• Proceedings of the Materials Research Society of Korea Conference
• /
• 2005.05a
• /
• pp.64-64
• /
• 2005

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.329-332
• /
• 1999

In this paper, BST((Bao.&o,dTi0:3) thin films were deposited by the rf magnetron sputtering method on Pt/$SiO_2$/Si substrate. Pt, $RuO_2$, Ag, Cu films for the formation of top electrode were deposited on BST thm films. And then Top Electrodes/BST/Pt capacitors were annealed with rapid thermal annealing(RTA) at various temperature. We have investigated effect of post-annealing on the electrical properties such as dielectric constant and leakage current of the capacitors. It was found that electrical properties of the capacitors were greatly depended on the annealing temperatures as well as the materials of top electrodes. In BST thin films with Pt top electrode was annealed at $700^{\circ}C$. the dielectric constant was measured to the value of 346 at l[kHzl and the leakage current was obtained to the value of $8.76\times10^8$[A/$\textrm{cm}^2$] at the forward bias of 2[V].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.168-171
• /
• 2003

Bismuth layered structure, Cerium-substituted $Bi_4Ti_3O_{12}$ ($(Bi,Ce)_4Ti_3O_{12}$) thin films were prepared on the $Pt/TiO_2/SiO_2/Si$ substrates by the pulsed laser deposition method. We investigated the Ce-subsitituted effect on the grain orientation and ferroelectric properties. $Ce^{3+}$ ion substitution for $Bi^{3+}$ ion in perovskite layers of BTO decreased the deeree of c-axis orientation and increased the remanent polariation (2Pr). The structure and morphology of the films were characterized using X-ray diffraction and atomic force microscopy. The $(Bi,Ce)_4Ti_3O_{12}$ (BCT) thin films, which were annealed $700^{\circ}C\;and\;800^{\circ}C$ for 10min and 30min, showed a perovskite phase and dense microstructure. As the thickness of the BCT film was decresed that the ferroelectric properties of the BCT thin films were good.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.8
• /
• pp.671-676
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various deposition conditions. We investigated the effect of deposition condition on the surface morphology and dielectric properties of SBN thin films. The optimum of the rougness showed about 4.33 nm in 70/30 of Ar/$O_2$ ratio. The crystallinity and rougness of SBN thin films were increased with the increase of rf power. Also, Deposition rate of SBN thin films was about 4.17 nm/min in 70 W of rf power. The capacitance of SBN thin films were increased with the increase of Ar/$O_2$ ratio, rf power and deposition temperature respectively.

• Journal of Magnetics
• /
• v.19 no.2
• /
• pp.121-125
• /
• 2014

$CoFe_2O_4(CFO)/BaTiO_3(BTO)/CoFe_2O_4(CFO)$ multilayered thin films were deposited on $Pt/TiO_2/SiO_2/Si$ substrates by the pulsed laser deposition (PLD) system with KrF excimer laser (${\lambda}=248nm$). BTO, CFO, BTO/CFO and CFO/BTO/CFO structured thin films were prepared and their crystal structures and microstructures, as well as their magnetic and magneto-electrical properties, were studied. The C-V characteristics of these multilayered thin films with different capacitor structures were obtained to confirm the change in their capacitances under a magnetic field. Finally, the capacitance of the CFO/BTO/CFO thin film as a function of bias voltage under an in-plane magnetic field of 1,000 Oe increased to 951.04 pF at 1 MHz, from 831.90 pF measured under no magnetic field, indicating 14.3% increase in magnetocapacitance.

• Journal of the Semiconductor & Display Technology
• /
• v.8 no.2
• /
• pp.11-14
• /
• 2009

The $Sr_{0.7}Bi_{2.3}Nb_2O_9$(SBN) thin films are deposited on Pt-coated electrode(Pt/Ti/$SiO_2$/Si) using RF sputtering method at various $Ar/O_2$ ratio. We investigated the effect of deposition condition(specially $Ar/O_2$ ratio) on the structural properties of SBN thin film. As $Ar/O_2$ ratio was increased, the peaks in the XRD pattern became more sharp. Also, the peaks(008)(115)(220) in 80/20 of $Ar/O_2$ ratio were suddenly appeared. The optimum of the rougness showed about 4.33 nm in 70/30 of $Ar/O_2$ ratio. The crystallinity of SBN thin films were increased with the increase of $Ar/O_2$ ratio. Also, Deposition rate of SBN thin films was about 4.17 nm/min in 70/30 of $Ar/O_2$ ratio. The capacitance of SBN thin films were increased with the increase of $Ar/O_2$ ratio.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.408-408
• /
• 2012

