• Journal of the Korean Ceramic Society
• /
• v.45 no.10
• /
• pp.584-588
• /
• 2008

Porous hydroxyapatite(HA) and HA-coated porous $Al_2O_3$ possessing pore characteristics required for bone substitutes were prepared by a slurry foaming method combined with gelcasting. The HA coating was deposited by heating porous $Al_2O_3$ substrates in an aqueous solution containing $Ca^{2+}$ and ${PO_4}^{3-}$ ions at $65{\sim}95^{\circ}C$ under ambient pressure. The pore characteristic, microstructure, and compressive strength were investigated and compared for the two kinds of samples. The porosity of the samples was about 81% and 80% for HA and $Al_2O_3$, respectively with a highly interconnected network of spherical pores with size ranging from 50 to $250{\mu}m$. The porous $Al_2O_3$ sample showed much higher compressive strength(25 MPa) than the porous HA sample(10 MPa). Fairly dense and uniform HA coating(about $2{\mu}m$ thick) was deposited on the porous $Al_2O_3$ sample. Since the compressive strength of cancellous bone is $2{\sim}12$ MPa, both the porous HA and HA-coated porous $Al_2O_3$ samples could be successfully utilized as scaffolds for bone repair. Especially the latter is expected suitable for load bearing bone substitutes due to its excellent strength.

• Journal of the Korean Ceramic Society
• /
• v.31 no.6
• /
• pp.671-677
• /
• 1994

To improve the low resistance of ceramics to tensile stress, many techniques, for introducing and retaining surface compressive stress have been suggested. In present work, in order to introduce the compressive stress on the surface of TZP ceramics TZP-Al2O3 composites were made with infiltration technique. Highly porous 3Y-TZP pre-sintered specimens were submerged in AlOOH(boehmite) sol and the sol penetrated into them through open pore channels with moderate depth after that specimens were sintered. It was known that controlling the number of infiltration time can vary the amount of Al2O3 phase and the fraction of alumina at surface reached up to 18%. The depth of composite surface layer were 100~200 ${\mu}{\textrm}{m}$, and these were acceptable in surface strengthening which were proved by Vickers hardness indentation method.

• Journal of the Korean Ceramic Society
• /
• v.53 no.1
• /
• pp.43-49
• /
• 2016

This analyzed a Young's modulus (E), a thermal expansion coefficient (TEC, ${\beta}$) and a thermal conductivity (${\kappa}$) of the material with simple cubic particulate inclusion using two model structures: a parallel structure and a series structure of laminated layers. The derived ${\beta}$ equations were applied to calculate the ${\beta}$ value of the W-MgO system. The accuracy was higher for the series model structure than for the parallel model structure. Young's moduli ($E_c$) of sintered porous alumina compacts were theoretically related to the development of neck growth of grain boundary between sintered two particles and expressed as a function of porosity. The series structure model with cubic pores explained well the increased tendency of $E_c$ with neck growth rather than the parallel structure model. The thermal conductivity of the three phase system of alumina-mullite-pore was calculated by a theoretical equation developed in this research group, and compared with the experimental results. The pores in the sintered composite were treated as one phase. The measured thermal conductivity of the composite with 0.5-25% porosity (open and closed pores) was in accordance with the theoretical prediction based on the parallel structure model.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.205-210
• /
• 2002

The HPS(High Porosity Support, 39.3%) and the LPS( Low Porosity Support, 18.7%) were fabricated to investigate the phase transformation and the chance of microstructure with porosity of alumina support. Alumina sol was made using aluminum tri-sec $butoxide(ATSB,\; Al(O-Bu)_3)$, the membrane on porous support with different porosity and the membrane without support were fabricated. The $\theta$-to ${\alpha}-A1_2O_3$ phase transformation in the membranes was investigated using thin film X-ray diffraction (XRD), and the change of microstructure was observed using scanning electron microscopy(SEM). XRD patterns showed that the membrane on LPS and HPS had 10$0^{\circ}C$, 5$0^{\circ}C$ higher $\theta$-to ${\alpha}-A1_2O_3$ transformation temperature compared to the unsupported membrane. A similar effect was also observed in microstructure of the membranes, theoritical temperature difference were 97$^{\circ}C$ and 44$^{\circ}C$ by Crapeyron equation.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.5
• /
• pp.595-605
• /
• 2000

