• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1996년도 제23회 학술대회
• /
• pp.83-86
• /
• 1996

In this study, CrN, TiN and TiN + CrN coatings have treated onto the steel substrates by ion plating to improve their tribological behaviors. Some of the specimens were ion nitriding treated to study the effect of ion nitriding on wear behavior. The wear tests were performed with these specimens by ball-onplate type and disc-on-plate type wear tester. It was demonstrated that ion nitriding treatment improve wear resistance of the coatings. The results of high temperature wear tests indicated that the specimens coated with CrN were exhibited the better wear resistance properties than the specimens with TiN coatings

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 1999년도 추계학술대회 논문집 - 한국공작기계학회
• /
• pp.332-338
• /
• 1999

Surface hardening of plain carbon steel (SM$%C) by Laser are usually much finer and stronger than those of the base metals. The present study was undertaken to investigate the wear resistance and a processing parameters such as, power density, pulse width, defocusing distance, and molten depth for surface modification of plain carbon steel. The wear test was carried out under experimental condition using the wear test device, and in which the annular surfaces of wear test specimens as well as mating specimen of alumina ceramics(Al2O3) was rubbed in dry sliding condition. It is shown that molten depth and width depend on defocusing distance. The wear loss on variation of sliding speed was much in lower speed range below 0.2m/sec and in higher speed range above 0.7m/sec, but wear loss was little in intermediate speed range. It depends on oxidation speed and wear speed.

• 한국주조공학회지
• /
• 제20권4호
• /
• pp.240-246
• /
• 2000

Surface layer properties such as composition, phase, hardness, and oxide layer condition are very important if the main failure mechanism of metals is wear. Generally, stable and dense oxide layers are known to decrease the wear rate of metals by prohibition of metallic junction occurred between bare metals. Addition of Si above 4 wt% to DCI(Ductile Cast Iron) is reported to enhance the significant oxidation resistance by forming the silicon-rich surface layer which inhibits further oxidation. And addition of up to 2 wt% Mo to high Si ductile iron produces significant increases in high temperature tensile strength, creep strength, thermal fatigue resistance and oxidation resistance. High pressure wear characteristics of unalloyed DCI(Ductile cast Iron), 4.46 wt% Si ductile iron, 4.3 wt% Si-0.52 wt% Mo ductile iron were investigated through unlubricated pin-on-disc wear test. Wear test was carried out at speed of 23m/min, under pressure of 3 MPa and 3.3 MPa. Wear surfaces of each specimen were observed by SEM to determine the wear mechanism under high pressure wear condition. Addition of Si 4.46 wt% severely deteriorated wear property of ductile iron compared to unalloyed DCI. But combined addition of Si 4.3 wt%andMo0.52wt%decreasedthefrictioncoefficient(${\mu}$)ofductileironsandremarkablydelayedthemild-severeweartransition.

• 대한기계학회논문집
• /
• 제17권6호
• /
• pp.1441-1455
• /
• 1993

본 연구에서는 최신기법에 의해서 제조된 HIP제 질화규소와 지르코니아를 실험재료로 하여 무윤활하에서의 미끄럼마찰·마멸실험을 수행하여 마찰·마멸특성을 규명하고, SEM을 이용한 마멸면의 미시적 관찰을 통해서 세라믹의 마멸기구를 조사하 여 세라믹마멸기구의 마멸모델을 제시하고자 한다. 제시된 마멸모델에서 파괴역학을 도입하여 이론해석과 고찰을 수행하여 보다 실용적인 세라믹의 마멸율울 평가할 수 있 는 새로운 무차원 파라메터를 제안하고자 한다.

• Tribology and Lubricants
• /
• 제15권2호
• /
• pp.156-163
• /
• 1999

The mechanical characteristics of the high speed steel by Powder metallurgy Process (PM-HSS) has been reported to improve with several alloying constituents, such as high carbon, vanadium and cobalt. In this paper, sliding wear test has been conducted using a pin-on-disc machine for three PM-HSS which contains 0%, 5% and 12% cobalt respectively, in order to evaluate the effect of cobalt on wear properties of PM-HSS. The results of this study showed that the wear resistance of PM-HSS has been increased by the addition of cobalt on the range of experimental friction velocities. When compared with the effect of addition of cobalt, the wear resistance of PM-HSS with 5% cobalt has been found to be superior to that of PM-HSS with 12% cobalt.

