This study was to figure out proper Formaldehyde/Urea molar ratio of UF resin with satisfactory bonding strength of plywood and properties of particleboard. The six kinds of UF resins were manufactured with F/U molar ratio 1.0, 1.2, 1.4, 1.6, 1.8, and 2.0. The boards were made of three kinds of raw materials : Veneer, Sliver-Particle and Strand-Particle. Manufacturing condition of plywood : amount of mixing resin was 150g/$m^2$. The fourty secs/mm simple-pressing schedule in the pressure 10kgf/$m^2$ was applied for 480mm${\times}$700mm board at the temperature of $110^{\circ}C$ in a hot press. Manufacturing condition of particleboard : Target density was 0.65g/$cm^2$. The stepwise 9 minutes- multi-pressing schedule in the maximum pressure 40kgf/$cm^2$, the minimum pressure 15kgf/$cm^2$ was applied for $480mm{\times}634mm{\times}12mm$ board at the temperature of $150^{\circ}C$ in a hot press. The results are as follows : I. In bonding strength, plywood which was made by F/U molar ratio 1.2 showed the highest value. Other molar ratio resin also gave the satisfied value of KS standard, 7.5kgf/$cm^2$. 2. In internal bond strength of particleboard, Sliver-Particleboard(SLPB) and Strand-Particleboard(STPB) varied respectively from 5.9kgf/$cm^2$ to 4.8kgf/$cm^2$, from 6.7kgf/$cm^2$ to 5.4kgf/$cm^2$. SLPB with F/U=1.2 and STPB with F/U=1.6 had higher IB value. Also, both SLPB and STPB showed lower IB value in F/U molar ratio 2.0 and 1.0. 3. SLPB and STPB with six kinds of UF resin respectively satisfied bending strength of KS standard 150 Type(130kgf/$cm^2$) and 200 Type(180kgf/$cm^2$). Bending strength data for both of SLPB and STPB showed little or no loss from F/U=1.8 to F/U=1.2. Also, STPB was approximately two times higher than that of SLPB. Therefore, the raw material's shape had more effect on bending strength than the FlU molar ratio. 4. F/U=1.6 and 1.4 showed the lower thickness swelling in SLPB and STPB. All of STPBs satisfied thickness swelling of KS standard, under 12%.