The purpose of this study was to investigate the fracture resistance of crown-root fractured teeth repaired with dual-cured composite resin and horizontal posts. 48 extracted human premolars were assigned to control group and three experimental groups. Complete crown-root fractures were experimentally induced in all control and experimental teeth. In the control group. the teeth (n=12) were bonded with resin cement and endodontically treated. Thereafter, the access cavities were sealed with dual-cured composite resin. In composite resin core-post group (n=12), the teeth were endodontically treated and access cavities were sealed with dual-cured composite resin. In addition, the fractured segments in this group were fixed using horizontal posts. In composite resin core group (n=12), the teeth were endodontically treated and the access cavities were filled with dual-cured composite resin without horizontal posts. In bonded amalgam group (n = 12), the teeth were endodontically treated and the access cavities were sealed with bonded amalgam. Experimental complete crown-root fractures were induced again on repaired control and experimental teeth. The ratio of fracture resistance to original fracture resistance was analyzed with Kruskal-Wallis test. The results showed that teeth in control and composite resin core-post group showed significantly higher resistance to re-fracture than those in amalgam core group (p < 0.05). The resistance to refracture was high in the order of composite resin - post group, control group, composite resin group and bonded amalgam group. Within the scope of this study, the use of horizontal post could be beneficial in increasing the fracture resistance of previously fractured teeth.
Kim, Hyun-Dong;Lee, Joo-Hee;Ahn, Kang-Min;Kim, Hee-Sun;Cha, Hyun-Suk
The Journal of Advanced Prosthodontics
/
v.5
no.2
/
pp.104-109
/
2013
PURPOSE. Among the surface treatment methods suggested to enhance the adhesion of resin cement to fiberreinforced composite posts, conflicting results have been obtained with silanization. In this study, the effects of silanization, heat activation after silanization, on the bond strength between fiber-reinforced composite post and resin cement were determined. MATERIALS AND METHODS. Six groups (n=7) were established to evaluate two types of fiber post (FRC Postec Plus, D.T. Light Post) and three surface treatments (no treatment; air drying; drying at $38^{\circ}C$). Every specimen were bonded with dual-curing resin cement (Variolink N) and stored in distilled water for 24 hours at $37^{\circ}C$. Shear-bond strength (MPa) between the fiber post and the resin cement were measured using universal testing device. The data were analyzed with 1-way ANOVA and by multiple comparisons according to Tukey's HSD (${\alpha}$=0.05). The effect of surface treatment, fiber post type, and the interactions between these two factors were analyzed using 2-way ANOVA and independent sample T-tests. RESULTS. Silanization of the FRC Postec Plus significantly increased bond strength compared with the respective non-treated control, whereas no effect was determined for the D.T. Light Post. Heat drying the silane coupling agent on to the fiberreinforced post did not significantly improve bond strength compared to air-syringe drying. CONCLUSION. The bond strength between the fiber-reinforced post and the resin cement was significantly increased with silanization in regards to the FRC Postec Plus post. Bond strength was not significantly improved by heat activation of the silane coupling agent.
Journal of the Korean Academy of Esthetic Dentistry
/
v.24
no.2
/
pp.122-133
/
2015
The requirements for the successful treatment of all-ceramic restorations are not so different from the ones of conventional restorations. "The provisional restoration followed by an adequate tooth reduction" and "the accurately fitting prostheses with corresponding to final impression" can be the examples of them. Nevertheless, the one which all-ceramic restorations are distinguished from conventional restorations is the additional procedure of so called "bonding". In addition to the application of resin cement between "inner surface of restoration and outer surface of abutment", bonding technology can be also applied to the treatment process of "Post and Core" in particular if the abutments are non-vital teeth. Core build-up for all-ceramic crown is conducted with fiber post and tooth colored composite by considering the properties of the restorations transmitting light. We know well that a vital abutment is easier than a non-vital one to get the targeted goals for clinical success in connection with esthetics and structure. The creation of "Post and Core" with bonding technique is a decisive factor for a long-term success if the abutment is non-vital tooth with dentinal collapse. I would like to share my clinical experience about "post & core build-up and all-ceramic restoration bonding" out of several success strategies of all-ceramic crown with this review article.
