• Journal of the Korean Magnetics Society
• /
• v.22 no.6
• /
• pp.221-227
• /
• 2012

High performance permanent magnets have become the subject of considerable attention because of the potential applications in the traction motors of hybrid and electric vehicles and wind generators. Nd-Fe-B magnets have attracted considerable interest due to a large maximum energy product. However, Nd-Fe-B magnet cannot be used in high temperature (${\sim}200^{\circ}C$) applications due to the thermal degradation of coercivity. Therefore, the development of high coercivity Nd-Fe-B permanent magnet is a challenging issue. In case of high coercivity Nd-Fe-B permanent magnet, an increment in the intrinsic coercivity can be easily achieved by substituting Nd atoms with Dy or Tb atoms. However, these heavy rare-earth elements are known to cause a decrease in remanence due to the antiferromagnetic coupling between Dy and Fe atoms. In addition, Dy is relatively expensive and being limited in quantity. Hence, a new technology that can increase the coercivity of Nd-Fe-B sintered magnet using only a small amount, or even, no amount of heavy rare-earth elements is being investigated. This article describes the research trend in reducing the heavy rare-earth elements in Nd-Fe-B magnets.

• Carbon letters
• /
• v.21
• /
• pp.16-22
• /
• 2017

Cobalt was electrodeposited onto chemical vapor deposition (CVD) graphene/Si/$SiO_2$ substrates, during different time intervals, using an electrolyte solution containing a low concentration of cobalt sulfate. The intention was to investigate the details of the deposition process (and the dissolution process) and the resulting magnetic properties of the Co deposits on graphene. During and after electrodeposition, in-situ magnetic measurements were performed using an (AGFM). These were followed by ex situ morphological analysis of the samples with ${\Delta}t_{DEP}$ 30 and 100 s by atomic force microscopy in the non-contact mode on pristine CVD graphene/$SiO_2$/Si. We demonstrate that it is possible to electrodeposit Co onto graphene, and that in-situ magnetic measurements can also help in understanding details of the deposition process itself. The results show that the Co deposits are ferromagnetic with decreasing coercivity ($H_C$) and demonstrate increasing magnetization on saturation ($M_{SAT}$) and electric signal proportional to remanence ($M_r$), as a function of the amount of the electrodeposited Co. It was also found that, after the end of the dissolution process, a certain amount of cobalt remains on the graphene in oxide form (this was confirmed by X-ray photoelectron spectroscopy), as suggested by the magnetic measurements. This oxide tends to exhibit a limited asymptotic amount when cycling through the deposition/dissolution process for increasing deposition times, possibly indicating that the oxidation process is similar to the graphene surface chemistry.

• Journal of the Korean Magnetics Society
• /
• v.6 no.2
• /
• pp.80-85
• /
• 1996

An externally applied magnetic field during annealing the $Nd_{2}Fe_{14}B/Fe_{3}B$ based spring magnet was found to enhance the exchange coupling between the hard and soft magnetic grains. More than 30 % increase in remanence values for melt-spun $Nd_{4}Fe_{73.5}Co_{3}(Hf_{1-x}-Ga_{x})B_{18.5}$(x=0, 0.5, 1.0) alloys was resulted from uniform distribution of $Fe_{3}B$, $\alpha$-Fe as well as $(Nd_{2}Fe_{14}B)$, and also from reduced grain size of those phases by 20 %. The result also showed that there is an optimum grain size exhibiting a high coercivity value which will be discussed in terms of previously simulated exchange coupling parameter.

• Journal of Magnetics
• /
• v.20 no.2
• /
• pp.97-102
• /
• 2015

The waste of sintered Nd-Fe-B magnets was recycled using the method of dopingPrNd nanoparticles. The effect of PrNd nanoparticle doping on the magnetic properties of the regenerated magnets has been studied. As the content of the PrNd nanoparticles increases, the coercivity increases monotonically, whereas both the remanence and the maximum energy products reach the maximum values for 4 wt% PrNd doping. Microstructural observation reveals that the appropriate addition of PrNd nanoparticles improves the magnetic properties and refines the grain. Domain investigation shows that the self-pinning effect of the rare earth (Re)-rich phase is enhanced by PrNd nano-particle doping. Compared to the magnet with 4 wt% PrNd alloy prepared using the dual-alloy method, the regenerated magnet doped with the same number of PrNd nanoparticles exhibits better magnetic properties and a more homogeneous microstructure. Therefore, it is concluded that PrNd nanoparticle doping is an efficient method for recycling the leftover scraps of Nd-Fe-B magnets.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.18 no.6
• /
• pp.477-483
• /
• 1998

Hysteresis loop, Barkhausen noise(BN), and hardness were measured in the neutron irradiated RPV steel for various fluence, irradiated dose up to $10^{18}n/cm^2$. The coercivity, remanence and maximum induction of neutron irradiated samples did not change significantly, but the BNA and BNE were decreased as the neutron irradiation increased. The changes of BNE and BNA were characterized by three stages with respect to neutron dose. The BNA and BNE were decreased with an increase of neutron dose to $10^{12}n/cm^2$, and remained nearly constant up to $10^{16}n/cm^2$, then were decreased rapidly with an increase of the neutron dose above $10^{16}n/cm^2$. On the other hand, the hardness was observed revesely with the change of BNA and BNE.

