• 한국재료학회지
• /
• 제16권11호
• /
• pp.681-686
• /
• 2006

Plasma nitrocarburising and plasma post oxidation were performed to improve the wear and corrosion resistance of S45C and SCM440 steel by a plasma ion nitriding system. Plasma nitrocarburizing was conducted for 3h at $570^{\circ}C$ in the nitrogen, hydrogen and methane atmosphere to produce the ${\varepsilon}-Fe_{2-3}$(N, C) phase. Plasma post oxidation was performed on the nitrocarburized samples with various oxygen/hydrogen ratio at constant temperature of $500^{\circ}C$ for 1 hour. The very thin magnetite ($Fe_3O_4$) layer $1-2{\mu}m$ in thickness on top of the $15{\sim}25{\mu}m$ ${\varepsilon}-Fe_{2-3}$(N, C) compound layer was obtained by plasma post oxidation. A salt spray test and electrochemical testing revealed that in the tested 5% NaCl solution, the corrosion characteristics of the nitrocarburized compound layer could be further improved by the application of the superficial magnetite layer. Throttle valve shafts were treated under optimum plasma processing conditions. Accelerated life time test results, using throttle body assembled with shaft treated by plasma nitrocarburising and post oxidation, showed that plasma nitrocarburizing and plasma post oxidation processes could be a viable technology in the very near future which can replace $Cr^{6+}$ plating.

• 한국연소학회:학술대회논문집
• /
• 한국연소학회 2002년도 제24회 KOSCO SYMPOSIUM 논문집
• /
• pp.157-162
• /
• 2002

The characteristics of DeNOx conversion process by plasma/post-heating system with the simulated gas containing ethene is investigated experimentally. Without plasma treatment, $NO-NO_2$ conversion doesn't occur by $400^{\circ}C$ in a mixture of $N_2/O_2$ with a trace gas of ethene. But $NO-NO_2$ conversion occurs as temperature increases above $400^{\circ}C$. The NO can, however, be converted to $NO_2$ at lower temperatures by treating the gas mixture with non-thermal plasma. The $NO-NO_2$ conversion enhances further by passing the plasma treated gas through the post-heating furnace. Results show that 20%${\sim}50%$ more conversion of NO to $NO_2$ is observed when the temperatures of the post-heating furnace are maintained at $300^{\circ}C$ or $400^{\circ}C$. The additional $NO-NO_2$ conversion by post-heating is due to the reaction of ethene with the byproducts or radicals generated from the plasma reaction.

• 열처리공학회지
• /
• 제18권1호
• /
• pp.24-28
• /
• 2005

New post plasma nitriding can achieve a high uniformity that have been difficult in DC nitriding and have a high productivity comparable to gas nitriding. However, it has not a enough high nitriding potential for a rapid nitriding, because surface activation or ion etching in the general plasma nitriding cannot be expected. Thus, in this study, the effects of pre-treatments with oxidation and reduction gas have been investigated to improve the nitriding kinetics of post plasma nitriding. An effective pre-treatment consisting of oxidation and reduction resulted in the increase of surface energy of STD 11. This induced the surface hardness and the effective nitriding depth of STD 11. It is thought that the increase of the surface energy and the surface area with pre-treatment promote the nucleation of nitriding layer.

• 한국작물학회:학술대회논문집
• /
• 한국작물학회 2022년도 추계학술대회
• /
• pp.330-330
• /
• 2022

In recent studies, cold plasma has been used to induce exudation of polyphenols and flavonoids from food materials, leading to enhancement of functional properties. And it is known that polyphenols interact with inflammation related metabolism. The objectives of this study were to investigate the effects of cold plasma treatments on the increase of total phenolic content (TPC), total flavonoid content (TFC), and anti-inflammatory activities of 'Sinpalkwang' peanut (Arachis hypogaea L.) hull. Plasma treatments were carried out using a dielectric barrier discharge gas exchange system at different radicals and temperatures (O₃-25℃, O₃-150℃, NO_x-150℃). Significant differences in TPC, TFC, and inflammatory mediator such as nitric oxide (NO) and tumor necrosis factor a (TNF-α) in lipopolysaccharide stimulated Raw 264.7 macrophages were observed between treated and non-treated peanut hull samples (p < 0.001). Cold plasma treated samples showed higher content (TPC: 2.87-2.93 mg/g sample, TFC: 0.96-0.98 mg/g sample) than non-treated sample (TPC: 2.47 mg/g sample, TFC: 0.78 mg/g sample). Cold plasma treated samples showed lower content of NO (3.3-5.0 uM) and TNF-α (141.4-162.2 ng/mL) than non-treated sample (NO: 11.1 uM, TNF-α: 210.2 ng/mL). This study suggests that cold plasma has potential to improve functionalities of food materials and that cold plasma treated peanut hull can be used as immune enhancing materials.

