• 한국전기전자재료학회논문지
• /
• 제34권6호
• /
• pp.442-448
• /
• 2021

In this work, the (K_1-xAg_x)(Ta_0.8Nb_0.2)O₃ (x=0.1-0.4) ceramics were fabricated using mixed-oxide method, and their structural and electrical properties were measured. All specimens represented a pseudo cubic structure with the lattice constant of 0.3989 nm. When 0.4 mol of Ag was added, second phases induced from metallic Ag and K₂(Ta,Nb)₆O₁₆ phase were observed. Dielectric constant and dielectric loss of K(Ta_0.8Nb_0.2)O₃ specimen doped with 0.3 mol of Ag were 2,737 and 0.446, respectively. The curie temperature was about -5℃, which does not change with Ag addition. The remanent polarization began to decrease sharply around 12~15℃, and the temperature at which the remanent polarization began to decrease as the applied voltage increased shifted to the high temperature side. The electrocaloric effect (ΔT) and electrocaloric efficiency (ΔT/ΔE) of the (K_0.7Ag_0.3)(Ta_0.8Nb_0.2)O₃ ceramics were 0.01024℃ and 0.01825 KmV^-1, respectively.

• 한국전기전자재료학회논문지
• /
• 제37권3호
• /
• pp.297-303
• /
• 2024

In this study, KTN heterolayer thin films were fabricated by alternately stacking films of K(Ta_0.70Nb_0.30)O₃ and K(Ta_0.55Nb_0.45)O₃ synthesized using the sol-gel method. The sintering temperature and time were 750℃ and 1 hour, respectively. All specimens exhibited a polycrystalline pseudo-cubic crystal structure, with a lattice constant of approximately 0.398 nm. The average grain size was around 130~150 nm, indicating relatively uniform sizes regardless of the number of coatings. The average thickness of a single-coated film was approximately 70 nm. The phase transition temperature of the KTN heterolayer films was found to be approximately 8~12℃. Moreover, the 6-coated KTN heterolayer film displayed an excellent dielectric constant of about 11,000. As the number of coatings increased, and consequently the film thickness, the remanent polarization increased, while the coercive field decreased. The 6-coated KTN heterolayer film exhibited a remanent polarization and coercive field of 11.4 μC/cm² and 69.3 kV/cm at room temperature, respectively. ΔT showed the highest value at a temperature slightly above the Curie temperature, and for the 6-coated KTN heterolayer film, the ΔT and ΔT/ΔE were approximately 1.93 K and 0.128×10^-6 K·m/V around 40℃, respectively.