• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.4
• /
• pp.57-66
• /
• 2015

This paper is a preliminary study to apply the lightweight concrete slabs reinforced with GFRP (glass fiber reinforced polymer) bars to the bridge deck slabs or some other concrete structures. So, some different behaviors between the conventional steel reinforced concrete slab and the lightweight concrete slab reinforced with GFRP bars were investigated. For this purpose, a number of slabs were constructed and then the three point bending test and numerical analysis for these slabs were performed. The flexural test results showed that the lightweight concrete slabs reinforced with GFRP bars were failed by the shear failure due to the over-reinforced design. The weight and failure load of the GFRP bar reinforced lightweight concrete slabs were 72% and 58% of the steel reinforced concrete slab with the same dimensions, respectively. Results of the numerical analysis for these slabs using a commercial program, midas FEA, showed that the load-deflection curve could be simulated well until the shear failure of the slabs, but the applied loads and the deflections continuously increased even beyond the shear failure loads.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.41 no.3
• /
• pp.218-224
• /
• 2014

This study was designed to evaluate the effectiveness of 5% sodium fluoride-polyvinyl alcohol (NaF-PVA) tape influencing enamel remineralization by analysing enamel surface microhardness (SMH) and variation of ${\Delta}F$ of QLF. After enamel demineralizing of specimen, these 60 specimens with average KHN of microhardness ranging from 50 to 100 and with ${\Delta}F$ of QLF ranging from -15 to -25 were divided into four groups : group 1 (control group), group 2 (NaF-PVA), group 3 (fluoride varnish, FluoroDose$^{(R)}$ varnish), group 4 (Casein phosphopeptide-amorphous calcium phosphate, Tooth mousse plus$^{TM}$). These specimens were treated with materials and then immersed in artificial saliva. We measured remineralization rate each using surface microhardness (SMH) and Quantitative light-induced fluorescence digital (QLF-D). As a result, NaF-PVA tape is better than group 1, 4 and have comparable remineralization effect with group 3 (p < 0.05).

• Steel and Composite Structures
• /
• v.27 no.6
• /
• pp.691-702
• /
• 2018

This paper presents experimental and analytical results of fiber reinforced polymer (FRP) confined steel tubular columns under transverse impact loads. Influences of applied impact energy, thickness of FRP jacket and impact position were discussed in detail, and then the impact responses of FRP confined steel tubes were compared with bare steel tubes. The test results revealed that the FRP jacket contributes to prevent outward buckling deformation of steel at the clamped end and inward buckling of steel at the impact position. For the given applied impact energy, specimens wrapped with one layer and three layers of FRP have the lower peak impact loads than those of the bare steel tubes, whereas specimens wrapped with five layers of FRP exhibit the higher peak impact loads. All the FRP confined steel tubular specimens displayed a longer duration time than the bare steel tubes under the same magnitude of impact energy, and the specimen wrapped with one layer of FRP had the longest duration time. In addition, increasing the applied impact energy leads to the increase of peak impact load and duration time, whereas increasing the distance of impact position from the clamped end results in the decrease of peak impact load and the increase of duration time. The dynamic analysis software Abaqus Explicit was used to simulate the mechanical behavior of FRP confined steel tubular columns, and the numerical results agreed well with the test data. Analytical solution for lateral displacement of an equivalent cantilever beam model subjected to impact load was derived out. Comparison of analytical and experimental results shows that the maximum displacement can be precisely predicted by the present theoretical model.

• Journal of the Korean Society of Safety
• /
• v.31 no.3
• /
• pp.16-21
• /
• 2016

Carbon Fiber Reinforced Plastic(CFRP) composite with a higher specific strength and rigidity is more excellent than conventional metallic materials or other organic polymer of FRP. It has been widely used in vehicles, aerospaces and high technology industries which are associated with nuclear power fields. However, CFRP laminated composite has several disadvantages as like a delamination, matrix brittleness and anisotropic fibers that are the weak points of the crack initiation. In this present work, the reinforced silicon carbide(SiC) particles were added to the interlayer of CFRP laminates in order to mitigate the physical vulnerability affecting the cracking and breaking of the matrix in the CFRP laminated composite because of excellent specific strength and thermal shock resistance characteristics of SiC. The 1wt% of SiC particles were spread into the CFRP prepreg by using a spray coating method. After that, CFRP prepregs were laminated for the specimen. Also, the twill woven type CFRP prepreg was used because it has excellent workability. Thus the mechanical and fracture behaviors of the twill woven CFRP laminated composite reinforced with SiC particles were investigated with the acoustic emission(AE) method under a fracture test. The results show that the SiC particles enhance the mechanical and fracture characteristics of the twill CFRP laminate composite.

• International Journal of Highway Engineering
• /
• v.18 no.1
• /
• pp.57-62
• /
• 2016

PURPOSES : Reflection cracking has been one of the major causes of distress when asphalt pavement is laid on top of concrete pavement. This study evaluated the reflection cracking resistance of asphalt mixtures reinforced with asphalt embedded glass fiber and carbon fiber using a Texas Transportation Institute (TTI) overlay tester. METHODS : Different asphalt mixtures such as polymer-modified mastic asphalt (PSMA) and a dense graded asphalt mixture were reinforced with asphalt-embedded carbon fiber and glass fiber. For comparison purposes, two PSMA asphalt mixtures and one dense graded asphalt mixture were evaluated without fiber reinforcement. Two different overlay test modes, the repeated overlay test (R-OT) and monotonic overlay test (M-OT), were used to evaluate the reflection cracking resistance of asphalt mixtures at $0^{\circ}C$. In the R-OT test, the number of repeated load when the specimen failed was obtained. In the M-OT test, the tensile strength at the peak load and tensile strain were obtained. RESULTS : As expected, the fiber-reinforced asphalt mixture showed a higher reflection cracking resistance than the conventional nonreinforced asphalt mixtures based on the R-OT test and M-OT test. The dense graded asphalt mixture showed the least reflection cracking resistance and less resistance than the PSMA. CONCLUSIONS : The TTI overlay tester could be used to differentiate the reflection cracking resistance values of asphalt mixtures. Based on the R-OT and M-OT results, the carbon-fiber-reinforced asphalt mixture showed the highest reflection cracking resistance among the nonreinforced asphalt mixtures and glass-fiber-reinforced asphalt mixture.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.18 no.5
• /
• pp.29-34
• /
• 2014

