• The Journal of Advanced Prosthodontics
• /
• 제5권4호
• /
• pp.423-427
• /
• 2013

PURPOSE. This study evaluated the bond strength between porcelain denture teeth (Bioblend 43D) and four different polymerized denture resins (Lucitone 199, Palapress, Acron MC, Triad) with and without a bonding agent and after four different types of surface treatment (polished, HF etched, sandblasted, air-abraded). MATERIALS AND METHODS. Central incisor porcelain denture teeth were divided into 32 groups of 5 each. Tensile bond strength (MPa) was determined using a testing machine at crosshead speed of 0.5 mm/min. Mean and standard deviation are listed. Data were analyzed by two-way ANOVA. Means were compared by Tukey-Kramer intervals at 0.05 significance level. RESULTS. All surface treatment increased bond strength compared to polished surface and the highest bond strength was found with Palapress resin with etched porcelain surface (8.1 MPa). Bonding agent improved the bond strength of all denture resins to porcelain teeth. Superior bonding was found with Palapress and air-abraded porcelain (39 MPa). CONCLUSION. Resins with different curing methods affect the bond strength of porcelain teeth to denture bases. Superior bonding was found with auto-polymerized resin (Palapress). Application of ceramic primer and bonding agent to porcelain teeth with and without surface treatment will improve the bond strength of all denture resins to porcelain teeth.

• 대한치과보철학회지
• /
• 제29권1호
• /
• pp.91-109
• /
• 1991

The purpose of this study were to comfirm the effects of the thickness and kinds of porcelain, etchants, illumination time, elapsed time for the measurement, and chemical cure component to the bond strength of porcelain laminate and composite resin cement, and to compare the effects between the light cured resin and the dual cured resins. The etched porcelain surface, the sectioned surface crossing porcelain and resin after bonding, and the debonded surfaces were observed by the SEM. One product of laminate porcelain powder, one light cured resin and two dual cured resins were selected. Each resin cements are lightened through the thin porcelain disc which was cut from cylindrical porcelain specimen by the diamond saw, and by the light through the porcelain disc they were bonded. Changes of thickness and kinds of porcelain, etchants, illumination time, and the elapsed time for the measurement were considered as variables for the bond strength. And the bond strength of porcelain and dual cured resins under the conditions of autopolymerization or the removal of chemical cure component were measured and compared. Bond strength were measured by shear stress. The etched surface, the cross-sectioned surface, and the debonded surface of porcelain or resin were observed by SEM. On the summary of this study, the following conclusions can be stated; 1. Bond strength of light cured resin was decreased inversely by the thickened porcelain laminate and showed the lowest value to the masking dentin porcelain among 4 kinds of porcelain powder. 2. Bond strength of autopolymerization of dual cured resin without illumination in dark chamber were from 75% to 98% to the data of dual cured resin with illumination. 3. Bond strength of dual cured resin used without chemical cured components were same to them of light cured resin. 4. Cross-sectioned surface treated by silane did not show the gap between the porcelain and resin. 5. Illumination over 80 seconds did not make the significant increase of bond strength on all kinds of resin.

• 대한치과보철학회지
• /
• 제28권2호
• /
• pp.147-163
• /
• 1990

Although dental porcelain demonstrates lasting esthetic results, it suffers from inherent brittle fractures. Various techniques and materials for intraoral porcelain repair has been suggested. This study investigated the in vitro shear strength of three porcelain repair systems according to aspects of the porcelain fractures. The purpose of this study was to evaluate the shear bond strength of three porcelain repair systems(All-bond, Clearfil, Scotchprime) according to fractured surface of porcelain - fused - to - metal restorations. For this study specimens were divided into five groups : group 1 represented fracture occurred at body porcelain layer, group 2 represented fracture occurred at opaque porcelain layer, group 3 represented fracture including 1/3 of metal exposure, group 4 represented fracture including 2/3 of metal exposure, and group 5 represented all metal surface was exposed. Specimens were stored in double deionized water(24Hr, $37^{\circ}C$) and thermocycling was performed(24Hr, 1080cycles), and subjected to a shear force parallel to the repair resin and porcelain interface by use of an University Testing Machine. The results of this study were obtained as follows : 1. In group 1 and 2, bond strength was relatively high, and bond strength showing reducing tendency as exposure of metal was increased. 2. In group 1, bond strength was relatively high, and no significant differences in porcelain repair system. 3. In group 2, 3 and 4, All-bond and Clearfil provided significantly higher bond strength than scotchprime. 4. In group 5, bond strength was the lowest among all groups and especially in case if Scotchprime. 5. Cohesive failure was observed in group 1 and 2, adhesive failure was observed in group 5, and cohesive / adhesive failures were observed in group 3 and 4.

