• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.2
• /
• pp.127-133
• /
• 2019

Purpose: The purpose of present study was to investigate fracture strength and mode of failure of endodontically treated teeth restored with metal cast post-core system, prefabricated fiber post system, and newly introduced polyetherketoneketone (PEKK) post-core system. Materials and methods: A total of 21 mandibular premolar were randomly grouped into 3 groups of 7 each according to the post material. Group A was for metal cast post core; Group B for prefabricated glass fiber post and resin core; and Group C for milled PEKK post cores. All specimens were restored with metal crown. The fracture strength of each specimen was measured by applying a static load of 135-degree to the tooth at 2 mm/min crosshead speed using a universal testing machine. After the fracture strength measurement, the mode of failure was observed. The results were analyzed using Kruscal-Wallis test and post hoc Mann-Whitney U test at confidence interval ${\alpha}=.05$. Results: Fracture resistance of PEKK post core was lower than those of cast metal post and fiber reinforced post with composite resin core. In the aspect of fracture mode most of the root fracture occurred in the metal post core, whereas the post detachment occurred mainly in the fiber reinforced post. In the case of PEKK post core, teeth and post were fractured together. Conclusion: It is necessary to select appropriate materials of post for extensively damaged teeth restoration and clinical application of the PEKK post seems to require more research on improvement of strength.

• Restorative Dentistry and Endodontics
• /
• v.24 no.1
• /
• pp.166-179
• /
• 1999

Apical sealing is essential for the success of surgical endodontic treatment. Root-end cavity is apt to be contaminated with moisture or blood, and is not always easy to be dried completely. The purpose of this study was to evaluate the influence of dry methods of retrocavity on the apical seal in endodontic surgery. Apical seal was investigated through the evaluation of apical leakage and adaptation of filling material over the cavity wall. To investigate the influence of various dry methods on the apical leakage, 125 palatal roots of extracted human maxillary molar teeth were used. The clinical crown of each tooth was removed at 10 mm from the root apex using a slow-speed diamond saw and water spray. Root canals of the all the specimens were prepared with step-back technique and filled with gutta-percha by lateral condensation method. After removing of the coronal 2 mm of filling material, the access cavities were closed with Cavit$^{(R)}$. Two coats of nail polish were applied to the external surface of each root. Apical three millimeters of each root was resected perpendicular to the long axis of the root with a diamond saw. Class I retrograde cavities were prepared with ultrasonic instruments. Retrocavities were washed with physiologic saline solution and dried with various methods or contaminated with human blood. Retrocavities were filled either with IRM, Super EBA or composite resin. All the specimens were immersed in 2% methylene blue solution for 7 days in an incubator at $37^{\circ}C$. The teeth were dissolved in 14 ml of 35% nitric acid solution and the dye present within the root canal system was returned to solution. The leakage of dye was quantitatively measured via spectrophotometric method. The obtained data were analysed statistically using one-way ANOVA and Duncan's Multiple Range Test. To evaluate the influence of various dry methods on the adaptation of filling material over the cavity wall, 12 palatal roots of extracted human maxillary molar teeth were used. After all the roots were prepared and filled, and retrograde cavities were made and filled as above, roots were sectioned longitudinally. Filling-dentin interface of cut surfaces were examined by scanning electron microscope. The results were as follows: 1. Cavities dried with paper point or compressed air showed less leakage than those dried with cotton pellet in Super EBA filled cavity (p<0.05). However, there was no difference between paper point- and compressed air-dried cavities. 2. When cavities were dried with compressed air, dentin-bonded composite resin-filled cavities showed less apical leakage than IRM- or Super EBA-filled ones (p<0.05). 3. Regardless of the filling material, cavities contaminated with human blood showed significantly more apical leakage than those dried with compressed air after saline irrigation (p<0.05). 4. Outer half of the cavity showed larger dentin-filling interface gap than inner half did when cavities were filled with IRM or Super EBA. 5. In all the filling material groups, cavities contaminated with blood or dried with cotton pellets only showed larger defects at the base of the cavity than ones dried with paper points or compressed air.