Dental ceramics have good aesthetics, biocompatibility, low thermal conductivity, abrasion resistance, and color stability. However poor resistance to fracture and shrinkage during firing process have been limiting factors in their use, particularly in multiunit ceramic restorations. A new method for making all-ceramic crowns that have high strength and low processing shrinkage has been developed and is referred to as the Vita In-Ceram method. This study was performed to investigate the effect of $CeO_2$ addition in borosilicate glasses on the strength of alumina-glass composites. Porous alumina compacts were prepared by slip casting and sintered at $1,100^{\circ}C$ for 2 hours. Dense composites were made by infiltration of molten glass into partially sintered alumina at $1,140^{\circ}C$ for 4 hours. Specimens were polished sequentially from #800 to #2000 diamond disk. and the final surface finishing on the tensile side was received an additional polishing sequence through $1{\mu}m$ diamond paste. Biaxial flexure test was conducted by using ball-on-three-ball method at a crosshead speed of 0.5mm/min. To examine the microstructural aspect of crack propagation in the alumina-glass composites, Vickers-produced indentation crack was made on the tensile surface at a load of 98.0 N and dwell time of 15 sec, and the radial crack patterns were examined by an optical microscope and a scanning electron microscope. The results obtained were summarized as follows; 1. The porosity rates of partially sintered alumina decreased with the rising of firing temperature. 2. The maximum biaxial flexure strength of 423.5MPa in alumina-glass composites was obtained with an addition of 3 mol% $CeO_2$ in glass composition and strength values showed the aspect of decrease with the increase of $CeO_2$ content. 3 The biaxial flexure strength values of alumina-glass composites were decreased with rising the firing temperature. 4. Observation of the fracture surfaces of alumina-glass composites indicated that the enhancement of strength in alumina-glass composites was due to the frictional or geometrical inter-locking of rough fracture surfaces and ligamentary bridging by intact islands of materials left behind the fracture front.

• The Korean Journal of Ceramics
• /
• v.1 no.4
• /
• pp.219-223
• /
• 1995

Ceramic membranes of the supported $TiO_2-CeO_2$ were prepared by dip-coating method on an $\alpha-Al_2O_3$ porous substrate. The mean pore diameter of an alumina support was 0.125 um. The mean particle diameter of $TiO_2-CeO_2$ top layer varied with firing temperature and ranged from 20 to 85 nm. The thermal stability of the composite membranes was studied from their surface microstructure after calcination at $600-900^{\circ}C$. The supported $TiO_2-CeO_2$ composite membranes exhibited much higher heat resistance than the $TiO_2$ membrane.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.3
• /
• pp.576-583
• /
• 2018

Silicon carbide is considered to be a potentially useful material for high-temperature electronic devices, as its band gap is larger than that of silicon and the p-type and/or n-type conduction can be controlled by impurity doping. Particularly, porous n-type SiC ceramics fabricated from ${\beta}-SiC$ powder have been found to show a high thermoelectric conversion efficiency in the temperature region of $800^{\circ}C$ to $1000^{\circ}C$. For the application of SiC thermoelectric semiconductors, their figure of merit is an essential parameter, and high temperature (above $800^{\circ}C$) electrodes constitute an essential element. Generally, ceramics are not wetted by most conventional braze metals,. but alloying them with reactive additives can change their interfacial chemistries and promote both wetting and bonding. If a liquid is to wet a solid surface, the energy of the liquid-solid interface must be less than that of the solid, in which case there will be a driving force for the liquid to spread over the solid surface and to enter the capillary gaps. Consequently, using Ag with a relatively low melting point, the junction of the porous SiC semiconductor-Ag and/or its alloy-SiC and/or alumina substrate was studied. Ag-20Ti-20Cu filler metal showed promise as the high temperature electrode for SiC semiconductors.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.5
• /
• pp.387-394
• /
• 2014

PURPOSE. Topographic analysis of treated ceramics provides qualitative information regarding the surface texture affecting the micromechanical retention and locking of resin-ceramics. This study aims to compare the surface microstructure following different surface treatments of feldspathic porcelain. MATERIALS AND METHODS. This in-vitro study was conducted on 72 porcelain discs randomly divided into 12 groups (n=6). In 9 groups, feldspathic surfaces were subjected to sandblasting at 2, 3 or 4 bar pressure for 5, 10 or 15 seconds with $50{\mu}m$ alumina particles at a 5 mm distance. In group 10, 9.5% hydrofluoric acid (HF) gel was applied for 120 seconds. In group 11, specimens were sandblasted at 3 bar pressure for 10 seconds and then conditioned with HF. In group 12, specimens were first treated with HF and then sandblasted at 3 bar pressure for 10 seconds. All specimens were then evaluated under scanning electron microscopy (SEM) at different magnifications. RESULTS. SEM images of HF treated specimens revealed deep porosities of variable sizes; whereas, the sandblasted surfaces were more homogenous and had sharper peaks. Increasing the pressure and duration of sandblasting increased the surface roughness. SEM images of the two combined techniques showed that in group 11 (sandblasted first), HF caused deeper porosities; whereas in group 12 (treated with HF first) sandblasting caused irregularities with less homogeneity. CONCLUSION. All surface treatments increased the surface area and caused porous surfaces. In groups subjected to HF, the porosities were deeper than those in sandblasted only groups.