• 한국세라믹학회지
• /
• 제49권6호
• /
• pp.592-600
• /
• 2012

Conventional methods for preparing ceramic bodies, such as cold isostatic pressing, gypsum-mold slip casting, and filter pressing are not completely suitable for fabricating large and thick ceramic plates owing to disadvantages of these processes, such as the high cost of the equipment, the formation of density gradients, and differential shrinkage during drying. These problems can be avoided by employing a pressure-vacuum hybrid slip casting approach that considers not only by the compression of the aqueous slip in the casting room (pressure slip casting) but also the vacuum sucking of the dispersion medium (water) around the mold (vacuum slip casting). We prepared the alumina formed bodies by means of pressure-vacuum hybrid slip casting with stepwise pressure loading up to 0.5 MPa using a slip consisting of 40 vol% solid, 0.6 wt% APC, 1 wt% PEG, and 1 wt% PVA. After drying the green body at $30^{\circ}C$ and 80% RH, the green density of the alumina bodies was about 56% RD. The sintered density of an alumina plate created by means of sintering at $1650^{\circ}C$ for 4 h exceeded 99.8%.This method enabled us to fabricate a $110{\times}110{\times}20$ mm alumina plate without cracks and with a homogeneous density, thus demonstrating the possibility of extending the method to the fabrication of other ceramic products.

• 한국세라믹학회지
• /
• 제50권2호
• /
• pp.142-148
• /
• 2013

Conventional cold isostatic pressing, slip casting, and filter pressing are not completely suitable for fabricating large plates because of disadvantages such as the high cost of equipment and formation of density gradient. These problems could be avoided by employing pressure-vacuum hybrid slip casting (PVHSC). In the PVHSC, the consolidation occurs not only by the compression of the slip in casting room, but also by vacuum sucking of the dispersion medium around the mold. We prepared the alumina bodies by the PVHSC in a static- or stepwise-pressure manner for loading up to 0.5 MPa using an aqueous slip. The green bodies were dried at $30^{\circ}C$ with 40 ~ 80% relative humidity. Under static pressure, casting induced a density gradient in the formed body, resulting in cracking and distortion after the firing. However, the stepwise pressure loading resulted in green bodies with homogeneous density, and the minimization of the appearance of those defects in final products. Desirable drying results were obtained from the cast bodies dried with 80% RH environment humidity. When sintered at $1650^{\circ}C$ for 4 h, the alumina plate made by stepwise-pressure casting reached full density (> 99.7% relative density).

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.396-401
• /
• 2013

The size of various alumina ceramics used in the semiconductor and display industries must be increased to increase the size of wafers and panels. In this research, large alumina ceramics were fabricated by pressure-vacuum hybrid slip casting (PVHSC) employing a commercial powder, followed by sintering in a furnace. In the framework of the PVHSC method, the consolidation occurs not only by compression of the slip in the casting room but also by suction of the dispersion medium from the casting room. When sintered at $1650^{\circ}C$ for 4 h, the fabricated large-size alumina ($1,550{\times}300{\times}30mm^3$) exhibited a dense microstructure corresponding to more than 99.2% of the theoretical density and a high purity of 99.79%. The flexural and compressive strengths of the alumina plate were greater than 340 MPa and 2,600 MPa, respectively.

• Journal of Advanced Marine Engineering and Technology
• /
• 제34권5호
• /
• pp.653-660
• /
• 2010

선미관 베어링은 프로펠러가 회전할 시 슬립을 방지하기 위하여 충분한 간섭량을 가지고 캐스팅에 강제 압입되어야 한다. 선미관 베어링을 캐스팅에 강제 압입 시에 필요한 힘을 계산할 때 사용되어지는 공식은 업체별로 각각 다르며, 계산 시 사용되어지는 요소들의 값도 상이하다. 이에 따라 조선소에서 선미관 베어링 강제 압입력을 계산할 때에는 업체별로 제시된 공식과 재질에 따라 고려되어지는 요소들의 값을 사용하지만 간섭량은 조선소의 경험에 기반한 값을 표준으로 사용하고 있다. 본 논문은 강제 압입법에 의한 시공시에 선미관 베어링에 사용되어지는 피팅관계식을 검토하여 선미관 베어링 업체별로 제시되어지는 값을 기반으로 한 결과를 실제 값과 비교하였다. 그 결과 업체별로 제시한 식이 두께가 두꺼운 실린더 이론을 이용하였음을 알 수 있었다. 특히 J사 및 B사의 경우에는 K사와는 달리 두께가 두꺼운 실린더 이론을 근간으로 하였지만, 두께가 얇은 실린더의 경우에도 사용할 수 있도록 변형하여 사용하고 있음을 알 수 있었다.

