• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.49-56
• /
• 2007

Effects of post-baking treatment conditions on the interfacial adhesion between electroless plated Ni and polyimide film were evaluated using $180^{\circ}C$ peel test. Measured peel strength values monotonically decrease from $38.6{\pm}1.1g/mm\;to\;26.8{\pm}2.2g/mm$ for the variations of post-baking treatment temperatures from $80^{\circ}C\;to\;180^{\circ}C$, respectively. Wet chemical treatment on the polyimide surface produces carboxyl and amide functional groups on the surface which is closely related to the change in interfacial adhesion between electroless Ni and polyimide films. It is speculated that interfacial adhesion seems to be controlled by carbonyl oxygen bonding near cohesive failure region during post-baking treatment.

• Journal of Welding and Joining
• /
• v.27 no.6
• /
• pp.62-67
• /
• 2009

Friction stir welding (FSW) was carried out for Al-Mg-Si series aluminum alloys which are being used for automotive body structure. Consequently, Post weld heat treatment (PWHT) was applied to the friction stir welds to evaluate the effect of the paint baking process which is one of the automotive fabrication process on friction stir welded zone (FSWZ) in 443K for 1.2Ks. Grain structure and its crystal orientation distribution was measured about both the as welded specimens and the post weld heat treated specimens. An optical microscope (OM) and an field emission scanning electron microscope (FE-SEM) was used for observing the grain structure and measuring its crystal orientation distribution, respectively. Changes on the grain structure and its crystal orientation distribution were not detected. From the present results, it was confirmed that the paint baking process after FSW do not affect on the grain structure and its crystal orientation distribution of FSWZ. The comprehensive investigations will be performed for various automotive aluminum alloys manufactured by different processes, in the future.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.5
• /
• pp.456-461
• /
• 2007

In this study, a surface treatment method using accelerated Ar ions was experimented for exposing the carbon nanotubes (CNT) from the screen-printed CNT paste. After making a cathode electrode on the glass substrate, photo sensitive CNT paste was screen-printed, and then back-side was exposed by UV light. Then, the exposed CNT paste was selectively remained by development. After post-baking, the remained CNT paste was bombarded by accelerated Ar ions for removing some binders and exposing only CNTs. As results, the field emission characteristics were strongly depended on the accelerating energy, bombardment time, and the power of RF plasma ion source. When Ar ions accelerated with 100 eV energy from the 100 W RF plasma source are bombarded on the CNT paste surface for 10 min, the emission level and the uniformity were best.

• 전자공학회논문지 IE
• /
• v.44 no.2
• /
• pp.26-31
• /
• 2007

A surface treatment was performed after the screen printing of a carbon nanotube paste for obtaining the carbon nanotube field emission array(CNT FEA) on the soda-lime glass substrate. In this experiment, Ar ion bombardment was applied as an effective surface treatment method. After making a cathode electrode on the glass substrate, photo sensitive CNT paste was screen-printed, and then back-side was exposure by uv light. Then, the exposed CNT paste was selectively remained by development. After post-baking, the remained CNT paste was bombarded by accelerated Ar ions for removing some binders and exposing only CNTs. As results, the field emission characteristics were strongly depended on the accelerating energy. At 100 eV, the emission was highest and as the acceleration energy increases more then 100 eV, the emission decreased. This was due to the removal of CNT itself as well as binders.