• Asian-Australasian Journal of Animal Sciences
• /
• 제33권12호
• /
• pp.1985-1990
• /
• 2020

Objective: The objective of this experiment was to investigate the effects of fat-soluble vitamin injection on plasma and tissue vitamin status in nursery pigs. Methods: A total of 16 pigs (initial body weight: 7.15±1.1 kg) were allotted to 2 treatments at d 7 post-weaning. Pigs were fed a corn-soybean meal-based basal diet with no supplemental vitamin A and i.m. injected with 300,000 IU of retinyl palmitate, 900 IU of d-α-tocopherol and 30,000 IU of vitamin D₃ with control pigs having no vitamin injection. Blood (d 0, 3, 7, and 14 post-injection) and tissue samples (liver, brain, heart, lung, and muscle; d 7 and 14 post-injection) were collected from pigs. Retinyl palmitate, retinol, and α-tocopherol concentrations were analyzed in plasma and tissues, while plasma was assayed for 25-hydroxycholecalciferol (25-OHD₃). Results: Plasma retinol and 25-OHD₃ concentrations increased by the vitamin injection from d 3 to 14 post-injection (p<0.05) whereas plasma retinyl palmitate was detected only in the vitamin treatment at d 3 and 7 post-injection (115.51 and 4.97 ㎍/mL, respectively). Liver retinol, retinyl palmitate, and retinol+retinyl palmitate concentrations increased by retinyl palmitate injection at d 7 and 14 post-injection (p<0.05) whereas those were not detected in the other tissues. The d-α-tocopherol injection increased α-tocopherol concentrations in plasma at d 3 and 7 post-injection (p<0.05) and in liver, heart (p<0.10), and muscle (p<0.05) at d 7 post-injection. Conclusion: Fat-soluble vitamin injection increased plasma status of α-tocopherol, retinol, retinyl palmitate and 25-OHD₃. As plasma levels decreased post-injection, vitamin A level in liver and vitamin E level in muscle, heart and liver increased. The α-tocopherol found in plasma after injection was distributed to various tissues but retinyl palmitate only to the liver.

• 반도체디스플레이기술학회지
• /
• 제9권1호
• /
• pp.35-40
• /
• 2010

We have investigated the effects of hydrogen injection via in-situ gas addition ($O_2$, $H_2$, or $O_2$ + $H_2$ gas) and plasma post-treatment (Ar or Ar + H plasma) on material properties of ZnO that is considered to be as a channel layer in transparent thin film transistors. The variations in the electrical resistivity, optical transmittance and bandgap energy, and crystal quality of ZnO thin films were characterized in terms of the methods and conditions used in hydrogen injection. The resistivity was significantly decreased by injection of hydrogen; approximately $10^6\;{\Omega}cm$ for as-grown, $1.2\;{\times}\;10^2\;{\Omega}cm$ for in-situ with $O_2/H_2\;=\;2/3$ addition, and $0.1\;{\Omega}cm$ after Ar + H plasma treatment of 90 min. The average transmittance of ZnO films measured at a wavelength of 400-700 nm was gradually increased by increasing the post-treatment time in Ar + H plasma. The optical bandgap energy of ZnO films was almost monotonically increased by decreasing the $O_2/H_2$ ratio in in-situ gas addition or by increasing the post-treatment time in Ar + H plasma, while the post-treatment using Ar plasma hardly affected the bandgap energy. The role of hydrogen in ZnO was discussed by considering the creation and annihilation of oxygen vacancies as well as the formation of shallow donors by hydrogen.

