• Korean Journal of Materials Research
• /
• v.20 no.7
• /
• pp.385-391
• /
• 2010

Twinning-induced plasticity (TWIP) steels have attracted great attention due to their excellent mechanical properties of high tensile strength (over 800MPa) and high ductility (over 50%), which result from the high strain hardening due to the mechanical twin formation during plastic deformation. The purpose of this study is to investigate the effect of annealing temperature and alloying elements on the mechanical properties of Fe-18Mn-0.6C TWIP steel. In 1.5%Al TWIP steel with 0.123%Ti content, the average recrystallized grain size was reduced to 2.5 ${\mu}m$ by cold rolling and annealing at $800^{\circ}C$ for 5 min, because of the pinning effect of the fine TiC carbides on grain coarsening. The tensile strength was decreased and the ductility was improved with the increase of the annealing temperature. However, a reversion of hardness and yield strength happened between $750^{\circ}C$ and $800^{\circ}C$ due to TiC and $M_3C$ type precipitation. 0.56% Ni added TWIP steel exhibited relatively lower yield strength, because Ni precipitates were not formed during the annealing process. When this specimen was annealed at $800^{\circ}C$ for 5min, the tensile strength and elongation were revealed at 1096MPa and 61.8%, respectively.

• Journal of Welding and Joining
• /
• v.13 no.2
• /
• pp.122-131
• /
• 1995

The effects of cooling rate on the microstructures, precipitation of Cu-cluster, .epsilon.-Cu and impact toughness of high strength low alloy(HSLA) steel were studied using hardness tester, impact tester, DSC(differential scanning calorimetry), AES(auger electron spectroscopy) and TEM(transmission electron microscopy). Not only the Cu-precipitates but also the segregation of Cu, As, Sb, P, S, N, Sn along grain boundary were not observed at the specimens heat treated from 800.deg. C to 300.deg. C with the cooling time of 12-125 sec. The Cu-cluster, .epsilon.-Cu are formed by introducing ageing after cooling and the effect of precipitates on hardening increase after cooling was the same in all cooling rate. The peak hardness was obtained at an ageing of 500.deg. C in all cooling conditions. The impact energy become higher as the cooling time increases. This fact can be explained to be due to the tempering effect applied on the cooling stage since the present alloy has a relatively high Ms temperature and the local high concentration of the retained austenite.

• Korean Journal of Materials Research
• /
• v.22 no.1
• /
• pp.16-23
• /
• 2012

Research into the development of high strength (1 GPa) and superior formability, such as total elongation (10%), and stretch-flangeability (50%) in hot-rolled steel was conducted with a thermomechanically controlled hot-rolling process. To improve the overall mechanical properties simultaneously, low-carbon steel using precipitation hardening of Ti-Nb-V multimicroalloying elements was employed. And, ideal microstructural characteristics for the realization of balanced mechanical properties were determined using SEM, EBSD, and TEM analyses. The developed steel, 0.06C-2.0Mn-0.5Cr-0.2(Ti + Nb + V), consisted of ferrite as the matrix phase and second phase of granular bainite with fine carbides (20-50 nm) in both phases. The significant factor of the microstructural characteristics that affect stretch-flangeability was found to be the microstructural homogeneity. The microstructural homogeneity, manifest in such characteristics as low localization of plastic strain and internally stored energy, was identified by grain average misorientation method, analyzed by electron backscattered diffraction (EBSD) and hardness deviation between the phases. In summar, a hot-rolled steel having a composition 0.06C-2.0Mn-0.5Cr-0.2(Ti + Nb + V) demonstrated a tensile strength of 998 MPa, a total elongation of 19%, and a hole expansion ratio of 65%. The most important factors to satisfy the mechanical property were the presence of fine carbides and the microstructural homogeneity, which provided low hardness deviation between the phases.

• Journal of the Korean Society for Heat Treatment
• /
• v.23 no.6
• /
• pp.338-343
• /
• 2010

Mechanical properties and microstructures of medium carbon high manganese steels were investigated in terms of alloying elements such as Mn, C contents, and heat treatment condition. Austenite volume fraction was increased with increasing Mn content, leading to hardness decrease in the range of Mn content of above 10% after quenching and tempering. Such results are also supported by microstructural analysis and X-ray diffraction in that the increase in mangaese content results in the increase in austenite fraction. Studies on tempering condition indicated that not only hardness and tensile strength but also charpy impact values were reduced as tempering temperature were raised in the range of $250^{\circ}C$ to $600^{\circ}C$. It was also observed that fracture mode was changed from dimple to intergranular fracture. Such results are thought to be due to very fine carbide precipitation or impurity segreagation at grain boundaries as tempering temperature goes up. Heat treatment of Fe-5Mn-2Si-1Al-0.4C can be optimized by austenitizing at $850^{\circ}C$, air cooling and tempering at $250^{\circ}C$, resulting in 1950 MPa in Tensile strength, 17% in elongation and 23.3 $J/cm^2$ in charpy impact energy with high work hardening characteristics.

• Journal of Welding and Joining
• /
• v.33 no.4
• /
• pp.30-36
• /
• 2015

Austenite stainless steel(SA213-TP347H) has widely been used for the superheater & reheater tube in USC(ultra-supercritica) coal boiler because of its high creep rupture strength and anti-oxidation. But recently, the short-term failures have happened frequently in heat affected zone for only 4,000~15,000hours of service. Many investigations have been conducted to understand the failure mechanism. The root cause of failure was comfirmed to "strain induce participation hardening crack" or "reheat cracking". This mechanism often occurred due to weld residual stress and precipitation of the Cr, Nb carbides in the stabilized stainless steel such as TP347H. This paper presents an analysis of failure tube and effect of the sample tubes that conducting stabilizing heat treatment in site after 11,380hours & 16,961hours of service. Visual inspection was performed. In addition, microscopic characteristics was identified by O.M, SEM, and hardness test was carried out to find out the heat treatment effects. Failures seem to happen because of being not conducted stabilizing heat treatment in site. And another cause is inadequate weld parameter such as pass, ampere, voltage, inter-pass temperature. Thus, this paper has the purpose to describe that how to prevent similar failures in those weld-joints.