• 대한치과기공학회지
• /
• 제9권1호
• /
• pp.39-49
• /
• 1987

This study done to evaluate some surface treatment methods in metal coping which can increase the bond strength between porcelain and metal. Therefore this experiment was performed according to the Mc Lean's Theory of bond strength between porcelain and strength between porcelain and metal. In the experiment the author measured respective thermal expansion coefficents in three types of metal(Tallasium, Vera Bond and Rexillium) and Vita Porcelain to get the differences in the coefficents between porcelain and metals. And using insteron testing machine, the author also performed Planar interface shear bond tests on the 45 specimens(15 specimens in oxide surface, rough surface and fine surface treatment methods respectively) to measure bond strength between metal and porcelain. The results Were as follows, 1. The differences in thermal expansion coefficients between three types of metal and Vita procelain: Talladium - $1.2\;10^{-6/0}\;C$, Vera Bond - $1.6\;10^{-6/0}\;C$, Rexillium - $1.9\;10^{-6/0}\;C$. 2. The bond strength in oxide surface on the Shear bond test was the lowest among the treatment methods. 3. There was no significant differences in treatment methods of rough surface of fine surface. 4. In the oxide surface treatment method, there were significant differences(P<0.05)between Vera bond and Rexillium, and between Talladium and Rexillium. 5. In the fine surface treatment, there was a significant difference(P<0.05)between Talladium and Rexillium.

• Restorative Dentistry and Endodontics
• /
• 제15권1호
• /
• pp.165-173
• /
• 1990

The purpose of this study was to measure the effect of two commercially available composite resin systems and GC dentin cement on the shear bond strength of the etched porcelain to enamel and dentin. The specimens were divided into six groups, and each group was as follows. Group I : etched enamel-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group II : etched enamel-Scotchbond 2-Silux-unfilled resin-silane-etched porcelain. Group III : dentin-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group IV : dentin-Scotchbond 2-Silux-unfilled resin-silane-etched porcelain Group V : dentin-GC dentin cement-dentin/enamel bonding agent-CHOICE-unfilled resin-silane-etched porcelain Group VI : dentin-GC dentin cement-Scotchbond 2-Silux- unfilled resin-silane-etched porcelain Following polymerization. the specimens were stored in 100% humidity for 24 hours before testing. Shear bond strength was measured with Instron universal testing machine. The results obtained were as follows; 1. The shear bond strength of the etched porcelain to enamel was greater than that of the etched porcelain to dentin. 2. The shear bond strength of Silux-Scotchbond 2 to dentin was greater than that of CHOICE-dentin/enamel bonding agent. 3. There was no significant difference in shear bond strength to dentin between the groups lined with GC dentin cement. 4. The shear bond strength of Silux-Scotchbond 2 to dentin was greater than that of the groups lined with GC dentin cement. 5. There was no significant difference in shear bond strength to dentin between the groups lined with GC dentin cement and the group directly bonded with CHOICE-dentin/enamel bonding agent.

• 대한치과보철학회지
• /
• 제41권3호
• /
• pp.379-386
• /
• 2003

Statement of problem. Resin cements are widely used in adhesive dentistry specially on all ceramic restorations. It is needed to find out adequate bonding strength between different porcelain surface treatments, commercially available porcelains, and different resin cement systems. Purpose. The purpose of this study was to evaluate shear bond strength of resin cements bonded to porcelains in three different modalities; 5 different porcelain surface treatments, 3 different resin cement systems and 3 different commercially available pressable porcelains. Material and Method. This study consisted of 3 parts. Part I examined the effect of five different surface treatments on the pressable porcelain. Fifty discs (5 mm in diameter and 3 mm in height) of Authentic porcelain were randomly divided into 5 groups (n = 10). The specimens were sanded with 320 grit SiC paper followed by 600 grit SiC paper. The specimens were treated as follow: Group 1-Sandblasting (aluminum oxide) only, Group 2 - sandblasting/ silane, Group 3 - sandblasting/ acid etching/ silane, Group 4 - acid etching only, Group 5 - acid etching/ silane. Part II examined the shear bond strength of 3 different resin cement systems (Duolink, Variolink II, Rely X ARC) on acid etching/ silane treated Authentic pressable porcelain. Part 3 examined the shear bond strength of Duolink resin cement on 3 different pressable porcelains (Authentic, Empress I, Finesse). All cemented specimens were stored in distilled water for 2 hours and tested with Ultradent shear bond strength test jig under Universal Instron machine until fracture. An analysis of variance(ANOVA) test was used to evaluate differences in shear bond strength. Result. The shear bond strength test resulted in the following: (1) Acid etched porcelains recorded greater shear bond strength values to the sandblasted porcelains. (2) Silane treated porcelains recorded greater shear bond strength values to non-silane treated porcelains. (3) There was no significant difference between sandblasting/ acid etching/ silane treated and acid etching/ silane treated porcelains. However those values were much higher than other three groups. (4) The shear bond strength with Variolink II was lower than the value of Duolink or Rely X ARC. (5) The shear bond strength of Finesse was lower than the value of Authentic or Empress I.

