• Journal of Powder Materials
• /
• v.11 no.1
• /
• pp.60-68
• /
• 2004

Pulsed wire evaporation (PWE) method is known as the promising production-technique for nanopowders. In this study, we developed and modified the previous single wire explosion equipment to the simultaneous two-wire explosion one for the fabrication of alloy or mixture of nano metallic powder. First of all, both the theoretical and empirical background of pulsed wire explosion of single wire were summarized, and compared with our experimental results for Cu and Al single wlre explosion. After then, the simultaneous wire evaporation equipment was designed, constructed, and tested. The current and voltage behavior were well matched between the calculated ones from the circuit equations, and the experimental results from simultaneous explosion of Cu and Al wire.

• Journal of Powder Materials
• /
• v.18 no.2
• /
• pp.112-121
• /
• 2011

This study investigated the effect of solvent on the fabrication of Ni-free Fe-based alloy nano powders by employing the PWE (pulsed wire evaporation) in liquid and compared the alloy particles fabricated by three different methods (PWE in liquid, PWE in Ar, plasma arc discharge), for high temperature oxidation-resistant metallic porous body for high temperature soot filter system. Three different solvents (ethanol, acetone, distilled water) of liquid were adapted in PWE in liquid process, while X-ray diffraction (XRD), field emission scanning microscope (FE-SEM), and transmission electron microscope (TEM) were used to investigate the characteristics of the Fe-Cr-Al nano powders. The alloy powder synthesized by PWE in ethanol has good particle size and no surface oxidation compared to that of distilled water. Since the Fe-based alloy powders, which were fabricated by PWE in Ar and PAD process, showed surface oxidation by TEM analysis, the PWE in ethanol is the best way to fabricate Fe-based alloy nano powder.

• Journal of Powder Materials
• /
• v.9 no.2
• /
• pp.124-132
• /
• 2002

Nano Cu powders, synthesized by Pulsed Wire Evaporation (PWE) method, have been compacted by Magnetic Pulsed Cojpaction(MPC) method. The microstructure and mechanical properties were analyzed. The optimal condition for proper mechanical properties with nanostructure was found. Both pure nano Cu powders and passivated nano Cu powders were compacted, and the effect of passivated layer on the mechanical properties was investigated. The compacts by MPC, which had ultra-fine and uniform nanostructure, showed higher density of 95% of theoretical density than that of static compaction. The pur and passivated Cu compacted at $300^{\circ}C$ exhibited maximum hardnesses of 248 and 260 Hv, respectively. The wear resistance of those compacts corresponded to the hardness.

• Journal of Powder Materials
• /
• v.18 no.2
• /
• pp.105-111
• /
• 2011

This study investigated the effect of wire diameter and applied voltage on the fabrication of Ni-free Fe-based alloy nano powders by employing the PWE (pulsed wire evaporation) in liquid, for high temperature oxidation-resistant metallic porous body for high temperature particulate matter (or soot) filter system. Three different diameter (0.1, 0.2, and 0.3 mm) of alloy wire and various applied voltages from 0.5 to 3.0 kV were main variables in PWE process, while X-ray diffraction (XRD), field emission scanning microscope (FE-SEM), and transmission electron microscope (TEM) were used to investigate the characteristics of the Fe-Cr-Al nano powders. It was controlled the number of explosion events, since evaporated and condensed nano-particles were coalesced to micron-sized secondary particles, when exceeded to the specific number of explosion events, which were not suitable for metallic porous body preparation. As the diameter of alloy wire increased, the voltage for electrical explosion increased and the size of primary particle decreased.

