• Journal of Technologic Dentistry
• /
• v.22 no.1
• /
• pp.39-47
• /
• 2000

This study is the know the difference bond strength according to painting method of Opaque porcelain. Among Porcelain powder for Porcelain, Noritake powder, Bonding agent 1 class and metal are selected as Base metal alloy. And painting method of Opaque porcelain is divided by 4 groups : PG, WG, NG and DG. Also it is to manufacture 24 sheets of Specimen by 6 each every method and to measure Crack-initiation Strength of Metal-porcelain and it is to observe it by Scanning electron microscope. I come to get a conclusion as follows. 1. As for Debonding strength of every experiment groups, it showed that WS group which executed Wash bake had highest value, 44.25MPa and NG group which used Normal powder had value, 42.11MPa and DG group which used Bonding agent had value, 35.88MPa and PG group which used Paste opaque had value, 35.39MPa. 2. In four painting methods of Opaque porcelain, PG group, WG group, NG group and DG group, there is no significant difference statistically in Crack-initiation Strength. 3. As a result of observing fracture surface with Scanning electron microscope, it was showde that PG group remained a lot of particle of porcelain on the surface of metal than WG group, NG group and DG group.

• Journal of Technologic Dentistry
• /
• v.31 no.4
• /
• pp.15-23
• /
• 2009

The aim of this study was to evaluate the bond strength of using a Au bonding agent applied on cp-Ti and nonprecious metal-gold-ceramic system. Metallic frameworks(diameter: 5mm, height: 20mm)(N=56, n=7per group) cast in Ni-Cr alloy, Co-Cr alloy and cp-Ti were obtained using acrylic templates and airborne particle abraded with $110{\mu}m$ aluminum oxide. Au bonding agent was applied on wash opaque firing as intermediate layer. SEM and SEM/EDS line profile were performed on the cutting the cross-section of the metal substrate-porcelain with intermediate Au coating. Groups were tested using shear bond strength(SBS) testing at 0.5mm/min. The mean SBS values for the ceramic-Au layer-metal combination were significantly higher than those ceramic-metal combination. While ceramic-Au layer-cp-Ti combinations failed to increase bond strength instead of using a titanium bonding porcelain. The appication of using Au intermediate layer significantly improve the bond strength combination with metal-ceramic system.

• Journal of Technologic Dentistry
• /
• v.38 no.2
• /
• pp.69-77
• /
• 2016

Purpose: This study was to evaluate the shear bond strength of ceramic fused to Ni-Cr alloy(Alophaloy) by heat treatment. Methods: The specimens were divided into 5 groups according to heat treatment conditions prior to porcelain application. Eighteen specimens from each group were subjected to the shear load a universal testing machine using a 0.1mm/min cross-head speed and two specimens from each group were observed with SEM and EDX line profile. Results: The observation of the oxide film on the metal surface by SEM photograph showed a coarsening with an increasing degassing hold time. The diffusion of metal oxide was observed farther from the opaque layer in the heat treated specimen than no heat treated specimen. The shear bond strength measured highest to A5(55.23MPa) in the 10min holding group and measured lowest from A1(24.38MPa) in the no heat treated group, and there was a significant difference(p<0.05). Conclusion: The shear bond strength of Ni-Cr alloy improved in the heat treatment compared to the no heat treatment specimen.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.24 no.1
• /
• pp.113-127
• /
• 2008

The purpose of this study was to evaluate effect of application of $ZirLiner^{(R)}$ and blasting treatments on shear bond strength of zirconia-veneered porcelain interface. 60 uncolored zirconia plates and 30 colored zirconia plates were fabricated and divided into nine groups of 10 according to blasting treatment such as as-ground, glass blasting and alumina blasting and zirliner application. Veneering porcelains were built up over the center of the treated zirconia ceramic surface using jig and fired according to the manufacturers' instructions. Each specimen was completely embedded in acrylic resin. The specimens were placed in a mounting jig and subjected to shear force by a universal testing machine. Load was applied at a crosshead speed of 0.5㎜/min until failure. Average shear strengths were analyzed with two-way analysis of variance and one-way analysis of variance and the Duncan's post-hoc test. The fracture surfaces of the failed specimens were examined by SEM. The obtained results were as follows: 1. Depending on surface treatment by blasting, the degree of roughness is revealed in the order of Glass-blasted, As-ground, and Alumnia-blasted. The roughness average of uncolored and colored zirconia ceramic were not significantly different from blasting treatments. 2. In uncolored zirconia ceramic, the shear bond strength were not significantly different from blasting treatments. However, the shear bond strength were significantly different from Zirliner application. 3. Used ZirLiner, mean shear bond strength of colored zirconia was lower than uncolored zirconia. Especially, mean shear bond strength of colored zirconia was quite low with alumina-blasting treatment. 4. SEM analysis showed that veneered porcelain failed in zirconia ceramic interface and there was no cohesive failure.

