• 한국건축시공학회지
• /
• 제18권4호
• /
• pp.329-335
• /
• 2018

본 연구의 목적은 기존 콘크리트 건물의 단면확대 내진보강 기술에서 필요한 고유동 고접착성의 보강 모르타르 배합의 개발이다. 보강 모르타르의 목표성능(플로우 220mm 이상, 압축강도 30MPa, 접착강도 1MPa 이상)을 위해 물-결합재비, 잔골재-결합재비, 폴리머-결합재비, 증점제 사용 및 초속경시멘트의 혼입 등을 변수로 단계적으로 배합실험을 수행하였다. 모르타르의 접착강도는 기존 콘크리트의 다양한 면 처리 상태에 따라 평가하였다. 실험결과로부터 단면증설용 보강 모르타르의 배합을 위해 폴리머-결합재비는 10%, 초속경시멘트의 치환율은 5%가 추천될 수 있었는데, 이 배합은 초기 플로우 220 mm, 높은 초기강도 발현, 압축강도 35 MPa 그리고 접착강도 1.2 MPa 이상의 성능을 보였다.

• 한국건축시공학회지
• /
• 제4권3호
• /
• pp.93-100
• /
• 2004

In recent years, it has widely been studied on the light-weight composites for the purpose of the large space and thermal insulation of building structures. The purpose of this study is to evaluate the properties of light-weight composites made by binders as cement, resin and polymer cement slurry. The concrete composites are prepared with various conditions such as polymer-cement ratio, void-filling ratio, type of resin, filler content and light-weight aggregate content, tested for thermal conductivity. From the test results, the thermal conductivity of concrete composites with the binder of cement tends to decrease with increasing polymer-cement ratio, and to increase with increasing void-filling ratio. The thermal conductivity of concrete composites with the binder of resin are markedly affected by the light-weight aggregate content, type of resin and filler content. The composites made by polymer-modified concrete and polymer cement slurry have a good thermal insulation property. From the this study, we can recommend the proper mix proportions for thermal insulation Panel or concrete. Expecially. the thermal conductivity of concrete composites made by polyurethane resin is almost the same as that of the conventional expanded polystyrene resin.

• 한국수소및신에너지학회논문집
• /
• 제5권1호
• /
• pp.51-57
• /
• 1994

Compaction techniques of hydrogen storage alloy 'powders, to solve the problems due to disintegration during the cyclic hydriding and dehydriding, by using polytetrafluoroethylene (PTFE) and silicon sealant as a polymer binder were studied. Optimum conditions of compaction were as follows. Binder content, 10 % for PTFE and 5 % for silicon sealant ; particle size of alloy powders, $-25{\mu}m$ ; compacting pressure, $4ton/cm^2$. Compacts obtained were easily activated and had a good strength even after 30 cycles of hydriding and dehydriding. PTFE added compacts showed very good rate capability, however, in the silicon added compacts hydrogen absorption rate was somewhat slow because of higher elasticity and adhesiveness of the binder.

• 콘크리트학회논문집
• /
• 제18권1호
• /
• pp.117-124
• /
• 2006

본 연구에서는 복합 재질 폐플라스틱(PA)을 이용한 폴리머콘크리트의 작업성, 경화시간 및 경화수축에 미치는 결합재 첨가량 및 PA 혼입량의 영향에 대하여 검토하였다. 그 결과 복합 재질 폐플라스틱을 재활용한 폴리머콘크리트의 작업성은 결합재 첨가량, PA 혼입량 및 필러 혼입량의 증가에 따라 증가하는 경향을 나타냈다. 복합 재질 폐플라스틱을 이용한 폴리머콘크리트의 경화시간은 촉매제 첨가량 및 양생온도의 증가에 따라 짧아지는 경향을 나타냈다. 복합 재질 폐플라스틱을 이용한 폴리머콘크리트의 길이변화는 결합재 첨가량 및 PA 혼입량의 증가에 따라 증가하는 경향을 보였다. 본 연구 결과가 복합 재질 폐플라스틱 종말품의 재활용에 조금이나마 기여할 수 있을 것을 기대하며 향후 지속적인 연구개발을 통하여 더욱 광범위한 복합재질 폐플라스틱 종말품의 재활용이 이루어질 수 있을 것으로 판단된다.

