• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 봄 학술발표회 논문집
• /
• pp.417-422
• /
• 2002

Strength and Durability of reinforced concrete exposed at deteriorated environment are decreased by cover spatting and corrosion of reinforcement. The purpose of this paper is to evaluate capacity of strengthening axial member using admixture-modified mortar. To investigate the capacity of strengthened axial member, behavior and strength of strengthening specimens were compared with a monolithic basic specimen. Admixture-modified mortar was prepared with silica fume, zeolite, polymer as cement modifier. From the result of this experiment, strengthening specimens using polymer-modified mortar have apparrent strengthening capacity because of good flexural strength and tensile strength.

• 콘크리트학회논문집
• /
• 제17권3호
• /
• pp.411-418
• /
• 2005

본 연구에서는 MMA(methyl methacrylate)계 아크릴 라텍스를 모노머 비에 따라 합성 제조하고, 각각의 모노머 비와 폴리머 시멘트 비에 따라 폴리머시멘트 모르타르를 제작한 후, 방수성, 염화물 이온 침투 저항성, 그리고 중성화에 대한 실험을 통해 MMA계 아크릴 라텍스를 혼입한 폴리머시멘트 모르타르의 내구성을 파악하고자 하였다. 실험결과, 폴리머시멘트 모르타르의 방수성과 염화물 이온 침투 저항성은 폴리머의 종류보다는 폴리머시멘트 비에 따라 많은 영향을 받는 것으로 나타나고 있으며, 폴리머시멘트 비가 높을수록 그 저항성도 증진되었다. 또 폴리머시멘트 모르타르의 중성화에 대한 저항성은 폴리머의 종류와 폴리머시멘트 비에 따라 많은 차이를 나타내고 있으며, 보통 시멘트 모르타르에 비해 현저히 증가하는 것으로 나타났다. 모노머의 종류에 따라서는 MMA/BA를 모노머로 이용한 폴리머시멘트 모르타르가 MMA/EA를 모노머로 한 폴리머시멘트 모르타르에 비해 그 성능이 우수하게 나타났다. 특히 폴리머시멘트 모르타르의 중성화는 세공구조에 따라서도 많은 영향을 받는 것으로 나타났으며 폴리머의 자체 저항능력으로 인해 폴리머의 혼입량이 높을수록 중성화에 대한 저항성도 증진되는 것으로 나타났다. 따라서 연구결과 본 실험에서 합성제조한 MMA계 아크릴 라텍스를 이용하여 폴리머시멘트 모르타르를 제작할 경우, 방수성, 염화물 이온 침투 저항성, 그리고 중성화에 대한 저항성을 크게 향상시킬 수 있었다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2001년도 학술논문발표회
• /
• pp.88-92
• /
• 2001

This paper discusses the strength properties of the polymer-modified mortars using redispersible polymer powders, which is widely used for the manufacture of prepackaged-type polymer-modified mortar products at present. The polymer-modified mortars using redispersible polymer powders are prepared with various polymer-cement ratios, and tested for air content, flexural and compressive strengths, and tensile strength. The strength properties are almost the same as those of polymer dispersion-modified mortars, depending on the polymer-cement ratios, and are improved over unmodified mortar. In particular, between tensile strength and glass transition point of polymer powder have a high correlation. It is concluded from the test results that polymer-modified mortars using redispersible polymer powders can be used in the same manner as ordinary polymer dispersion-modified mortars.

• 콘크리트학회논문집
• /
• 제25권3호
• /
• pp.313-320
• /
• 2013

이 연구에서는 환경을 고려한 고성능 보수 보강재료 개발을 위하여 섬유를 보강한 폴리머 시멘트 모르타르의 특성을 연구하였다. 친환경 수지인 UM 수지를 일반 시멘트 모르타르와 일정 비율로 혼합하였다. 강도 증진의 영향을 확인하기 위해서 PVA 섬유, 강섬유 그리고 PVA섬유와 강섬유를 일정한 비율로 혼합한 하이브리드 섬유를 일정한 비율로 첨가하였다. 강도특성을 파악하기 위하여 섬유를 보강한 폴리머 시멘트 모르타르에 대하여 압축강도, 쪼갬 인장강도, 휨강도 실험을 수행하였다. 내구성을 파악하기 위하여 폴리머 시멘트 모르타르에 대하여 흡수율 실험, 내약품성 실험을 수행하였다. 실험 결과 UM 수지 폴리머 시멘트 모르타르는 내구성능이 개선되었고, 이러한 폴리머 시멘트 모르타르에 섬유를 보강하면 콘크리트 및 모르타르의 취약점인 인장강도와 휨강도가 증가하였다. 향후 외부 노출된 콘크리트 구조물의 내구성 향상을 위한 보수보강재료로 사용성을 확인하였다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2001년도 봄 학술발표회 논문집
• /
• pp.1011-1016
• /
• 2001