• Journal of dental hygiene science
• /
• v.4 no.1
• /
• pp.21-25
• /
• 2004

In modern times, children's trauma is increasing every year because of car accidents and life environment changes. There is a limit to prevent traumatic damage for oral cavity organization. The fundamental data of trauma treatment and prevention will be presented through the survey and analysis of traumatic teeth damage. I examined 113 patients from Oct. 4th, 2000 to Feb. 27th, 2004 at Dept. of Children's Dental Clinic, Kangnung National University. The results are as follows. (1) The trauma frequency of male subjects is higher than that of female at a rate of 2.05:1. The average age is 5.27 for men and 5.27 for women. The highest percentage of trauma patients is among 2 year old children. It is 21.2%. (2) A patient survey was taken at a trauma treatment hospital. On the first day 34.4% of the patients had come to receive treatment of their first set of teeth. However, after a week, 38.8% of the patients had received treatment on their permanent teeth. (3) As a result of falling, 59% of patients needing treatment on their first set of teeth. 55.1% of patients is permanent teeth. As a result of bump against physical solid, 26.6% of patients is the first set of teeth and 26.5% of patients is permanent teeth. (4) Teeth damage happened at home. 42.1% were male. 35.1% were female. According to trauma, 59.4% of teeth damage happened at home. 28.6% of permanent teeth damage happened at school or kindergarten. (5) According to trauma, the number of teeth damaged was in the first set of teeth are as follows: 56.3%, one-31.3%, three or four-6.3% each. For permanent teeth: two-46.9%, one-28.6%, four over-16.3% and three-8.2%. Over four teeth is larger number for permanent teeth. (6) 56% of first set of teeth patients and 43.4% of permanent teeth patients were male. 56.8% of first set of teeth patients and 43.2% of permanent teeth were female. Trauma happened to both male and female frequently in the first set of teeth. (7) Most of the tooth damage which was in the first set of teeth and permanent teeth was done to the upper jaw. 75% of patients are the first set of teeth. 63.8% of patients are permanent teeth. Trauma is very high in the two mid teeth of the upper jaw. (8) According to trauma survey, 30.2% is from impulse. 28.0% is from crown fracture, 14.7% is from depression. 8.9% is from concussion. 7.1% is from full dislocation of a joint. 2.2% of patients are extrusion. 1.8% is from displacement. According to teeth damage trauma, 35.8% is pulse in the first set of teeth. The breaking of the crown of a tooth happened a lot in permanent teeth. (9) According to data, 43.2% of teeth damage in the first set of teeth goes without treatment. In permanent teeth, it is 38.9%. After treatment, 22.0% of first set of teeth treatment requires a dental pulp treatment. In permanent teeth, which is used for temporary acid etching resin restoration.

• The Journal of Korean Academy of Prosthodontics
• /
• v.42 no.5
• /
• pp.514-523
• /
• 2004