• 콘크리트학회논문집
• /
• 제14권4호
• /
• pp.608-614
• /
• 2002

본 연구는 고로슬래그 미분말 및 SBR 라텍스를 혼입한 폴리머 시멘트 모르타르의 강도성상에 미치는 고로슬래그 치환율 및 폴리머-결합재비의 영향에 대해 검토하였다. 그 결과, 고로슬래그 미분말을 혼입한 오토클래이브 양생 폴리머 시멘트 콘크리트의 압축 및 인장강도는 고로슬래그 치환율이 증가함에 따라 증가하였고, 고로슬래그 치환율 40%에서 최대치에 달하였다. 고로 슬래그 미분말을 혼입한 오토클래이브 양생 폴리머 시멘트 콘크리트의 압축 및 인장강도는 폴리머-결합재 비의 증가에 따라 증가하는 경향을 보였다. 특히, 고로슬래그 치환율 40%의 오토클래이브 양생 SBR 혼입 폴리머 시멘트 콘크리트는 고로슬래그 미분말 및 SBR 미혼입 폴리머 시멘트 콘크리트보다 약 3배 이상의 높은 인장강도를 나타냈다. 이같이 높은 강도 개선은 SBR 라텍스의 혼입에 의해 시멘트 수화물과 골재간의 접착력이 개선되기 때문이라 판단된다.

• 폴리머
• /
• 제34권2호
• /
• pp.89-96
• /
• 2010

Methyl methacrylate(MMA), ethyl acrylate(EA), n-butyl acrylate(BA), styrene(St) 단량체를 수용성 개시제인 ammonium persulfate(APS)와 음이온 유화제인 sodium dodecyl benzene sulfonate(SDBS)를 사용하여 organic/organic core-shell 구조의 접착바인더를 중합 후 부직포와 피혁에 함침시키고 플라즈마 표면 처리 후 속도론적인 해석과 기계적인 물성을 평가하였다. Core-shell 바인더 중합시 전환율은 단량체의 조성이 등몰에서 MMA/EA, MMA/BA core-shell 복합입자 모두 90% 이상이 되었다. 등몰에서 부직포/부직포에 core-shell 복합입자를 함침시키고 플라즈마 처리 후의 상태접착 박리강도는 MMA/St, EA/BA, BA/MMA, EA/St, EA/MMA의 순으로 되었고, 또한 부직포/피혁에 core-shell 복합입자를 함침시키고 플라즈마 처리 후의 상태접착 박리강도는 MMA/BA, BA/EA, MMA/EA, St/MMA, EA/St의 순으로 되었다.

• Elastomers and Composites
• /
• 제58권1호
• /
• pp.44-56
• /
• 2023

Additive manufacturing (AM) or three-dimensional (3D) printing of metals has been drawing significant attention due to its reliability, usefulness, and low cost with rapid prototyping. Among the various AM technologies, fused deposition modeling (FDM) or fused filament fabrication is receiving much interest because of its simple manufacturing processing, low material waste, and cost-effective equipment. FDM technology uses metal-filled polymer filaments for 3D printing, followed by debinding and sintering to fabricate complex metal parts. An efficient binder is essential for producing polymer filaments and the thermal post-processing of printed objects. This study involved an in-depth investigation of and a fabrication route for a novel multi-component binder system with steel alloy powder (45 vol.%) ranging from filament fabrication and 3D printing to debinding and sintering. The binder system consisted of polyvinyl pyrrolidone (PVP) as a binder and thermoplastic polyurethane (TPU) and polylactic acid (PLA) as a carrier. The PVP binder held the metal components tightly by maintaining their stoichiometry, and the TPU and PLA in the ratio of 9:1 provided flexibility, stiffness, and strength to the filament for 3D printing. The efficacy of the binder system was examined by fabricating 3D-printed cubic structures. The results revealed that the thermal debinding and sintering processes effectively removed the binder/carrier from the cubic structures, resulting in isotropic shrinkage of approximately 15.8% in all directions. The scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) patterns displayed the microstructure behavior, phase transition, and elemental composition of the 3D cubic structure.