• Journal of Technologic Dentistry
• /
• v.39 no.2
• /
• pp.101-107
• /
• 2017

Purpose: The purpose of this study was to compare the shear bond strength of the metal-heat pressed glass ceramic bilayer structure. Methods: Metal framework specimens were prepared and surface is spreaded opaque(IPS InLine system opaque, IvoclarVivadent, Liechtenstein). There were 10 specimens for each bilayer dental ceramic group. The first group was porcelain fused metal, Press on metal IPS Inline press group, and press on metal HASS prototype group. Specimens measured for the shear bond strength on Schwickerath test by Instron universal testing machine(Instron3345, Instron Corp., USA). Mean average bond strength values of each specimen group were analyzed using a one-way ANOVA analysis of variance Saphiro-wilk's test. Statistical analysis were performed using IBM SPSS 23.0(IBM Co., Armonk, USA) Results: $RMS{\pm}SD$ The highest mean average HASS POM showed a bond strength value ($47.55{\pm}12.80Mpa$). The lowest mean average values Porcelain fused metal ($33.30{\pm}2.00Mpa$). Independent t-test was conduct to analysis the significant difference (p<0.05) (Table 3). Conclusion: Three kinds of Metal/ glass bilayer dental ceramics bond strength were clinical acceptability. Especially, as lithium disilicate containing represents higher bond strength.

• The korean journal of orthodontics
• /
• v.45 no.6
• /
• pp.299-307
• /
• 2015

Objective: The aims of this study were to compare the shear bond strength between orthodontic metal brackets and glazed zirconia using different types of primer before applying resin cement and to determine which primer was more effective. Methods: Zirconia blocks were milled and embedded in acrylic resin and randomly assigned to one of four groups: nonglazed zirconia with sandblasting and zirconia primer (NZ); glazed zirconia with sandblasting, etching, and zirconia primer (GZ); glazed zirconia with sandblasting, etching, and porcelain primer (GP); and glazed zirconia with sandblasting, etching, zirconia primer, and porcelain primer (GZP). A stainless steel metal bracket was bonded to each target surface with resin cement, and all specimens underwent thermal cycling. The shear bond strength of the specimens was measured by a universal testing machine. A scanning electron microscope, three-dimensional optical surface-profiler, and stereoscopic microscope were used to image the zirconia surfaces. The data were analyzed with one-way analyses of variance and the Fisher exact test. Results: Group GZ showed significantly lower shear bond strength than did the other groups. No statistically significant differences were found among groups NZ, GP, and GZP. All specimens in group GZ showed adhesive failure between the zirconia and resin cement. In groups NZ and GP, bonding failed at the interface between the resin cement and bracket base or showed complex adhesive and cohesive failure. Conclusions: Porcelain primer is the more appropriate choice for bonding a metal bracket to the surface of a full-contour glazed zirconia crown with resin cement.

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.2
• /
• pp.67-84
• /
• 1991

This study was carried out to investiagate the residual stress caused by the mismatch of thermal expansion and the bond failure resistance of alloy-porcelain specimens. The thermal expansions of alloys and porcelains were measured by using a straight push-rod dilatometer. Porcelain glass transition temperatures, thermal expansion coefficients, and thermal compatibility indices were derived from length-versus-temperature curves. Strain gauges were used to experimentally determine the Young's moduli of porcelains, the residual stresses of porcelain surface, and tensile bond strengths of the specimens of simulated porcelain metal crown. The obtained results were as follows: 1. The coefficients of thermal expansion for alloys were the minimum of $13.53\mu/^{\circ}C$ and the maximum of $20.11\mu/^{\circ}C$ in the range of $100\sim600^{\circ}C$ and those for porcelains were the minimum of $7.72\mu/^{\circ}C$ and the maximum of $31.24\mu/^{\circ}C$ in the range of $100\sim500^{\circ}C$. 2. The glass transition temperature of porcelains exhibited the same value without my relation to the healing rate, and the thermal disharmony of porcelain and alloy was more affected by porcelains than by the alloys. 3. The Young's moduli of body porcelains were larger than those of opaque porcelains(P<0.01) 4. It seemed that the residual stresses of porcelain surfaces in the porcelainalloy systems were more affected by porcelains than by alleys. 5. The bond strengths of the procelain-base metal alloy systems were larger than those of the porcelain-precious metal alloy systems. The fracture strengths of porcelain surfaces showed significant difference between porcelains (P<0.05).

