• Restorative Dentistry and Endodontics
• /
• 제37권1호
• /
• pp.2-8
• /
• 2012

The limited durability of resin-dentin bonds severely compromises the longevity of composite resin restorations. Resin-dentin bond degradation might occur via degradation of water-rich and resin sparse collagen matrices by host-derived matrix metalloproteinases (MMPs). This review article provides overview of current knowledge of the role of MMPs in dentin matrix degradation and four experimental strategies for extending the longevity of resin-dentin bonds. They include: (1) the use of broadspectrum inhibitors of MMPs, (2) the use of cross-linking agents for silencing the activities of MMPs, (3) ethanol wet-bonding with hydrophobic resin, (4) biomimetic remineralization of water-filled collagen matrix. A combination of these strategies will be able to overcome the limitations in resin-dentin adhesion.

• The Journal of Advanced Prosthodontics
• /
• 제11권2호
• /
• pp.120-127
• /
• 2019

PURPOSE. To determine wear amount of single molar crowns, made from four different restoratives, and opposing natural teeth through computerized fabrication techniques using 3D image alignment. MATERIALS AND METHODS. A total of 24 single crowns (N = 24 patients, age range: 18 - 50) were made from lithium disilicate (IPS E-max CAD), lithium silicate and zirconia based (Vita Suprinity CAD), resin matrix ceramic material (Cerasmart, GC), and dual matrix (Vita Enamic CAD) blocks. After digital impressions (Cerec 3D Bluecam, DentsplySirona), the crowns were designed and manufactured (Cerec 3, DentsplySirona). A dualcuring resin cement was used for cementation (Variolink Esthetic DC, Ivoclar). Then, measurement and recording of crowns and the opposing enamel surfaces with the intraoral scanner were made as well as at the third and sixth month follow-ups. All measurements were superimposed with a software (David-Laserscanner, V3.10.4). Volume loss due to wear was calculated from baseline to follow-up periods with Siemens Unigraphics NX 10 software. Statistical analysis was accomplished by Repeated Measures for ANOVA (SPSS 21) at = .05 significance level. RESULTS. After 6 months, insignificant differences of the glass matrix and resin matrix materials for restoration/enamel wear were observed (P>.05). While there were no significant differences between the glass matrix groups (P>.05), significant differences between the resin matrix group materials (P<.05) were obtained. Although Cerasmart and Enamic were both resin matrix based, they exhibited different wear characteristics. CONCLUSION. Glass matrix materials showed less wear both on their own and opposing enamel surfaces than resin matrix ceramic materials.

• 대한치과보철학회지
• /
• 제44권5호
• /
• pp.503-513
• /
• 2006

Statement of the problem: The cold-cured resins used in fabrication of the provisional crown and fixed partial dentures could cause pulpal damage by heat generated during exothermic polymerization reactions. Purpose: In this in vitro study investigates the how external conditions such as material of the matrix, thickness of the matrix and thickness of dentin affect the temperature of the tooth during polymerization reaction of the cold-cured resins. Material and methods : To measure the temperature of the resin, metal die was maintained to the temperature of $37^{\circ}C$ with water bath to simulate the temperature of thetooth and thermocouple was placed in the center of the metal die. Acrylic pipe was cut in height of 1, 2, 3, 6, 10 mm and placed on the metal die and mixed resin was pored in the acrylic pipe As the resin polymerized temperature was recorded with the thermometer. Temperature of the resin using matrix was recorded by using the individual tray relieved in different thickness 2, 5, 7, 10 mm. The material of the matrix was irreversible hydrocolloid impression material, vinyl polysilloxane impression material and vacuum-formed template Temperature rise of the resin using different thickness of tooth section was record ed by placing tooth section on the metal die and placing resin over the tooth section. Results : Conclusion : 1. Temperature rise increased as the thickness of the resin increased but there was no significant differences over 3 mm thickness of the resin. 2. The lowest temperature rise was showed in irreversible hydrocolloid impression material and vinyl polysilloxane impression material vacuum-formed template as in orders. 3, Temperature rise of the resin decreased regardless of the thickness of the matrix when vinyl polysilloxane impression material was used as the matrix. 4 When irreversible hydrocolloid impression material was used as matrix, the temperature rise of the resin decreased as the thickness of the matrix increased and there was no temperature rise when thickness of the matrix reached 10 mm, 5. The temperature rise of the resin did not decreased when Polypropylene vacuum-formed template was used as the matrix. 6, The temperature of the resin increased as the thickness of the dentin decreased.

• 한국세라믹학회지
• /
• 제34권11호
• /
• pp.1151-1158
• /
• 1997

Fracture of uni-directional carbon fiber reinforced carbon matrix composite is strongly dependent on the orientation of basal plane in graphite matrix when it is limited within matrix. The orientation of basal planes are vertically stacked to carbon fiber which results in the weakness for applied tensile or shear force in thermosetting resin derived-carbon matrix composite. Microtextural control of the matrix was tried through chemical interaction between metal carbides and furan resin derived-carbon matrix. SiC and TiO2 addition made the orientation disordered. However, porosity increased due to decomposition of SiC. Interfacial bonding could be controlled by TiO2 addition, but carbon fiber was considerably reacted with TiC during thermal treatment higher than 2$600^{\circ}C$. Therefore, it is desirable to control the thermal treatment temperature at which decomposition of SiC was not serious and TiC/C was not formed eutectoid.