Domingo Santos Pantaleon;Joao Paulo Mendes Tribst;Franklin Garcia-Godoy
The Journal of Advanced Prosthodontics
/
v.16
no.2
/
pp.77-90
/
2024
PURPOSE. The study aims to investigate the influence of the ferrule effect and types of posts on the stress distribution in three morphological types of the maxillary central incisor. MATERIALS AND METHODS. Nine models were created for 3 maxillary central incisor morphology types: "Fat" type - crown 12.5 mm, root 13 mm, and buccolingual cervical diameter 7.5 mm, "Medium" type - crown 11 mm, root 14 mm, and buccolingual cervical diameter 6.5 mm, and "Slim" type - crown 9.5 mm, root 15 mm, and buccolingual cervical diameter 5.5 mm. Each model received an anatomical castable post-and-core or glass-fiber post with resin composite core and three ferrule heights (nonexistent, 1 mm, and 2 mm). Then, a load of 14 N was applied at the cingulum with a 45° slope to the long axis of the tooth. The Maximum Principal Stress and the Minimum Principal Stress were calculated in the root dentin, crown, and core. RESULTS. Higher tensile and compression stress values were observed in root dentin using the metallic post compared to the fiber post, being higher in the slim type maxillary central incisor than in the medium and fat types. Concerning the three anatomical types of maxillary central incisors, the slim type without ferrule height in mm presented the highest tensile stress in the dentin, for both types of metal and fiber posts. CONCLUSION. Post system and tooth morphology were able to modify the biomechanical response of restored endodontically-treated incisors, showing the importance of personalized dental treatment for each case.
Paula Pontes Garcia ;Aline Cappoani ;Ricardo Susin Schelbauer ;Gisele Maria Correr ;Carla Castiglia Gonzaga
Restorative Dentistry and Endodontics
/
v.45
no.4
/
pp.49.1-49.11
/
2020
Objectives: The aim of this study was to perform a clinical and radiographic analysis of endodontically treated teeth (ETT) restored with cast metal posts (CMPs) or prefabricated glass fiber posts (GFPs) and crowns. Materials and Methods: Fifty ETT were restored with 25 CMPs and 25 GFPs at a private dental clinic between 2001 and 2016. The restorations consisted of 12 all-ceramic crowns, 31 metal-ceramic crowns, and 7 composite resin crowns. Demographic data, type of teeth, type of post-and-core system, time of placement, crown restorations, the number of proximal contacts, the type of antagonist, and reports of any complications after post-and-core placement were recorded for each patient. Assessments were performed at baseline (radiographic) and follow-up (radiographic and clinical). Data were analyzed by the McNemar test, the Pearson χ2 test, and Kaplan-Meier survival curves (α = 0.05). The mean follow-up was 67.6 months. Results: No significant difference was observed for any of the radiographic parameters when the baseline and final radiographs were compared. In the clinical evaluation, anatomical form (p = 0.009) and occlusion (p = 0.001) showed significant differences according to the type of crown restoration; specifically, metal-ceramic and all-ceramic crowns outperformed composite resin crowns. Conclusions: CMPs and GFPs showed favorable results for restoring ETT after 6 years of follow-up. All-ceramic and metal-ceramic crowns showed higher survival rates and better clinical outcomes.
The purpose of this study is to evaluate the color differences in the In-Ceram according to coping thickness and various abutment core materials ; amalgam, precious alloy, composite resin, non-precious alloy. After the porcelain was built up on the In-Ceram coping at the thicknes of 0.3mm and 0.5mm then it was cemented with glass ionomer cement to the post & core materials. The following results were obtained. 1. There were significant differences in the $L^*$ values $a^*$ and $b^*$ values in the cementation of different cores, to the In-Ceram(P<0.01). $L^*$ values were not significantly different between the composite resin to the In-Ceram and the $a^*\;b^*$ values were not significantly different between the amalgam and the non-precious alloy. 2. All of cementations of In-Ceram to the core materisal had color difference(${\Delta}E^*ab$) compared to the In-Ceram. In the 0.3mm thickness of the In-Ceram copping non-precious alloy indicated the greatest value, while the composite resin core showed the lowest value with a thickness of 0.5mm In-Ceram copping. 3. By controlloing the In-Ceram coping thickness $L^*$ value was significatly different(P<0.01), but not in $a^*$ and $b^*$ values. 4. In an amalgam, precious & non-prcious alloys there was a 1,74 to 3.06 range color difference in the controlled thickness of In-Ceram coping at the thickness of 0.3mm and 0.5mm. The above results suggest that the requirement of the sufficient thickness of In-Ceram coping and the suitable core material in order to get an estheti restoration by In-Ceram and also to intercept the original core color.
