• The Journal of Korean Academy of Prosthodontics
• /
• v.31 no.2
• /
• pp.181-190
• /
• 1993

The purpose of this study was to evaluate the effect of shear bond strength between various percentage of reused dental ceramic alloys and porcelain. One hundred specimens were made of one semiprecious alloy and three nonprecious alloys. Each alloy group was subdevided into five groups according to the additional precentage of new alloy. Group I specimens were made of 100% new alloy and served as the control of the investigation. Group II specimens were made of once-cast alloy with 75% new alloy. Group III specimens were made of once-cast alloy with 50% new alloy. Group IV specimens were made of once-cast alloy with 25% new alloy. Group V specimens were made of 100% recast alloy. Five specimens were made for each group of the alloy combinations. The test specimens were prepared by firing porcelain doughnuts on the alloy rod surface, and invested in dental stone. Bond strengths were measured by Instron universal testing machine at a crosshead speed of 0.5mm/min. The fractured surface of metal specimens were examined under the scanning electron microscope. The obtained results were as follows : 1. The shear bond strength of Albabond showed no significant difference between control group and reused alloy group. 2. The shear bond strength of reused alloy groups of nonprecious alloys were lower than that of control groups. 3. The shear bond strength between porcelain and metal in semiprecious alloy was higher than in nonprecious alloys 4. In nonprecious alloys. Rexillium III showed the highest bond strength value and Excelalloy showed the lowest shear bond strength value. 5. Regardless of the type of alloys and additional proportion of new alloys, scanning electron microscope photographs of the fracture surface between alloy and porcelain revealed simillar semiprecious alloy and nonprecious alloys.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.1
• /
• pp.44-50
• /
• 2013

PURPOSE. The aim of this study was to evaluate the effects of repeated porcelain firing process on the corrosion rates of the dental alloys. MATERIALS AND METHODS. Cr-Co, Cr-Ni and Pd-Ag alloys were used for this study. Each metal supported porcelain consisted of 30 specimens of 10 for 7, 9 and 11 firing each. Disc-shaped specimens 10 mm diameter and 3 mm thickness were formed by melting alloys with a propane-oxygen flame and casted with a centrifuge casting machine and then with the porcelain veneer fired onto the metal alloys. Corrosion tests were performed in quintuplicate for each alloy (after repeated porcelain firing) in Fusayama artificial saliva solution (pH = 5) in a low thermal-expansion borosilicate glass cell. Tamhane and Sheffe test was used to compare corrosion differences in the results after repeated firings and among 7, 9 and 11 firing for each alloy. The probability level for statistical significance was set at ${\alpha}$=0.05. RESULTS. The corrosion resistance was higher (30 mV), in case of 7 times firing (Commercial). On the other hand, it was lower in case of 11 times firing (5 mV) (P<.05). Conclusion. Repeated firings decreased corrosion resistance of Pd-Ag, Cr-Co and Cr-Ni alloys. The Pd-Ag alloy exhibited little corrosion in in vitro tests. The Cr-Ni alloy exhibited higher corrosion resistance than Cr-Co alloys in in vitro tests.

• Korean Journal of Dental Materials
• /
• v.43 no.4
• /
• pp.317-322
• /
• 2016

The effect of ice-quenching after degassing on the hardness change during simulated porcelain firing in a metal-ceramic Pd-Au-Ag alloy was investigated by means of hardness test, field emission scanning electron microscopic observations, and X-ray diffraction analysis. The hardness decreased by ice-quenching after degassing, which was induced by the homogenization of the ice-quenched specimen. The decreased hardness by ice-quenching after degassing was recovered from the 1st opaque stage which was the first stage of the remaining firing process for bonding porcelain. The microstructural change showed that the increase in hardness during the remaining firing process was caused by precipitation. The ice-quenching after degassing did not affect the hardness change during the subsequent porcelain firing process.