It is well known that magnetic random access memory (MRAM) is nonvolatile memory devices using ferromagnetic materials. MRAM has the merits such as fast access time, unlimited read/write endurance and nonvolatility. Although DRAM has many advantages containing high storage density, fast access time and low power consumption, it becomes volatile when the power is turned off. Owing to the attractive advantages of MRAM, MRAM is being spotlighted as an alternative device in the future. MRAM consists of magnetic tunnel junction (MTJ) stack and complementary metal- oxide semiconductor (CMOS). MTJ stacks are composed of various magnetic materials. FePt thin films are used as a pinned layer of MTJ stack. Up to date, an inductively coupled plasma reactive ion etching (ICPRIE) method of MTJ stacks showed better results in terms of etch rate and etch profile than any other methods such as ion milling, chemical assisted ion etching (CAIE), reactive ion etching (RIE). In order to improve etch profiles without redepositon, a better etching process of MTJ stack needs to be developed by using different etch gases and etch parameters. In this research, influences of $O_2$ gas on the etching characteristics of FePt thin films were investigated. FePt thin films were etched using ICPRIE in $CH_4/O_2/Ar$ gas mix. The etch rate and the etch selectivity were investigated in various $O_2$ concentrations. The etch profiles were studied in varying etch parameters such as coil rf power, dc-bias voltage, and gas pressure. TiN was employed as a hard mask. For observation etch profiles, field emission scanning electron microscopy (FESEM) was used.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.04b
• /
• pp.18-21
• /
• 2004

An alkoxide-based sol-gel method was used to fabricate $Ba_{0.6}Sr_{0.4}TiO_3$ thin films doped by Bi from 5 to 20 mol% on a $Pt/Ti/SiO_2/Si$ substrate. The structural and dielectric properties of BST thin films were investigated as a function of Bi dopant concentration. The dielectric properties of the Bi doped BST films were strongly dependent on the Bi contents. The dielectric constant and dielectric loss of the films decreased with increasing Bi content. However, the leakage current density of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin film showed the lowest value of $5.13{\times}10^{-7}\;A/cm^2$ at 5 V. The figure of merit (FOM) reached a maximum value of 32.42 at a 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films. The dielectric constant, loss factor, and tunability of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films were 333, 0.0095, and 31.1%, respectively.

• Proceedings of the KIEE Conference
• /
• 2005.11a
• /
• pp.87-89
• /
• 2005

$Bi_{3.25}Y_{0.75}Ti_{3}O_{12}$[BYT] ferroelectric thin films were deposited by RF-Sputtering method on the $Pt/Ti/SiO_2/Si$. We investigated the effects of processing condition (especially post-annealing) on the structural and ferroelectric properties of the BYT thin films. Increasing the annealing temperature, the peak intensity of (117) increased and c-axis orientation decreased. The BYT thin films crystallized well at $600^{\circ}C$ for 30min. No secondary phases observed in the XRD pattern. At annealing temperature of $700^{\circ}C$, the thin films had no cracks and the grain was uniform. The calculated lattice constants of BYT thin films were a=0.539nm, b=0.536nm, c=3.288nm. The remnant polarization of the $Bi_{3.25}Y_{0.75}Ti_{3}O_{12}$ capacitor reached $1.8uC/cm^2$ at an applied field about 400kV/cm. The BYT thin films can be used as capacitors in Ferroelectric Random Access Memory device.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2001.07a
• /
• pp.114-118
• /
• 2001

졸-겔법으로 Pt/Ti/$SiO_2$/Si 기판위에 $Bi_{3.7}$/$La_{0.75}$$Ti_3O_{12}$(BLT) 강유전체 박막을 형성하였다. As-coated BLT 박막은 $600^{\circ}C$의 후속 열처리온도에서 결정화 되었으며 전형적인 Bi 층상 페롭스카이트 결정구조를 나타내었다. 또한 후속 열처리온도를 증가함에 따라 결정성이 향상되었다. $700^{\circ}C$의 온도에서 후속 열처리된 BLT 박막의 비 유전상수($\varepsilon_{r}$)와 유전손실($\textrm{tan}\delta$)은 5KHz 주파수에서 약 402와 0.04를 각각 나타내었다 $800^{\circ}C$에서 후속 열처리된 BLT박막의 경우 5V의 인가 전압에서 잔류분극 2Pr($Pr^{+}$-$Pr^{-}$)값은 약 32.5$\mu$C/$Cm^2$을 나타내었다.