• Korean Journal of Materials Research
• /
• v.17 no.11
• /
• pp.593-600
• /
• 2007

Aluminum was anodized in a $H_2SO_4$ solution, and titanium (IV) oxide ($TiO_2$) was electrodeposited into nanopores of anodic porous alumina in a mixed solution of $TiOSO_4$ and $(COOH)_2$. The photocatalytic activity of the prepared film was analyzed for photodegradation of methylene blue aqueous solution. Consequently, we found it was possible to electrodeposit $TiO_2$ onto anodic porous alumina, and synthesized it into the nanopores by hydrolysis of a titanium complex ion under AC 8-9 V when film thickness was about $15-20{\mu}m$. The photocatalytic activity of $TiO_2$-loaded anodic porous alumina ($TiO_2/Al_2O_3$) at an impressed voltage of 9 V was the highest in every condition, being about 12 times as high as sol-gel $TiO_2$ on anodic porous alumina. The results revealed that anodic porous alumina is effective as a substrate for photocatalytic film and that high-activity $TiO_2$ film can be prepared at low cost.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.5
• /
• pp.217-223
• /
• 2010

For an application as templates of high performance with proper pore size and shape, porous anodic alumina films were prepared by anodization in oxalic acid, and formation behaviors of anodic alumina layer as well as dissolution process in acid solution have been investigated. The surface characteristics on anodic alumina layer were shown to be dependent on the fabrication parameters for anodization. For the dissolution behaviors of anodic alumina, the thickness of the barrier-type alumina layer decreased linearly with the rate of 0.98 nm/min in $H_3PO_4$ solution at $30^{\circ}C$. The changes of the anodic alumina layers were analyzed by SEM and TEM.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.625-628
• /
• 2004

Porous anodic alumina(PAA) which has arrays of nano size holes, was incorporated into organic light emitting devices. Porous anodic alumina on glass scattered the light generated from emitting layer and was decreased the waveguiding modes within the glass. An increase in the device coupling-out factor for the scattering structure is demonstrated.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.769-772
• /
• 2004

We report on the developed fabrication method of lanthanide-doped xerogel/porous anodic alumina structures for an image formation via the aluminum anodization, the sol-gel synthesis, and the photolithography process. The structures of europium- or terbium-doped xerogel/porous anodic alumina are also considered in view of application in electroluminescent devices.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.2
• /
• pp.349-352
• /
• 2014

Anodic alumina oxide (AAO), a self-ordered hexagonal array, has various applications in nanofabrication such as the fabrication of nanotemplates and other nanostructures. In order to obtain highly ordered porous alumina membranes, a two-step anodization or prepatterning of aluminum are mainly conducted with straight electric field. Electric field is the main driving force for pore growth during anodization. However, impurities in aluminum can disturb the direction of the electric field. To confirm this, we anodized two different aluminum foil samples with high purity (99.999%) and relatively low purity (99.8%), and compared the differences in the surface morphologies of the respective aluminum oxide membranes produced in different electric fields. Branched pores observed in porous alumina surface which was anodized in low-purity aluminum and the size; dimensions of the pores were found to be usually smaller than those obtained from high-purity aluminum. Moreover, anodization at high voltage proceeds to a significant level of conversion because of the high speed of the directional electric field. Consequently, anodic alumina membrane of a specific morphology, i.e., meshed pore, was produced.

• Journal of the Korean institute of surface engineering
• /
• v.43 no.5
• /
• pp.248-254
• /
• 2010

Porous $Al_2O_3$ film can be utilized as template for fabrication of nano-structured materials. Porous anodic alumina layer as template was prepared by anodization of aluminum in oxalic acid, and the pore diameter and barrier-type alumina layer can be controlled for proper anodizing parameter by widening process in $H_3PO_4$ solution. The $SiO_2$ nanodot and Ni nanowire was fabricated using anodic alumina template and their characteristics were investigated using SEM and TEM with EDS. Especially the growth mechanism of $SiO_2$ nanodot in alumina membrane compared with thinning of the alumina barrier layer during anodization was also investigated.

• Korean Journal of Materials Research
• /
• v.12 no.2
• /
• pp.121-128
• /
• 2002

Anodic alumina layer can be used as templates for preparation of nano-structured materials, because porous oxide layer on aluminum shows a uniform pore size and a high pore density. In order to find out possibility for template material to prepare nano wire, the effects of the anodic applied potential, anodic time and the temperature of electrolyte on pore diameter of anodic alumina layer were studied using SEM and AFM. The pore diameter of anodic alumina layer increased with applied anodic potential and electrolytic temperature. Especially, the pore diameter of anodic oxide layers formed in chromic acid can be well replicated by widening process in $H_3$$PO_4$solution.

• Journal of environmental and Sanitary engineering
• /
• v.13 no.3
• /
• pp.72-78
• /
• 1998

For investigation into gas permeation characteristics, the porous alumina membrane with asymmetrical structure, having upper layer with 10 nanometer under of pore diameter and lower layer with 36 nanometer of pore diameter, was prepared by anodic oxidation using DC power supply of constant current mode in an aqueous solution of sulfuric acid. The aluminium plate was pre-treated with thermal oxidation, chemical polishing and electrochemical polishing before anodic oxidation. Because the pore size depended upon the electrolyte, electrolyte concentration, temperature, current density, and so on, the the membranes were prepared by controling the current density, as a very low current density for upper layer of membrane and a high current density for lower layer of membrane. By control of current quantity, the thicknesses of upper layer of membranes were about $6{\;}{\mu}m$ and the total thicknesses of membranes were about $80-90{\;}{\mu}m$. We found that the mechanism of gas permeation depended on model of the Knudsen flow for the membrane prepared at each condition.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.9
• /
• pp.801-806
• /
• 2003

In recent years, there has been large interest in the fabrication of the self organized nanoscale structures since not only their potential utilization in electronic, optoelectronic, and magnetic devices but also their fundamental interest such as uniformity and regularization. An attractive candidate of these materials is anodic porous alumina film(Al$_2$O$_3$) which is formed by the anodization of aluminum in an appropriate acid solution. In this study to fabricate the porous alumina film with very uniform and nearly parallel pores the anodization was carried out under constant voltage mode in 0.3M oxalic acid as an electrolyte. The hexagonally ordered arrays with a few $\mu\textrm{m}$ in size two-dimensional polycrystalline structure were obtained of which pore densities were 1.1${\times}$10$\^$10//$\textrm{cm}^2$.

• Journal of the Korean Vacuum Society
• /
• v.15 no.5
• /
• pp.518-526
• /
• 2006

Nanoporous alumina film was fabricated by anodization of an aluminum sheet. Highly ordered nanowellstructured and nanonets-tructured metal films were fabricated by vacuum evaporation of several metals(Al, Sn, and Co) using the anodic nanoporous alumina film as a template. In this experiment, an anodic porous alumina film with the cell size of 100 nm and the pore diameter of 60 nm was used. The resistance heating method was adopted for evaporating a desired metal, and vapor deposition was carried out under the base pressure of torr. It was founded that whether the structure fabricated by vacuum evaporation is nanowell or nanonet is dependent on the amount of deposited material. When an anodic porous alumina film with the cell size of 100 nm and the pore diameter of 60 nm was used, a nanowell-structured film was fabricated when a sufficient amount of metal was suppled to cover the surface pores. On the other hand, nanonet-structured film was fabricated bellow a half the amount of metal required for nanowell-structured film.