• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 춘계학술대회논문집A
• /
• pp.49-54
• /
• 2000

Cr-Mo-V steel is widely used as a material for the turbine structural component in fossil power plants. It is well known that this material shows the various material degradation phenomenons such as temper embrittlement, carbide coarsening. and softening etc. or ins to the severe operation conditions as high temperature and high pressure. These deteriorative factors cause tile change of mechanical properties as reduction of fracture toughness. Therefor it is necessary to evaluate tile extent of degradation damage for Cr-Mo-V steel in life assessment of turbine structural components. In this paper. the electrochemical potentiokinetic reactivation(EPR) test in $50wt%-Ca(NO_3)_2$ solution is performed to develop the newly technique for degradation damage evaluation of Cr-Mo-V steel. The results obtained from the EPR test are compared with those in small punch(SP) tests recommended by semi-nondestructive testing method using miniaturized specimen. The evaluation parameters used in EPR test are tile reactivation current density$(I_R)$ and charge$(Q_{RC})$ reactivation rate$(I_R/I_{Crit},\;Q_R/Q_{Crit})$. The results suggest that $I_R/I_{Crit}$ in these parameters shows a good correlation with SP test results.

• 대한기계학회논문집A
• /
• 제26권7호
• /
• pp.1241-1249
• /
• 2002

The extent of materials deterioration can be evaluated accurately by mechanical test such as impact test or creep test. But it is almost impossible to extract a large test specimen from in-service components. Thus material degradation evaluation by non-destructive method is earnestly required. In this paper, the material degradation for virgin and several aged materials of a Cr-Mo-V steel, which is an candidated as structural material of the turbine casing components for electric power plant, is nondestructively evaluated by reactivation polarization testing method. And, the results obtained from the test are compared with those in small punch(SP) tests recommended as a semi-nondestructive testing method using miniaturized specimen. In contrast to the aged materials up to 1,000hrs which exhibit the degradation behaviors with increased ${\Delta}[DBTT]_{SP}$, the improvement of mechanical property can be observed on the 2,000hrs and 3,000hrs aged materials. This is because of the softening of material due to the carbide precipitation, the increase of ferritic structures and the recovery of dislocation microstructure by long-time heat treatment. The reactivation rates($I_R/I_{Crit},\;Q_R/Q_{Crit}$) calculated by reactivation current densityt ($I_R$) and charge($Q_R$) in the polarization curves exhibit a good correlation with ${\Delta}[DBTT]_{SP}$ behaviors.

• Corrosion Science and Technology
• /
• 제2권3호
• /
• pp.117-126
• /
• 2003

Due to excellent corrosion resistance and mechanical properties, austenitic stainless steel is widely used as the material for chemical plants. nuclear power plants, and food processing facilities. But, the zone affected by heat in the range of 400 to $800^{\circ}C$ during welding loses corrosion resistance and tensile strength since Cr-carbide precipitation like $Cr_{23}C_6$ forms at the grain boundary and thereby takes place the intergranular corrosion. In this study, AISI 304 stainless steel with the added Nb of 0.3 to 0.7 wt% was solutionized at $1050^{\circ}C$ and sensitized at $650^{\circ}C$. Specimen was welded by MIG. The phase and the microstructure of the specimens were examined by an optical microscope, a scanning electron microscope, and a x-ray diffractometer. The corrosion characteristics of specimens were tested by electrolytic etching and by double loop electrochemical potentiokinetic reactivation method(EPR) in the mixed solution of 0.5M $H_2SO_4$ + 0.01M KSCN. The melting zone had dendritic structure constituted of austenitic phase and $\delta$-ferrite phase. Cr carbide at the matrix did not appear, as Nb content increased. At the grain boundaries of the heat affected zone, the precipitates decreased and the twins appeared. The hardness increased, as Nb content increased. The hardness was highest in the order of the heat affected zone>melted zone>matrix. According to EPR curve, as the Nb content decreased, the reactivation current density(Ir) and the activation current density(la) were highest in the order of the melted zone

