• Journal of the Korean Electrochemical Society
• /
• v.17 no.1
• /
• pp.65-70
• /
• 2014

In this study, crosslinked poly(POEM-co-AMPSLi-co-GMA)s were prepared by epoxy coupling of GMA after radical copolymerization of AMPS, POEM and GMA followed by acid-base titration reaction between sulfonic acid of AMPS and $Li_2CO_3$. It was observed that the crystalline melting temperature of POEM was effected by mol% of components and shifted to lower value by lithiation of AMPS group. The ionic conductivity of crosslinked polymer electrolyte was decreased by addition of GMA but maintained over $1.0{\times}10^{-6}S\;cm^{-1}$ until 16 mol%. Particularly, the self-doped polymer electrolyte with 2 mol% of GMA showed its ionic conductivity as high as $4.08{\times}10^{-6}S\;cm^{-1}$ at room temperature and electrochemical stability up to 6 V. In addition, 0.11 MPa of modulus and 270% of elongation were obtained from the free standing film of crosslinked polymer electrolyte.

• Applied Chemistry for Engineering
• /
• v.10 no.5
• /
• pp.701-706
• /
• 1999

The effect of siloxane oligomer content on thermal stability and internal stress of DGEBA epoxy resin was investigated. Siloxane-epoxy polymers having terminal epoxy group were prepared by reaction of siloxane-DDM prepolymer with DGEBA epoxy resin. Thermal stability was studied in terms of the initial decomposition temperature(IDT), temperature of maximum rate of weight loss($T_{max}$), integral procedural decomposition temperature(IPDT), and decomposition activation energy($E_t$) using TGA data. The thermal stability increased with increasing the siloxane oligomer content and showed a maximum value in the case of 5 wt% siloxane oligomer content in the blend system. While, the coefficient of thermal expansion(${\alpha}_r$) and the flexural modulus($E_r$) allowed us to study internal stress of the blend system. As the content of siloxane oligomer increases, the internal stress systematically decreases as decreasing both ${\alpha}_r$ and $E_r$.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.06a
• /
• pp.1507-1510
• /
• 2005

This study was carried out as a part of the research on the development of a maskless and electroless process for fabricating metal micro/nanostructures by using a nanoindenter and an electroless deposition technique. $2-\mu{m}-deep$ indentation tests on Ni and Cu samples were performed. The elastic recovery of the Ni and Cu was 9.30% and 9.53% of the maximum penetration depth, respectively. The hardness and the elastic modulus were 1.56 GPa and 120 GPa for Ni and 1.49 GPa and 100 GPa for Cu. The effect of single-point diamond machining conditions such as the Berkovich tip orientation (0, 45, and $90^{\circ}$) and the normal load (0.1, 0.3, 0.5, 1, 3, and 5 mN), on both the deformation behavior and the morphology of cutting traces (such as width and depth) was investigated by constant-load scratch tests. The tip orientation had a significant influence on the coefficient of friction, which varied from 0.52-0.66 for Ni and from 0.46-0.61 for Cu. The crisscross-pattern sample showed that the tip orientation strongly affects the surface quality of the machined area during scratching. A selective deposition of Cu at the pit-like defect on a p-type Si(111) surface was also investigated. Preferential deposition of the Cu occurred at the surface defect sites of silicon wafers, indicating that those defect sites act as active sites for the deposition reaction. The shape of the Cu-deposited area was almost the same as that of the residual stress field.

• Korean Journal of Materials Research
• /
• v.20 no.4
• /
• pp.217-222
• /
• 2010