• 대한치과보철학회지
• /
• 제45권4호
• /
• pp.419-430
• /
• 2007

Purpose: This in vitro study evaluated shear bond strengths of surface treatment porcelains with four porcelain repair systems simulating intraoral bonding of composite resin to feldspathic porcelain or pressable porcelain. Material and methods: Eighty Porcelain disks were prepared. Group A: forty disk specimens were fabricated with Feldspathic Porcelain($Omega^{(R)}900$, Vident, Menlo Park, CA, USA). Group B: forty disk specimens were fabricated with Pressable Porcelain(IPS Empress 2 ingot, Ivoclar-Vivadent, Schaan, Liechtenstein, Germany). Each groups was divided into 4 subgroups and composite resin cylinders were bonded to specimen with one of the following four systems: Clearfil Porcelain Bond(L. Morita, Tustin, CA, USA), Ulradent Porcelain Etch. (Ultradent, Salt Lake City UT, USA), Porcelain Liner-M(Sun Medical Co., Kyoto, Japan), Cimara Kit(Voco, Germany). After surface conditioning with one of the four porcelain repair systems substrate surfaces of the specimen were examined microscopically(SEM). Shear bond strengths of specimens for each subgroup were determined with a universal testing machine (5mm/min crosshead speed) after storing them in distilled water at $37{\pm}1^{\circ}C$ for 24 hours. Stress at failure was measured in $MP_a$, and mode of failure was recorded. Differences among four repair systems were analyzed with two way ANOVA and Duncan test at the 95% significance level. Results: In the scanning electron photomicrograph of the treated porcelain surface, hydrofluoric acid etched group appeared the highest roughness. The shear bond strength of the phosphoric acid etched group was not significantly(p>0.05) different between feldspathic porcelain and pressable porcelain. But in no treatment and roughened with a bur group, the shear bond strength of the feldspathic porcelain was significantly higher than that of the pressable porcelain. In hydrofluoric acid etched group, the shear bond strength of the pressable porcelain was significantly higher(p<0.05). Conclusion: 1. Treatment groups showed significantly greater shear bond strengths than no treatment group(p<0.05). 2. Group with more roughened porcelain surface did not always show higher shear bond strengths. 3. In phosphoric acid etched group, there was no significant difference in shear bond strength between feldspathic porcelain and pressable porcelain(p>0.05). However in the other groups, there were significant differences in shear bond strengths between feldspathic porcelain and pressable porcelain(p<0.05).

• 대한치과기공학회지
• /
• 제7권1호
• /
• pp.19-25
• /
• 1985

In oder to compare and measure bond strength of ceramometal system with use of ceramco porcelain powder including SnO2 and uni metal, Rexillium III, Vera Bond as non precious alloys manufactured for porecelain-metal restorations. Total 24 test sample were constructed. All Test sample were measured with a Mitutoyo micrometer graduated to 0.01mm. It is as follows measured of thickness 3.3mm(metal : 1.1mm, porcelain: 2.2mm), width 12mm, length 30mm(porcelain 12mm x 12mm), Compared maximum bending stress test. The results obtained were as follows: 1. Bond strength of each metal with ceramco porcelain powder showed statistical significance.(P<0.05) 2. Vera Bond and uni metal, uni metal and Rexillium III revealed no statistical Significance.(P>0.05) Vera Bond and Rexillium III showed statistical significance.(P<0.05) 3. The order of maximum bending stress was Rexillium III, uni metal, vera Bond. The order of bond strength ratio making bending stress was Vera bond, uni metal, Rexillium III.

