• Korean Journal of Materials Research
• /
• v.14 no.9
• /
• pp.627-633
• /
• 2004

Lithium titanate whiske($Li_{x}Ti_{4}O_9$) was prepared by an ion-exchange reaction. To this end, the initial material, potassium tetratitanate ($K_{2}Ti_{4}O_9{\cdot}nH_{2}O$) was prepared by calcination of a mixture of $K_{2}CO_3\;and\;TiO_2$ with a molar ratio of 2.8 at $1050^{\circ}C$ for 3 h, followed by boiling water treatment of the calcined products for 10 h. Fibrous potassium tetratitanate could be transformed into layered hydrous titanium dioxide ($H_{2}Ti_{4}O_9{\cdot}nH_{2}O$) through an exchange of $K^{+}\;with\;H^{+}$ using 0.075 M HCl. Also, lithium titanate whisker was finally prepared as $Li^{+}\;and\;H^{+}$ ions were exchanged by adding 20 mL of a mixture solution of LiOH and $LiNO_3$ to 1g whisker and stirring for $5\~15$ days. The average length and diameter of the $Li_{x}Ti_{4}O_9$ whiskers were $10\~20{\mu}m\;and\;1\~3{\mu}m$, respectively.

• Applied Chemistry for Engineering
• /
• v.8 no.3
• /
• pp.410-415
• /
• 1997

Fibrious potassium hexatitanate whisker was produced from the calcination process using a mixture of the natural rutile ore and industrial $K_2CO_3$. Fibrous Potassium titanate was prepared by the following procedures the starting material consisting of $K_2O{\cdot}4.4TiO_2$ was calcined at $1050^{\circ}C$ for 3 hrs. The calcined products obtained under the above condition consisted mainly of potassium hexatitanate with a small admixture of potassium dititanate and potassium tetratitanate. Therefore the single phase of potassium hexatitanate was obtained by heat treatment of $850^{\circ}C$, 3 hrs.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1999.11a
• /
• pp.213-218
• /
• 1999

Friction and wear characteristics of novolac resin-based friction materials reinforced with aramid pulp and potassium titanate were investigated by using a pad-on-disk type friction tester. Friction properties such as friction stability, surface morphology, and wear rate varied according to the relative amount of aramid pulp and potassium titanate. The friction materials reinforced with both aramid pulp and potassium titanate showed superior friction stability and wear resistance due to the formation of durable transfer layer.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.26 no.4
• /
• pp.150-154
• /
• 2016

Method for synthesizing a $K_2Ti_6O_{13}$ whisker is a solid-state method, hydrothermal synthesis method, calcination method, flux method, slow-cooling method, melting method, kneading-drying-calcination method, sol-gel method etc. $K_2Ti_6O_{13}$ whisker have been synthesized by a flux method. The average size and distribution of the synthesized $K_2Ti_6O_{13}$ whisker can be controlled by a kind of potassium precursors and reaction temperature and time. The average size of the synthesized $K_2Ti_6O_{13}$ whisker was about in the size range of 500 nm to $2{\mu}m$. The effect of synthesis parameters, such as the molar ratio of KOH to $TiO_2$, pH, reaction temperature and time, are discussed. The synthesized $K_2Ti_6O_{13}$ whisker were characterized by x-ray diffraction analysis (XRD), field emission scanning electron microscopy (FE-SEM).

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.1
• /
• pp.9-17
• /
• 2017

$K_2Ti_6O_{13}$ whisker have been synthesized by hydrothermal process at low temperature and pressure condition. The average length of the synthesized $K_2Ti_6O_{13}$ whisker was about in the range of 300 nm to $1.5{\mu}m$. The average diameter of the synthesized $K_2Ti_6O_{13}$ whisker was 15 nm to 60 nm. The aspect ratio of the synthesized $K_2Ti_6O_{13}$ whisker was below 12. The average length and diameter of the synthesized $K_2Ti_6O_{13}$ whisker can be controlled by reaction temperature and time, KOH molar ratio. $K_2Ti_6O_{13}$ whisker was synthesized from more than $210^{\circ}C$ and 4 h at reaction temperature and time. The length of the whisker is increased with increasing reaction temperature. Characterization of the synthesized $K_2Ti_6O_{13}$ whisker was carried out using the XRD and FE-SEM.

• Applied Chemistry for Engineering
• /
• v.5 no.1
• /
• pp.160-175
• /
• 1994

Fibrous potassium hexatitanate whisker with the size of $ID=0.5{\sim}1{\mu}m$ and length=$100{\sim}1000{\mu}m$ (aspect ratio=100~1000) was produced through the reaction between titanium dioxide and potassium carbonate using the slow-cooling calcination followed by water leaching treatment. The optimum condition for the production of fibrous potassium titanate was calcination temperature of $1100^{\circ}C$ for 5hrs, $TiO_2$ mole ratlo to $K_2CO_3$ of 4.5 and slow-cooling rate of $0.5^{\circ}C/min$ to $860^{\circ}C$. Fibrous crystal are grown by the association between the solid potassium titanate and liquid phase during the slow-cooling process. The Proper water leaching condition for removing of K component was leaching time of 10hrs in boiling water. Pressurizing of the mixture of $K_2CO_3$ and $TiO_2$ to be calcinated became effective on the growth of fibrous crystal.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.5 no.3
• /
• pp.261-268
• /
• 1995

In transforming $K_2Ti_4O_9$ whisker, synthesized by calcination and slow cooling method, into $K_2Ti_6O_{13}$ whisker with boiling water and hydrochrolic acid, the effect of their treatment time and concentration on phase transformation, surface state and scattering of whisker was examined. The result was that the surface state of whisker was improved and whisker with a small diameter and a considerable aspect ratio was obtained by inducing scattering of a bundle of whisker. The treatment by boiling water and hydrochrolic acid induced the phase transformation of $K_2Ti_4O_9$ into $K_2Ti_6O_{13}$ and the phase transformation proceeded by extration of $K^+$ ion.