• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 1997년도 제26회 추계학술대회
• /
• pp.110-116
• /
• 1997

The tribological behaviour of WS$_2$ solid lubricant was investigated using a ball-on-disk type tester. The WS$_2$ powder was spray-coated at room temperature and the effects of specimen configuration, atmosphere, applied load and rotating spccd on the friction coefficient was examined. WS$_2$ coated ball and disk showed the lowest friction coefficient of 0.05 in the nitrogen atmosphere under 0.3 kgf and 100 rpm, whereas relatively high coefficient of 0.1 - 0.15 was observed in air atmosphere. This confirmed that the spray-coated WS$_2$ solid lubricant was effective in reducing the friction coefficient and improving wear life in nitrogen atmosphere.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 1993년도 추계학술강연 및 발표대회강연 및 발표논문 초록집
• /
• pp.5-5
• /
• 1993

• 한국세라믹학회지
• /
• 제46권3호
• /
• pp.330-335
• /
• 2009

We investigated the effects of the re-oxidation temperature and time on the positive temperature coefficient (PTC) of resistivity characteristics of Sm-doped $BaTiO_3$ sintered at $1200{\sim}1260^{\circ}C$ for 2 h in a reducing atmosphere (3% $H_2/N_2$), followed by re-oxidization processes in air, in which re-oxidization temperature and time were $600{\sim}1000^{\circ}C$ and $1{\sim}10$h, respectively. The result reveals that Smdoped (Ba,Ca)$TiO_3$ ceramics fired in a reducing atmosphere exhibit low PTC characteristics, whereas the sample re-oxidized at $800^{\circ}C$ for 1 h in air exhibit pronounced PTC characteristics. The room-temperature resistivity and jumping characteristics of resistivity (${\rho}_{max}/{\rho}25^{\circ}C$) decrease with Sm contents. The PTC characteristics with reoxidization time at $800^{\circ}C$ have improved about $2{\sim}3$ orders of magnitude whereas differed according to the sintering temperature. The 0.7 at% Sm-doped (Ba,Ca)$TiO_3$ samples reveal the best PTC characteristics in the present range of formula and processes.

• 대한전자공학회:학술대회논문집
• /
• 대한전자공학회 2001년도 The 6th International Symposium of East Asian Resources Recycling Technology
• /
• pp.605-609
• /
• 2001

Low density ceramic supporter was prepared by using fly ash as a starting material for the application to the biological aerated filter (BAF) system, and the effect of additives and sintering atmosphere on the apparent and bulk density of the carrier was examined. Borax, Na$_2$O and glass powders were added to produce liquid phase. The density of the supporter decreased as the amount of borax increased. The bulk density of 0.79 g/㎤ and the apparent density of 1.10 g/㎤ were obtained when the fly ash with 15% of borax was sintered at 116$0^{\circ}C$ for 15 minutes. The density also decreased as the plate glass powders past through 22${\mu}{\textrm}{m}$ size were mixed. When the fly ash with 12% of grass powder was sintered at 128$0^{\circ}C$ for 10 minutes, the bulk and apparent density were 0.90g/㎤ and 1.00 g/㎤, respectively. Apparent density of 1.6~1.8g/㎤ was obtained when the fly ash was sintered at 120$0^{\circ}C$ in a weak reducing atmosphere. By maintaining the reducing atmosphere and sintering at a high heating rate, the liquid phase was farmed from the reduced composition of fly ash. This resulted in the formation of closed pores that enabled the low apparent density.

