We have investigated that the effect of post annealing on the structural and electrical properties of $Ba_{0.5}Sr_{0.5}TiO_3$ thin films. The BST thin films were deposited on n-type 4H-silicon carbide(SiC) using pulsed laser deposition (PLD). The deposition was carried out in oxygen ambient 100mTorr for 5 minutes, which results in about 300nm-thick BST films. For the BST/4H-SiC, 200nm thick silver was deposited on the BST films bye-beam evaporation. The X-ray diffraction patterns of the BST films revealed that the crystalline structure of BST thin films has been improved after post-annealing at $850^{\circ}C$ for 1 hour. The root mean square (RMS) surface roughness of the BST film measured by using a AFM was increased after post-annealing from 5.69nm to 11.49nm. The electrical properties of BST thin film were investigated by measuring the capacitance-voltage characteristics of a silver/BST/4H-SiC structure. After the post-annealing, dielectric constant of the film was increased from 159.67 to 355.33, which can be ascribed to the enhancement of the crystallinity of BST thin films.

• 전기전자학회논문지
• /
• 제26권2호
• /
• pp.232-239
• /
• 2022

우리는 인산리튬(Li₃PO₄) 고체 상태 박막에 대한 후열처리의 영향을 분석했다. Li₃PO₄ 박막은 무선 주파수(RF) 스퍼터링에 의해 증착되었으며, 이후 200-400 ℃에서 박막을 열처리 했다. 샘플 표면의 SEM 이미지는 열처리된 샘플가 열처리되지 않은 샘플 사이의 형태에 유의미한 차이를 나타내지 않았다. XRD 분석은 샘플이 비정질과 유사한 구조로 구성되어 있음을 나타낸다. 열처리 후 결합 에너지의 변화는 XPS 분석에 의해 확인하였으며, -6 V에서의 누설 전류 밀도는 400 ℃에서 열처리된 소자가 열처리되지 않은 소자에 비해 약 7.15배 더 낮은 것으로 측정되었다. 후열처리 온도가 증가함에 따라 누설전류가 감소함을 확인하였다.

• 대한전자공학회:학술대회논문집
• /
• 대한전자공학회 2000년도 하계종합학술대회 논문집(2)
• /
• pp.274-277
• /
• 2000

Thin Film Transistor(TFTs) were fabricated from poly-Si crystallized by a two-step annealing process on glass substrates. The combination of low-temperature(500$^{\circ}C$) Metal-Induced Lateral Crystallization(MILC) furnace annealing and high -temperature (700$^{\circ}C$) rapid thermal annealing leads to the improvement of the material quality The TFTs measured with this two-step annealing material exhibit better characteristics than those obtained by using conventional MILC furnace annealing.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.117-118
• /
• 2008

High-pressure deuterium annealing process is proposed and investigated for enhanced electrical and reliability properties of 512Mb DDR2 DRAM without increase in process complexity. High pressure deuterium annealing (HPDA) introduced during post metal anneal (PMA) improves not only DRAM performance but also reliability characteristics of MOSFET. Compared with a control sample annealed in a conventional forming gas, additional annealing in a high pressure deuterium ambient at $400^{\circ}C$ for 30 min decreased G1DL current and junction leakage. The improvements can be explained by deuterium incorporation at $SiO_2$/Si substrate interface near isolation trench edge.

• 열처리공학회지
• /
• 제25권5호
• /
• pp.239-243
• /
• 2012

$SnO_2$ thin films were prepared on the Si substrate by radio frequency (RF) magnetron sputtering and then post deposition vacuum annealed to investigate the effect of annealing temperature on the structural properties and hydrogen gas sensitivity of the films. The films that annealed at $300^{\circ}C$ show the higher sensitivity than the other films annealed at $150^{\circ}C$. From atomic force microscope observation, it is supposed that post deposition annealing promotes the rough surface and also, increase gas sensitivity of $SnO_2$ films for hydrogen gas. These results suggest that the vacuum annealed $SnO_2$ thin films at optimized temperatures are promising for practical high-performance hydrogen gas sensors.

