Recently, there are many efforts focused on development of more economical non-fluorinated membranes for PEMFCs (Proton Exchange Membrane Fuel Cells). In this study, sulfonated poly (ether ether ketone) (sPEEK) membrane reinforced with poly imide was made to enhance of membrane durability. In order to test durability of single (un-reinforced) membrane and reinforced membrane MEA (Membrane and Electrode Assembly), degradation accelerated stress test was used. Before and after degradation, I-V polarization curve, hydrogen crossover current, electrochemical surface area, membrane resistance and charge transfer resistance were measured. As a result of experiments, hydrogen crossover current of reinforced MEA was lower than that of single MEA, therefor durability of reinforced MEA was higher than that of single MEA. There was not especially short phenomena in reinforced MEA after degradation accelerated stress test.

• Korean Chemical Engineering Research
• /
• v.60 no.2
• /
• pp.217-222
• /
• 2022

It is very important to analyze the OCV change behavior during the open circuit potential holding (OCV holding) process, which accelerates the evaluation of the electrochemical durability of the PEMFC membrane. In this study, an empirical formula using the experimental data of three MEAs with different durability was created and compared. The durability evaluation time of the reinforced membrane MEA without radical scavenger inside the membrane was 383 h, and the durability evaluation time of the reinforced membrane MEA with radical scavenger inside the membrane was 1,000 and 1,650 h, respectively. The degradation of the membrane was divided into the reversible degradation that can be recovered by activation and the irreversible degradation that is not recovered. The irreversible degradation of the membrane was indicated by an increase in hydrogen permeability, and the change in hydrogen permeability was similar to the irreversible degradation constant c of all three MEAs. The initiation of irreversible deterioration without recovery is indicated by an increase in hydrogen permeability, and the OCV is not recovered due to an increase in hydrogen permeability, so the slope of the OCV recovery line (ORL) decreases, which can be confirmed by an increase in the constant c value of the empirical formula.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.3
• /
• pp.90-95
• /
• 2000

Today fiber composite materials are routinely used in such wide applications as ships automobiles aircraft space vehi-cles containers sporting goods and appliances. The current knowledge of machining glass fiber reinforced polyester com-posites unfortunately is inadequate for its optimum utilization in many applications. Therefore This paper deals with drilling characteristic of glass fiber reinforced polyester composites. In the drilling of glass fiber reinforced polyester the quality of the cut surfaces is strongly dependent on the drilling parameters. drilling tests were carried out on glass fiber reinforced polyester using standard HSS tools. The material containing random chopped strand fibers and woven roving was fabricated by hand lay-up The entrance and exit surface of the holes was examined. The cutting force was also mea-sured to analyze the drilling characteristics,.