• Korean Journal of Materials Research
• /
• v.25 no.4
• /
• pp.183-190
• /
• 2015

Fatigue crack growth rate tests were conducted as a function of temperature, dissolved hydrogen (DH) level, and frequency in a simulated PWR environment. Fatigue crack growth rates increased slightly with increasing temperature in air. However, the fatigue crack growth rate did not change with increasing temperature in PWR water conditions. The DH levels did not affect the measured crack growth rate under the given test conditions. At $316^{\circ}C$, oxides were observed on the fatigue crack surface, where the size of the oxide particles was about $0.2{\mu}m$ at 5 ppb. Fatigue crack growth rate increased slightly with decreasing frequency within the frequency range of 0.1 Hz and 10 Hz in PWR water conditions; however, crack growth rate increased considerably at 0.01 Hz. The decrease of the fatigue crack growth rate in PWR water condition is attributed to crack closure resulting from the formation of oxides near the crack tips at a rather fast loading frequency of 10 Hz.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.10
• /
• pp.2391-2397
• /
• 1993

The distribution of fatigue crack growth rate is influenced by the measuring interval and methods of calculation of crack growth rate. The purpose of this paper is to suggest a method for the evaluation of crack growth rate distribution without the influence. The constant ${\Delta}P$ test and the constant .DELTA.K test are executed by using the CT specimen. The measuring interval of (${\Delta}a$/W=0.0067~0.014) crack length is not affected by methods of the calculation of the fatigue crack growth rate is suggested.

• Nuclear Engineering and Technology
• /
• v.53 no.6
• /
• pp.1991-1999
• /
• 2021

The response changes of the specific growth rate of Lemna minor duckweed was modeled using the logarithms of frond numbers on tritium activity concentration and gamma radiation dose from cobalt 60. The concept of average specific growth rate depends on the general exponential growth pattern, where toxicity is estimated based on the effect on the growth rate. One of the main questions of the effect of the radiation dose on duckweed is how to correlate the effect of beta radiation with the effect of any other radiation for modeling radiation on Lemna minor. Experimental data were extrapolated by utilizing the OECD guidelines. A linear relationship of absorbed dose and activity concentration was obtained for the average dependency growth rate of Lemna minor as D = (0.1257)·A^0.585. The dose rate of gamma irradiation from ⁶⁰Co increases with tritium activity dependence, on the specific growth rate of the Lemna minor duckweed. An increase in the tritium activity causes a decrease in the specific growth rate of the Lemna minor duckweed. It indicates that as the quantity of the beta radiation dose increase in Lemna minor duckweed, a higher quantity of gamma radiation will be required to cause the same effect in the specific growth rate of Lemna minor duckweed. The relation between the inhibition of the Lemna minor seedling growth and gamma and beta radiation dosage agrees roughly with that between the decrease of survival rate or fertility and dosage.

• Journal of Korea Foundry Society
• /
• v.5 no.4
• /
• pp.258-270
• /
• 1985

The structures and mechanical properties of undirectionally solidified Sn-Zn eutectic alloys have been examined over the growth range 7mm/h to 6,000mm/h. The structures of unidirectionally solidified Sn-Zn eutectic alloys were primarily broken-lamellar at growth rates below 760mm/h and became fibrous at higher growth rates above that. At a growth rate 3,084mm/h the structures were fibrouse only. There is no dendrites at any growth rates, but occasionally ribbon-like morphologies were seen. The under cooling increased parabolically with growth rate increase. The hardness of specimes increased with growth rates increase but heat-treated specimen decreased after growth rates 760mm/h and became constant value. The effect of heat-treatment was good at lower growth rate. At room temperature tensile strength increased with growth rates up to R=990mm/h and then tensile strength became near-constant value. The effect of heat-treatment was well at lower growth rate.

• The Journal of Asian Finance, Economics and Business
• /
• v.7 no.5
• /
• pp.91-102
• /
• 2020

The study investigates the relationship between the inflation rate and economic growth to find out the optimal inflation threshold for economic growth. Therefore, this study applied an ordinary least square model (OLS) and the ordinal regression model, and collected the time-series data from 1996 to 2017 to test the relationship between inflation and economic growth in the short-term and long-term. The sample fits the model and is statistically significant. The study showed that 96.6% of correlation between inflation rate and economic growth are close and 4.5% of optimal inflation threshold is appropriate for economic growth. It finds that the optimal inflation threshold is base to perform economic growth, besides the inflation rate is positively related to economic growth. The results support the monetary policy appropriately. This study identifies issues for Government to consider: have a comprehensive solution among macroeconomic policies, monetary policy, fiscal policy and other policies to control and maintain the inflation and stimulate growth; have appropriate policies to regulate inflation to stimulate economic growth over the long term; set a priority goal for sustainable economic growth; not pursue economic growth by maintaining the inflation rate in the long term, but take appropriate measures to stabilize the inflation at the optimal inflation threshold.

• Journal of Power System Engineering
• /
• v.17 no.4
• /
• pp.86-93
• /
• 2013

This paper deals with the effects of driving force and material properties on statistical distribution of fatigue crack growth rate (FCGR) for the friction stir welded joints of Al 7075-T651 aluminum plate. In this work, the statistical probability distribution of fatigue crack growth rate was analyzed by using our previous constant stress intensity factor range controlled fatigue crack growth test data. As far as this study are concerned, the statistical probability distribution of fatigue crack growth rate for the friction stir welded (FSWed) joints was found to evaluate the variability of fatigue crack growth rate for base metal (BM), heat affected zone (HAZ) and weld metal (WM) specimens. The probability distribution of fatigue crack growth rate for FSWed joints was found to follow well log-normal distribution. The shape parameter of BM and HAZ was decreased with increasing the driving force, however, the shape parameter of WM was decreased and increased with increasing the driving force. The scale parameter of BM, HAZ and WM was increased with the driving force.

