• Journal of the Korean Ceramic Society
• /
• v.51 no.1
• /
• pp.19-24
• /
• 2014

Three-layer porous alumina-mullite composites with a symmetric gradient porosity are prepared using a controlled freeze/gel-casting method. In this work, tertiary-butyl alcohol (TBA) and coal fly ash with an appropriate addition of $Al_2O_3$ were used as the freezing vehicle and the starting material, respectively. When sintered at $1300-1500^{\circ}C$, unidirectional macro-pore channels aligned regularly along the growth direction of solid TBA were developed. Simultaneously, the pore channels were surrounded by less porous structured walls. A high degree of solid loading resulted in low porosity and a small pore size, leading to higher compressive strength. The sintered porous layered composite exhibited improved compressive strength with a slight decrease in its porosity. After sintering at $1500^{\circ}C$, the layered composite consisting of outer layers with a 50 wt% solid loading showed the highest compressive strength ($90.8{\pm}3.7MPa$) with porosity of approximately 26.4%.

• Smart Structures and Systems
• /
• v.26 no.2
• /
• pp.253-262
• /
• 2020

In this paper, a new higher order shear deformation model is developed for static analysis of functionally graded beams with considering porosities that may possibly occur inside the functionally graded materials (FGMs) during their fabrication. The model account for higher-order variation of transverse shear strain through the depth of the beam and satisfies the zero traction boundary conditions on the surfaces of the beam without using shear correction factors. The present work aims to study the effect of the distribution forms of porosity on the bending of simply supported FG beam. Based on the present higher-order shear deformation model, the equations of motion are derived by the principle of virtual works. Navier type solution method was used to obtain displacement and stresses, and the numerical results are compared with those available in the literature. A comprehensive parametric study is carried out to assess the effects of volume fraction index, porosity fraction index, and geometry on the bending of imperfect FG beams. It can be concluded that the proposed model is simple and precise for the resolution of the behavior of flexural FGM beams while taking into account the shape of distribution of the porosity.

• Structural Engineering and Mechanics
• /
• v.67 no.2
• /
• pp.115-123
• /
• 2018

By using the first order shear deformation plate theory (FSDT) in the present paper, the effect of porosity on the buckling behavior of carbon nanotube-reinforced composite porous plates has been investigated analytically. Two types of distributions of uniaxially aligned reinforcement material are utilized which uniformly (UD-CNT) and functionally graded (FG-CNT) of plates. The analytical equations of the model are derived and the exact solutions for critical buckling load of such type's plates are obtained. The convergence of the method is demonstrated and the present solutions are numerically validated by comparison with some available solutions in the literature. The central thesis studied and discussed in this paper is the Influence of Various parameters on the buckling of carbon nanotube-reinforced porous plate such as aspect ratios, volume fraction, types of reinforcement, the degree of porosity and plate thickness. On the question of porosity, this study found that there is a great influence of their variation on the critical buckling load. It is revealed that the critical buckling load decreases as increasing coefficients of porosity.

• Geomechanics and Engineering
• /
• v.17 no.3
• /
• pp.307-316
• /
• 2019

Dam deformation should be strictly controlled for the construction of 300 m-high rockfill dams, so the rockfill materials need to have low porosity. A method of using composite grout is proposed to reduce the porosity of rockfill materials for the construction of high rockfill dams. The composite grout is a mixture of fly ash, cement and sand with the properties of easy flow and post-hardening. During the process of rolling compaction, the grout admixture sprinkled on the rockfill surface will gradually infiltrate into the inter-granular voids of rockfill by the exciting force of vibratory roller to reduce the porosity of rockfill. A visible flowing test was firstly designed to explore the flow characteristics of composite grout in porous media. Then, the compressibility, shear strength, permeability and suffusion susceptibility properties of composite grout-modified rockfill are studied by a series of laboratory tests. Experimental results show that the flow characteristics of composite grout are closely related to the fly ash content, the water-to-binder ratio, the maximum sand size and the content of composite grout. The filling of composite grout can effectively reduce the porosity of rockfill materials, as well as increase the compression modulus of rockfill materials, especially for loose and gap-graded rockfill materials. Composite grout-modified rockfill tends to have greater shear strength, larger suffusion erosion resistance, and smaller permeability coefficient. The composite grout mainly plays the roles of filling, lubrication and cementation in rockfill materials.