• 구강회복응용과학지
• /
• 제22권3호
• /
• pp.211-220
• /
• 2006

Need of porcelain-repair system is largely demanding as dental porcelain restorations are increased in clinical dentistry. This study investigated shear bond strength of commercial porcelain-repair systems on dental porcelain and their reliability. Experimental groups were as follows; Group A Super Bond C&B, Group B Porcelain repair kit, Group C Ceramic repair, and Group D Spectrum system as a control. Porcelain disks were fired and embedded in epoxy resin. Porcelain surface were ground using 220 grit SiC disk, then cleaned in ultrasonic bath. Then porcelain specimens were treated with each repair system. A clear polystyrene cylinder 3.5 mm in internal diameter was filled with composite resin. Then the resin cylinder was polymerized with a visible light curing unit. Thirty one specimens at each group were prepared and stored at $37^{\circ}C$ distilled water for 48 h. Specimens were tested in an Instron testing machine according to ISO TR 11405. Mean shear bond strength and standard deviation of each group was $15.7{\pm}4.1MPa$ (Group A), $12.8{\pm}4.9MPa$ (Group B), $7.2{\pm}3.0MPa$ (Group C) and $9.6{\pm}2.2MPa$ (Group D). ANOVA and Tukey HSD post-hoc test showed that there were significant differences between groups (p<0.05). Data of bond strength were analyzed with two-parameter Weibull distribution. Confidence interval of Weibull modulus (m-parameter) at 95% of Group A (3.5-6.3) and Group D (3.6-6.0) were significantly higher than Group B (2.2-3.7) and Group C (2.0-3.4). There was little correlation between mean shear bond strength and Weibull modulus. Results indicated that acid-etching of porcelain surface increased porcelain-resin shear bonding strength.

• 대한치과보철학회지
• /
• 제30권2호
• /
• pp.135-154
• /
• 1992

This study was performed to analyze bond strength, the alterations of the interfaces between metal films which are populary used and considered to contribute to the chemical reaction with porcelain, according to constant ion- beam- mixing, and the relation between interfacial chemical reactions and bond strength in metal/porcelain specimens. For this study, three seperate metals : selected-gold, indium and tin were chosen ; each to be bonded to a seperate body porcelain. Bonding occurs when the metal is deposited to the body porcelain using a vacuum evaporator. The vacuum evaporator used $10^{-5}\sim10^{-6}$ Torr vacuum states for the evaporation of various metals (Au, Sn, In). Ion-beam-mixing of the porcelain/metal interfaces caused reactions when the Ar+ was implanted into thin films using a 80 KeV accelerator. These ion-beam-mixed specimens were then compared with an unmixed control group. An analysis of bond strength and ionic changes between the the metal and porcelain was performed by electron spectroscopy of chemical analysis (ESCA) and scratch test. The finding led to the following conclusions : 1. Light microscopic views of the scratch test : The ion-beam-mixed Au/porcelain specimen showed narrower scratched streams than the unmixed specimen. However, the Sn/porcelain, In/porcelain specimens showed no differences in the two conditions. 2. Acoustic emissions in scratch tests : The ion-mixed Au/porcelain, In/porcelain specimens showed signals closer to the metal/porcelain interfaces than unmixed specimens. Conversely, the ion-mixed Sn/porcelain specimen showed more critical signals in superficial portions than unmixed specimens. 3. After ion- beam-mixing, the Au/porcelain specimen showed apparently increased bond strength, and the In/porcelain specimen showed very slightly increased bond strength. However, the Sn/porcelain specimen showed no differences between ion mixed specimen and the unmixed one. 4. ESCA analysis : The ion-beam-mixed Au/porcelain specimen showed a higher peak separated value (4.3eV) than that of the unmixed specimen(3.65eV), the ion-beam-mixed In/porcelain specimen showed a higher peak separated value (9.43eV) than that of the unmixed specimen(7.6eV) and the ion-beam-mixed Sn/porcelain specimen showed a higher peak separated value (8.79eV) than that of the unmixed specimen(8.5eV). 5. Interfacial changes were observed in the ion-mixed Au/porcelain, In/porcelain and Sn/porcelain specimens. Especially, significant interfacial changes were measured in the ion- mixed Sn/porcelain specimen. Tin dioxide(SnO2) and a combination of pure tin and tin dioxide (Sn+SnO2) were produced. 6. In the Au/porcelain specimen, the interfacial chemical reaction showed increased bond strength between gold and porcelain substrate. But, in the In/porcelain, Sn/porcelain specimens, interfacial chemical reactions did not affected the bond strength between metal and porcelain substrate. Especially, bonding strength on the ion mixed Sn/porcelain specimen showed the least amount of difference.