Journal of Dental Rehabilitation and Applied Science
/
v.16
no.1
/
pp.51-60
/
2000
The purpose of this study was to compare the microleakage at the interface of cast post and tooth according to the type of cement. Forty anterior teeth with single root were used. The teeth were cut 2 mm coronal from the cementoeamel junction and chamfer finish line was made on 1 mm coronal from the cementoeamel junction. After the routine endodontic treatment, post space was prepared using #5.5 Parapost drill to a depth of 7 mm. After the pick up impression, core building was made to 3 mm of clinical crown with burnout wax, then post and core was cast with nonprecious metal. The teeth were divided into four groups of ten each. In Group I, post and core were cemented with Fleck's(Zinc phosphate cement) In Group II, post and core were cemented with Fuji I(Glass ionomer cement) In Group III, post and core were cemented with Superbond C & B(Composite resin cement) In Group IV, post and core were cemented with Panavia 21(Composite resin cement) All cemented teeth were stored in normal saline at $37^{\circ}C$ for 7 days and thermocycled from $5^{\circ}C$ to $55^{\circ}C$ for 500 cycles with a dwell time of 30 seconds. After thermocycling, teeth were immersed in 1% Basic fuchsin dye for 48 hours. All 40 teeth were then embedded in the epoxy resin and cut buccolingually with a cutting instrument. The degree of penetration of dye at interface was graded on a scale of 0 to 4 using a stereomicroscope at 25 to 40 times magnification. Through the findings of this study, the following conclusion were obtained. 1. All the groups showed the microleakage at the interface of cast post core and tooth. 2. Group I showed the highest microleakage score among the groups with a significant difference(p<0.05). 3. Group II showed higher microleakage score than Group III and Group IV with a significant difference(p<0.05). 4. Group IV showed the lowest microleakage score but there were no significant difference with Group III(p>0.05).
The paper describes the mechanical behavior of short concrete-filled steel tube (CFT) columns with circular section. The efficiency of the steel tube in confining the concrete core depending on concrete strength and the steel tube thickness was examined. Fifteen columns were tested to failure under concentric axial loading. Furthermore, a mechanical model based on the interaction between the concrete core and the steel tube was developed. The model employs a volumetric strain history for the concrete, characterized by the level of applied confining stress. The situation of passive confinement is accounted for by an incremental procedure, which continuously updates the confining stress. The post-yield behavior of the columns is greatly influenced by the confinement level and is related to the efficiency of the steel tube in confining the concrete core. It is possible to classify the post-yield behavior into three categories: strain softening, perfectly plastic and strain hardening behavior. The softening behavior, which is due to a shear plane failure in the concrete core, was found for some of the CFT columns with high-strength concrete. Nevertheless, with a CFT column, it is possible to use high-strength concrete to obtain higher load resistance and still achieve a good ductile behavior.
The requirements for the successful treatment of all-ceramic restorations are not so different from the ones of conventional restorations. "The provisional restoration followed by an adequate tooth reduction" and "the accurately fitting prostheses with corresponding to final impression" can be the examples of them. Nevertheless, the one which all-ceramic restorations are distinguished from conventional restorations is the additional procedure of so called "bonding". In addition to the application of resin cement between "inner surface of restoration and outer surface of abutment", bonding technology can be also applied to the treatment process of "Post and Core" in particular if the abutments are non-vital teeth. Core build-up for all-ceramic crown is conducted with fiber post and tooth colored composite by considering the properties of the restorations transmitting light. I would like to share my clinical experience about "silica based ceramic and non silica based ceramic restoration.
This clinical report describes the dental treatment of canine teeth fractures in three cats. These animals were diagnosed by oral examination and dental radiography as having fractured teeth with pulpal exposure. After endodontic treatment was completed, root canal filling material was removed from the coronal access and a trial post placement was performed. The post was permanently cemented after shortening. Teeth were etched and a bonded composite resin core formed and then shaped using rotary instruments. Fractured canine teeth were treated without any complications observed during a six-month follow-up period, proving that fractured cat canine teeth can be treated successfully with root canal therapy followed by restorative treatment with posts and composite resin.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.