The purpose of this study is to find out the effect of polymer glass transition temperature on mechanical properties of polymer latex-modified mortars in comparison with ordinary cement mortar. The Polymer latex-modified mortars are prepared with 5, 10, 15 and 20% of polymer cement ratio respectively, and properties of modified mortars such as air content, compressive, flexural and tensile strengths are tested. The test results indicate that the types of polymer dispersion and the polymer-cement ratio are very important factors to characterize the properties of polymer-modified mortars, and also the glass transition temperature of polymer dispersions has an important effect on the performance of polymer-modified mortars. The modifying effects of two kinds of polymer dispersion, St/BA-1 and SBR, are evaluated.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2019년도 추계 학술논문 발표대회
• /
• pp.162-163
• /
• 2019

The purpose of this study is to evaluate the adhesion in flexure of SBR-modified mortar adding Fly Ash(FA). From the test results, the adhesion in flexure is seriously affected by polymer-binder ratios and adding content of FA. The maximum adhesion in flexure of SBR- modified mortar is about 1.46 times, the plain cement mortar. It is apparent that the adhesion in flexure of SBR-modified mortars by polymer-binder ratios is much more improved than that by adding contents of AF.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 봄 학술발표회 논문집(I)
• /
• pp.231-236
• /
• 1998

In general, the drying shrinkage of polymer-modified mortars using redispersible polymer powders is much higher than that of unmodified mortar. The purpose of this study is to reduce the drying shringkage of polymer-modified mortars using a redispersible poly(ethylene-vinyl acetate) (EVA) powder, which is widely used for the manufacture of prepackaged-type polymer-modified mortar products at present. Polymer-modified mortars using the redispersible EVA powder with powdered shrinkage-reducing agent were prepared with various polymer-cement ratios and shrinkage-reducing agent contents, and tested for drying shrinkage and strength. From the test results, the drying shrinkage of the redispersible EVA powder-modified mortars with a powdered shrinkage agent is remarkably reduced with increasing shrinkage-reducing agent content, and becomes approximately a half of that of the redispersible EVA powder-modified mortars with the same polymer-cement ratios and without the shrinkage-reducing agent at a shrinkage-reducing agent content of 6%.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.691-694
• /
• 2004

The effects of polymer-cement ratio and antifoamer content on the setting time and durability of high-fluidity polymer-modified mortars using redispersible polymer powder are examined. As a result, the setting time of the polymer-modified mortars using redispersible polymer powder tend to delayed with increasing polymer-cement ratio, regardless of the antifoamer content. The water absorption and chloride ion penetration depth of the high-fluidity polymer-modified mortars using redispersible polymer powder decrease with increasing polymer-cement ratio and antifoamer content. The water absorption and chloride ion penetration improvement is attributed to the improved bond between cement hydrates and aggregates because of the incorporation of redispersible polymer powder.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 가을 학술발표논문집(II)
• /
• pp.350-355
• /
• 1998

Preplaced aggregate concrete in the building fields has recently been used in the partial repair works for damaged reinforced concrete structures, and polymer-modified mortars have been employed as grouting mortars for the preplaced aggregate concrete. The objective of this study is to clear the properties of polymer-modified grouting mortars. Polymer-modified mortars using a polystyrene acrylic(St/Ac) emulsion as grouting mortars for preplaced aggregate concrete are prepared with various mix proportions, and tested for flexural and compressive strengths, adhesion in tension. The flexural strength of emulsion-modified grouting mortars does not give much variation with increasing fly ash replacement for cement and sand-binder ratio. With increasing polymer-binder ratio, the flexural strength and adhesion in tension of St/Ac emulsion-modified grouting mortars increases, become nearly constant or reaches a maximum at a polymer-binder ratio of 5%. From the test results, St/Ac emulsion-modified grouting mortar with a polymer-binder ratio of 5%, a fly ash replacement of 10% for cement and sand-binder ratio of 1.0 is recommended as a grouting mortar for preplaced aggregate concrete.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 봄 학술논문 발표대회
• /
• pp.96-97
• /
• 2020

Polymer modified cement mortar (PCM) is commonly used as a repair material. However, in high-temperature environments such as fire, it is more likely to explode than cement mortar. The polymer is thermally decomposed at a high temperature to form a gas, and the gas remaining inside the structure increases the internal pressure to generate a burst. When an spalling occurs, the coating is peeled off and dropped, and high temperature is transmitted to the inside of the structure. In severe cases, even the reinforcing bar is exposed, which can lead to the collapse of the structural member due to severe loss of strength. In this study, in order to reduce spalling of PCM, a fiber mixing method was selected from the refractory method to find an appropriate blending ratio of fibers and polymers.