Statement of problem: All-ceramic restorations have been advocated for superior esthetics. Various post and core systems have been used to improve the strength of damaged teeth, but it is unclear whether they affect the final shade of finished all-ceramic restorations. Purpose: The influence of different types of post and core systems on light transmission through all-ceramic crowns was assessed by spectrophotometric analysis. Also the masking effect of different thickness of ceramic ingot was evaluated. Material and Methods : Forty-five sample disks (15mm in diameter) at several thickness(1.0, 1.5, 2.0mm) and value(shade 100, 200, 300) were made in heat pressed ceramic(IPS-Empress). Background specimens simulating gold-alloy cast posts(Type III casting gold alloy), metal posts(Ni-Cr casting alloy) and ceramic posts(CosmoPost) were fabrica-ted. Resin composite(Z250, A3 shade) was used as a tooth substrate reference. For each combination, the change in color was measured with a spectrophotometer. Readings were performed for 2 conditions (1) ability of ceramic to mask the core in relation to its thickness(1.0, 1.5, or 2.0mm) ; (2) influence of post and core types on the final color of the ceramic. Data were recorded according to the CIE $L^*a^*b^*$ systems and color difference($\Delta$E) was calculated. Results: 100 shade ingot: when ceramic thickness was 1.0mm, $\Delta$E value for ceramic post larger than 1 but $\Delta$E value for metal and gold post was larger than 2. For ceramic thickness of 1.5mm, only $\Delta$E value for metal was larger than 2, and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 2. 200 shade ingot: when ceramic thickness was 1.0mm, $\Delta$E value for ceramic post was smaller than 1 but $\Delta$E value for metal and gold post was larger than 2. For ceramic thickness of 1.5 mm, only the $\Delta$E value for metal was larger than 2, and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 1. 300 shade ingot: when ceramic thickness was 1.0mm, only $\Delta$E value for metal was larger than 2 and the other samples' $\Delta$E value was smaller than 2. For ceramic thickness of 1.5mm, $\Delta$E values for all specimens was smaller than 1. For ceramic thickness of 2.0mm, $\Delta$E values for all specimens was smaller than 1. Conclusion: The final esthetic result of the IPS-Empress glass-ceramic restoration was not affected by the presence of different core materials when the thickness was more than 2.0 mm. When ceramic thickness decreases to 1.5mm, it is advised to take the substrate aspects into consideration. If the ceramic thickness is less than 1.0mm, using the tooth color matched substrate is strongly recommended.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.35 no.2
• /
• pp.278-286
• /
• 2008

Many studies regarding Casein phosphopeptides-amorphous calcium phosphate(CPP-ACP) have demonstrated the remineralization ability on the demineralized enamel surface. A question is still remained that how deep can the calcium (Ca) and phosphorus (P) ions supplied by the CPP-ACP paste penetrate into the enamel subsurface. The aims of this study were to measure the penetrating depth of Ca and P ions in the demineralized human enamel in vitro, and were to determine the amount and depth of Ca and P ions according to the duration. The amount and depth of Ca and P ions were measured by microscopic observation with Field Emission Scanning Electron Microscopy (FE-SEM; LEO SUPRA 55, Carl Zeiss, Germany) and Energy Dispersive X-ray Spectrometer (EDS; GENESIS 2000, EDAX, USA: Linescan of Calcium and Phosphorus). Freshly extracted four human 1st premolars were obtained from the Dept. of Pediatric Dent., Kyung Hee Univ. Buccal surfaces of the 1st premolars were covered with nail varnish to form a window on the middle third of buccal surface. All of the teeth with enamel windows were immersed in a solution of 0.1 M lactic acid, Carbopol C907 (carboxypolymethylene BF Goodrich, Cleveland, OH, USA) at pH 4.8, and then incubated for 7 days. Each tooth crown was sawn in half through the midline of buccal window along the long axis of premolar. The four blocks of premolars were immersed in a 10-times diluted solution of CPP-ACP paste (Tooth Mousse, GC Corp., Tokyo, Japan) for 1, 2, 3 and 5 weeks while the rests were immersed in a placebo solution (distilled water) for the same duration. Each specimen was embedded in epoxy resin, and was sectioned perpendicular to the window, using a water-cooled diamond blade saw. The spectrum density indices of Ca and P were measured in the sound, de- and remineralized enamels by FE-SEM and EDS. The Student's t test was performed to compare the Spectrum Density Indices (SDI) of sound, re-and demineralized enamels, and to compare the differences among the durations. Followings are the conclusion : 1. The penetration depth of the remineralizing ions (Ca & P) of CPP-ACP paste is related to the depth of demineralized enamel (approximately $1050{\sim}1350{\mu}m$). It is revealed that the penetration depth of both ions reaches full thickness of decalcification and even slightly into the sound enamel. 2. The Ca & P levels of remineralized enamels in 1, 2 weeks were significantly higher than those of the sound enamels (p<0.05). 3. No statistically significant difference of Ca & P levels was found in relation with the increasing duration of remineralization (p>0.05).