• Tribology and Lubricants
• /
• 제16권3호
• /
• pp.194-200
• /
• 2000

In order to evaluate the effect of Nb on wear properties of high speed steel(HSS) by powder metallurgy, niobium-alloyed HSS have been prepared by adding 0%, 1%, 3% and 5%Nb to HSS of 6%W-5%Mo-4 %Cr-5%V-5%Co. Sliding wear tests were conducted at various sliding speed conditions under the constant pressure using a pin-on-disc type machine. The results of this study show that the wear resistance of HSS by powder metallurgy was increased by the addition of Nb within the range of sliding speed used in this experimental study. However, the amount of Nb did not improve the wear resistance. It may be due to the thermal stability of carbide and high temperature properties of the matrix containing Nb comparing to that without Nb.

• 연구논문집
• /
• 통권25호
• /
• pp.193-205
• /
• 1995

Plasma 용사 코팅 기술은 전자산업과 정보산업의 기초인 Micro 반도체 산업의 기능성 목적으로 응용되고 있으며, 항공기 등의 첨단산업에서 디젤엔진이나 가스터빈 등 응용 범위를 점차 확대하고 있는 실정이다. 또한 첨단요소 부품에 적용하여 내마모성, 내열성, 내피로성, 내부식성 등을 부여하고 있다. 기능성 부품에 후처리하여 제품의 부가가치를 향상시킬 수 있어, Plasma 용사 코팅기술의 중요성은 날로 증대되고 있는 실정이다. 본 연구에서는 Plasma 용사 기술을 이용하여 코팅을 형성 내마모시험을 통해 국내 첨단요소 부품에 기능성 부여과 낙후된 용사 기술을 향상시키는 데 있다.

• 한국표면공학회지
• /
• 제29권6호
• /
• pp.634-639
• /
• 1996

In oder to improve the wear resistance as well as oxidation resistance at high temperature a AISI H13 steel was treated by a duplex process of calorizing followed by plasma nitriding. The surface properties of the duplex-treated AISI H13 steel was characterized and compared with those treated by single surface process of calorizing and plasma nitriding, in terms of microstruture, microhardness, wear resistance at $500^{\circ}C$, and the oxidation behaviours at $700^{\circ}C$, Duplex process on H13 steel had created duplex layer of approximately $190\mu\textrm{m}$ on the surface, and surface microhardness was measured to be above 1450Hv(0.1Kgf). There was considerable improvement of the high temperature wear resistance at $500^{\circ}C$ in the duplex-treated steel when both wear volume and weight change due to oxidation were considered. In addition the duplex-treated steel showed an improved high temperature oxidation resistance than the plasma nitrided steel at $700^{\circ}C$.

• 한국생산제조학회지
• /
• 제20권2호
• /
• pp.162-168
• /
• 2011

In this research, nitrogen plasma source ion implantation(PSII) of non-coated tungsten carbide endmill tools was conducted with low heat treatment for increasing wear resistance. After the low heat treatment of PSIIed tools to give a homogeneity of wear resistance, the surface modification of tools was analyzed by hardness test, surface roughness and cutting forces. As for the resultant cutting forces, low heat treatment in temperature of $400^{\circ}C$ and $500^{\circ}C$ is stable because of low cutting resistance. The 20-minutes heat treated tool at spindle speed 25000rpm has superiority of surface roughness, Ra of $0.420{\mu}m$ and was found to have good wear resistance. The higher hardness value was obtained by increasing temperature from $300^{\circ}C$ to $600^{\circ}C$ for PSIIed tools with low heat treatment. As the PSIIed tools under 10minutes at temperature of $600^{\circ}C$ have the highest hardness as Hv of 2349.8, It was analyzed that temperature processing give much influences on hardness.

• 열처리공학회지
• /
• 제16권6호
• /
• pp.335-340
• /
• 2003

To improve properties of wear resistance and anti-corrosion of the trivalent chromium platings, oxinitrocarbunsing and steam oxidation were conducted. Armophous trivalent Cr platings could be transformed to chromium carbides of high hardness, that showed low friction and wear rate. Even though micro-cracks were within as platings, superior anti-corrosion property was obtained by these treatments due to healing of cracks at the interface between the trivalent chromium platings and substrate.