• The Journal of Advanced Prosthodontics
• /
• v.11 no.5
• /
• pp.297-304
• /
• 2019

PURPOSE. This in vitro study investigated the repair bond strength of the zirconia ceramic after different aging conditions. MATERIALS AND METHODS. In order to imitate the failure modes of veneered zirconia restorations, veneer ceramic, zirconia, and veneer ceramic-zirconia specimens were prepared and were divided into 4 subgroups as: control ($37^{\circ}C$ distilled water for 24 hours ) and 3000, 6000, 12000 thermal cycling groups (n=15). Then, specimens were bonded to composite resin using a porcelain repair kit according to the manufacturer recommendation. The repair bond strength (RBS) test was performed using a universal testing machine (0.5 mm/min). Failure types were analyzed under a stereomicroscope. Two-way ANOVA and Bonferroni test were used for statistical analysis. RESULTS. The RBS values of zirconia specimens were statistically significant and higher than veneer ceramic and veneer ceramic-zirconia specimens in control, 3000 and 6000 thermal cycling groups (P<.05). When 12000 thermal cycles were applied, the highest value was found in zirconia specimens but there was no statistically significant difference between veneer ceramic and veneer ceramic-zirconia specimens (P>.05). Veneer ceramic specimens exhibited cohesive failure types, zirconia specimens exhibited adhesive failure types, and veneer ceramic-zirconia specimens exhibited predominately mixed failure types. CONCLUSION. Thermal cycling can adversely affect RBS of composite resin binded to level of fractured zirconia ceramics.

• Journal of Technologic Dentistry
• /
• v.35 no.1
• /
• pp.43-48
• /
• 2013

Purpose: This study aimed to investigate the shear bond strength for non-precious alloy castings without beryllium, which has been used repeatedly for economical reason. Methods: The Schmitz-Schulmeyer test method was used to evaluate the shear bond strength between the non-beryllium Ni-Cr alloy Vera Bond 2V(AlbaDent, Inc. USA) and the Ceramco 3(Dentstply, York, PA, USA) porcelain powder. The maximum loading and shear bond strength were measured. The average shear strength(MPa) was analyzed with the one-way ANOVA and the Tukey's test( =.05). The fracture specimens were examined using Microscope to determine the failure pattern. Results: The mean shear bond strengths(SD) in MPa were group A(100% new metal) control 28.72(3.31); group B(50% new + 50% reused) 27.28(1.13); group C(all reused) 26.61(5.47). Microscope examination showed that group A and B specimens presented mixed failure, and group C specimens showed adhesive failure. Conclusion: In conclusion, forward this non-precious alloy dose not contain beryllium for how should use a more systematic study and for future advanced research is performed giving effect to be considered desirable.

• Restorative Dentistry and Endodontics
• /
• v.19 no.1
• /
• pp.159-168
• /
• 1994

The purpose of this study was to evaluate the shear bond strength of the porcelain laminate specimens according to the surface roughness of the cut enamel of human anterior teeth. Flat enamel surfaces were prepared in 30 extracted human anterior teeth with diamond disc which were divided into two groups. Group 1 Coarse enamel surface group prepared with LVS-3 bur. Group 2 Fine enamel surface group prepared with superfine diamond bur. 30 teeth specimens of two group were stored in normal saline during 24 hours. 30 disk - type porcelain laminate specimens with diameter 4mm and thickness 1mm were made and sand - blasted on internal surface which were to cemented on enamel surface. Porcelain laminate specimens were cemented on enamel surface with Choice Veneer System (Bisco Dental, U.S.A) according to manufacture's instructions. All teeth specimens of two groups were manipulated with same method and stored In normal saline before testing. An Universal Testing machine (Model No.UTM-4206,Instron, U.S.A) was used to apply shear loads in the vertical directed, and the force required for separation was recorded with a cross head speed of 3mm/min and 500kg in full scale. The results were as follow ; 1. The mean shear bond strength of coarse surface group was 36.30kg and that of fine surface group was 44.39 kg, but there was no significant difference in breaking strength of two groups(p>0.05).