• Journal of Technologic Dentistry
• /
• v.27 no.1
• /
• pp.89-95
• /
• 2005

In the manufacture of ceramo-metal crown, difference of fracture strength according to the metal depth has been known to be an important influence on enough intensity and internal stress to endure an occlusion-pressure as well as aesthetics of rehabilitating similar colour such as natural teeth. Depth of ceramic material could be determined by that of metal in three groups: first case of thin depth, second case of thick depth, and third case of constant depth. For the enhancement of the fracture strength between metal and ceramic materials and aesthetic satisfaction, a study on the bonding force, fracture strength, and aesthetics have been required more. In this study, therefore metal coping were made in three groups of A, B and C by using both ceramic powder of Norithe and metal of Columbium, which have been used primarily in the market. A group was made in $0.2mm\times10mm\times10mm$, B group was made in $0.4mm\times10mm\times10mm$, and, C group was made in $0.8mm\times10mm\times10mm$, respectively. The number of metal coping in each group was 10, and total sample numbers used in this study were 30 metal copings. After these metal coping tissue were in the process of build-up in 1.5mm constant depth of porcelain, firing, and glazing, the fracture strength about each metal coping tissue was investigated using oil press. It was found that the average values of durable occlusion pressure for separation of ceramic material in the porcelain fused to metal crown (PFM) in the each group showed the increasing order of A group (30 bar), B group (42 bar), and C group (44 bar), respectively. Proper depth of metal coping in the PFM was considered to be 0.4mm in the B group because this metal size showed higher durable property to the occlusion pressure and better coupling strength in the ceramo-metal crown.

• The Journal of the Korean dental association
• /
• v.19 no.1 s.140
• /
• pp.20-22
• /
• 1981

• Journal of the Korean Academy of Esthetic Dentistry
• /
• v.1 no.1
• /
• pp.45-49
• /
• 1992

• The Journal of the Korean dental association
• /
• v.22 no.8 s.183
• /
• pp.655-657
• /
• 1984

• Journal of Technologic Dentistry
• /
• v.45 no.3
• /
• pp.55-60
• /
• 2023

Purpose: This study aimed to evaluate the effects of a special heat treatment on Pd-Au-Ag metal-ceramic alloy after degassing treatment and on changes in the hardness of the alloy during the firing process. Methods: Specimen alloys were cast and subjected to degassing at 900℃ for 10 minutes. These specimens were then subjected to a special heat treatment at 600℃ for 15 minutes in a dental porcelain furnace. Further, the specimens were subjected to simulated firing in the porcelain furnace. The resulting specimens were then tested for hardness, and changes in the microstructure were observed. Results: There was a decrease in the hardness of the alloy during the simulated firing of the cast alloy due to the coarsening of the particles. Meanwhile, additional heat treatment after degassing was found to play a crucial role in preventing a decrease in hardness. This treatment effectively suppressed the coarsening of the precipitates during repeated firing at high temperatures. Conclusion: Specific heat treatment of the Pd-Au-Ag metal-ceramic alloy prevented a decrease in its hardness and extended the lifespan of the metal-ceramic prosthesis.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.16 no.7
• /
• pp.4357-4363
• /
• 2015

This study is to compare the differences of bonding strength based on the Degassing temperatures and various opaque materials for Ni-Cr alloy specimen which does not contain beryllium(Be). Numerous comparison tests have been performed to measure the bonding strength by experimenting 3-point flexural rigidity tests in order to find out ways of stabilization and enhancement of bonding strength between metal and porcelain. AVOVA, surface component observation experiment by SAM/EDS, and Tukey's HSAD posteriori tests results are as follows: First, The bonding strength in all groups has exceeded the minimum (25MPa) of ISO9693 bonding strength regulation for dental mental-porcelain specimen. Second, The bonding strength of Group V1 was $32.37{\pm}1.91MPa$, $38.25{\pm}1.38MPa$ in Group V2, $46.43{\pm}2.14MPa$ in Group V3 and $47.21{\pm}1.72MPa$ Group V4. The difference has been statistically meaningful. Tukey's HSAD posteriori tests results have shown that the bonding strength in Group V4 was higher than that of Group V1. Third, the bonding strength between metal and porcelain without degassing process was higher than that of with degassing process, and the bonding strength of powder opaque was higher than that of paste opaque. Fourth, Group V4 has ranked the highest on the comparison table of metal and porcelain bonding strength.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.20 no.2
• /
• pp.109-120
• /
• 2004

INTRODUCTION: The build-up method has been used for application of porcelain powder on the metal framework to make final tooth shape conventionally. This method takes time and need skill to mimic final shade and shape of porcelain fused to metal crown. The purpose of this study was to develop standard shape and shade laminating porcelain forms to reduce build-up time. METHODS: To make tooth form porcelain paste, several liquid organic compounds were added to conventional feldspathic porcelain. The amount of additives and rheologic property were tested to find out best composition. Comparison of mixing methods to reduced porosity, proper heating schedule, and measurement of shrinkage amount and residual organic materials were performed to set-up standard procedures. Finally, biaxial flexural strength and color of preformed laminated paste porcelain were compared with those of porcelain which fabricated by the conventional build-up method. RESULTS: There was no significant difference in physical properties and color stability between two fabrication methods after various testing methods. Conclusion: This new build-up method can be applied to fabricate the PFM crown and bridge without any loss of strength and optical properties.