• Geomechanics and Engineering
• /
• v.30 no.2
• /
• pp.153-167
• /
• 2022

This study proposes a method to analyze the distribution of coal porosity disturbances after the excavation of ultra-large-diameter water jet boreholes using a coal wetting and softening model. The high-pressure jet is regarded as a short-term high-pressure water injection process. The water injection range is the coal softening range. The time when the reference point of the borehole wall is shocked by the high-pressure water column is equivalent to the time of high-pressure water injection of the coal wall. The influence of roadway excavation with support and borehole diameter on the ultra-large-diameter jet drilling excavation is also studied. The coal core around the borehole is used to measure the gas permeability for determining the porosity disturbance distribution of the coal in the sampling plane to verify the correctness of the simulation results. Results show that the excavation borehole is beneficial to the expansion of the roadway excavation disturbance, and the expansion distance of the roadway excavation disturbance has a quadratic relationship with the borehole diameter. Wetting and softening of the coal around the borehole wall will promote the uniform distribution of the overall porosity disturbance and reduce the amplitude of disturbance fluctuations.

• Steel and Composite Structures
• /
• v.51 no.6
• /
• pp.601-617
• /
• 2024

This work aims to explore the static behaviour of a tapered functionally graded porous plate (FGPP) with even and uneven porosity distributions resting on two parametric elastic foundations. The plate under investigation is subjected to bi-sinusoidal loading and the edges of the plate are exposed to different combinations of edge restrictions. In order to examin the static behaviour, bending factors (BF) related to bending and normal stresses have been evaluated using classical plate theory. To achieve this, the governing equations have been derived employing the energy concept. And to solve it, the Rayleigh-Ritz method with an algebraic function has been utilised; it is simple, precise, and computationally intensive. After convergence and validation analyses, new findings are made available. The BF of the plate have been exhaustively examined to explain the influence of aspect ratios, material property index, porosity factor, taper factor, and Winkler and Pasternak stiffness. It is observed that the BF of an elastically supported FGPP are influenced by the index of material propery and the aspect ratio. Findings also indicate that the impact of porosity is more when it is spread evenly, as opposed to when it is unevenly distributed. Further, the deformed plate's structure is significantly influenced by the different thickness variations. Examination of bending characteristics of FGPP having different new cases of thickness variations with different types of porosity distribution under fifteen different mixed edge constraints is the prime novality of this work. Results presented are reliable enough to be taken into account for future studies.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.34 no.5
• /
• pp.1-17
• /
• 2002

The immobilization and consolidation of the model coatings based on the plastic pigment and latex binder of known particle sizes were theoretically Studied in terms of the dense random packing of binary spheres and varying extent of latex film shrinkage. The porosity of the model coatings was calculated based on three proposed latex shrinkage models: Maximum, Minimum, and Linearly Decreasing Latex Shrinkage. The increasing extent of latex shrinkage was calculated up to the critical pigment volume concentration(CPVC) as a function of plastic pigment volume fractions, and the maximum latex shrinkage was estimated from the CPVC. Also, the number of pores and the average equivalent spherical pore diameters were calculated based on those proposed models. The opacity and gloss of the model coatings on polyester films were measured and their porosity was also determined by a simple coat weight-thickness method. As expected, various coating structure-property-composition relationships, such as opacity, gloss, porosity, etc., were shown to exhibit sharp transitions near the CPVC. The CPVC values determined by the opacity, gloss, and porosity vs. PVC relationships, respectively, agreed very well with each other. Especially, the CPVC's determined by the opacity and porosity vs. PVC curves were identical. The comparison between the theoretically calculated and experimental porosity values showed that the intermediate value between the maximum and minimum latex shrinkage would best fit the experimental porosity data. The effect of plastic pigment particle size on the optical properties and porosity of model coatings was also studied and it was observed that the coating opacity and porosity increased with increasing plastic pigment particle size, but the gloss decreased. The ink gloss of the uncalendered model coatings applied onto commercial sheet offset coated papers was shown to be affected by both the coating gloss and porosity: the higher the coating gloss, the higher the ink gloss, but the higher the coating porosity, the lower the ink gloss. Their printability was also studied in terms of the number of passes-to-fail and the rate of ink setting as a function of both plastic pigment volume fractions and plastic pigment particle sizes. A minimum crack-free temperature(MCR) of latex-bound coatings was proposed to better predict the behaviors of latexes as coating binders. The wet state of model coating dispersions, the surfaces of consolidated model coatings, and their internal structure were examined by both electron and atomic force microscopy, and their micrographs were found to be consistent with our immobilization and consolidation models.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.37 no.4
• /
• pp.217-224
• /
• 2021