• Journal of Powder Materials
• /
• v.11 no.2
• /
• pp.105-110
• /
• 2004

In this study the possibility to obtain a homogeneous mixture and to produce solid solutions and intermetallic compounds of Fe and Al nano particles by simultaneous pulsed wire evaporation (S-PWE) have been investigated. The Fe and Al wires with 0.45 mm in diameter and 35 mm in length were continuously co-fed by a special mechanism to the explosion chamber and simultaneously exploded. The characteristics, e.g., phase composition, particle shape, and specific surface area of Fe-Al nano powders have been analyzed. The synthesized powders, beside for Al and $\alpha$-Fe, contain significant amount of a high-temperature phase of $\gamma$-Fe, Fe Al and traces of other intermetallics. The phase composition of powders could be changed over broad limits by varying initial explosion conditions, e.g. wire distance, input energy, for parallel wires of different metals. The yield of the nano powder is as large as 40 wt ％ and the powder may include up to 46 wt % FeAl as an intermetallic compound.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.168-170
• /
• 2005

Nickel base brazes containing boron and silicon as melting point depressants are used extensively in the joining and repair of hot-section components in next generation nuclear reactor and aero-engine. Therefore, the present study has investigated the preliminary applicability of nickel based alloying nano powders. Nano Ni-based alloying powders synthesized by Pulsed Wire Evaporation (PWE) method. It's powder morphology and phase transformation temperature were analyzed by scanning electron microscopy, transmission electron microscopy, and differential scanning calorimeter(DSC). The powder particle size was approximately 10${\sim}$100nm and exhibits a quite even equiaxed shape. The results of DSC measurement show that both the nano Inconel 625 nano powder and Inconel 718 nano powder presents similar liquidus temperatures approximately $1373^{\circ}C$ and $1380^{\circ}C$ respectively.

• Journal of Powder Materials
• /
• v.17 no.4
• /
• pp.270-275
• /
• 2010

Ethylene glycol-based Cu nanofluids were prepared by pulsed wire evaporation (PWE) method. The structural properties of Cu nanoparticles were studied by X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). The average diameter and Brunauer Emmett Teller (BET) surface area of Cu nanoparticles were about 100 nm and $7.46\;m^2/g$, respectively. The thermal conductivity and viscosity of copper nanofluid were measured as functions of Cu concentration and temperature. As the volume fraction of Cu nanoparticles increased, both the enhanced ratios of thermal conductivity and viscosity of Cu nanofluids increased. As the temperature increased, the enhanced ratio of thermal conductivity increased, but that ratio of viscosity decreased.

• Journal of Powder Materials
• /
• v.11 no.3
• /
• pp.210-216
• /
• 2004

The possibility to decrease agglomeration of Cu nano powders and their separation during pulsed wire evaporation (PWE) process was investigated by controlling the working gas system, i.e., the design of the gas path, the type and pressure of the atmospheric gas. As a result, it was possible to choose the optimal design of the gas path providing large specific surface area and high degree of separation of the synthesized Cu nano powders. It was also shown that an Ar+10∼50$N_2$ mixture can be used in production of Cu nano powders, which do not react with nitrogen.

• Journal of the Korean Magnetics Society
• /
• v.24 no.5
• /
• pp.135-139
• /
• 2014

Iron-oxide nanopowders were synthesized by a pulsed wire evaporation (PWE) in various ambient gas conditions. SEM measurement indicates that the spherical iron nanoparticles are about 50 nm in diameter. The phase analysis for the produced iron-oxide powders was systematically investigated by using $M\ddot{o}ssbauer$ spectra and the results show that classified phases of $Fe_2O_3$ and $Fe_3O_4$ can be controlled by regulating the oxygen concentration in the mixed gas during the PWE process. A quadrupole line on the center of $M\ddot{o}ssbauer$ spectrum represents the superparamagnetic phase of 12 % from ${\gamma}-Fe_2O_3$ phase.

• Journal of Hydrogen and New Energy
• /
• v.20 no.6
• /
• pp.485-491
• /
• 2009

In present work, NiO/YSZ anode functional layer was prepared by nano NiO powder and 8YSZ powder. The nano NiO powders were made by Pulsed wire evaporation (PWE) method. Nano NiO- YSZ functional layer was sintered at the temperature of $900-1400^{\circ}C$. The prepared functional layer was characterized by scanning electron microscopy (SEM) and electrochemical impedance spectroscopy. The nano NiO- YSZ anode functional layer sintered at $1300^{\circ}C$ shows the lowest polarization resistance. Nano NiO- YSZ anode functional layer shows about two times smaller polarization resistance than the anode functional layer made by commercial NiO-YSZ powders. Based on these experimental results, it is concluded that the nano NiO-YSZ cermet is suitable as a anode functional layer operated at $800^{\circ}C$.