• 한국세라믹학회지
• /
• 제28권3호
• /
• pp.179-188
• /
• 1991

The semiconducting BaTiO3 ceramics used in this study were sintered in the reducing atomosphere(hydrogen gas) and neutral atmosphere(nitrogen gas), then were heat-treated in air to vary defect concentrations. In this experiment, the correlations between the composition analysis and electrical characteristics of these samples were investigated. When the BaTiO3 ceramics were sintered in N2 atmosphere, it was observed that the Ba contents near the interface were lower than that of the grain center, and these samples showed superior PTCR effects. From analysis of the resistivities of grains and grain boundaries by CIRM(Complex Impedance Resonance Method), it was confirmed that the PTCR effects were caused by the resistivity of grain boundaries. And from measurement of the capacitance at each temperature, the samples sintered in N2 atmosphere show the increase of room temperature resistance and the decrease of capacitance as a result of the increase of the charge depletion layers. This phenomenon agrees well with the cation deficiencies in the analytical results.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.826-829
• /
• 2002

$MoO_3$ thin films were deposited on electrode and heater screen-printed alumina substrates in en atmosphere by RF reactive sputtering. The deposition was performed at $300^{\circ}C$ with 350W of a forward power in an $Ar-O_2$ atmosphere. The working pressure was maintained at $3{\times}10^{-2}$mtorr and all deposited films were annealed at $500^{\circ}C$ for 5hours. The surface morphology of films was observed by using a SEM and crystalline phases were analyzed by XRD. The sensing properties were investigated in term of gas concentration under exposure of reducing gases such as $H_2$, $NH_3$ and CO.

• 대한화학회지
• /
• 제29권4호
• /
• pp.437-440
• /
• 1985

유기아지드화물은 일산화탄소대기압하, 실온에서 높은 선택적 환원시약인 테트라카르 보닐철산염의 존재하에서 높은 수득율의 아민으로 환원되었다. 특히 벤조일아지드는 동일시약내 일산화탄소 대기압 실온에서는 에틸페닐카바메이트를 주나, -40$^{\circ}$에서는 정량적으로 벤즈아미드가 얻어졌다.

• 한국세라믹학회지
• /
• 제27권6호
• /
• pp.741-746
• /
• 1990

Dielectrics which do not lose their high insulation resistance in reducing atmosphere are necessary for multilayer ceramic capacitors with Ni internal electrode. In this study we investigated the Ca ion site occupancy in A-site excess Ca-doped BaTiO3 by measuring the insulation resistance, lattice constant and Curie temperature. Its Curie temperature, which was lower than that of the pure BaTiO3, was more lowered by sintering in reducing atmosphere. Lattice constnat of c-axis decreased and that of a-axis increased, suggesting substitution of Ca ions for Ti ions. Hence CaTi" acts as an acceptor to maintain high insulation resistance.ance.

• Journal of Ceramic Processing Research
• /
• 제13권spc1호
• /
• pp.59-63
• /
• 2012

Ga2O3-core/CdO-shell nanowires were synthesized by a two step process comprising thermal evaporation of GaN powders and sputter-deposition of CdO. Transmission electron microscopy (TEM) and X-ray diffraction (XRD) analyses revealed that the cores and the shells of the annealed coaxial nanowires were single crystal of monoclinic Ga2O3 and FCC CdO, respectively. As-synthesized Ga2O3 nanowires showed a broad emission band at approximately 460 nm in the blue region. The blue emission intensity of the Ga2O3 nanowires was slightly decreased by CdO coating, but it was significantly increased by subsequent thermal annealing in a reducing atmosphere. The major emission peak was also shifted from ~500 nm by annealing in a reducing atmosphere, which is attributed to the increases in the Cd interstitial and O vacancy concentrations in the cores.

• Journal of Ceramic Processing Research
• /
• 제13권spc2호
• /
• pp.189-192
• /
• 2012

Manufacturing process for silicate glass phosphors containing Eu2+ activator and their photoluminescence property have been studied. We adopted powder sintering process instead of traditional glass melting process for making glass phosphor. At first, phosphor powders were synthesized at 1200 ℃ for 2-3 hours under a reducing atmosphere with 10% H2-90% N2 gas mixture. The reduced powders were compacted into discs and then the discs weresintered at 1400 ~ 1500 ℃ for 1 hr under a reducing atmosphere of 5H2-95% N2. The enhancement of PL intensity by Al2O3 addition, XPS binding energy shift of Si 2p and O 1s, sintering shrinkage, and crystallization were characterized.