• Korean Chemical Engineering Research
• /
• v.50 no.4
• /
• pp.639-645
• /
• 2012

Waterborne polyurethane dispersion (PUD) was synthesized by capping the NCO groups of polyurethane prepolymers, prepared from isophorone diisocyanate, polycarbonate diol and dimethylol propionic acid, with aminopropyl triethoxysilane (APS). Subsequently, silylated acrylic polyurethane dispersion was synthesized by reacting the PUD with the mixture of acrylate monomers, 2-hydroxyethyl methacrylate and methyl methacrylate. The average particle size of silylated acrylic polyurethane dispersion, measured by the dynamic light scattering method, was increased from 39.0 nm to 399.8 nm by increasing the addition amounts of APS. Also, the pencil hardness of coating films of silylated acrylic polyurethane dispersion was enhanced from B grade to F grade with increasing APS content.

• Korean Chemical Engineering Research
• /
• v.50 no.4
• /
• pp.614-620
• /
• 2012

Polyurethane prepolymers were prepared from poly (carbonate diol), isophrone diisocyanate and dimethylol propionic acid. Then, aniline terminated waterborne polyurethane dispersion (ATPUD) was synthesized by capping the NCO group of the prepolymer with aniline monomer. Subsequently, ATPUD and waterborne polyurethane dispersion (PUD), respectively, were blended with conducting polymer, poly (3,4-ethylenedioxythiophene)/polystyrene sulfonate [PEDOT/PSS], to yield antistatic coating solutions, and the mixture was coated on the polycarbonate substrates. At adequate addition amounts of PEDOT/PSS less than or equal to 2.5 g, the surface resistances ($1.0{\times}10^{11}{\sim}2.5{\times}10^8{\Omega}/cm^2$) of coating films from ATPUD showed better electronic conductivities than those ($5.0{\times}10^{11}{\sim}6.3{\times}10^9{\Omega}/cm^2$) from PUD. However, at excess amount of PEDOT/PSS of 3.0 g, the surface resistance from ATPUD showed similar electronic conductivity with that from PUD.

• Textile Coloration and Finishing
• /
• v.19 no.4
• /
• pp.26-31
• /
• 2007

Nanocomposite resin(PUD-CNT) composed of Carbon nanotube(CNT) and Polyurethane Dispersion (PUD) was prepared by different contents of CNT($0{\sim}5%$). PUD-CNT was coated on samples, and their electrical conductivity was investigated. With increasing CNT content, static change, half life and surface resistance decreased. Composites having 5% CNT showed $10^9{\Omega}/cm$(surface resistance), and 40V (stactic charge). Respectively, From this results, PUD-CNT can be used as a antistatic material.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.1
• /
• pp.178-185
• /
• 2021

In this study, polyvinyl alcohol (PVA) and polypropylene glycol (PPG)-based polyurethane dispersion resin for wound coating was synthesized. And the physical properties of the sample were coated on the surface of the film sample and the leather (Full-Grain) to study the physical properties change. In the case of tensile strength, PUD-PA1, which reacted with the least amount of PVA, showed the highest resistance at 2.00 kgf/㎟. Likewise, the rate of elongation was measured as high as 554% for PUD-PA1, which reacted with the least amount of PVA. The abrasion resistance measurement result showed that as the PVA response increased, the strength of the surface decreased to 36.77 mg.loss.

• Journal of the Korean Applied Science and Technology
• /
• v.31 no.2
• /
• pp.296-304
• /
• 2014

For this research, prepared polyurethane dispersion of hard segment type and polyethylene emulsion wax. Use these resin, this article has been analyzed about mechanical properties variation by increasing amount of polyethylene emulsion wax on Lam skin leather and dried film. According to measure data for solvent resistance, PUD had good property. As known in the results, increase of polyethylene wax constant did not influence to big variation of hybrid resin properties. As test of tensile strength, PUD had good tensile characteristic($1.235kg_f/mm^2$) and PUD-EW4 had lowest tensile characteristic($1.022kg_f/mm^2$). As same as tensile characteristic, abrasion test determined PUD(52.225 mg.loss) had highest properties. In elongation case, PUD showed 698 % modulus which was best properties in this experiment.

