• 대한치과기공학회지
• /
• 제39권4호
• /
• pp.243-251
• /
• 2017

Purpose: The purpose of this study was to investigate the effects of etching by monitoring the etched surfaces and the shear bonding strength of resin and porcelain with etched zirconia. Methods: The CAD/CAM was used to produce 24 zirconia blocks in groups of six. The zirconia specimen surfaces were sandblasted, and they were then divided into 12 specimens with surface etching and 12 specimens without etching for the control group. 12 specimens of composite resin were bonded using a curing light, and 12 specimens of porcelain underwent vita porcelain build-up sintering and the shear bonding strength was measured using a universal testing system. The SEM photographs were taken in order to observe any differences in the surfaces before and after etching, and they were magnified by a factor of 8 in order to observe fractured surface types. Results: The results of the shear bonding strength measurements are as follows: For the composite resin tests, between zirconia and resin, the shear bonding strength of the control group (NZR) without surface etching was 4.68 Mpa and the experimental group (EZC) with surface etching was 9.65 Mpa, which is significantly higher. The crystal structure of the zirconia was confirmed to be different in observations of the surfaces before and after etching. Conclusion : In comparing the shear bonding strength of zirconia and composite resin, the effects of etching were found to be significant. The effects of surface etching were also observed in fractured surfaces between zirconia and porcelain. This is expected to be applicable to various prosthetics as surface etching on zirconia is used in clinics.

• 한국산학기술학회논문지
• /
• 제16권4호
• /
• pp.2585-2592
• /
• 2015

3D 프린팅 기술은 최근 치과용 보철물 제작 기술로 도입이 되었다. 본 연구의 목적은 3D 프린팅 기술에 의해 제작된 금속 코어와 상부 도재와의 전단결합강도를 평가하는 것이다. 본 연구를 위해 30개의 금속 코어를 제작하였다(cast 15개, 3D printing 15개). 금속 코어에 치과용 도재를 축성하여 시편 제작을 완료하였다. 완성된 시편의 전단결합강도는 crosshead speed 1mm/min으로 하중을 가하여 측정하였으며, 두 그룹의 전단결합강도 값 사이에는 통계적으로 유의한지 알아보기 위하여 Mann-Whitney test를 이용하였다(유의수준 0.05). 측정이 끝난 후 시편을 대상으로 파절양상을 분석하였다. 본 연구를 위한 실험 설계, 금속 코어 제작, 도재 축성 등의 시편 제작부터 실험 수행과 수행 후 실험 데이터 분석과 통계 분석 그리고 파절된 시편을 대상으로 한 파절 양상 분석까지 총 6개월이 소요되었다. 실험 결과 cast 50.14, 3D printing 54.36 MPa를 갖는 것으로 조사되었고, 통계적으로도 유의하였다. 파절양상은 두 집단 모두 시편의 대부분이 혼합형 파절양상을 보였다. 이와 같은 결과들로 미루어볼 때 3D 프린팅에 의해 제작된 금속도재관 제작을 위한 금속 코어는 임상적으로 허용이 가능할 것으로 사료된다.