• 대한치과보철학회지
• /
• 제35권1호
• /
• pp.221-243
• /
• 1997

The objective of this study was to characterize the mechanical properties of $Y_{2}O_{3}$-containing glass infiltrated ceramic core material, which was made by pressureless powder packing method. A pure alumina powder with a grain size of about $4{\mu}m$ was packed without pressure is silicon mold to form a bar shaped sample, and applied PVA solution as a binder. Samples were sinterd at $1350^{\circ}C$ for 1 hour. After cooling, $Y_{2}O_{3}$-containing glass($SiO_{2},\;Y_{2}O_{3},\;B_{2}O_{3},\;Al_{2}O_{3}$, ect) was infiltrated to the sinterd samples at $1300^{\circ}C$ for 2 hours and cooled. Six different proportions $Y_{2}O_{3}$ of were used to know the effect of the mismatch of the thermal expansion coefficient between alumina powder and glass. The samples were ground to $3{\times}3{\times}30$ mm size and polished with $1{\mu}m$ diamond paste. Flexural strength, fracture toughness, hardness and other physical properties were obtained, and the fractured surface was examined with SEM and EPMA. Ten samples of each group were tested and compared with In-Ceram(tm) core materials of same size made in dental laboratory. The results were as follows : 1. The flexural strengths of group 1 and 3 were significantly not different with that of In-Ceram, but other experimental groups were lower than In-Ceram. 2. The shrinkage rate of samples was 0.42% after first firing, and 0.45% after glass infiltration. Total shrinkage rate was 0.87%. 3. After first firing, porosity rate of experimental groups was 50%, compared with 22.25% of In-Ceram. After glass infiltration, porosity rate of experimental groups was 2%, and 1% in In-Ceram. 4. There was no statistical difference in hardness between two materials tested, but in fracture toughness, group 2 and 3 were higher than In-Ceram. 5. The thermal expansion coefficients of experimental groups were varied to $4.51-5.35{\times}10^{-6}/^{\circ}C$ according to glass composition, also the flexural strengths of samples were varied. 6. In a view of SEM, many microparticles about $0.5{\mu}m$ diameter and $4{\mu}m$ diameter were observed in In-Ceram. But in experimental group, the size of most particles was about $4{\mu}m$, and a little microparticles was observed. The results obtained in this study showed that the mismatch of the thermal expansion coefficients between alumina powder and infiltrated glass affect the flexural strength of alumin/glass composite. The $Y_{2}O_{3}$-containing glass infiltrated ceramic core made by powder packing method will takes less time and cost with sufficient flexural strength similar to all ceramic crown made with slip casting technique.

• 멤브레인
• /
• 제27권2호
• /
• pp.199-204
• /
• 2017

본 연구에서는 펄프공정으로부터 배출되는 리그닌 추출물 내의 금속이온분리를 위한 연구를 진행하였다. ${\alpha}$-Alumina 분말에 DMAc (N,N-dimethylacetamide) 용매와 PESf (Polyethersulfone) 고분자를 혼합하고 PVP (Polyvinylpyrrolidone) 분산제를 첨가하여 슬립 캐스팅 방법으로 분리막을 제조하였다. 분리막은 CFP (Capillary Flow Porometer) 장치를 통해 기공크기를 측정하고 FE-SEM (Field Emission Scanning Electron Microscope) 장치를 이용하여 실제 분리막 표면과 단면을 관찰하였다. 플럭스는 분리 실험장치를 이용하여 시간당 여과된 무게를 측정하여 계산하였다. 기공크기측정은 0 psi에서 30 psi까지 서서히 증가하는 승압조건에서 진행하였다. 분리막의 기공크기는 $0.4{\mu}m$ 크기를 가지며 플럭스는 분리막의 파울링에 의해 초기 플럭스 값인 $6.36kg{\cdot}m^{-2}{\cdot}h^{-1}$에서 $1.98kg{\cdot}m^{-2}{\cdot}h^{-1}$으로 감소하여 3시간 이후부터 일정해지는 것을 확인하였다. 투과 실험 후 막 오염물질은 간단한 세척을 통해 제거 가능하였다. 분리실험을 통해 초기 리그닌 추출물 내에 포함되어 있던 Na은 69%만큼 줄었고, Fe은 87%, K은 95%, Ca은 93%, Mg은 96%만큼 제거됨을 보였다.