• Journal of Adhesion and Interface
• /
• v.8 no.2
• /
• pp.15-21
• /
• 2007

To prepare a natural rubber-based pressure-sensitive adhesive (PSA) for protection film of opto- functionalized sheet, natural rubber (NR) was blended with a DCPD type tackifier and three types of aliphatic hydrocarbon resins, respectively. Also, to supply low cohesion strength of NR, in the fixed ratio of tackifier, synthetic rubber, styrene-isoprene-styrene (SIS) block copolymer was blended with NR as a function of SIS contents. PSA performance of prepared PSAs was evaluated using probe tack and peel strength. Probe tack of NR/tackifier blends was increased with increasing tackifier contents, and showed maximum peak. In addition, probe tack of NR/tackifier blends slightly increased with increasing softening point of aliphatic hydrocarbon resins. Their peel strength increased up to 50 wt% of tackifier contents, but in the over contents of tackifier, they showed stick-slip failure mode. Finally, probe tack of NR/SIS/tackifier blends showed the maximum values at 20~40 wt% of tackifier contents, but at 20 wt% of tackifier contents, they showed fibrillation. For this reason, peel strength showed maximum values at 40 wt% of tackifier contents.

• Journal of Adhesion and Interface
• /
• v.6 no.3
• /
• pp.19-25
• /
• 2005

Synthetic rubber based pressure-sensitive adhesives (PSAs) usually containing SIS or SBS block copolymer, tackifier, plasticizer, and other additives are now widely used on various applications. As these PSAs are physically crosslinked and can be applied without the use of solvent, they are thermally processable and environmentally friendly. However these PSAs cannot be used in high temperature applications and in applications where solvent and chemical resistance properties are required. We developed the PSA adding UV curable system, such as thiol-ene system, to increase adhesion properties at elevated temperature. The adhesion properties such as probe tack, peel strength, shear adhesion failure temperature (SAFT) were evaluated. The probe tack test was conducted with varying probe materials and coating thickness of PSAs. Using the contact angle, the surface property of the cured PSAs was also observed.

• Journal of Adhesion and Interface
• /
• v.7 no.2
• /
• pp.12-18
• /
• 2006

Recently, as industries and technologies are increased, superior adhesives having more and more developed functions and properties have been demanded. In this article, to use the merits and viscoelastic properties of poly(ethylene/butylene) rubber resin and to supplement the demerits, semi-structure pressure sensitive adhesives (PSAs) are developed. Aslo, it can be said environmentally friendly PSAs because of not use the organic solvent and not emit volatile organic compounds (VOCs).

• Polymer(Korea)
• /
• v.38 no.4
• /
• pp.491-495
• /
• 2014

Pressure sensitive adhesive (PSA) based on 2-ethylhexyl acrylate (2-EHA)/acrylic acid (AA) copolymer was synthesized using different photoinitiators. Results showed that PSA with Irgacure$^{(R)}$651 (benzyldimethylketal) and Irgacure$^{(R)}$184(1-hydroxy-cyclohexylphenyl ketone) proved to be good for adhesion properties. This may be attributed to strong absorption near 350 nm wavelength and also high solubility in monomer mixtures. The addition of Irgacure$^{(R)}$819, bisacylphosphine oxides as a photoinitiator caused cohesive failure with high loading in a peel test owing to the additional radical formation. It is assumed that the insoluble photoinitiator reacts with oxygene, which may act as a hydrogen donor.

• Polymer(Korea)
• /
• v.36 no.3
• /
• pp.315-320
• /
• 2012

Ultra violet (UV) curable pressure sensitive adhesives (PSA) were prepared by controlling both the structure of acryl copolymer and the functionality and content of multi-functional monomers. Acryl copolymer worked as the base polymer for giving the tackiness. Multi-functional monomers were used to vary the crosslinked structure and the degree of crosslink. Acryl copolymer showed the reduced peel strength after UV curing by decreasing the content of 2-ethylhexyl acrylate in the monomer composition. Both the peel strength of PSA and the content of residue found on silicon wafer decreased after UV curing by increasing the functionality of multi-functional monomers. UV curable PSA containing 20 phr six-functional monomer showed the higher peel strength before UV curing and the lower peel strength and the least residue on silicon wafer after UV curing.

