• Journal of Korea Foundry Society
• /
• v.16 no.2
• /
• pp.141-148
• /
• 1996

In high chromium cast iron, the control of matrix microstructure as well as carbide structure is important to the performance as a wear resistant material. In this study, 3.0% C-24.0% Cr white cast irons with various molybdenum contents(residual, 1.0%, 3.0% and 5.0%) were solidified conventionally and unidirectionally for studying their effects on the microstructure and hardness. In the conventional casting, two sets of castings were poured from each melt. One set of the castings consisted of cylindrical bars of 10 and 20mm by 155mm long. The second set of the castings was a cylindrical bar of 30mm by 200mm long. On the other hand, a pep-set mold set on the Cu plate was employed to make the solidification unidirectionally. X-ray diffraction method was used to observe retained austenite and carbides in the high chromium cast iron. The morphology of eutectic $M_7C_3$ carbides changed from needle-like type to nodular type with the increase of Mo content. And, the presence of $M_2C$ carbides was identified in the sample where Mo was added over 3.0 %. Primary and eutectic carbides appeared as rod type and corngrain type, respectively in the unidirectionally solidified samples which were cut to parallel to the solidification direction. In the EDX analysis, Cr concentration was higher in the primary and eutectic $M_7C_3$ carbides, Mo in the $M_2C$ carbides, and Fe in the matrix.

• Journal of Korea Foundry Society
• /
• v.33 no.3
• /
• pp.127-133
• /
• 2013

The influences of a small amount of CaO addition on the microstructure and corrosion behavior of AZ81 casting alloy have been investigated by means of optical microscopy, scanning electron microscopy, X-ray photoelectron spectroscopy, immersion and electrochemical tests. The added CaO led to the refinement of ${\alpha}$-Mg grains and the decrease in ${\beta}$ precipitate content by the formation of an $Al_2Ca$ phase. The AZ81-CaO alloy had a better corrosion resistance than the AZ81 alloy. The microstructural characterization on the corroded surface revealed that the enhanced corrosion resistance of the CaO-containing alloy may well be ascribed to the increased barrier effect of precipitates formed more continuously along the grain boundaries and the incorporation of Al and Ca elements into the corrosion film, by which it became more protective.

• Proceedings of the Korea Information Processing Society Conference
• /
• 2005.05a
• /
• pp.1623-1626
• /
• 2005

초음파 영상 기법은 장기, 연조직, 혈류를 검사하는데 쓰이는 영상 진단법이다. 초음파 장비를 통해 얻어진 초음파 볼륨 데이터는 장비 특성상 많은 잡음(speckle noise)을 포함하기 때문에, 깨끗한 영상을 얻기 위해서는 잡음 필터링(noise filtering)이 필요하다. 그런데, 볼륨 데이터 모든 영역에 대해 잡음 필터링을 적용할 경우 전처리 시간이 길어져 실시간으로 초음파 볼륨 데이터를 렌더링하기 어렵다. 본 논문에서는 실시간으로 입력되는 초음파 볼륨 데이터를 가시화 하기위하여 전처리 시간 없이 잡음을 제거하는 방법을 제안한다. 전처리 시간에 전체 볼륨 데이터에 대해 잡음 필터링을 적용하지 않고, 영상을 생성하는 동안 참조되는 복셀(voxel)에 대해서만 잡음 필터를 적용하여 얻은 값을 사용한다. 이때 필터링에 소요되는 시간을 최소화하기 위해 가장 단순한 평균화 필터를 사용한다. 그리고 복셀에 적용되는 3차원 필터를 3단계의 1차원 필터 연산 단계로 분할 한 후, 각 단계별 연산을 거친 복셀들에 대해서는 다시 연산을 하지 않도록 하여 중복을 피한다. 이를 통해 전처리 시간 없이 기존 방법과 동일한 화질을 유지하는 최종 영상을 만들어 낸다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.9-9
• /
• 2011

There has been strong demand for novel nonvolatile memory technology for low-cost, large-area, and low-power flexible electronics applications. Resistive memories based on metal oxide thin films have been extensively studied for application as next-generation nonvolatile memory devices. However, although the metal oxide-based resistive memories have several advantages, such as good scalability, low-power consumption, and fast switching speed, their application to large-area flexible substrates has been limited due to their material characteristics and necessity of a high-temperature fabrication process. As a promising nonvolatile memory technology for large-area flexible applications, we present a graphene oxide-based memory that can be easily fabricated using a room temperature spin-casting method on flexible substrates and has reliable memory performance in terms of retention and endurance. The microscopic origin of the bipolar resistive switching behaviour was elucidated and is attributed to rupture and formation of conducting filaments at the top amorphous interface layer formed between the graphene oxide film and the top Al metal electrode, via high-resolution transmission electron microscopy and in situ x-ray photoemission spectroscopy. This work provides an important step for developing understanding of the fundamental physics of bipolar resistive switching in graphene oxide films, for the application to future flexible electronics.

