The aim of this study is to investigate the effect of hydrogen embrittlement od Zr-2.5Nb CANDU pressure tube. The test were performed at three hydrogen contents for transverse tensile and CCT specimens while the test temperatures were changed (RT to 300$^{\circ}C$). The specimens were directly machined from the tube retaining original curvature using electric discharge machine. Both the transverse tensile and the fracture toughness tests showed the hydrogen embrittlement clearly at RT but this phenomenon was disappeared while the test temperature arrived over 250$^{\circ}C$. From the fracture toughness test, it was found that fracture toughness dJ/da was increased up to 200$^{\circ}C$ and then decreased.