• Journal of the Korean Magnetics Society
• /
• v.9 no.3
• /
• pp.154-158
• /
• 1999

Magnetic properties and microstructure of nanocrystalline $\alpha$-(Fe, Co)-based Nd-(Fe, Co)-B-Nb-Cu alloys have been investigated. $Nd_x(Fe_{0.9}Co_{0.1})_{90-x}B_6Nb_3Cu_1$(x=2, 3, 4, 5, 6) alloys prepared by rapid solidification process show amorphous phase except the one with x=2. By a proper annealing, the amorphous in the alloy is changed to a nanocrystalline phase. It is confirmed that the nanocrystalline alloys are composed of $\alpha$-(Fe, Co) and $Nd_2(Fe, Co)_{14}B_1$ phase. The optimally annealed $Nd_3(Fe_{0.9}Co_{0.1})_87B_6Nb_3Cu_1$ alloy shows the highest remanence of 1.55 T. The coercivity increases with the increase of Nd content The maximum coercivity of 4.6 kOe is obtained from an optimally annealed $Nd_6(Fe_{0.9}Co_{0.1})_84B_6Nb_3Cu_1$ alloy, resulting in the maximum energy product of 10.6 MGOe.

• Journal of Magnetics
• /
• v.20 no.1
• /
• pp.31-39
• /
• 2015

Macroscopic hysteresis loops and microscopic magnetic moment distributions have been determined by a three-dimensional (3D) model for exchange-coupled Sm-Co/${\alpha}-Fe$/Sm-Co trilayers with in-plane collinear easy axes. These results are carefully compared with the popular one-dimensional (1D) micromagnetic models and recent experimental data. It is found that the results obtained from the two methods match very well, especially for the remanence and coercivity, justifying the calculations. Both nucleation and coercive fields decrease monotonically as the soft layer thickness $L^s$ increases while the largest maximum energy product (roughly 50 MGOe) occurs when the thicknesses of hard and soft layers are 5 nm and 15 nm, respectively. Moreover, the calculated angular distributions in the thickness direction for the magnetic moments are similar. Nevertheless, the calculated nucleation and pinning fields as well as the energy products by 3D OOMMF are systematically smaller than those given by the 1D model, due mainly to the stray fields at the corners of the films. These demagnetization fields help the magnetic moments at the corners to deviate from the previous saturation state and facilitate the nucleation. Such an effect enhances as $L^s$ increases. When the thicknesses of hard and soft layers are 10 nm and 20 nm, respectively, the pinning field difference is as large as 30%, while the nucleation fields have opposite signs.

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.4
• /
• pp.137-142
• /
• 2018

Room temperature ferromagnetism of Co doped ZnO was studied using (ZnO/Co) multilayer structure, and the effects of ZnO sub-layer thickness on the RT ferromagnetism was investigated. As for the as-deposited state, the diamagnetism was observed for ($ZnO\;20{\AA}/Co\;x{\AA}$) while the ferromagnetism was observed for ($ZnO\;40{\AA}/Co\;x{\AA}$). After vacuum-annealed, both showed the RT ferromagnetism and ($ZnO\;40{\AA}/Co\;x{\AA}$) structure interestingly showed negative remanence magnetization behavior. UV-Vis spectrometer revealed that Co atoms were substituted with Zn in ZnO and Co cluster was not found in XPS and HRTEM EDS analysis.

• Korean Journal of Metals and Materials
• /
• v.49 no.6
• /
• pp.505-513
• /
• 2011

A magnetic device which enables the application of a strong and uniform magnetic field to thin film during sputtering was designed for controlling the magnetic anisotropy using a three dimensional finite element method, and the effects of the external magnetic field on the magnetic properties of sputtered thin films were investigated. Both the intensity and the uniformity of the magnetic flux density in the sputter zone (50 mm ${\times}$50 mm) was dependent on not only the shape and size of the magnet device but also the magnitude of stray fields from the magnet. For the magnet device in which the distance between two magnets or two pure iron bars was 80-90 mm, the magnetic flux density along the direction normal to the external magnetic field direction was minimum. The two row magnets increased the magnetic flux density and uniformity along the external magnetic field direction. An Fe thin film sputtered using the optimized magnet device showed a higher remanence ratio than that fabricated under no external magnetic field.

• Korean Journal of Metals and Materials
• /
• v.49 no.1
• /
• pp.85-91
• /
• 2011

Alnico magnets can be used as magnetic bearings for the precise electric power measuring instruments such as watt-hour meters because they have high remanence ($B_r$), relatively high maximum energy product ($(BH)_{max}$), and excellent temperature stability. In this study, Alnico composite magnets were fabricated by appropriately mixing alnico alloy powders with epoxy resin and binder. The Alnico powders mixed with epoxy resin and a hardening agent with a mixing ratio of 96:4 were pressed and then cured to be a toroid-type ring magnet with an outer diameter (${\Phi}_{out}$) of 15 mm, an inner diameter (${\Phi}_{in}$) of 6.5 mm and a thickness (t) of 2.5 mm, respectively. The magnetic properties of the Alnico ring magnets were varied with the mixing ratio of Alnico powders that possess different average particle sizes. The Alnico ring magnet prepared by mixing 5 wt% of $50{\mu}m$ (small size) powder, 15~20 wt% of $150{\mu}m$ (medium size) powder, and 75~80 wt% of $300{\mu}m$ (large size) powder showed the best magnetic properties (remanent induction, coercive force, maximum energy product, and surface flux density). In addition, measurements of temperature and moisture characteristics for the Alnico ring magnets showed that the surface flux densities of the N and S poles decreased little and the repulsive distance between the magnets decreased as small as 0.05 mm after 10 days.