Particulate reinforced composite is composed of hard particles and polymer matrix. This material has been widely applied for engineering industry such as automobile, construction and aerospace. For the safe application, it is important to assess crack resistance behavior. Especially in aerospace industry, crack could cause significant problem when the material is used for solid rocket fuel. Therefore, it is inevitable to estimate the characteristics of the crack propagation. In this study, crack propagation tests were conducted using particulate reinforced composite under crosshead rate 2.54 mm/min in the range of temperature $-60^{\circ}C$ to $60^{\circ}C$. The strain contour of surface for specimen was generated using digital image correlation method.

• Journal of the Microelectronics and Packaging Society
• /
• v.25 no.4
• /
• pp.155-161
• /
• 2018

A Si chip with the Cu/Au bumps of $100-{\mu}m$ diameter was flip-chip bonded using different anisotropic conductive adhesives (ACAs) onto the local stiffness-variant stretchable substrate consisting of polydimethylsiloxane (PDMS) and flexible printed circuit board (FPCB). The average contact resistances of the flip-chip joints processed with ACAs containing different conductive particles were evaluated and compared. The specimen, which was flip-chip bonded using the ACA with Au-coated polymer balls as conductive particles, exhibited a contact resistance of $43.2m{\Omega}$. The contact resistance of the Si chip, which was flip-chip processed with the ACA containing SnBi solder particles, was measured as $36.2m{\Omega}$, On the contrary, an electric open occurred for the sample bonded using the ACA with Ni particles, which was attributed to the formation of flip-chip joints without any entrapped Ni particles because of the least amount of Ni particles in the ACA.

• Applied Chemistry for Engineering
• /
• v.22 no.4
• /
• pp.439-443
• /
• 2011

It was performed to test the combustive properties of low density polyethylene and ethylene vinyl acetate (LDPE-EVA) mixture by the addition of magnesium hydroxide. Flame retardant of natural magnesium hydroxide was added to the mixture of LDPE-EVA in 40 to 80 wt% concentration. The composite was compounded to prepare specimen for combustive analysis by cone calorimeter (ISO 5660-1). Comparing with virgin LDPE-EVA, the specimens including the magnesium hydroxide had lower combustive properties. It is supposed that the combustion-retardation properties in the composites improved due to the endothermic decomposition of magnesium hydroxide. The specimens with magnesium hydroxide showed both the lower peak heat release rate (PHRR) and lower effective heat of combustion (EHC) than those of virgin polymer. As the magnesium hydroxide content increases, time to ignition increased and the peak heat release rate decreased.

• Corrosion Science and Technology
• /
• v.20 no.6
• /
• pp.451-465
• /
• 2021

In this investigation, electrochemical characteristics and damage behavior of 316L stainless steel polymer electrolyte membrane fuel cell(PEMFC) were analyzed by potentiodynamic and potentiostatic tests in cathode operating condition of PEMFC. As the result of potentiodynamic polarization test, range of passive region was larger than range of active region. In the result of potentiostatic test, damage depth and width, pit volume, and surface roughness were increased 1.57, 1.27, 2.48, and 1.34 times, respectively, at 1.2 V compared to 0.6 V at 24 hours. Also, as a result of linear regression analysis of damage depth and width graph, trend lines of damage depth and width according to applied potentials were 16.6 and 14.3 times larger, respectively. This demonstrated that applied potential had a greater effect on pitting damage depth of 316L stainless steel. The damage tendency values were 0.329 at 6 hours and 0.633 at 24 hours with applied potentials, representing rapid growth in depth direction according to the test times and applied potentials. Scanning electron microscopy images revealed that surface of specimen exhibited clear pitting damage with test times and applied potentials, which was thought to be because a stable oxide film was formed by Cr and Mo.

• Structural Engineering and Mechanics
• /
• v.80 no.5
• /
• pp.503-522
• /
• 2021

This paper investigates experimentally and numerically the influence of drilling process on the mechanical and thermomechanical behaviors of woven glass fiber reinforced polymer (GFRP) composite plate. Through the experimental analysis, a CNC machine with cemented carbide drill (point angles 𝜙=118° and 6 mm diameter) was used to drill a woven GFRP laminated squared plate with a length of 36.6 mm and different thicknesses. A produced temperature during drilling "heat affected zone (HAZ)" was measured by two different procedures using thermal IR camera and thermocouples. A thrust force and cutting torque were measured by a Kistler 9272 dynamometer. The delamination factors were evaluated by the image processing technique. Finite element model (FEM) has been developed by using LS-Dyna to simulate the drilling processing and validate the thrust force and torque with those obtained by experimental technique. It is found that, the present finite element model has the capability to predict the force and torque efficiently at various drilling conditions. Numerical parametric analysis is presented to illustrate the influences of the speeding up, coefficient of friction, element type, and mass scaling effects on the calculated thrust force, torque and calculation's cost. It is found that, the cutting time can be adjusted by drilling parameters (feed, speed, and specimen thickness) to control the induced temperature and thus, the force, torque and delamination factor in drilling GFRP composites. The delamination of woven GFRP is accompanied with edge chipping, spalling, and uncut fibers.