• Journal of Adhesion and Interface
• /
• v.15 no.2
• /
• pp.49-56
• /
• 2014

In this study, properties of adhesion between adhesion promoter-containing rubber compound and zinc coated steel cord was investigated. Cobalt salt, resorcinol formaldehyde resin (RF resin) and hexamethoxymethylmelamine (HMMM) were used to adhesion promoter. Since cobalt salts accelerate sulphidation rate of zinc at zinc coated steel cord surface, pullout force of rubber compound applying cobalt salts was increased compared to that of rubber compound without applying cobalt salts. Pullout force and rubber coverage of rubber compounds applying all adhesion promoters were superior because strong interlocking between rubber matrix increased modulus due to applying RF resin and HMMM and grown zinc sulfides at zinc coated steel cord surface.

• Applied Chemistry for Engineering
• /
• v.3 no.3
• /
• pp.422-429
• /
• 1992

The morphology and adhesion properties of rubber compounds containing resorcinol formaldehyde(RF) resin and hexamethoxymethylmelamine(HMMM) used in adhesion of rubber to brass-plated steel cord was investigated. The resins were spherical particles about $2000{\AA}$ diameter and distributed in rubber compounds homogeneously, and the cured compound with steel cord showed migration of resin to steel cord. Also, modulus was increased with increasing HMMM contents. The loss of adhesion between rubber and steel cord was likely to be at initial stages by thermal aging. Considering the physical properties, suability of adhesion layer and thermal aging property, optimum ratio of RF resin and HMMM was 1 : 0.9.

• Macromolecular Research
• /
• v.8 no.2
• /
• pp.53-58
• /
• 2000

Stabilities and structures of resorcinol formaldehyde resins (RF resins) and their dependence on solvent were studied by molecular mechanics and molecular dynamics. Dimers to decamers of the RF resins in the conditions of dielectric constant = 1.00, 21.01, 36.64, and 80.10 were calculated. The average distance between oxygen atoms in 1-hydroxyl groups of adjacent resorcinols of the resins became longer with increased dielectric constant of the environment. The number of intramolecular hydrogen bonds of the resins decreased by increasing the dielectric constant of the environment. The RF resin structure on the surface of fabric or steel cord was explained based on the present calculation.

• Journal of the Korean Applied Science and Technology
• /
• v.24 no.1
• /
• pp.23-30
• /
• 2007

Kevlar was chemically surface modified with resorcinol-formaldehyde(RF) prepolymer and VP rubber latex for application to high strength tirecords. RF prepolymer was easily obtained by polymerization at room temperature in the presence of a base catalyst. The mechanical and thermal properties of Kevlar were not significantly changed during surface treated under various conditions. The change of adhesion with rubber were investigated through H-test method. Maximum increase of adhesion force between rubber and Kevlar was obtained up to 40% than that of untreated one when the fiber was soaked in RFL dipping solution and thermally treated at $170^{\circ}C$ for 3 - 5min.

• Korean Chemical Engineering Research
• /
• v.48 no.5
• /
• pp.568-573
• /
• 2010

Adhesive strength was evaluated for the polyester fabric treated with various concentration of polymeric isocyanate to introduce functional group on the surface. Also experiments were performed to find out the type of latex, F/R mole ratio, and FR resin/latex weight ratio for the RFL solution to optimize adhesion between HNBR compound and the treated polyester fabric. Optimum adhesion strength was obtained when 7 wt% of the concentration of polymeric isocyanate, NBR latex because of the compatibility of HNBR compound, 1/1 of F/R mole ratio, and 20 wt% of FR resin/latex were applied. Optimum cure temperature for the RFL solution was $200^{\circ}C$ according to the results of peel test and the reason was determined by analyzing the ATR FTIR spectra of the RF resin according to the curing temperature.

• Analytical Science and Technology
• /
• v.15 no.3
• /
• pp.236-242
• /
• 2002

A method was investigated to determine the thickness of coating on steel sheet using rf glow discharge atomic emission spectrometer. The RF gas-jet boosted glow discharge has such salient feature as good pleasure stability and high sputtering efficiency that it was possible to determine the thickness of silicon resin film on zinc electroplated steel. The erosion speed variation is dependent on discharge power, gas flow rate and discharge pressure. therefore determine discharge condition to measure the thickness of coating on steels. The fundamental studies have been carried out to investigate an optimum condition for in-depth analysis and composition of zinc coating on steel. In this study, the calibration curve for thickness determination of silicon resin film was found to be linear in the range of $1000{\sim}3500mg/m^2$ film thickness. The developed rf gas-jet boosted glow discharge was applied to the analysis of zinc coating and silicon resin film on steel made by RIST.

• The Korean Journal of Applied Statistics
• /
• v.27 no.4
• /
• pp.543-552
• /
• 2014

High bandwidth RF such as Bluetooth, GPRS, EDGE, 3GSM, HSDPA is papular in the mobile phone market. A non-conducting metal coating process requires an e-beam deposition of metal, two steps of UV hard coating primer and top coating; however, it is inefficient. We navigate to the electron beam irradiation conditions(resin surface treatment conditions) in the PC/ABS resin injection process. By analyzing the experimental results, we find the optimum development conditions for the electro deposition pre-treatment process and mass production lines using the plasma generated electron beam source.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.65-66
• /
• 2009

This paper describes a procedure developed to fabricate negative photo resist SUMS to a semi-insulating (SI)-GaAs-based substrate. SU-8 is attractive for micromachine multi-layer circuit fabrication, because it is photo-polymerizable resin, leading to safe, and economical processing. This work demonstrates SUMS photo resist can be used for RFIC/MMIC application.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.2
• /
• pp.9-18
• /
• 2004

This study was carried out to find the efficient methods for preventing resin exudation from spruce board during high temperature environment service.In the dry-air oven test, in-use temperature related to resin exudation of 110℃ could be obtained by the appropriate kiln drying without any special treatment, and the in-use temperature of the radio-frequency/vacuum (RF/V)-dried boards was about 20℃ higher than that of the conventional kiln-dried boards.In the autoclave test, resin exudation was not found from any board dried in the conventional kiln and in the RF/V kiln after the low pressure steam explosion (SE) treating, while for the control resin exudations were more severe in the autoclave test above 130℃ than in the dry-air oven test. It, therefore, would be suggested that resin exudation during high temperature service condition can be prevented more effectively by super-heated steaming green boards than by high-temperature drying boards with low moisture.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2004.10a
• /
• pp.96-99
• /
• 2004

Silica fillers were coated by plasma polymer coatings of 1,3-diaminopropane, allylamine, pyrrole, 1,2-epoxy-5-hexene, allyl mercaptan and allyl alcohol using RF plasma (13.56 MHz). The coated fillers were then mixed with biphenyl epoxy, phenol novolac (curing agent) and/or triphenylphosphine (catalyst), and subjected to DSC analyses in order to elucidate the chemical reaction between functional moieties in the plasma polymer coatings and the epoxy resin. Only the samples with 1,3-diaminopropane and allylamine plasma polymer coated silica fillers showed heat of reaction peaks when they were mixed with biphenyl epoxy resin only, while these samples as well as the samples with 1,3-diaminopropane, allylamine and pyrrole plasma polymer coated silica fillers exhibited heat of reaction peaks when mixed with both biphenyl epoxy and phenol novolac (curing agent).