• Animal Bioscience
• /
• 제36권12호
• /
• pp.1821-1830
• /
• 2023

Objective: This study investigated the effect of adding seminal plasma to frozen-thawed semen on the quality of sperm and pregnancy following insemination in dromedary camels. Methods: In experiment 1, the frozen-thawed semen from 9 collections (3 bulls) was further diluted with either the base extender or homologous seminal plasma (HSP). In the second experiment, a pooled sample of frozen-thawed semen was diluted with either seminal plasma from another three bulls. Live percentage, total and progressive motility, functional and acrosome integrity, and sperm kinematics were evaluated at 15, 60, and 120 minutes post-thawing and compared to the non-treated control. In experiment 3, frozen semen was used to inseminate camels in the following experimental groups: 1-Single insemination with double dose undiluted frozen semen (n = 9); 2-Re-insemination in 6 hours with undiluted semen (n = 13); 3-Single insemination with HSP treated sperm (n = 14). Results: Frozen-thawed sperm diluted in HSP or the non-homologous seminal plasma from Bull C indicated an improvement in all parameters after 1 hour post-thawing incubation (p<0.05). The proportion of total and progressively motile sperm did not drop significantly at 60 minutes post-thawing when diluted with the seminal plasma of Bull C (p>0.05). Double insemination with nontreated sperm and single insemination with HSP-treated sperm resulted in similar pregnancy rates (15.3% vs 21.4%, p>0.05). None of the camels conceived with double-dose single insemination of nontreated sperm. Conclusion: Seminal plasma improves sperm longevity and motility after thawing in dromedary camel with a significant between-bull variation in effect. Low post-thaw sperm longevity might be the cause behind the low pregnancy rates in frozen semen insemination of dromedary camels.

• 한국표면공학회지
• /
• 제40권6호
• /
• pp.250-253
• /
• 2007

Plasma nitrocarburizing and plasma oxidizing treatments were performed to improve the wear and corrosion resistance of SKD 11 steel. Plasma nitrocarburizing was conducted for 12 h at $520^{\circ}C$ in the nitrogen, hydrogen and methane atmosphere to produce the $\varepsilon-Fe_{2-3}(N,C)$ phase. It was found that the compound layer produced by plasma nitrocarburising was predominantly composed of $\varepsilon-phase$, with a small proportion of $\gamma'-Fe_4(N,C)$ phase. The thickness of the compound layer was about $5{\mu}m$ and the diffusion layer was about $150{\mu}m$ in thickness, respectively. Plasma post oxidation was performed on the nitrocarburized samples with various oxygen/hydrogen ratio at constant temperature of $500^{\circ}C$ for 1 hour. The very thin magnetite($Fe_3O_4$) layer $1-2{\mu}m$ in thickness on top of the compound layer was obtained by plasma post oxidation. It was confirmed that the corrosion characteristics of the nitrocarburized compound layer could be further improved by the application of the superficial magnetite layer.

• 한국표면공학회지
• /
• 제48권6호
• /
• pp.269-274
• /
• 2015

In this experiment, post-nitriding treatment was performed at $400^{\circ}C$ on AISI 316 stainless steel which was plasma carburized previously at $430^{\circ}C$ for 15 hours. Plasma nitriding was implemented on AISI 316 stainless steel at various gas compositions (25% $N_2$, 50% $N_2$ and 75% $N_2$) for 4 hours. Additionally, during post nitriding Ar gas was used with $H_2$ and $N_2$ to observe the improvement of surface properties. After treatment, the behavior of the hybrid layer was investigated by optical microscopy, X-ray diffraction, and micro-hardness testing. Potentiodynamic polarization test was also used to evaluate the corrosion resistance of the samples. Meanwhile, it was found that the surface hardness increased with increasing the nitrogen gas content. Also small percentage of Ar gas was introduced in the post nitriding process which improved the hardness of the hardened layer but reduced the corrosion resistance compared with the carburized sample. The experiment revealed that AISI 316L stainless steel showed better hardness and excellent corrosion resistance compared with the carburized sample, when 75% $N_2$ gas was used during the post nitriding treatment. Also addition of Ar gas during post nitriding treatment degraded the corrosion resistance of the sample compared with the carburized sample.

• Medical Lasers
• /
• 제9권2호
• /
• pp.187-189
• /
• 2020

Cold atmospheric plasma (CAP) is a material that generates free radicals through the ionization of air. Despite the application in various medical fields, the efficacy and safety of CAP on post-inflammatory hyperpigmentation due to atopic dermatitis have not been reported. Herein, we report the improvement in post-inflammatory hyperpigmentation of atopic dermatitis, after CAP treatment of three sessions weekly, 10 minutes per session. We examined the clinical severity indexes before and after treatment, including the Investigator's Global Assessment, modified Atopic Dermatitis Antecubital Severity, Eczema Area and Severity Index, and pruritus visual analogue scores. Our results indicate that CAP alleviates the post-inflammatory hyperpigmentation and clinical severity of atopic dermatitis, and effectively improves the atopic skin lesion without severe safety issues. We believe that the previously reported anti-bacterial effects and production of interleukin-6 after CAP treatment are probably responsible for the underlying mechanisms leading to clinical improvement.