• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.814-815
• /
• 2006

The removal of oxygen during sintering by carbothermic reduction was studied for steel compacts Fe-Cr-Mo-C and Fe-Mo-C prepared from prealloyed powders. The compacts were prepared by pressing at 600 and 1000 MPa and sintering at 1100 and $1300^{\circ}C$ in vacuum. It showed that for the Cr-Mo steel, deoxidation strongly depends on the sintering temperature, in contrast to the plain Mo steel; at $1300^{\circ}C$ very low oxygen levels were measured with the standard density compact while at high density still significant oxygen is contained. This indicates inhibition of final deoxidation by pore closure, but apparently without adverse effect on the mechanical properties.

• Journal of the Korean Society for Precision Engineering
• /
• v.15 no.2
• /
• pp.28-34
• /
• 1998

Powder metallurgy processes are able to form Net-Shape products and have been widely used in the production of automobile parts to improve its productivity. However, because of pores in powder products, the toughness of powder products are generally poor. Therefore, forged products are used in parts which suffer severe fatigue loads. In this paper, the choice of powder materials and production processes such as mixing, compaction, sintering, heat treatment to produce automobile spline hub are studied. Three type of materials are selected and processed and its microstructure and properties are investigated by tensile test, compression ring test, and impact test. Materials and processing methods are selected from the results. Finally, experimental spline hubs are manufactured by selected processes from selected powders and proved by torsional durability test.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.549-550
• /
• 2006

The corrosion performance of a powder metallurgical aluminum alloy in aeronautical environments was studied for both as sintered and heat treated states. Sintered samples were obtained by uniaxial pressing of an Al-Cu-Mg prealloyed powder followed by liquid phase sintering. The heat treatments applied were T4 and T6. Corrosion behaviour was assessed by means of potentiodynamic polarization. Results for the equivalent commercial wrought counterpart, AA2024-T3, are also presented for comparison. Similar corrosion performance was observed for both as sintered and AA2024-T3 samples, while corrosion resistance of the PM materials was improved by the heat treatment, especially in the T4 state.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.387-388
• /
• 2006

The influence of porosity (P) on Young's modulus (E) and Poisson's ratio $(\upsilon)$ of sintered steels produced from four types of steel powders was investigated. The values of E and $(\upsilon)$ depend mainly on the value of P, and those were a little affected by alloying elements. The relationships between E, $(\upsilon)$, and P were described as following equations: $E\;=\;E_0{\cdot}(1\;-\;k_E{\cdot}P)^2$ and $\upsilon\;=\;({\upsilon}_0\;-\;\upsilon_{sub}){\cdot}(1\;-\;k_{\upsilon}{\cdot}P)2+\upsilon_{sub}$, where subscript 0 means P = 0, and $k_E,\;k_{\upsilon}$ and ${\upsilon}_{sub}$ are empirical constants. These approximate equations showed good agreement with empirical results.

• Journal of Powder Materials
• /
• v.1 no.1
• /
• pp.60-65
• /
• 1994

When a commercial prealloyed Fe-powder(Fe-5Cr-lMo-2Cu-0.5P-3C) is liquid phase sintered at 116$0^{\circ}C$, liquid precipitates with various shapes form within solid grains during the initial stage of sintering. The shape of a liquid precipitate changes pith the increment of their size from sphere(with radius<0.3$\mu\textrm{m}$), a transient polyhedron with more than 7 faces(1~2 $\mu\textrm{m}$), cuboid(3~5 $\mu\textrm{m}$), and finally to sphere(>5 $\mu\textrm{m}$). The shapes of liquid precipitates closely resemble the growth shapes predicted on the basis of solid-liquid interfacial energy and the coherency strain energy with anisotropic elastic constants in the diffusion zone around the precipitates.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2004.11a
• /
• pp.46-47
• /
• 2004

The microstructure and mechanical properties of the hypereutectic prealloyed Al-Si powders prepared by the gas atomization process were described in this paper. With increasing the gas pressure of the atomization, the average powder size was decreased from about $145{\mu}m\;to\;80{\mu}m$. The primary eutectic Si particles were uniformly distributed in the Al matrix and their size varied in the range of $8-10{\mu}m$. The high densified specimens with above 96% of the theoretical density were fabricated the hot pressing process. The UTS mechanical properties of VN1 specimens were much higher than that of conventional hypoeutectic Al-Si alloys.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.933-934
• /
• 2006

The present study examines the sintering behaviour and effect of manganese addition both mechanically-blended and mechanically alloyed on Cr-Mo low alloyed steels to enhance the mechanical properties. Mn sublimation during sintering provides some specific phenomena which facilitate the sintering of alloying elements with high oxygen affinity. First step is the optimization of milling time to attain a master alloy with 50% of Mn which is diluted in Fe-1.5Cr-0.2Mo water atomized prealloyed powder by normal mixing. These mixtures are pressed to a green density of $7.1g/cm^3$ and sintered at $1120^{\circ}C$ in $90N_2-10H_2$ atmosphere.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.931-932
• /
• 2006

The microstructures of Ni-containing P/M steels produced by admixed powders or diffusion alloyed powders are usually heterogeneous. To improve the microstructure homogeneity, the effects of Mo and Cr additions in the prealloyed powder form were examined. The results showed that the microstructural homogeneity was improved and superior mechanical properties were achieved with increases in the alloy content, particularly for the Cr. Such a beneficial effect was attained due to the reduction of the repelling effect between Ni and C, as was demonstrated through thermodynamic analysis using the Thermo-Calc software.

• Korean Journal of Materials Research
• /
• v.23 no.10
• /
• pp.574-579
• /
• 2013

The milling and particulate characteristics of Al alloy-$Al_2O_3$ powder mixtures for a reaction-bonded $Al_2O_3$ (RBAO) process were studied. A commercially available prealloyed Al powder with Zn, Mg, Cu and Cr alloying elements (7475 series) was mixed with a calcined sinter-active $Al_2O_3$ powder and then milled in centrifugal milling equipment for ~48 hrs. The Al alloy-$Al_2O_3$ powder mixtures after milling were characterized and evaluated in various ways to reveal their particulate characteristics during milling. The milling efficiency of the Al alloy increased with a longer milling time. Comminution of the Al alloy particles started with its elongation, showing a high aspect ratio. With a longer milling time, the elongated Al alloy particle changed in terms of its shape and size, becoming equiaxially fine particles. Regardless of the milling efficiency of the Al alloy particles, all of the Al alloy particles repeatedly experienced strong plastic deformation during milling, giving rise to higher density of surface defects, such as microcracks, and leading to higher residual microstress within the Al alloy particles. The chemical reactions, oxidation behavior and hydration behavior of the Al alloy particles and the hydrolysis characteristics of their reaction with the environment were also observed during the milling process and during the subsequent powder handling steps.

• Journal of Powder Materials
• /
• v.20 no.1
• /
• pp.7-12
• /
• 2013

The effect of particle size distribution on green and sintered properties of Fe-Cr-Mo prealloy powder was investigated in this study. For the study, prealloyed Fe-Cr-Mo powders with different particle sizes were mixed as various ratios and cold compacted at various pressure and sintered at $1250^{\circ}C$ for 30 min, $90%N_2+10%H_2$ atmosphere in the continuous sintering furnace. The results shows that the powders with large particle size distribution have high compressibility and low ejection force. However the green strength are much less than those with small particle size distribution. Tensile prperties of the sintered specimes with large particles size also have high strength and elongation.