• 한국콘텐츠학회논문지
• /
• 제10권11호
• /
• pp.228-234
• /
• 2010

치과도재용 합금으로 사용되는 합금 중 베릴륨이 함유된 비귀금속 Ni-Cr합금과 베릴륨이 함유되지 않은 비귀금속 Ni-Cr합금 그리고 베릴륨이 함유되지 않은 비귀금속 Co-Cr 합금과 세라믹간의 결합강도와 파절양상 그리고 계면특성을 분석하고자 하였다. 결합강도는 만능시험기를 이용하여 전단력시험을 통하여 전단결합력을 측정하였으며, 전단시험에 의한 파단면을 이용하여 파절양상을 관찰하였다. 그리고 합금-도재간의 계면을 관찰하였다. 전단결합강도 측정 결과, 베릴륨이 포함된 T-3가 41.13(${\pm}5.11$)MPa로 가장 높게 나타났으며, 베릴륨이 포함된 VeraBond(40.72(${\pm}5.98$)MPa), Co-Cr 합금인 Wirobond(38.40(${\pm}9.66$)MPa), 베릴륨이 포함되지 않은 Verabond 2V(32.77(${\pm}4.31$)MPa), Bellabond N(28.63(${\pm}6.39$)MPa), Bellabond plus(24.97(${\pm}6.13$)MPa), Argeloy N.P. Star(22.69(${\pm}3.41$)MPa) 순으로 나타났다. 비귀금속 합금들과 세라믹간의 파절양상은 모든 시편에서 금속표면에 세라믹이 일부 부착된 복합파절(mixed failure) 양상을 보였다.

• 대한치과기공학회지
• /
• 제19권1호
• /
• pp.37-42
• /
• 1997

The interfacial bond strengh and microstructural analysis of pre-heat treated porcelain-fusedmetal(PFM) were investigated using a mechanical three-point bending tester and scanning electron microscope(SEM). Four kinds of heat treated samples were prepared as follows ; A: Heating $1200^{\circ}F{\to}1600^{\circ}F$, holding 1min, reheating ${\to}1850^{\circ}F$, hold 3min under vacuum, B: heating $1200^{\circ}F{\to}1600^{\circ}F$, holding 1min, reheating${\to}1850^{\circ}F$ under vacuum conditon, C: heating $1200^{\circ}F{\to}1600^{\circ}F$, holding 1min, reheating${\to}1850^{\circ}F$, holding 3min in the air, repeat same heat treatment process under vacuum condition, D: heating $1200^{\circ}F{\to}1600^{\circ}F$, holding 1min, reheating${\to}1850^{\circ}F$, holding 1min in the air. The three-point bening test result shows that the interfacial bond strength of specimen B and C were higher than that of A and D. The SEM study indicate that Specimen C shows the highest surface density.

• 대한치과기공학회지
• /
• 제31권2호
• /
• pp.45-52
• /
• 2009

Esthetic restorations have been widely used in dental practice, although many studies have focused on the development and improvement of all ceramic restorations. The success of esthetic restorations depends primarily on an optimal bond strength between various veneered ceramics and core materials for esthetic restorations. The purpose of this study was to compare the shear bond strength between various veneered ceramics and core materials for esthetic restorations. 30 metal cores and 20 zirconia cores were fabricated and divided into five groups according to veneered ceramic materials such as Creation porcelain powder, Cercon Ceram Kiss, and IPS e.max ZirPress. Thirty spacimens were prepared using Creation porcelain powder, veneered 3mm height and 3mm in diameter, over the metal cores (n=10). Twenty specimens were prepared using Cercon Ceram Kiss and Zirpress, veneered 3mm height and 3mm in diameter, over the zirconia cores (n=10). The shear bond strength test was performed in a universal testing machine with a crosshead speed of 1mm/min. Ultimate shear bond strength data were analyzed with One-way ANOVA and the Scheffe's test (p=.05). Within the limits of this study, the following conclusions were drawn: The mean shear bond strengths (MPa) were: 18.44 for Uni metal VH/Creation (NCUC); 18.72 for Heraenium/Creation (NCHC); 16.23 for Wirobond C/Creation (NCWC); 13.88 for Zirconia core/$110{\mu}m$ $Al_2O_3$ sandblasting/Cercon Ceram Kiss (ZS110P); 14.61 for Zirconia core/No surface treatment/IPS e.max ZirPress (ZNTH). The mean shear bond strength for NCUC (Uni metal VH/Creation), NCHC (Heraenium/Creation) and NCWC (Wirobond C/Creation) were significantly superior to ZS110P (Zirconia core/$110{\mu}m$ $Al_2O_3$ sandblasting/Cercon Ceram Kiss) and ZNTH(Zirconia core/No surface treatment/IPS e.max ZirPress) (p<0.05).