Purpose: The purpose of this study was to evaluate the porosity of resin modified glass ionomer (RMGI) by different mixing methods. Materials and Methods: Five specimens were prepared for each groups according to capsules and mixing methods. Two RMGI capsule and two mixing machines were used for this study. One resin-modified glass ionomer cement is Fuji II LC (F2LC) and the other is Photac Fil Quick Aplicap (PFQ). For Mixing of RMGI capsule, Rotomix using rotating motion and CM-II using shaking motion were used. After measuring height, radius and mass of specimens, Density was calculated. And porosity was measured using micro-computed tomography (micro-CT). All data were statistically analyzed using T-test, two-way ANOVA to compare between groups at 95% significance level to evaluate the affect of capsule and mixing method on the porosity. Results: The porosity was observed in all specimens generally. And there is significant differece between porosities according to RMGI capsule and Mixing method. The porosity of PFQ was lower than that of F2LC and the porosity of Rotomix was lower than that of CM-II. Conclusion: There was a difference of porosity according to kind of capsules and mixing methods. When using same capsule, less porosity was observed on PFQ than F2LC. When using same mixing mehod, less porosity was observed on Rotomix than CM-II. Using mixing machine of same coporation as that of RMGI capsule did not lead to lower porosity. Therefore, Selecting optimal mixing machine is important.

• Geophysics and Geophysical Exploration
• /
• v.15 no.4
• /
• pp.163-176
• /
• 2012

Effective porosity has been measured for cement specimen as a function of vacuum time and pressure in the vacuum saturation process. Six cement specimen are used; three of them are made of the same ratio of cement and sand, the other three are 100% cement mortar, of which average porosity is about 25% and 40%, respectively. Using the 6 samples, measured effective porosities are compared and examined with 5 different vacuum pressures (2, 4, 6, 8, 10 torr) and times (20, 40, 60, 80, 100 minute), respectively. Comparing measured effective porosity from experiments when vacuum time varies from 100 minute to 20 minute with 20 minute step and vacuum pressure is fixed to 10, 6, and 2 torr, average deviation decreases as 0.6, 0.5, and 0.2% respectively. Comparing measured effective porosity from experiments when vacuum pressure varies from 2 torr to 10 torr with 2 torr step and vacuum time is fixed to 100, 60, and 20 minute, average deviation increases as vacuum time decreases. These results can be a background of suggested method of ISRM that describes the vacuum time longer than 60 minute and vacuum pressure higher than 6 torr. In this study, only qualitative discussion can be possible for the effects on the effective porosity by decreasing 20 minute vacuuming time at the same pressure or by decreasing 2 torr of vacuum pressure at the same vacuum time. This is because the sample could not reached to perfectly dried condition even though the sample were dried at $105^{\circ}C$ and following the ISRM suggested method, so that initial water content could not be the same at each experiment.

• Steel and Composite Structures
• /
• v.34 no.2
• /
• pp.215-226
• /
• 2020

The aim of this study is to investigate free vibration of functionally graded porous nanocomposite rectangular plates where the internal pores and graphene platelets (GPLs) are distributed in the matrix either uniformly or non-uniformly according to three different patterns. The elastic properties of the nanocomposite are obtained by employing Halpin-Tsai micromechanics model. The GPL-reinforced plate is modeled using a semi-analytic approach composed of generalized differential quadrature method (GDQM) and series solution adopted to solve the equations of motion. The proposed rectangular plates have two opposite edges simply supported, while all possible combinations of free, simply supported and clamped boundary conditions are applied to the other two edges. The 2-D differential quadrature method as an efficient and accurate numerical tool is used to discretize the governing equations and to implement the boundary conditions. The convergence of the method is demonstrated and to validate the results, comparisons are made between the present results and those reported by well-known references for special cases treated before, have confirmed accuracy and efficiency of the present approach. New results reveal the importance of porosity coefficient, porosity distribution, graphene platelets (GPLs) distribution, geometrical and boundary conditions on vibration behavior of porous nanocomposite plates. It is observed that the maximum vibration frequency obtained in the case of symmetric porosity and GPL distribution, while the minimum vibration frequency is obtained using uniform porosity distribution.