• Elastomers and Composites
• /
• v.52 no.4
• /
• pp.295-302
• /
• 2017

Polyurethane dispersion (PUD) polymers were synthesized by using polyether and polyester polyol. The effect of ionomeric centers, r(NCO / OH) values, chain extender process, and chain extender types on the adhesion properties was investigated. In the case of polyether-based PUD, the ionic center, r value, chain extension process and chain extender types were not adjusted even after adjustment. In the case of polyester-based PUD, when the ionic center content was more than 2.5%, the state of adhesive strength was $2.0kgf/cm^2$ or more. On the other hand, the initial adhesive strength was excellent at about $1kgf/cm^2$ when the ionic center content was over 3.5%. When the r value was 1.3 or more, it was found that the initial bonding strength and the state of bonding strength were excellent at about $1kgf/cm^2$ and $2.1kgf/cm^2$ or higher, respectively. An IR spectrum analysis of the synthesized PUD confirmed that PUD was composed of urethane based on the N-H characteristic peak at $3340cm^{-1}$ and the urethane characteristic peak at $1730cm^{-1}$. Moreover, the characteristic peaks of the isocyanate ($2260cm^{-1}$) used in the preparation of the prepolymer were not observed. As a result, the residual -NCO was not observed, and urethane was completely synthesized.

• Journal of Adhesion and Interface
• /
• v.9 no.1
• /
• pp.16-21
• /
• 2008

Hybrid emulsions consisting of polyurethane and acrylic polymer were prepared by emulsion polymerization of acrylic monomers and polyurethane water dispersions (PUD) as an emulsifier. At first, cationic type of PUD was synthesized with IPDI, PTMG1000, MDEA, and acetic acid. Then, acrylic monomers, such as MMA and n-BA, were copolymerized with the PUD without adding further surfactant. The tensile properties and water resistance increased with increasing acrylic monomer ratio. The hybrid emulsions showed better properties than the emulsions simply blended with the PUD and the acrylic emulsions.

• Korean Chemical Engineering Research
• /
• v.50 no.4
• /
• pp.632-638
• /
• 2012

Waterborne polyurethane dispersions (PUD) were synthesized from isophorone diisocyanate (IPDI), polycarbonate diol (PCD) and dimethylol propionic acid (DMPA) as starting materials. Subsequently, waterborne polyurethane-acrylic hybrid solutions were prepared by reacting the PUD with different amounts of the mixture of acrylate monomers, HEMA (2-hydroxyethyl methacrylate) and MMA (methyl methacrylate). As a result, the average particle size of waterborne polyurethane-acrylic hybrid solutions was increased with increasing the addition amounts of acrylate monomers. Also, the prepared coating films from waterborne polyurethane-acrylic hybrid solutions showed better abrasion resistance and chemical resistance than those of pure PUD.

• Korean Chemical Engineering Research
• /
• v.50 no.3
• /
• pp.427-434
• /
• 2012

Waterborne polyurethane dispersions (PUD) were synthesized from poly (carbonate diol), isophrone diisocyanate and dimethylol propionic acid at different NCO/OH molar ratios. Subsequently, the PUD was mixed with different types of alkali metal salts ($LiClO_4$, $NaClO_4$, and $KClO_4$) to prepare antistatic waterborne polyurethane coating solutions. Effects of the types and amounts of alkali metal salts were investigated on the surface resistances of the resulting coating films. The surface resistances of coating films were decreased with increasing the amounts of alkali metal salts added in the PUD. The coating films prepared with the same amount of alkali metal salts showed increased ionic conductivity with the order of $LiClO_4$ > $NaClO_4$ > $KClO_4$. Also, the surface resistances of coating films were increased with increasing the molar ratios of NCO/OH in the PUD.

• Applied Chemistry for Engineering
• /
• v.27 no.2
• /
• pp.221-226
• /
• 2016

Production of eco-friendly and biologically harmless materials is strongly required in all industries. In particular, reducing volatile organic compounds in coating processes is extremely important to secure worker's safety. During recent two decades, extensive research works on water-borne polyurethane dispersion (PUD) have been continuously developed as an alternative to solvent-borne polyurethane. However, PUD was shown inferior mechanical properties to the organic solvent-borne polyurethane due to a limit to the molecular weight increase, which resulted in the limit of applications. To overcome this drawback, several approaches have been examined such as polymer blends and thermal/radiation induced crosslinking. Among these methods, the radiation curing system was suitable for industrialization because of the high crosslinking density and fast curing speed. In this study, we overcame the drawback for PUD via introducing benzophenone radiation curable units to PUD. We synthesized PUD films which possessed good dispersion in water for 30 days, increased Tg and Td more than $5^{\circ}C$ after UV curing film as well as improved young's modulus more than double.