• 대한치과기공학회지
• /
• 제33권3호
• /
• pp.185-192
• /
• 2011

Purpose: This study was to evaluate the shear bond strength of the ceramic fused to Ni-Cr alloy(Bellabond plus) and Co-Cr alloy(Wirobond C) by heat treatment. Methods: Metal specimens were divided into 5 groups for each alloy according to heat treatment conditions prior to porcelain application. Fifteen specimens from each group were subjected to a shear load a universal testing machine using a 0.1mm/min cross-head speed and one specimen from each group was observed with EDX line profile. Results: The diffusion of metal oxide observed far in the specimen heat treated than no heat treated in the opaque layer. The shear bond strength measured highest to BP3(50.50MPa), WC2(50.49MPa) groups and measured lowest from BP1(35.1MPaa), WC1(39.66MPa) groups which were not treated with heat, and there was a significant difference (p<0.05). Conclusion: The shear bond strength of Ni-Cr alloy(Bellabond plus) and Co-Cr alloy(Wirobond C) measured similar 5 groups all.

• Restorative Dentistry and Endodontics
• /
• 제42권2호
• /
• pp.95-104
• /
• 2017

Objectives: This study evaluated the influence of a multi-mode universal adhesive (MUA) containing silane (Single Bond Universal, 3M EPSE) on the bonding of resin cement to lithium disilicate. Materials and Methods: Thirty IPS e.max CAD specimens (Ivoclar Vivadent) were fabricated. The surfaces were treated as follows: Group A, adhesive that did not contain silane (ANS, Porcelain Bonding Resin, Bisco); Group B, silane (S) and ANS; Group C, hydrofluoric acid (HF), S, and ANS; Group D, MUA; Group E, HF and MUA. Dual-cure resin cement (NX3, Kerr) was applied and composite resin cylinders of 0.8 mm in diameter were placed on it before light polymerization. Bonded specimens were stored in water for 24 hours or underwent a 10,000 thermocycling process prior to microshear bond strength testing. The data were analyzed using multivariate analysis of variance (p < 0.05). Results: Bond strength varied significantly among the groups (p < 0.05), except for Groups A and D. Group C showed the highest initial bond strength ($27.1{\pm}6.9MPa$), followed by Group E, Group B, Group D, and Group A. Thermocycling significantly reduced bond strength in Groups B, C, and E (p < 0.05). Bond strength in Group C was the highest regardless of the storage conditions (p < 0.05). Conclusions: Surface treatment of lithium disilicate using HF and silane increased the bond strength of resin cement. However, after thermocycling, the silane in MUA did not help achieve durable bond strength between lithium disilicate and resin cement, even when HF was applied.

• 대한치과보철학회지
• /
• 제47권1호
• /
• pp.61-69
• /
• 2009

서론: 인접 자연치와 아름답고 자연스런 조화를 이루는 심미적 치료를 위해 도재 수복물은 대중적인 치료방법의 하나로 잡고 있다. 임상에서 도재 수복물이 제작 후 치아에 시멘트로 접착을 하기 전 먼저 구강 내에서 시적할 때 수복물 표면에 타액, 혈액, 시적용 시멘트 등으로 인해 오염될 수 있다. 연구 목적: 이 연구의 목적은 도재 수복물로 사용되고 있는 라미네이트 도재에 실란 결합제의 처리 시기를 달리할 때와 도재 수복물을 치아에 시적 할 때 타액의 오염여부가 실란 결합제의 물리적, 화학적 반응성에 미치는 영향을 관찰하여 도재와 레진 시멘트 사이의 결합력의 안정성을 평가하는 것이다. 연구 재료 및 방법: 라미네이트용 도재를 360개의 원반모형과 5개의 정사각형 모형으로 제작하여 20군으로 나눈다. 각 군에 표면처리를 달리 한 뒤 푸리에 적외선 분광계, 접촉각 측정기와 인스트론 만능 시험기를 이용해 화학적, 물리적 비교를 하였다. 통계는 각 군의 전단 결합 강도의 유의성을 검증하기 위하여 일원분산분석(ANOVA) 후 사후검정은 던넷 다중비교 (Dunnett's multiple comparison)를 시행하였다 (P > .05). 연구 결과: 푸리에 적외선 분광 자료에 의해 본 타액 오염 및 실란의 처리 시기에 따른 화학적 변화는 크지 않았다. 접촉각은 타액 오염 후 낮아졌으나 인산으로 산 부식 후 각도가 증가하였다. 전단 결합강도값은 열 순환후의 군에서 미리 실란으로 보호한 경우에 유의한 차이가 있었다. 결론: 수복물의 내구성에 영향을 미치는 다양한 구강환경과 유사한 조건에서 수복물의 물성평가를 같이 고려해 볼 때 실란 결합제를 이용한 수복물의 접착시 실란 결합제를 수복물에 미리 도포하여 일정시간의 경과 후 수복물을 접착하며, 타액 오염이 발생할 경우 인산으로 수복물을 세척하는 것이 유용한 방법 임을 알 수 있었다

