408-416
• /
• 1990

The application of this new design approach called fracture mechanics allow one to determine the maximum allowable stress from the knowledge of the largest expected flow size and the plane strain fracture toughness of a material. In this study we examined the relation between retained austenite, mechanical property and fracture toughness accompanied by austempering heat treatment. Fracture toughness values and retained austenite volume were higher with the ADI(austempered ductile iron) which were austempered at $380^{\circ}C$ than austempered at $320^{\circ}C$. Additionally, fracture toughness values were increased for 1~2 hour austempering time but it was slowly decreased for 5 hour ADI maintaining the predominant fracture toughness($K_{IC}:83MPa{\sqrt{m}}$) is obtained following condition, namely, austempering temperature and time ($380^{\circ}C$ and 1 hour).

• Journal of Korea Foundry Society
• /
• v.25 no.2
• /
• pp.95-101
• /
• 2005

This study has been carried out to investigate the microstructure of austempered high carbon cast steel with the variation of silicon and heat treatment conditions. The results show that an lower ausferritic structure is formed at the low austemepring temperature ($250{\sim}300^{\circ}C$) and an upper ausferritic structure is formed at the high austemepring temperature ($350{\sim}400^{\circ}C$). As an austempering temperature increased, the retained austenite volume fraction increased, however hardness decreased. Also, as a silicon content increased, the precipitation of cementite was suppressed, therefore 2nd reaction of autempering transformation was delayed.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.16 no.6
• /
• pp.141-147
• /
• 2008

Hot-dip galvannealed sheet (GA) with high strength of 590MPa grade in tensile strength, has developed for automotive applications. However, for a successful application, the microstructure and galvannealing behavior of galvannealed TRIP steel sheets must be strictly controlled. High silicon contents steel has problems with weld-ability, zinc coating and reduction of retained austenite volume fraction after galvannealing process. The main purpose of this study is to solve the problem as indicated above.

• Journal of the Korean Society for Precision Engineering
• /
• v.13 no.7
• /
• pp.36-44
• /
• 1996

Drilling tests were carried out austempered ductile cast iron(ADI) to clarify the factors influencing the drilling characteristics of ADI material. The machinability of material was evaluated using high speed steel drill and cobalt contained drill of 6mm diameter. The spheroidal graphite cast iron materials were austemized at 900 .deg. C for 1 hour and then wear was kept at 375 .deg. C for 2 hours. Austempered ductile cast iron contains a great deal of retained austenite which contribustes to an improvement of impact strength. In this paper, machinability of ADI was invastigated by drilling experimentation. The results obtained are as follows:a) Flank wear incresses logarithmically with the increases of cutting time and proportionally with the increases of cutting force. b) Drilling hole number of about 2 times can be educed more step feed than ordinary feed due to the high hardness of ADI material and hardness increasing ascribed to the martensite of retained austenite.

• Journal of Korea Foundry Society
• /
• v.14 no.6
• /
• pp.548-557
• /
• 1994

Grey iron containing a small amount of Cu and Mo to improve the effect of heat treatment and microstructures were poured in to the mold and them austenized at $900^{\circ}C$. After austenitizing the specimens of castings were austempered $210^{\circ}C$, $250^{\circ}C$, $300^{\circ}C$ and $350^{\circ}C$. The effects of matrix structures, mechanical properties and wear characteristics were investigated by austempering temperatures. Tensile strength and hardness of austempered grey iron are increased and the amount of retained austenite is decreased as austempering temperature is lower even though the amount of retained autenite in it only 4%. The amount of rolling wear loss are increased as rolling revolution is increased and wear loss of austempered grey iron under dry rolling condition is characterized by three models; initial wear, stationary wear and abnormal wear. It has been found that the amount of wear loss was increased with increasing maxium compressive stress and rolling revolution.

• Journal of the Korean Society for Heat Treatment
• /
• v.11 no.3
• /
• pp.216-226
• /
• 1998

Heat treatment conditions and the formation of microstructures were studied for improving the transformation-induced plasticity(TRIP) effect of retained austenite and mechanical properties of Fe-0.2%C-1.5%Si-1.5%Mn sheet steel. An excellent combination of elongation about 30% and high strength over 760MPa was achieved by processing of intercritical annealing and isothermal holding Intercritical annealing the sheet steel produced fine particles($1{\sim}2{\mu}m$) of retained austenite which were stabilized due to C enrichment by subsequent holding in bainite transformation range. Heat treatment conditions were depended on the shape and distribution of second phases as well as the volume fraction and stability of retained austenrte. In this work, the heat treatment condition of optimal strength-elongation balance was obtained by holding the steel at $400^{\circ}C$ for 200sec, after intercritical annealing at $790^{\circ}C$ for 300sec.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2008.11a
• /
• pp.39.1-39.1
• /
• 2008

• Proceedings of the KWS Conference
• /
• 1993.05a
• /
• pp.73-75
• /
• 1993