Pt(80nm)/$SiO_2$(150nm)/Si 기판위에 $Ba_{0.7}Sr_{0.3}TiO_3$ 박막을 rf-magnetron Sputtering 방법을 이용하여 기판온도 590$^{\circ}C$에서 33nm 두께를 증착했을 때 비유전율은 268 이었다. 비유전율이 3.9인 $SiO_2$와 비교했을 때 유효 두께인 Tox는 0.45nm 이었다. 누설 전류 밀도는 1.5V 전압을 인가했을 때 $4.21\times10^{-7}A/cm^2$이었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.455-458
• /
• 2001

The thin films of high pemitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)$TiO_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/$SiO_2/Si$ substrate at 4,000 [rpm] for 10 seconds. The devices of BST thin films to composite $(Ba_{0.7},Sr_{0.3})TiO_3$ were fabricated by changing of the depositing layer number on $Pt/Ti/SiO_2/Si$ substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was $2500[\AA]$, $3500[\AA]$, $3800[\AA]$. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency l[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.455-458
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/SiO$_2$/Si substrate at 4,700 [rpm] for 10 seconds. The devices of BST thin films to composite (Ba$\_$0.7/Sr$\_$0.3/)TiO$_3$ were fabricated by changing of the depositing layer number on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was 2500[${\AA}$], 3500[${\AA}$], 3800[${\AA}$]. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency 1[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1997.02a
• /
• pp.38-38
• /
• 1997

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.211-211
• /
• 2003

PbTiO$_3$ 씨앗층을 이용하여 완화형 강유전체 Pb(Mg$_{1}$3/Ta$_{2}$3/)O$_3$ (PMT) 박막의 페로브스카이트 상안정화와 열처리 조건에 따른 미세구조변화, 이에 따른 전기적 특성 변화에 관하여 조사하였다. PbTiO$_3$ 박막을 스핀코팅법으로 3000 rpm에서 20초간(111) 방향으로 배향된 Pt / Ti / SiO$_2$/ Si 기판에 증착하여 안정화된 페로브스카이트 박막을 얻었다. 이렇게 제조된 PbTiO$_3$를 Buffer 층으로 사용하고 그 위에 Pb(Mg$_{1}$3/Ta$_{2}$3/)O$_3$를 박막을 Spin coating방법으로 증착한 후, 급속열처리 방법(RTA)으로 550- $650^{\circ}C$ 사이에서 열처리하였다. 제조된 박막의 열처리 온도에 따른 미세구조 변화와 결정성을 XRD, SEM, TEM으로 분석하였고 박막의 저온 강유전 특성을 RT66A를 이용하여 평가하였다. Pb(Mg$_{1}$3/Ta$_{2}$3/)O$_3$ 박막의 경우 씨앗층이 없는 경우에는 pyrochlore상이 주상이었지만 씨앗층을 사용한 경우 페로브스카이트 상이 주상임을 확인하였고 열처리 온도가 증가할수록 페로브스카이트상의 상대적 양이 증가함을 확인하였다. 미세구조와 상의 변화에 따른 전기적 특성 변화에 관하여 자세하게 논의할 것이다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.245-245
• /
• 2012

Syntheses of oxide supported metal catalysts by wet-chemical routes have been well known for their use in heterogeneous catalysis. However, uniform deposition of metal nanoparticles with controlled size and shape on the support with high reproducibility is still a challenge for catalyst preparation. Among various synthesis methods, arc plasma deposition (APD) of metal nanoparticles or thin films on oxide supports has received great interest recently, due to its high reproducibility and large-scale production, and used for their application in catalysis. In this work, Au and Pt nanoparticles with size of 1-2 nm have been deposited on titania powder by APD. The size of metal nanoparticles was controlled by number of shots of metal deposition and APD conditions. These catalytic materials were characterized by x-ray diffraction (XRD), inductively coupled plasma (ICP-AES), CO-chemisorption and transmission electron microscopy (TEM). Catalytic activity of the materials was measured by CO oxidation using oxygen, as a model reaction, in a micro-flow reactor at atmospheric pressure. We found that Au/$TiO_2$ is reactive, showing 100% conversion at $110^{\circ}C$, while Pt/$TiO_2$ shows 100% conversion at $200^{\circ}C$. High activity of metal nanoparticles suggests that APD can be used for large scale synthesis of active nanocatalysts. We will discuss the effect of the structure and metal-oxide interactions of the catalysts on catalytic activity.

• Journal of the Korean Ceramic Society
• /
• v.35 no.5
• /
• pp.465-471
• /
• 1998

Lead titanate(PT) and lead magnesium niobate(PMN) ceramic powders were prepared by microwave hy-drothermal method using teflon bomb. Raw materials were Pb(NO3)2 and TiO2 for lead titanate and Pb(NO3)2 Nb2O5 and Mg(NO)3.6H2O for PMN with NaOH as mineralizer in both cases. in lead titanate synthsis rate of microwave hydrothermal method was faster three times than one f conventional hydrothermal methods In lead magnesium niobate synthsis the mixture of perovskite and pyrochlore phases was obtained by single step technique and the PMN was not obtained by double step technique due to low temperature limitation of teflon bomb.

• Korean Journal of Materials Research
• /
• v.6 no.5
• /
• pp.449-456
• /
• 1996

BaO, SrCI2.6H2O 그리고 Ti(OPri)4를 출발 원료로 사용하여 균일한 BaxSr1-xTiO3(BST) 솔을 합성하였고, BST 박막을 회전 코팅 법으로 Si 및 Pt/Ti/SiO2/Si 기판위에 제조하였다. 적외선 및 NMR 스펙트럼 분석으로 킬레이션 조제로 사용한 acetylacetone(AcAc)이 엔올 형태로 Ti-알콕사이드와 결합하여 솔 안정화에 기여함을 확인하였다. Xedrogel에 대한 DT/TGA 및 적외선 스펙트럼 결과로부터 페로브스카이트 상생성이 $600^{\circ}C$ 이상에서 이루어짐을 관찰하였다. $700^{\circ}C$에서 열처리한 박마은 -300(10 KHz)의 상대유전율을 나타내었고, 결정립의 저항 및 입계의 병렬 RC 성분으로 등가회로를 구성할 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.39-40
• /
• 2005

Ferroelectric Eu-substituted $Bi_4Ti_3O_{12}$ (BET) thin films with a thickness of 200 nm were deposited on Pt(111)/Ti/SiO$_2$/Si(100) substrate by means of the liquid delivery MOCVD system and annealed at several temperatures in an oxygen atmosphere. At annealing temperature above $600^{\circ}C$, the microstructure of layered perovskite phase was observed. The remanent polarization of these films increased with increase in annealing temperature. The remanent polarization values ($2P_r$) of the BET thin films annealed at $720^{\circ}C$ were $37.71{\mu}C/cm^2$ at an applied voltage of 5 V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.67-69
• /
• 2004

The $Pb(Zr,Ti)O_3$ thin films were fabricated with $Pb(La,Ti)O_3$ buffers in-situ onto $Pt/Ti/SiO_2/Si$ substrates by pulsed laser deposition technique using a Nd:YAG laser with energy density of $2.5J/cm^2$, and deposited for 10 minutes at $550^{\circ}C$ of substrate temperature. And then, the films have been annealed at $550^{\circ}C$ in oxygen ambient pressure. The remanent polarization value is increased by using buffer layers but coercive field of films is slightly increased.