• Transactions on Electrical and Electronic Materials
• /
• 제16권2호
• /
• pp.99-102
• /
• 2015

Thin film transistors (TFTs) with amorphous 2 wt% silicon-doped zinc tin oxide (a-2SZTO) channel layer were fabricated using an RF magnetron sputtering system, and the effect of post-annealing treatment time on the structural and electrical properties of a-2SZTO systems was investigated. It is well known that Si can effectively reduce the generation of oxygen vacancies. However, it is interesting to note that prolonged annealing could have a bad effect on the roughness of a-2SZTO systems, since the roughness of a-2SZTO thin films increases in proportion to the thermal annealing treatment time. Thermal annealing can control the electrical characteristics of amorphous oxide semiconductor (AOS) TFTs. It was observed herein that prolonged annealing treatment can cause bumpy roughness, which led to increase of the contact resistance between the electrode and channel. Thus, it was confirmed that deterioration of the electrical characteristics could occur due to prolonged annealing. The longer annealing time also decreased the field effect mobility. The a-2SZTO TFTs annealed at 500℃ for 2 hours displayed the mobility of 2.17 cm²/Vs. As the electrical characteristics of a-2SZTO annealed at a fixed temperature for long periods were deteriorated, careful optimization of the annealing conditions for a-2SZTO, in terms of time, should be carried out to achieve better performance.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 춘계학술대회 논문집 디스플레이 광소자 분야
• /
• pp.58-61
• /
• 2005

In an effort to improve the electrical properties of ZnO:Al transparent electrode films, post-annealing treatment in hydrogen atmosphere was attempted with varying annealing time at 573 K for compatibility with typical display device fabrication processes. It was observed that carrier concentrations and mobilities increased with longer annealing time with small changes in crystallinity. This resulted in substantial decrease in resistivity from $4.80{\times}10^{-3}$ to $8.30{\times}10^{-4}{\Omega}cm$ due to increased carrier concentration. Such improvements in electrical properties are attributed to the passivation of the grain boundary surfaces. The optical properties of the films, which changed in accordance with the Burstein-Moss effect, were consistent with the observed changes in electrical properties.

• 한국세라믹학회지
• /
• 제37권8호
• /
• pp.731-738
• /
• 2000

KLN(K3Li2Nb5O15) has attracted a great deal of attention for their potential usefulness in piezoelectric, electro-optic, nonlinear optic, and pyroelectirc devices. Especially, the KLN single crystal has been studied in the field of optics and electronics. However it is hard to produce good quality single crystals due to the crack propagation during crystal growing. One of the solutions of this problem is prepartion of thin film. But the intensive study has not been conducted so far. In this study, after the KLN thin film were prepared by R.F. magnetron Sputtering method on SiO2/Si substrate, the post-annealing methods of RTA(rapid thermal annealin) and IPA(insitu post annealing) were employed. The deposition condition of KLN thin film was RF power(100 W), Working pressure(100 mtorr). The commonness of both RAT and IPA was that the higher were deposition and post annealing temperature, the higher was the intensity of XRD but the less surface roughness. The difference of post-annealing methods affected XRD phase and surface condition very much. And in IPA process, the influence of O2 had much effect on the formation of KLN phase.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1999년도 추계학술대회 논문집
• /
• pp.136-139
• /
• 1999

The post-annealing treatments on RF (Radio Frequency) magnetron sputtered PZI(Pb$\_$1.05/(Zr$\_$0.52/, Ti$\_$0.48/)O$_3$thin films(4000${\AA}$) have been investigated. for a structure of PZT/Pt/Ti/SiO$_2$/Si Crystallization pproperties of PZT films were strongly dependent on RTA(Rapid Thermal Annealing) annealing temperature. We were able to obtain a perovskite structure of PZT at a low temperature of 600$^{\circ}C$. P-E curves of Pd/PZT/Pt capacitor annealed at 700$^{\circ}C$ demonstrate typical hysteresis loops. The measured values of P$\_$r/, E$\_$c/, by post annealed at 700$^{\circ}C$ were 12.1 ${\mu}$C/$\textrm{cm}^2$, 120KV/cm respectively.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제36회 동계학술대회 초록집
• /
• pp.171.1-171.1
• /
• 2009