• 폴리머
• /
• 제24권4호
• /
• pp.459-468
• /
• 2000

유리 또는 아라미드 섬유를 보강재로 사용한 섬유강화 복합재료의 기계적 물성을 증진시키기 위하여 복합재료 적층판을 서로 다른 매트릭스 수지와 섬유를 선정하여 이들의 인장, 굴곡 특성을 조사하였다. 불포화 폴리에스테르와 개질된 표면의 아라미드 섬유 복합재료의 경우, 굴곡 물성의 최대값은 실란 농도가 0.5 wt%일 때 관찰되었다. 불포화 폴리에스테르 수지와 유리섬유 복합재료의 인장 물성은 vinylester계가 가장 높게 나타났으며, 굴곡물성은 isophthalic계가 가장 높은 물성을 나타내었다. 유리섬유와 불포화 폴리에스테르 수지 복합재료의 기계적 물성을 증진시키기 위해 겹침 적층판과 기계적 물성과의 상관 관계에 대해서도 연구가 병행되었다.

• 대한의용생체공학회:의공학회지
• /
• 제18권1호
• /
• pp.1-8
• /
• 1997

This study was performed to evaluate the effect of resin and filler type on the compressive strength of light-activated composite resins. Experimental composite resins containing either amorphous spherical silica or crushed quartz in two matrix resins of BisGMA/TEGDMA and UTMA/TEGDMA were prepared and the specimens of 3 m in diameter and 6m in length were made. Compressive test was subjected to a crosshead speed of 0.5 mm/min, and the fracture surFaces were examined by SEM. The compressive strength of UTMA-based composite resin was higher than that of BisGMA-based composite resin. The loading rate of spherical silica was higher than that of crushed silica when the size dis- tribution of fillers was same. Strength decrease of Bis-GMA-based composite resin was severer than that of UTMA-based composite resin in a $37^{\circ}$c water environment. Fracture surface showed that the composite resin failure developed along the matrix resin and the filler/resin interface region.

• 대한전기학회논문지
• /
• 제41권6호
• /
• pp.640-651
• /
• 1992

This paper describes the electric properties of mica reinforced silicone composites with the parameter of curing condition of silicone resin, application amount of silane coupling agent to the mica paper and the mica wt% to the composite. Heat-resistant silicone resin and mica paper made of mica flakes are used to prepared the mica/silicone composite as matrix and filler, respectively. To improve the dielectric properties and interfacial adhesion between matrix and filler, silane coupling agent is applied on the mica paper. As for matrix, tan$\delta$ value of 30$0^{\circ}C$ heat-treated silicone resin is the lowest under 1%. The optimal wt% of coupling agent is 0.3% to the weight of mica paper. 80 wt% of mica as filler to the mica/silicone composite shows the best electric properties. And the mica reinforced silicone composite shows good high-frequency and mechanical tensile stress properties.

• 폴리머
• /
• 제38권2호
• /
• pp.171-179
• /
• 2014

우수한 성능을 지닌 대형 구조의 섬유강화 고분자(FRP) 복합재료 제품을 제조하기 위해 저온 경화형 프리프레그 개발이 활발히 진행되고 있다. 본 연구에서는 저온 경화형 프리프레그 제조에 적합한 매트릭스 수지를 확보하기 위하여 에폭시 수지, 경화제, 경화 촉진제로 구성된 저온 경화형 에폭시 수지 조성물의 경화거동 및 화학유변학을 고찰하였다. 경화반응 특성은 시차주사열량분석법과 유변물성측정법을 활용하여 승온 및 등온 조건에서 분석하였다. 연구 결과 매트릭스 수지로 제안된 저온 경화형 에폭시 수지 조성물은 $80^{\circ}C$에서 3시간에 경화시킬 수 있었고, 80과 $90^{\circ}C$에서의 젤화 시간은 각각 120분과 20분인 것으로 나타났다. 저온 경화형 수지를 경화시킨 수지 경화물의 열적, 기계적 물성은 고온 경화형 수지 경화물의 물성과 거의 동등하였다.

• Restorative Dentistry and Endodontics
• /
• 제45권1호
• /
• pp.9.1-9.7
• /
• 2020

The restorative procedure in posterior teeth involves clinical steps related to professional skill, especially when using the incremental technique, which may fail in the long term. A recent alternative is bulk-fill resins, which can reduce polymerization shrinkage, decreasing clinical problems such as marginal leakage, secondary caries, and fracture. This scientific study aims to report a clinical case using bulk-fill resin with an occlusal matrix. As determined in the treatment plan, an acrylic resin matrix was produced to establish an improved oral and aesthetic rehabilitation of the right mandibular first molar, which presented a carious lesion with dentin involvement. The occlusal matrix is a simple technique that maintains the original dental anatomy, showing satisfactory results regarding function and aesthetic rehabilitation.

• Carbon letters
• /
• 제1권2호
• /
• pp.60-63
• /
• 2000

In this work, the carbon fibers-reinforced carbon matrix composites made with different carbon char yields of phenolic resin matrix have been characterized by mechanical flexural tests for acoustic emission properties. The composites had been fabricated in the form of two-dimensional polyacrylonitrile based carbon fibers during the carbonization process. It was found that the composites made with the carbon char yield-rich of resin matrix result in better mechanical interfacial properties, i.e., the interlaminar shear strength (ILSS) of the composites. The data obtained from the acoustic emission monitored appeared to show that the composites made with carbon char yield-rich were also more ductile. From the acoustic emission results, the primary composite failure was largely depended on the debonding at interfaces between fibers and matrix. The interlaminar shear strengths of the composites were correlated with the acoustic emission results.