• Journal of the Korean Ceramic Society
• /
• v.49 no.4
• /
• pp.318-324
• /
• 2012

Reaction-bonded silicon nitrides containing rare-earth oxide sintering additives were densified by gas pressure sintering. The sintering behavior, microstructure and mechanical properties of the resultant specimens were analyzed. For that purpose, $Lu_2O_3-SiO_2$ (US), $La_2O_3$-MgO (AM) and $Y_2O_3-Al_2O_3$ (YA) additive systems were selected. Among the tested compositions, densification of silicon nitride occurred at the lowest temperature when using the $La_2O_3$-MgO system. Since the $Lu_2O_3-SiO_2$ system has the highest melting temperature, full densification could not be achieved after sintering at $1950^{\circ}C$. However, the system had a reasonably high bending strength of 527 MPa at $1200^{\circ}C$ in air and a high fracture toughness of 9.2 $MPa{\cdot}m^{1/2}$. The $Y_2O_3-Al_2O_3$ system had the highest room temperature bending strength of 1.2 GPa.

• Journal of the Korean Ceramic Society
• /
• v.37 no.2
• /
• pp.158-163
• /
• 2000

Six different SiC ceramics with SiO2-Re2O3 (Re=Yb, Er, Y, Dy, Gd, Sm) as sintering additives have been fabricated by hot-pressing the SiC-Re2Si2O7 compositions at 1850$^{\circ}C$ for 2 hr under a pressure of 25 MPa. The room temperature strneth and the fracture toughness of the hot-pressed ceramics were characterized and compared with those of the ceramics sintered with YAG (Y3Al5O12). Five SiC ceramics (Re=Yb, Er, Y, Dy, Gd) investigated herein showed sintered densities higher than 94% of theoretical. Tthe SiC-Re2Si2O7 compositions showed lower strength and comparable toughness to those from SiC-YAG composition, owing to the chemical reaction between SiO2 and SiC during sintering. SiC ceramics fabricated from a SiC-Y2Si2O7 composition showed the best mechanical properties of 490 MPa and 4.8 MPa$.$m1/2 among the compositions investigated herein.

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.777-783
• /
• 1994

Oxidation behavior of hot-pressed silicon nitride ceramics with various sintering additives has been investigated. The weight gain of each specimens has shown in the range of 0.11 mg/$\textrm{cm}^2$ ~3.4 mg/$\textrm{cm}^2$ at 140$0^{\circ}C$ for 192 h and eleven compositions have shown good oxidation resistance with the weight gain below 0.5 mg/$\textrm{cm}^2$. The oxidation rate has been shown to obey the parabolic rate law and the oxidized surface has consisted of $\alpha$-cristobalite and M2Si2O7 or MSiO3 (M=rare earth or transition metals) phase. The oxidation rate of each specimens has related to the eutectic temperature between additive oxide and SiO2, and ionic radius of additive oxides, respectively. From the above results, it could be concluded that the oxidation behavior of hot pressed silicon nitride is dominated by the high temperature properties of grain boundary glassy phase and the high temperature properties of grain boundary glassy phase are affected by the ionic radius of additive oxides.

• Journal of the Korean Ceramic Society
• /
• v.49 no.4
• /
• pp.301-307
• /
• 2012

SiAlON glasses are silicates or alumino-silicates, containing Mg, Ca, Y or rare earth (RE) ions as modifiers, in which nitrogen atoms substitute for oxygen atoms in the glass network. These glasses are found as intergranular films and at triple point junctions in silicon nitride ceramics and these grain boundary phases affect their fracture behaviour. This paper provides an overview of the preparation of M-SiAlON glasses and outlines the effects of composition on properties. As nitrogen substitutes for oxygen in SiAlON glasses, increases are observed in glass transition temperatures, viscosities, elastic moduli and microhardness. These property changes are compared with known effects of grain boundary glass chemistry in silicon nitride ceramics. Oxide sintering additives provide conditions for liquid phase sintering, reacting with surface silica on the $Si_3N_4$ particles and some of the nitride to form SiAlON liquid phases which on cooling remain as intergranular glasses. Thermal expansion mismatch between the grain boundary glass and the silicon nitride causes residual stresses in the material which can be determined from bulk SiAlON glass properties. The tensile residual stresses in the glass phase increase with increasing Y:Al ratio and this correlates with increasing fracture toughness as a result of easier debonding at the glass/${\beta}-Si_3N_4$ interface.