• Textile Coloration and Finishing
• /
• v.19 no.4
• /
• pp.10-17
• /
• 2007

Chitosan(CS) and cellulose acetate(CA) composite films were prepared using formic acid as a cosolvent by casting, solvent evaporating and neutralization method. This study examines if the blending method, which uses formic acid as a cosolvent is efficient in improving the mechanical properties of CS film, especially wet strength and elongation. Formic acid is an effective cosolvent for the blend of CS and CA. Under wet condition, tensile strength and elongation of the composite films were obviously higher than those of the films made from pure CS. FTIR, DSC, and X-ray diffraction showed that the composite films exhibit a high level of compatibility and that strong interaction between the CS and CA was caused by intermolecular hydrogen bonding. The affinity series of composite film to transition metal ions are Cu(II) > Cd(II) > Cr(III). The adsorption of Cu((II) ion was shown to be highly pH sensitive.

• Journal of the Korean Ceramic Society
• /
• v.31 no.9
• /
• pp.969-974
• /
• 1994

After adding 8Y-ZrO2 powders to 3Y-ZrO2 powders at ratios of 0, 33, 50, 67, and 100% by weight, the mixed yttria-stabilized zirconia specimens were fabricated into thin plate using tape~casting method and then sintered at 150$0^{\circ}C$ for 4h in air. The crystalline structure, microstructure and electrical properties of the sintered zirconia thin plates were investigated by using X-ray diffractometer, scanning electron microscope and impedance analyser, respectively. At the temperatures higher than 75$0^{\circ}C$, the sintered thin plate with 33% 8Y-ZrO2 content shows higher mechanical properties and lower electrical resistivity than 8Y-ZrO2 thin plate which is generally used as an electrolyte for solid oxide fuel cells. This is due to the fact that the zirconia thin plates with low 8Y-ZrO2 content maintain the slope of low temperature region up to high temperatures, whereas at temperatures higher than 50$0^{\circ}C$ the slope decrease in the zirconia thin plates with high 8Y-ZrO2 content.

• Polymer(Korea)
• /
• v.25 no.2
• /
• pp.160-167
• /
• 2001

The various compositions of polyimide (PI)/polyamideimide (PAI) composites were prepared by heat treatment of the solvent cast PI precursors/PAI blends. The optical micrographs showed that a good compatibility was observed between poly(amic acid) (PAA) and PAI, but in the case of PAME/PAI mixtures, a phase separation apparently occurred due to the absence of ionic and/or H-bonding forces. Regardless of PI precursors, the similar tensile properties were observed. The tensile modulus of the composites were higher than that of the neat polyimide. The X-ray diffraction patterns of the composites showed that the chain rearrangement of PI was increased due to the plasticizing effect of PAI, which has lower glass transition temperature than that of PI, during thermal imidization process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.5
• /
• pp.445-449
• /
• 2005

Aging phenomena of 0.2PMN-0.8PZT multilayered ceramic actuators(MCA) have been investigated at the room temperature. The piezoelectric materials were synthesized as conventional ceramic process, and MCA were fabricatedby tape casting methods. The crystalline structures and lattice parameters were investigated by X-ray diffraction analysis, showing the structure was tetragonal and c/a was about 1.01. And, the effective electromechanical coupling coefficient keff and pseudo-piezoelectric constant $d_{33}$were measured. Variable unipolar electric fields, $2{\sim}4kV/mm$, were applied to MCh to investigate the aging characteristics. After 2 kV/mm unipolar electric field, keff and $d_{33}$ were 0.454 and 4.44 respectively. The measured and simulated values using for aging phenomena analysis, had a good fit to the linear logarithmic stretched exponential law.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2003.12a
• /
• pp.163-168
• /
• 2003

In the present study, the piezoelectricity and polarization of multilayer ceramic actuator, being designed to stack PMN-PZ-PT ceramic layers and Ag-Pd electrode layers alternatively, were investigated under a consideration of geometric factor, the volume ratio of the ceramic to the electrode layers. The actuators were fabricated by tape casting of $0.2Pb(Mg_{1/3}Nb_{2/3)O_3-0.38PbZrO_3-0,42PbTiO_3$ followed by lamination and burnout & co-firing processes. The actuators of $10\times10\times0.6~2\textrm{mm}^3$ in size were formed in a way that $60 ~ 200\mu\textrm{m}$ thick were stacked alternatively with $5\mu\textrm{m}$ thick electrode layer. Increases in polarization and electric field-induced displacement with thickness of the ceramic layer were attributed to change of $90^{\circ}$/$180^{\circ}$ domain ratio, which was affected by interlayer internal stress. The piezoelectricity and actuation behaviors were found to depend upon the volume ratio (or thickness ratio) of ceramic to electrode layers.

• Journal of Technologic Dentistry
• /
• v.35 no.4
• /
• pp.343-352
• /
• 2013

Purpose: The purpose of this study was to investigate to effect of the ZrN coated on corrosion resistance and physical property of dental Co-Cr alloys using various instruments. Methods: The specimens were used, respectively, for experiment, Arc Ion plating was carried out for dental casting alloys using ZrN coated materials with nitrogen gas. ZrN coated surface of each specimen was observed with field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS), vickers hardness tester, and electrochemical tester. Results: The current density of ZrN coated specimen was smaller than that of non-coated specimen in 0.9% NaCl solution. Pit nucleated at scratch of specimen. The pitting corrosion resistant |$E_{max}-E_{rep}$| increased in order of ZrN coated (110 mV), and non-coated wire (100 mV). Conclusion: The corrosion potential of the ZrN coated specimen was comparatively high. the surface of ZrN coated specimen was more smooth than that of other kinds of non-coated specimen. ZrN coated surface showed higher hardness than that of non-coated surface.