• Journal of Ocean Engineering and Technology
• /
• v.1 no.2
• /
• pp.93-100
• /
• 1987

Corrosion fatigue cracking of the austenitic stainless steel(bese metal & heat affected zone by TIG weld) was studied experimentally under the environments of various specific resistance and air. The characteristics of corrosion fatigue crack growth rate and the environmental constants of paris' rule were investigated for SUS 304 weldments in the various specific resistance. The influences of stress intensity factor range and corrosion on the crack growth rate were compared. The characteristics of corrosion fatigue cracking for the weldments were inspected from mechanical, electrochemical and microstructural point of view. Main results obtained are as follows: 1) As the specific resistance decreases, the environmental constant C of paris'rule increases(hence the corrosion fatigue crack growth rate is rapid), but the environmental constant m decreases, so the effect of corrosion to the crack growth rate is more susceptible than thet of stress intensity factor range. 2) As the stress intensity factor range decreases, the corrosion fatigue crack growth rate of heat affected zone is more susceptible than that of the base metal. 3) The corrosion fatigue crack growth rate of the heat affected zone is more rapid than that of the base metal, because of the phenomenon of softening and the less noble potential coused by wedlding heat cycle. 4) The corrosion fatigue cracking of SUS 304 weldment appears transgranular fracture.

• Journal of Applied Reliability
• /
• v.15 no.2
• /
• pp.90-100
• /
• 2015

Reliability growth rate (or reliability growth curve slope) have the two cases of trend as a constant or changing one during the reliability growth testing. The changing case is very common situation. The reasons of reliability growth rate changing are that the failures to follow the NHPP (None-Homogeneous Poisson Process), and the solutions implemented during test to break out other problems or not to take out all of the root cause permanently. If the changing were big, the "Goodness of Fit (GOF)" of reliability growth curve to test data would be very low and then reduce the accuracy of assessing result with test data. In this research, we are using Duane model and AMSAA model for assessing test data and projecting the reliability level of complex and repairable system as like construction equipment and vehicle. In case of no changing in reliability growth rate, it is reasonable for reliability engineer to implement the original Duane model (1964) and Crow-AMSAA model (1975) for the assessment and projection activity. However, in case of reliability growth rate changing, it is necessary to find the method to increase the "GOF" of reliability growth curves to test data. To increase GOF of reliability growth curves, it is necessary to find the proper parameter calculation method of interesting reliability growth models that are applicable to the situation of reliability growth rate changing. Since the Duane and AMSAA models have a characteristic to get more strong influence from the initial test (or failure) data than the latest one, the both models have a limitation to contain the latest test data information that is more important and better to assess test data in view of accuracy, especially when the reliability growth rate changing. The main objective of this research is to find the parameter calculation method to reflect the latest test data in the case of reliability growth rate changing. According to my experience in vehicle and construction equipment developments over 18 years, over the 90% in the total development cases are with such changing during the developing test. The objective of this research was to develop the newly assessing method and the process for GOF level increasing in case of reliability growth rate changing that would contribute to achieve more accurate assessing and projecting result. We also developed the new evaluation method for GOF that are applicable to the both models as Duane and AMSAA, so it is possible to compare it between models and check the effectiveness of new parameter calculation methods in any interesting situation. These research results can reduce the decision error for development process and business control with the accurately assessing and projecting result.

• Nuclear Engineering and Technology
• /
• v.51 no.4
• /
• pp.1060-1068
• /
• 2019

This work aims to establish a model of a primary water stress corrosion crack growth rate of Alloy 690 material for the head penetration nozzles of Korean pressurized water reactors. The test material had an inhomogeneous microstructure with bands of fine-grains and intragranular carbides in the matrix of coarse-grains, which was similar to the archive materials of the head penetration nozzles. The crack growth rate was measured from the strain-hardened materials as a function of the stress intensity factor in simulated primary water at various temperatures and dissolved hydrogen contents. The effects of strain-hardening, temperature, and dissolved hydrogen on the crack growth rate were analyzed independently, and were then introduced as normalizing factors in the crack growth rate model. The crack growth rate model proposed in this work provides a key element of the tools needed to assess the progress of a stress corrosion crack when detected in thick-wall Alloy 690 components in Korean reactors.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.7 s.166
• /
• pp.1120-1128
• /
• 1999

An elastic-viscoplastic finite element analysis is performed to investigate detailed growth behavior of creep cracks and the numerical results are compared with experimental results. In Cr-Mo steel stress fields obtained from the crack growth method by mesh translation were compared with both cases that the secondary creep rate is only used as creep material property and the primary creep rate is included. Analytical stress fields, Riedel-Rice(RR) field, Hart-Hui-Riedel(HR) field and Prime(named in here) field, and the results obtained by numerical method were evaluated in details. Time vs. stress at crack tip was showed and crack tip stress fields were plotted. These results were compared with analytical stress fields. There is no difference of stress distribution at remote region between the case of 1st creep rate+2nd creep rate and the case of 2nd creep rate only. In case of slow velocity of crack growth, the effect of 1st creep rate is larger than the one of fast crack growth rate. Stress fields at crack tip region we, in order, Prime field, HR field and RR field from crack tip.