Zirconium diboride (ZrB2) and mixed diboride of (Zr0.7Ta0.3)B2 containing 30 vol.% silicon carbide (SiC) composites were prepared by hot-pressing at $1800^{\circ}C$. XRD analysis identified the high crystalline metal diboride-SiC composites at $1800^{\circ}C$. The TaB2 addition to ZrB2-SiC showed a slight peak shift to a higher angle of 2-theta of ZrB2, which confirmed the presence of a homogeneous solid solution. Elastic modulus, hardness and fracture toughness were slightly increased by addition of TaB2. A volatility diagram was calculated to understand the oxidation behavior. Oxidation behavior was investigated at $1500^{\circ}C$ under ambient and low oxygen partial pressure (pO2~10-8 Pa). In an ambient environment, the TaB2 addition to the ZrB2-SiC improved the oxidation resistance over entire range of evaluated temperatures by formation of a less porous oxide layer beneath the surface SiO2. Exposure of metal boride-SiC at low pO2 resulted in active oxidation of SiC due to the high vapor pressure of SiO (g), and, as a result, it produced a porous surface layer. The depth variations of the oxidized layer were measured by SEM. In the ZrB2-SiC composite, the thickness of the reaction layer linearly increased as a function of time and showed active oxidation kinetics. The TaB2 addition to the ZrB2-SiC composite showed improved oxidation resistance with slight deviation from the linearity in depth variation.

• Polymer(Korea)
• /
• v.25 no.5
• /
• pp.691-698
• /
• 2001

Nanocomposites based on epoxy acid nanoclay were prepared employing organically modified mica type silicate (OMTS), diglycidyl ether of bisphenol A (DGEBA) type epoxy. curing agent (dicyandiamide; DICY), and catalyst (benzyl dimethyl amine; BDMA). Both melt mixing and solution mixing were und for the sample preparation and structural developments with curing reaction were analyzed using X-ray diffractometer (XRD) and small angle X-ray scattering (SAXS). Because of the different curing rate between extra-gallery and intra-gallery reactions of epoxy mixtures, only intercalated structure was observed for the sample prepared by melt mixing while fully exfoliated structure was observed for the sample prepared by solution mixing. Mechanical properties of exfoliated epoxy nanocomposite were investigated using a dynamic mechanical analyzer (DMA). The dynamic storage modulus of the nanocomposite in both glass and rubbery plateau regions were increased with increasing OMTS contents, but glass transition temperatures ($T_g$) remained unchanged. Thermal properties of epoxy nanocomposite were investigated using thermogravimetric (TGA) and limit oxygen index (LOI) methods. Thermal decomposition onset points and LOI values were increased with increasing OMTS contents due to barrier effects of OMTS sheets.

• Polymer(Korea)
• /
• v.34 no.2
• /
• pp.104-107
• /
• 2010

Polyurethane (PU) sheets were fabricated by the reaction of polypropylene glycol (PPG) and liquid diphenyl methane diisocyanate (L-MDI) with various trimethylol propane (TMP) contents. The $T_g$ value was varied from 34.8 $^{\circ}C$ to 49.9 $^{\circ}C$ according to the TMP content. As the content of TMP was increased from 4 to 12 wt%, the modulus of the PU sheet was increased from 322 MPa to 423 MPa, its tensile strength was increased from 10.6 MPa to 14.8 MPa, and its elongation was decreased from 62.8% to 49%. In case of acoustic properties, the sound speed of PU sheet was increased while its attenuation coefficient was decreased as the content of TMP was increased. The fabricated PU sheet was stable in water bath for 4 weeks.

• Polymer(Korea)
• /
• v.25 no.3
• /
• pp.421-426
• /
• 2001

11-Aminododecanoic acid, to insert the functional group of -COOH reacted with the end group of poly($\varepsilon$-caprolactone) diol, and cetyltrimethylammonium bromide (CTMA), to increase the d-spacing of Montmorillonite (MMT), were intercalated into $Na^+;_-$MMT. The modified MMT was reacted with poly(${varepsilon}-caprolactone$) diol ($M_n{=2000$) in THF solution at $80^{\circ}C$ for 4 hrs. After reaction, poly(${varepsilon}-caprolactone$) ($M_n{=80000$) was mixed into the solution for 12 hrs. To prepare the PCL/clay nanocomposite film this solution was cast into the silicon mold at $60^{\circ}C$ in vacuum oven for 6 hrs. From the results of XRD and TEM, it was found that the exfoliated PCL/clay nanocomposite were prepared. The effects of the amount of MMT on the mechanical properties and thermal properties of PCL/clay nanocomposites have been investigated by tensile tester and DSC. Because the MMT was dispersed homogeneously in PCL matrix, the Young's modulus of the nanocomposite were found to be excellent. However, MMT dispersed in PCL matrix had almost no effect on the tensile strength of the composites. The crystallization temperature of PCL increased in proportion to 3 wt% MMT in the PCL matrix.