• Polymer(Korea)
• /
• v.38 no.2
• /
• pp.199-204
• /
• 2014

To prepare acrylic pressure sensitive adhesives (PSAs), quaternary copolymer syrups were photopolymerized from 2-ethylhexyl acrylate and 2-hydroxyethyl acrylate as default constituents and isobornyl acrylate and tetrahydrofurfuryl acrylate (THFA) as variable constituents. After polymerization, 1,6-hexanediol diacrylate and photoinitiator were added and then crosslinked by UV-irradiation to prepare the PSAs. The characteristics of the syrup such as viscosity, molecular weight, and solid content were investigated. As increasing THFA contents, the relationship between molecular weight and solid content of the syrup was reciprocal. Also, the relationship between peel strength and surface energy of the PSAs showed the same tendency. All the PSA samples showed high transmittance (more than 92%), low haze (less than 1.0%) and low color-difference (less than 1.0).

• Journal of Adhesion and Interface
• /
• v.14 no.1
• /
• pp.43-48
• /
• 2013

The physical properties of the acrylic pressure sensitive adhesives (PSAs) can be easily controlled by a proper functional monomer which has functional groups for crosslinking. This study was to investigate the effect of crosslinking agents, isocyanate and epoxy types, of acrylic PSAs on adhesive properties. 2-Ethylhexyl acrylate, acrylic acid (AA), and 2-hydroxy ethyl methacrylate as monomer were used. The obtained samples with different AA contents were partially crosslinked with epoxy- or isocyanate-typed agent. Peel strength, balltack, holding power test and contraction percentage of the obtained PSA were evaluated. Most properties of acrylic PSAs were increased with AA content and acrylic PSAs with epoxy-typed crosslinking agent (4 crosslinking sites) which produces flexible link (ether), showed better properties than those of isocyanate-typed one (3 crosslinking sites).

• Polymer(Korea)
• /
• v.38 no.5
• /
• pp.682-686
• /
• 2014

To prepare transparent acrylic pressure sensitive adhesives (PSAs), terpolymer syrups were photopolymerized from 2- ethylhexyl acrylate and 2-hydroxyethyl acrylate with third monomer having different chemical structure. After polymerization, 1,6-hexanediol diacrylate as a crosslinker and a photoinitiator were added and then UV-irradiated to prepare the PSAs. The adhesion performances and optical characteristics of the PSAs were investigated. Their adhesion performance was dependent on the composition of monomers in the polymer chain but optical properties were maintained at a suitable level. The PSAs prepared by bulky and heteroatom-containing monomers such as IBOA, THFA, and ACMO showed better adhesion performance than others.

• Korean Chemical Engineering Research
• /
• v.48 no.5
• /
• pp.609-614
• /
• 2010

In this study, emulsion polymerizations for synthesizing acrylic pressure-sensitive adhesive(PSA) were carried out using 2-ethylhexyl acrylate(2-EHA), n-butyl acrylate(n-BA), methyl metacrylate(MMA) as fundamental monomers and acrylic acid(AAc) as a functional monomer in the presence of anionic SLS (sodium lauryl sulfate). To obtain the optimized synthetic condition in the polymerization, we analyzed the polymerization variables such as the effect of surfactant concentration and hydrophilic lipophilic values(HLB). At the same time, the final adhesive properties were also analyzed by the function of the initiator concentration and buffer concentration. In the results, the most stable emulsion was obtained at the surfactant concentrations between 3 and 5 wt%. It was also determined the effect of HLB value of nonionic surfactant and the initiator concentrations on the gel content. Stable emulsion is obtained using the surfactant having HLB value of 12.3. The rate of emulsion polymerization was increased at the initiator concentration greater than 1 wt%, but the stability of the emulsion was decreased. Finally, the effect of the buffer concentrations on the pH and the conversion of the acrylic emulsion product were experimentally measured. At the sodium bicarbonate concentration above 0.4 wt%, the buffer infulence was apparent. The buffer effect was fully acceptable at the concentrations between 0.6 and 0.8 wt% regardless of the monomer composition.

• Journal of Adhesion and Interface
• /
• v.20 no.1
• /
• pp.15-22
• /
• 2019

In this study, polybutadiene based di-functional urethane acrylate oligomer (PB-UAO) were synthesized from polybutadiene diol and isophorone diisocyanate. And then, pressure sensitive adhesive films were prepared by mixing with synthesized oligomer, tri-functional acrylate monomer (Tris(2-acryloyloxyethyl) isocyanurate (TAOEIC) or Trimethylolpropane triacrylate (TMPTA) or Pentaerythritol triacrylate (PETA)), mono-functional acrylate monomer (Stearyl acrylate) and UV initiators. Effects of types and contents of trifunctional acrylate monomers on peel strength, tensile strength, elongation, thermal stability and water absorption property were studied. As the contents of tri-functional acrylate monomer increased, and as the molecular weight of tri-functional acrylate monomer decreased, peel strength, elongation and water absorption showed a tendency to decrease whereas tensile strength and thermal stability showed a tendency to increase.