• Transactions on Electrical and Electronic Materials
• /
• 제5권3호
• /
• pp.122-125
• /
• 2004

ITO films were deposited on polyethylene terephthalate substrate by a dc reactive magnetron sputtering using rf bias without substrate heater and post-deposition thermal treatment. The dependency of rf substrate bias on plasma sputter processing was investigated to control energetic particles and improve ITO film properties. The substrate was applied negative rf bias voltage from 0 to -80 V. The composition of indium, tin, and oxygen atoms is strongly depended on the rf substrate bias. Oxygen deficiency is the highest at rf bias of -20 V. The electrical and optical properties of ITO films also are dominated obviously by negative rf bias.

• 한국표면공학회지
• /
• 제35권2호
• /
• pp.113-121
• /
• 2002

We have investigated insulating properties of $SiO_2$ interlayer for the thin film strain gauge, which were prepared by RF magnetron sputtering method in various deposition conditions, such as Ar pressure, gas flow rates and sputtering gases. SEM, AFM and FT-IR techniques were used to analyze its structures and composition. As the Ar pressure and the flow rate increased, the insulating interlayer showed low insulating resistance due to its porous structure and defects. Oxygen deficiency in $SiO_2$ was decreased as fabricated by hydrogen reactive sputtering. We could enhance the surface mobility of sputtered adatoms by using Ar/$H_2$ sputtering gas and obtain a good surface roughness and insulating property. The optimum insulating resistance of 9.22 G$\Omega$ was obtained in Ar/30% $H_2$ mixed gas, flow rate 10sccm, and 1mTorr.

• 열처리공학회지
• /
• 제13권6호
• /
• pp.398-404
• /
• 2000

The Ti-Al-V-N films have been deposited on various substrates by d.c and r.f reactive magnetron sputtering from a Ti-6Al-4V alloy target in mixed $Ar-N_2$ discharges. The films were investigated by means of XRD, AES, SEM/EDX, microhardness, TG and scratch test. The XRD and SEM results indicated that the films were of single B1 NaCl phase having dense columnar structure with the (111) preferred orientation. The composition of Ti-Al-V-N film was the Ti-7.1Al-4.3V-N(wt%) films. Adhesion and microhardness of Ti-Al-V-N films deposited by r.f magnetron sputtering method were better than those deposited by d.c magnetron sputtering method. The anti-oxidation properties of Ti-Al-V-N films were also superior to that of Ti-N film deposited by the same deposition conditions.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.395-398
• /
• 2000

Reactive radio frequency (RF)magnetron sputter with incident angle has been used to deposit AlN thin film on a crystalline Si substrate. (002)Preferred orientation of AlN thin film has been obtained at low sputtering pressure. Also it has been shown that depostion rate of AIN thin film is affected by fraction Ar and $N_2$ partial pressure. But substrate temperature didn't affect depostion rate of AIN thin film . As sputtering pressure increased preferred orientation degraded. The internal stress changed from tensile stress to compressive stress as fraction of $N_2$ partial pressure increased. At low nitrogen partial pressure cermet$^{[1]}$ AIN thin film is obtained.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2006년도 춘계학술발표회 초록집
• /
• pp.160-160
• /
• 2006

• 반도체디스플레이기술학회지
• /
• 제8권1호
• /
• pp.33-38
• /
• 2009

We have investigated the effect of the ambient gases on the characteristics of AZO thin films for the OLED (organic light emitting diodes) devices. These AZO thin films are deposited by rf-magnetron sputtering under different ambient gases (Ar, Ar+$O_2$, and Ar+$H_2$) at 300. In order to investigate the influences of the oxygen and hydrogen, the flow rate of oxygen and hydrogen in argon mixing gas has been changed from 0.2sccm to 1sccm and from 0.5sccm to 5sccm, respectively. The AZO thin films were preferred oriented to (002) direction regardless of ambient gases. The electrical resistivity of AZO film increased with increasing flow rate of $O_2$ under Ar+$O_2$ while under Ar+$H_2$ atmosphere the electrical resistivity showed minimum value near 1sccm of $H_2$. All the films showed the average transmittance over 80% in the visible range. The OLED device was fabricated with different AZO substrates made by configuration of AZO/$\acute{a}$-NPD/DPVB/$Alq_3$/LiF/Al to elucidate the performance of AZO substrate.

• 전자공학회논문지D
• /
• 제34D권8호
• /
• pp.8-14
• /
• 1997

RuO$_{2}$ thin films are prepared by RF magnetron reactive sputtering and their characteristics of crystallization, microstructue, surface roughness and resistivity are studied with various O$_{2}$/(Ar+O$_{2}$) ratios and substrate temperatures. As O$_{2}$/(Ar+O$_{2}$) ratio decreas and substrate temperature increases, the preferred growing plane of RuO$_{2}$ thin films are changed from (110) to (101) plane. With increase of the O$_{2}$/(Ar+O$_{2}$) ratio from 20% to 50%, the surface roughness and the resistivity of RuO$_{2}$ thin films increase form 2.38nm to 7.81 nm, and from 103.6.mu..ohm.-cm to 227.mu..ohm.-cm, resepctively, but the deposition rate decreases from 47 nm/min to 17nm/min. On the other hand, as the substrate temperature increases form room temperature to 500.deg. C, resistivity decreases from 210.5.mu..ohm.-cm to 93.7.mu..ohm.-cm. RuO$_{2}$ thin film deposited at 300.deg. C shows a execellent surface roughness of 2.38nm. As the annealing temperature increases in the range between 400.deg. C and 650.deg. C, the resistivity decreases because of th improvement of crystallinity. We find that RuO$_{2}$ thin film deposited at 20% of O$_{2}$/(Ar+O$_{2}$) ratio and 300.deg. C of substrate temperature shows execellent combination of surface smoothness and low resistrivity so that it is well qualified for bottom electrodes for ferroelectric thin films.