• Journal of Powder Materials
• /
• v.26 no.5
• /
• pp.415-420
• /
• 2019

SiAlON ceramics are used as ceramic cutting tools for heat-resistant super alloys (HRSAs) due to their excellent fracture toughness and thermal properties. They are manufactured from nitride and oxide raw materials. Mixtures of nitrides and oxides are densified via liquid phase sintering by using gas pressure sintering. Rare earth oxides, when used as sintering additives, affect the color and mechanical properties of SiAlON. Moreover, these sintering additives influence the cutting performance. In this study, we have prepared $Yb_{m/3}Si_{12-(m+n)}Al_{m+n}O_nN_{16-n}$ (m = 0.5; n = 0.5, 1.0) ceramics and manufactured SiAlON ceramics, which resulted in different colors. In addition, the characteristics of the sintered SiAlON ceramics such as fracture toughness and microstructure have been investigated and results of the cutting test have been analyzed.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.364-371
• /
• 2013

The sintering behavior of monolithic SiC is examined using the binary sintering additive of $Al_2O_3$-rare earth oxide ($RE_2O_3$, where RE = Sc, Nd, Dy, Ho, or Yb). Through hot pressing at 20 MPa and $1750^{\circ}C$ for 1 h in an Ar atmosphere for 52 nm fine ${\beta}$-SiC powder added with 5 wt% sintering additive, a SiC density of > 97% is achieved, which indicates the effectiveness of $Al_2O_3-RE_2O_3$ system as a sintering of additive for SiC. Based on this result, 7 wt% of $Al_2O_3-Sc_2O_3$ is tested as an additive system for the fabrication of a continuous SiC fiber-reinforced SiC-matrix composite ($SiC_f$/SiC). Electrophoretic deposition combined with the application of ultrasonic pulses is used to efficiently infiltrate the matrix phase into the voids of $Tyranno^{TM}$-SA3 fabric. After hot pressing, a composite density of > 97% is obtained, along with a maximum flexural strength of 443 MPa.

• The Korean Journal of Ceramics
• /
• v.5 no.3
• /
• pp.211-216
• /
• 1999

Four different $\beta-Si_3N_4$ ceramics with silicon oxynitrides $[Y_10(SiO_4)_6N_2, Yb_4Si_2N_2O_7, Er_2Si_3N_4O_3, \;and La_{10}(SiO_4)_6N_2$, respectivley] as secondary phases have been fabricated by hot-pressing the $Si_3N_4-Re_4Si_2N_2O_7$ (Re=Y, Yb, Er, and La) compositions at $1820^{\circ}C$ for 2h under a pressure of 25 MPa. The high temperature strength and oxidation behavior of the hot-pressed ceramics were characterized and compared with those of the ceramics fabricated from $Si_3N_4-Si_2O_7$ compositions. The $Si_3N_4-Re_4Si_2N_2O_7$composition investigated herein showed comparable high temperature strength to those from $Si_3N_4-Re_2Si_2O_7$ compositions. Si3N4 ceramics from a $Si_3N_4-Y_4Si_2N_2O_7$ composition showed the highest strength of 877 MPa at $1200^{\circ}C$ among the compositions. All $Si_3N_4$ ceramics investigated herein showed a parabolic weight gain with oxidation time at $1400^{\circ}C$ and the oxidation products of the ceramics were $SiO_2$ and $Re_2Si_2O_7$. The $Si_3N_4-Re_4Si_2N_2O_7$ compositions showed inferior oxidation resistance to those from $Si_3n_4-Re_2Si_2O_7$ compositions, owing to the incompatibility of the secondary crystalline phases of those ceramics with $SiO_2$, the oxidation product of Si3N4.Si3N4 ceramics from a $Si_3N_4-Er_4Si_2N_2O_7$ composition showed the best oxidation resistance of 0.375mg/$\textrm{cm}^2$ after oxidation at $1400^{\circ}C$ for 102 h in air among the compositions.