• Corrosion Science and Technology
• /
• 제19권1호
• /
• pp.37-42
• /
• 2020

Even though 304 low-carbon (304L) stainless steel was developed to enhance the resistance to intergranular corrosion and stress corrosion cracking, it is occasionally subject to degradation in harsh environments. The degree of sensitization (DOS) of 304L stainless steel was studied as a function of sensitization using a double-loop electrochemical potentiokinetic reactivation (DL-EPR) method. Sensitizing heat treatment was performed in an Ar atmosphere at 500℃, 600℃, and 700℃, with heat treatment times varying from 0 to 96 h. DOS was measured by the ratio of the peak current density value of the forward scan to that of the reverse scan. After the EPR experiment, the specimen surface was observed by scanning electron microscopy and energy dispersive spectroscopy. The DOS of the specimens heat-treated at 600℃ increased with heat treatment times up to 48 h and then decreased due to a self healing effect. The DOS was higher in specimens heat-treated at 600℃ than those at 500℃ or 700℃. Corrosion of the sensitized specimens occurred mainly at the δ-γ phase boundary. The corrosion morphology at the δ-γ phase boundary changed with sensitizing heat-treatment conditions due to differences in chromium activity in γ austenite and δ ferrite.

• 한국표면공학회지
• /
• 제38권6호
• /
• pp.227-233
• /
• 2005

Electrochemical characteristics of welded stainless steels containing Ti have been studied by using the electrochemical techniques in 0.5 M $H_2SO_4$+0.01 M KSCN solutions at $25^{\circ}C$. Stainless steels with 12 mm thick-ness containing $0.2{\~}0.9 wt\%$ Ti were fabricated with vacuum melting and following rolling process. The stainless steels were solutionized for 1hr at $1050^{\circ}C$ and welded by MIG method. Samples were individually prepared with welded zone, heat affected zone, and matrix for intergranular corrosion and pitting test. Optical microscope, XRD and SEM are used for analysing microstructure, surface and corrosion morphology of the stainless steels. The welded zone of the stainless steel with lower Ti content have shown dendrite structure mixed with $\gamma$ and $\delta$ phase. The Cr-carbides were precipitated at twin and grain boundary in heat affected zone of the steel and also the matrix had the typical solutionized structure. The result of electrochemical measurements showed that the corrosion potential of welded stainless steel were Increased with higher Ti content. On the other hand, reactivation($I_r$), passivation and active current($I_a$) density were decreased with higher Ti content. In the case of lower Ti content, the corrosion attack of welded stainless steel was remarkably occurred along intergranular boundary and ${\gamma}/{\delta}$ phase boundary in heat affected zone.

• 공업화학
• /
• 제3권3호
• /
• pp.527-534
• /
• 1992

Raney nickel 촉매를 이용하여 알칼리형 연료전지의 수소극을 제작하였다. $700^{\circ}C$에서 소결한 Raney nickel로 제작한 수소극의 경우 가장 좋은 전극성능을 갖는 $450mA/cm^2$의 전류밀도를 나타냈으며 이때의 평균촉매입자 크기는 $90{\AA}$이었다. CO-chemisorption 측정 및 분극곡선과 Tafel slope를 통하여 PTFE의 첨가량에 대한 전극의 전기화학적 성능을 고찰하였다. CO-chemisorption 측정 결과 5wt%의 PTFE가 첨가되었을 때 최고값을 갖는 것이 확인되었으나 전극에서의 전류밀도와 Tafel slope를 비교한 결과 10wt%의 PTFE를 첨가하는 경우가 가장 적당함을 알았다. Raney nickel제조시 nicke과 aluminum의 함량비는 60:40의 경우에 가장 좋은 전극 특성을 나타내었으며 담지량은 $0.25g/cm^2$의 경우가 적당하였다. 전극제조시 촉매층의 press압 및 촉매층과 기체확산층과의 접합시의 Press압에 대한 영향도 검토하였다. 또한 촉매의 표면 구조를 SEM으로 관찰하였으며 활성화시간 및 열처리 온도 등 여러가지 조건에 대한 전극의 영향도 고찰하였다.