• 한국정보통신학회논문지
• /
• 제6권5호
• /
• pp.696-702
• /
• 2002

RF magnetron reactive sputtering 법으로 BST(Bal-xSrxTiO$_3$)(50/50) 박막을 제작하여, 박막의 결정화 특성 및 표면상태와 함께 박막의 두께에 따른 전기적 특성을 조사하였다. XRD와 AFM을 이용하여 BST 박막의 결정화 특성과 표면상태를 관찰한 결과, 80$0^{\circ}C$ 에서 2분간 후열처리한 박막은 완전한 perovskite 구조를 가지며 표면거칠기도 16.1$\AA$으로 양호한 값을 나타내었다. 박막의 두께가 80nm에서 240nm으로 증가함에 따라 10KHz에서 비유전률은 199에서 265로 증가하였고, 250㎸/cm의 전기장에서 누설 전류밀도는 $0.779 {\mu}m/{cm^2}에서 0.184 {\mu}A/{cm^2}$으로 감소하였다. 두께 240nm인 BST 박막의 경우, 5V에서의 전하축적 밀도와 누설전류밀도는 각각 50.5 $fC/{{\mu}m^2} 와 0.182 {\mu}A/{cm^2}$로, 이는 DRAM의 캐패시터 절연막 응용에 매우 유망한 물질임을 나타내는 결과이다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1999년도 제17회 학술발표회 논문개요집
• /
• pp.103-103
• /
• 1999

CeO2 는 cubic 구조의 일종인 CeF2 구조를 가지며 격자 상수가 0.541nm로 Si의 격자 상수 0.543nm와 거의 비슷하여 Si과의 부정합도가 0.35%에 불과하여 CeO2를 Si 기판 위에 에피택셜하게 성장시킬 수 있는 가능성이 크다. 따라서 SOI(Silicon-On-Insulator) 구조의 실현을 위하여 Si 기판위에 CeO2를 에피택셜하게 성장시키려는 많은 노력이 있었다. 또한 CeO2 는 열 적으로 대단히 안정된 물질로서 금속/강유전체/반도체 전계효과 트랜지스터(MFSFET : metal-ferroelectric-semiconductor field effect transistor)에서 ferroelectric 박막과 Si 기판사이에 완충층으로 사용되어 강유전체의 구성 원자와 Si 원자들간의 상호 확산을 방지함으로써 경계면의 특성을 향상시기키 위해 사용된다. e-beam evaporation와 laser ablation에 의한 Si 기판 위의 CeO2 격자 성장에 관한 많은 보고서가 있다. 이 방법들은 대규모 생산 공정에서 사용하기 어려운 반면 RF-magnetron sputtering은 대규모 반도체 공정에 널리 쓰인다. Sputtering에 의한 Si 기판위의 CeO2 막의 성장에 관한 보고서의 수는 매우 적다. 이 논문에서는 Ce target을 사용한 reactive rf-magnetron sputtering에 의해 Si(100) 과 Si(111) 기판위에 성장된 CeO2 의 구조 및 전기적 특성을 보고하고자 한다. 주요한 증착 변수인 증착 power와 증착온도, Seed Layer Time이 성장막의 결정성에 미치는 영향을 XRD(X-Ray Diffractometry) 분석과 TED(Transmission Electron Diffration) 분석에 의해 연구하였고 CeO2 /Si 구조의 C-V(capacitance-voltage)특성을 분석함으로써 증차된 CeO2 막과 실리콘 기판과의 계면 특성을 연구하였다. CeO2 와 Si 사이의 계면을 TEM 측정에 의해 분석하였고, Ce와 O의 화학적 조성비를 RBS에 의해 측정하였다. Si(100) 기판위에 증착된 CeO2 는 $600^{\circ}C$ 낮은 증착률에서 seed layer를 하지 않은 조건에서 CeO2 (200) 방향으로 우선 성장하였으며, Si(111) 기판 위의 CeO2 박막은 40$0^{\circ}C$ 높은 증착률에서 seed layer를 2분이상 한 조건에서 CeO2 (111) 방향으로 우선 성장하였다. TEM 분석에서 CeO2 와 Si 기판사이에서 계면에서 얇은 SiO2층이 형성되었으며, TED 분석은 Si(100) 과 Si(111) 위에 증착한 CeO2 박막이 각각 우선 방향성을 가진 다결정임을 보여주었다. C-V 곡선에서 나타난 Hysteresis는 CeO2 박막과 Si 사이의 결함때문이라고 사료된다.

• 센서학회지
• /
• 제16권4호
• /
• pp.301-306
• /
• 2007

AlN thin film for SAW filter application was deposited on (100) silicon wafers by reactive magnetron sputtering method. The structural characteristics were dependent on the deposition conditions such as sputtering pressure, RF power, substrate temperature, and nitrogen partial pressure. Scanning Electron Microscope (SEM), X-ray Diffraction (XRD), Electron Probe MicroAnalyzer (EPMA) and Atomic Force Microscope (AFM) have been used to find out structural properties and preferred orientation of AlN thin films. Insertion loss of SAW devices was 28.51 dB and out of band rejection was about 24 dB.