• 한국분말재료학회지
• /
• 제14권5호
• /
• pp.298-302
• /
• 2007

In recent years, a rapid increase in demands for the soft magnetic composite parts has been created and it has been tried to improve their properties by various processing methods, alloying elements and compaction parameters. Warm compaction method has been used for the reduction of residual stress, the improvement of magnetic properties and the higher densities. In this work, the effects of warm compaction and polymer binder on magnetic properties of Fe powder core were investigated. The sintering powder, Fe oxide, was ball-milled for 30n hours. And then ball-milled Fe oxide powder was reduced through hydrogen reduction process. The hydrogen reduced Fe powder and polymer binder were mixed by 3-D turbular mixer. And then the mixed powder was warm-compacted. The magnetic properties such as core loss and permeability were measured by B-H curve analyzer.

• 농업과학연구
• /
• 제37권2호
• /
• pp.277-283
• /
• 2010

Research on permeable pavement like asphalt and concrete pavement with porous structure has been increasing due to environmental and functional need such as reduction of run off and flood. This study was performed to evaluate void ratio, permeability coefficient, and compressive strength of permeable polymer concrete (PPC) using crushed and recycled coarse aggregate that is obtained from waste concrete. Also, 6 mm length of polypropylene fiber was used to increase toughness and interlocking between aggregate and aggregate surrounded by binder. Binder and filler used were unsaturated polyester resin and CaCO3, respectively. The mix proportions were determined to satisfy the requirement for the workability and slump according to aggregate sizes 5~10 mm. In the test results, regardless of kinds of aggregates and fiber contents, the void ratio, permeability coefficient and compressive strength of all types of PPC showed the higher than the criterion of porous concrete that is used in permeable pavement in Korea. Also, strengths of PPC with increase polypropylene fiber volume fraction showed slightly increased tendency due to increase binder with increase of fiber volume fraction. Accordingly, polypropylene fiber and recycled coarse aggregate can be used for permeable pavement.

• 한국건축시공학회지
• /
• 제12권3호
• /
• pp.275-283
• /
• 2012

본 연구는 철근 콘크리트 구조물의 장수명화를 위해 고성능 다기능 폴리머 시멘트 복합체의 개발을 목적으로, 우수한 성능을 갖는 VA/E/MMA (Vinyl Acetate/Ethylene/Methyl Methacrylate) 터폴리머 분말수지와 아질산형 하이드로칼루마이트를 병용한 폴리머 시멘트 모르타르의 염화물이온 침투 저항성, 중성화 저항성, 건조수축 및 철근부식 촉진시험을 통하여 그 내구성과 방청성을 검토하는 것이다. 그 결과, 폴리머 결합재비에 관계없이 칼루마이트의 치환에 의해 폴리머 시멘트 모르타르의 내구성이 일부 저하하는 경향을 보였으나, 이는 폴리머 결합재비의 증가에 따라 크게 개선되었다. 방청성의 경우 VA/E/MMA 분말수지 사용으로 시멘트 매트릭스 내 생성된 폴리머 필름에 의한 이온 및 가스투과 저항성 증대와 칼루마이트의 이온교환반응에 따른 염화물 이온 흡착 및 아질산 이온을 방출하는 자기방청기능에 의하여 우수한 방청효과를 보였다. 따라서, 철근콘크리트 구조물의 장수명화를 위해 VA/E/MMA 터폴리머 분말수지와 아질산형 하이드로칼루마이트의 병용에 의해 우수한 방청성과 내구성을 갖는 폴리머 시멘트 복합체의 개발이 가능할 것으로 판단된다.