• Korean Journal of Materials Research
• /
• v.2 no.3
• /
• pp.191-196
• /
• 1992

The new epoxy resin, diglycidyl ether of bisphenol A(DGEBA)/4, 4'-methylene dianiline (MDA)/succinonitrile system, containing the reactive additive succionitrile was investigated through the impact test and the stress-strain test on the basis of the behavior of cure reaction and the cure mechanism. The new epoxy resin system, having the different succinonitrile contents, were cured at $80^{\circ}C$for 1.5 hour and then in order to cure completely at $150^{\circ}C$ for 1 hour. It was shown that as the succinonitrile content increased, impact strength was gradually increased, tensile strength was decreased, almost constantly Young's modulus was sustained and elongation was increased until the succinonitrile content was increased to 10phr, and then decreased. From the experimental results, it can be concluded that the chemical bonding length between the main chains was extended by adding the reactive additive succinonitrile. It was also found that the flexibility of epoxy resin was improved by adding the succinonitrile.

• Journal of the Korean Ceramic Society
• /
• v.23 no.1
• /
• pp.51-59
• /
• 1986

It was the first time the MgO-C brick was developed for the lining materials in the hot spots in electric are furnace in 1972. MgO-C brick is high registant to thermal and structural spalling. Futhermore for the reason that carbon is hard to react with slag and MgO is high fireproof MgO-C brick shows a high corrosion registance to slag attack compared with conventional basic refractories. Owing to their excellent properties the use of MgO-C refractories are being developed widely in the field of shaped refractories and even in that of monolithic refractories. In this paper the oxidation of carbon the infiltration of slag into the brick texture and effects of additions were investigated. The results obtained were as follows : 1) The use of fused MgO-clinker and high purity carbon as raw materials increased the corosion registance and hot modulus of rupture of MgO-C brick. 2) As the oxidation reaction of the carbon proceeded the slag infiltrated into the brick texture. And then the slag components reacted with the MgO grains and formed low melting point compounds particulary CaO.MgO.$SiO_2$ and 3CaO.MgO.$2SiO_2$ that resulted in the wear of the brick. 3) It is recongnized the Al, Si, $B_3C$ effects on the oxidation registant properties of MgO-C brick by contribu-ting to the decrease of permeability according to the formation of $Al_4C_3$, SiC, $B_2O_3$ and the decrease of open pores relating to the formation of MgO.Al2O3, $SiO_2$, 3MgO.$B_2O_3$ at the decarbonized layer.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.1230-1231
• /
• 2008

The effect of content of $Al_2O_3+Y_2O_3$ sintering additives on the densification behavior, mechanical and electrical properties of the pressureless-sintered $SiC-ZrB_2$ electroconductive ceramic composites was investigated. The $SiC-ZrB_2$ electroconductive ceramic composites were pressureless-sintered for 2 hours at 1,700[$^{\circ}C$] temperatures with an addition of $Al_2O_3+Y_2O_3$(6:4 mixture of $Al_2O_3$ and $Y_2O_3$) as a sintering aid in the range of 8${\sim}$20[wt%]. Phase analysis of $SiC-ZrB_2$ composites by XRD revealed mostly of ${\alpha}$-SiC(6H), $ZrB_2$ and In Situ YAG($Al_5Y_3O_{12}$). The relative density, flexural strength, Young's modulus and vicker's hardness showed the highest value of 89.01[%], 81.58[Mpa], 31.437[GPa] and 1.34[GPa] for $SiC-ZrB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature respectively. Abnormal grain growth takes place during phase transformation from ${\beta}$-SiC into ${\alpha}$-SiC was correlated with In Situ YAG phase by reaction between $Al_2O_3$ and $Y_2O_3$ additive during sintering. Compositional design and optimization of processing parameters are key factors for controlling and improving the properties of SiC-based electroconductive ceramic composites. In this paper, it is convinced that ${\beta}$-SiC based electroconductive ceramic composites for heaters or ignitors can be manufactured by pressureless sintering.