• 한국산학기술학회논문지
• /
• 제16권7호
• /
• pp.4357-4363
• /
• 2015

본 연구는 베릴륨 함유하지 않은 Ni-Cr계 도재용 금속에 전용도재를 도포, 소성된 시편을 3점 굴곡 시험으로 결합강도를 측정하고, SAM/EDS로 표면성분관찰 실험한 AVOVA와 Tukey HSAD 사후검정을 실시한 결과는 다음과 같은 결론을 얻었다. 첫째. 모든 군에서 ISO 9693의 치과용 금속-도재 시편의 최소 결합강도의 최소치인 25 MPa의 전단결합강도를 상위하며 안정적인 결과값을 나타냈다. 둘째. 결합 강도는 대조군 V1은 $32.37{\pm}1.91MPa$으로 나타났고, 실험군 V2 $38.25{\pm}1.38MPa$, 실험군 V3 $46.43{\pm}2.14MPa$, 그리고 실험군 V4 $47.21{\pm}1.72MPa$, 순으로 나타났으며 통계적으로 유의한 차이를 보였다. 사후 검정 (Tukey's HSD test) 결과, 결합강도 실험결과 실험군 V4는, 대조군 V1보다 높게 나타났다. 셋째. 금속-도재의 결합에서 산화처리를 시행한 군보다 시행하지 않고 불투명 도재를 도포하고 소성한 군이 높게 나타났으며, paste불투명 도재보다 분말 불투명도재의 사용에 따른 결합강도가 더 높게 나타났다. 넷째. 실험군 V4는 금속과 도재의 결합강도 비교에서 가장 높게 나타났다.

• 대한치과기공학회지
• /
• 제23권2호
• /
• pp.161-170
• /
• 2002

The Purpose of this study was to investigate the chemically improvement of metal-ceramics bond strength in the course of recasting Ni-Cr metal composite system with 10wt.%, 20wt.% and 30wt.% aluminum respectively. We have tested the bond strength, micro-structure, chemical composition of each metal composites and metal- ceramic bond interfaces by 3-point bending strength tester, SEM and EDS. We have made the conclusions through this study as follow: 1. The most suitable amount of aluminum to the Ni-Cr metal composite recasting is 20wt. % for improving metal-ceramics bond strength with debonding strength value of 49.54 kgf/mm2. 2. The aluminum must be changed to small spread alumina like phases and second aluminum-metal composites phases in the morphology of Ni-Cr metal composite system by adding during it's casting. These second phases have inclined functional oxide phases mixed with metal elements and they must take roll to improvement of metal-ceramics bond strength. 3. In the case of 30wt.% aluminum appended to Ni-Cr metal composite system, an excess of second inclined functional oxide phases produce cracks and spalling of them apart from it's base material. It must be a important factor of reduction of metal-ceramics bond strength.